Structural refinement, optical and ferroelectric properties of microcrystalline Ba(Zr0.05Ti0.95)O-3 perovskite

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Comparison of Physicochemical Surface Conditioning Methods for Adhesion of bis-GMA Resin Cement to Particulate Filler Composite and Surface Characterization

This study compared the effect of physicochemical surface conditioning methods on the adhesion of bis-GMA-based resin cement to particulate filler composite (PFC) used for indirect dental restorations. PFC blocks (N (block)=54, n (block)=9 per group) were polymerized and randomly subjected to one of the following surface conditioning methods: a) No conditioning (Control-C), b) Hydrofluoric acid (HF)etching for 60s (AE60), c) HF for 90s (AE90), d) HF for 120s (AE120), e) HF for 180s (AE180), and f) air-abrasion with 30 mu m silica-coated alumina particles (AB). The conditioned surfaces were silanized with an MPS silane, and an adhesive resin was applied. Resin composite blocks were bonded to PFC using resin cement and photo-polymerized. PFC-cement-resin composite blocks were cut under coolant water to obtain bar specimens (1mmx0.8mm). Microtensile bond strength test (mu TBS)was performed in a universal testing machine (1mm/min). After debonding, failure modes were classified using stereomicroscopy. Surface characterization was performed on a set of separate specimen surfaces using Scanning Electron Microscopy (SEM), X-Ray Dispersive Spectroscopy (XDS), X-Ray Photoelectron Spectroscopy (XPS), and Fourier Transform-Raman Spectroscopy (FT-RS). Mean mu TBS (MPa) of C (35.6 +/- 4.9) was significantly lower than those of other groups (40.2 +/- 5.6-47.4 +/- 6.1) (p<0.05). The highest mu TBS was obtained in Group AB (47.4 +/- 6.1). Prolonged duration of HF etching increased the results (AE180: 41.9 +/- 7), but was not significantly different than that of AB (p>0.05). Failure types were predominantly cohesive in PFC (34 out of 54) followed by cohesive failure in the cement (16 out of 54). Degree of conversion (DC) of the PFC was 63 +/- 10%. SEM analysis showed increased irregularities on PFC surfaces with the increased etching time. Chemical surface analyses with XPS and FT-RS indicated 11-70% silane on the PFC surfaces that contributed to improved bond strength compared to Group C that presented 5% silane, which seemed to be a threshold. Group AB displayed 83% SiO2 and 17% silane on the surfaces.

Large-Area Plasmonic Substrate of Silver-Coated Iron Oxide Nanorod Arrays for Plasmon-Enhanced Spectroscopy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of some volatile compounds evolved from the thermal decomposition of atenolol

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Síntese e caracterização de micropartículas de etilcelulose e seu uso na encapsulação do fungicida tebuconazole

Pós-graduação em Química - IQ

Sn(1-x)LaxO2 thin films deposited on AISI 304 stainless steel substrates

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Potentiated Electron Transference in alpha-Ag2WO4 Microcrystals with Ag Nanofilaments as Microbial Agent

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Very Intense Distinct Blue and Red Photoluminescence Emission in MgTiO 3 Thin Films Prepared by the Polymeric Precursor Method: An Experimental and Theoretical Approach

MgTiO3 (MTO) thin films were prepared by the polymeric precursor method with posterior spin-coating deposition. The films were deposited on Pt(111)/Ti/SiO2/Si(100) substrates and heat treated at 350 °C for 2 h and then heat treated at 400, 450, 500, 550, 600, 650 and 700 °C for 2 h. The degree of structural order−disorder, optical properties, and morphology of the MTO thin films were investigated by X-ray diffraction (XRD), micro-Raman spectroscopy (MR), ultraviolet− visible (UV−vis) absorption spectroscopy, photoluminescence (PL) measurements, and field-emission gun scanning electron microscopy (FEG-SEM) to investigate the morphology. XRD revealed that an increase in the annealing temperature resulted in a structural organization of MTO thin films. First-principles quantum mechanical calculations based on density functional theory (B3LYP level) were employed to study the electronic structure of ordered and disordered asymmetric models. The electronic properties were analyzed, and the relevance of the present theoretical and experimental results was discussed in the light of PL behavior. The presence of localized electronic levels and a charge gradient in the band gap due to a break in the symmetry are responsible for the PL in disordered MTO lattice.

Long-range and short-range structures of cube-like shape SrTiO3 powders: microwave-assisted hydrothermal synthesis and photocatalytic activity

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Efeito da aplicação de filmes de carbono tipo diamante por plasma no destorque de pilares de implantes com conexões cônicas internas

Pós-graduação em Odontologia Restauradora - ICT

Desenvolvimento de revestimentos siloxano-PMMA reforçados por nanotubos de carbono, óxido de grafite e óxido de grafite reduzido para aplicações anticorrosivas

Pós-graduação em Química - IQ

Preparo e caracterização de compósitos polímero/cerâmica com potencial aplicação como sensor multifuncional

Pós-graduação em Química - IQ

Descontaminação do resíduo industrial de couro, uma proposta para o desenvolvimento sustentável nos curtumes

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Fabricação e caracterização de cerâmicas multifuncionais à base de CaSr3Cu3-xTi4O12 para aplicações ópticas e eletro-eletrônicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeitos da terapia a laser associada ou não ao plasma rico em plaquetas na reparação do tecido muscular de ratos

Pós-graduação em Fisioterapia - FCT