Dielectric and viscoelastic properties of cross-linked polyethylene aged under multi stressing conditions

Different measurements were performed in cross-linked polyethylene (XLPE) employed as insulating material in coaxial cables that were field-aged and laboratory-aged under multi-stressing conditions at room temperature. Samples were peeled from the XLPE cable insulation in three different positions: just below the external semiconductor layer (outer layer), in the middle (middle layer) and just above the internal semiconductor layer of the cable (inner layer). The imaginary part of the electric susceptibility showed three peaks that obey the Dissado-Hill model. For laboratory-aged XLPE samples peeled from the inner and from the middle positions the peak at very low frequency region increased while in samples from the outer position a quasi-DC conduction process was observed. In medium frequency range a broadening of the peak was observed for all samples. Viscoelastic properties determined through dynamic mechanical analysis suggested that the aging generates processes that promoted changes of the crystallinity and the cross-linking degrees of the polymer. Fourier transform infrared spectroscopy (FTIR) measurements revealed an increase of oxidation products (esters), evidence of polar residues of the bow-tie tree and the presence of cross-linking by-products (acetophenone). Optical and scanning electronic microscope (SEM) measurements in aged samples revealed the existence of voids and bow-tie trees that were formed during aging in the middle region of the cable.

Porous polyethylene for tissue engineering applications in diabetic rats treated with calcitonin: Histomorphometric analysis

Purpose: The purpose of this work was to study the bone tissue reaction after porous polyethylene (Polipore) implantation into surgical defects in the parietal bones of rats with streptozotocin-induced diabetes, treated with salmon calcitonin. Materials and Methods: Porous polyethylene implants were placed in bone defects created in 36 adult female rats. The rats were divided into 3 equal groups: diabetic treated with calcitonin (DCa), diabetic (D), and control (C). The animals of the DCa group received applications of salmon calcitonin on alternating days immediately after the surgery until sacrifice. The rats were sacrificed after 15, 30, 60, and 90 days, and the defects were examined histologically and statistically through histomorphometric analysis. Results: Histomorphometric analysis showed that there was no statistically significant difference in the mean quantity of inflammatory cells among all study groups after 15 and 90 days. At 30 days, a statistically significant difference was observed between the D and C groups and the D and DCa groups. At 60 days, there was no statistically significant difference between the D and DCa groups. Discussion: Porous polyethylene can be considered an option for implant material when there are investigations that prove its biocompatibility and stability in the host tissues. Salmon calcitonin positively aided the bone repair and attenuated the inflammatory response until 30 days after the surgery. Conclusion: Porous polyethylene was tolerated by the host tissues in all groups, and moderate chronic inflammatory reaction was observed up to the 90-day period. Salmon calcitonin attenuated the inflammatory response up until 30 days.

Production of four cultivars of iceberg lettuce, under protected cultivation, with and without black polyethylene ground cover

The aim of the work was to evaluate the performance of four cultivars of iceberg lettuce, in a greenhouse, with and without ground cover. The experimental design adopted was that of subdivided parcels, where parcels were provided with and without ground cover consisting of black polyethylene and the subparcels consisted of the cultivars. There were three repetitions per treatment and six central plants of each parcel were evaluated. Drip irrigation was utilized. The cultivars studied were: 'Laurel', 'AF-389', 'Mayara' and 'Tainá'. The seeds were planted in Styrofoam trays with 288 cells containing the substrate Plantmax Hortaliças® A. The trays were kept in a greenhouse until transplanting, 25 days after seeding. The parameters examined were: fresh weight of the aerial part per plant, longitudinal (DL) and transverse (DT) diameters of the head, height of the plant and mean number of leaves per plant. Only among the cultivars there were significant differences in transverse and longitudinal diameters of the head and height of the plant. No significant interactions were detected between ground cover and cultivars. With regard to longitudinal and transverse diameters, 'AF-839' (DL = 27.11 cm; DT = 24.53 cm) showed smaller diameters than those of 'Laurel' (DL = 31.13 cm; DT = 30.55 cm), but did not differ from the other cultivars. In regard to height of the plants, 'Laurel' (20.66 cm) had the greatest value and 'AF-839' (16.02 cm) the lowest. The cultivars did not differ with respect to mean number of leaves and fresh weight of the aerial part of the plant. It is concluded that there were no significant differences in the cultivation of the iceberg lettuce with and without ground cover. The cultivar 'Laurel' stood out with respect to longitudinal and transverse diameters and height of the plant, only differing from the 'AF-839' with regard to the diameters.

Evaluation of the biocompatibility of root canal sealers using subcutaneous implants

The purpose of this study was to evaluate in vivo the biocompatibility of Endométhasone, Pulp Canal Sealer EWT and AHPlus root canal sealers after implantation in rat connective tissue. Twenty-four Wistar-Furth rats were used. Polyethylene tubes were filled with the sealers and implanted into specific dorsal subdermal tissue sites of the rats. Implants were removed after 3, 7 and 30 days, fixed and processed for glycol methacrylate-embedding technique to be examined microscopically. On the 3rd day, there was a mild inflammatory reaction to Pulp Canal Sealer EWT implants, but a severe response to the other sealers with presence of acute inflammatory cells. On the 7th day, tissue organization was more evident with attenuation of the inflammatory reaction, especially for the AH-Plus implants. On the 30th day, connective tissue with few inflammatory cells was observed in contact with all sealer implants. In this time interval, the tissue in contact with Pulp Canal Sealer EWT implants was more organized, while the tissue close to Endométhasone and AH-Plus implants showed a mild persistent inflammatory reaction and had similar results to each other. In conclusion, the sealers had a similar pattern of irritation, which was more severe in the beginning and milder with time, in such a way that all sealers showed a persistent mild reaction. Pulp Canal Sealer EWT yielded better tissue organization than Endométhasone and AH-Plus, which, in turn, showed similar results to each other.

Polyethylene gel in the subcutaneous tissue of rats: Histopathologic and systemic evaluation

Purpose: To evaluate the histological and systemic response to subcutaneous injection of polyethylene gel in rats. Methods: Twenty-one white male rats were divided into 3 groups (G): G1 and G2 received subcutaneous polyethylene gel injection in the dorsal midline and were sacrificed at 30 and 60 postoperative days, respectively. G3 was not exposed to the polyethylene gel and was sacrificed after 60 days. Blood levels of lactate dehydrogenase (LDH), creatine kinase (CK), and alkaline phosphatase (ALP) were evaluated. The heart, kidney, liver, adrenal gland, injection site, and adjacent tissues were histologically examined. The results were submitted to statistical analysis. Results: There was no clinical evidence of extrusion, reduction of the injected volume, or abnormalities in the adjacent tissues. Blood levels of CK and LDH were normal and similar in all groups. ALP levels were significantly lower in G2 than in G1 and G3. The systemic organs were normal on histological examination in the 3 groups evaluated. Microscopically, the polyethylene gel was surrounded by a thin pseudocapsule formation and minimal inflammatory cell response, which decreased from G1 to G2. Conclusion: The subcutaneous injection of polyethylene gel in rats elicited minimal local inflammatory response and no systemic side effects. Copyright © 2008 Informa Healthcare USA, Inc.

Biocompatibility of acetazolamide pastes in the subcutaneous tissue of rats

This aim of this study was to investigate the biocompatibility of two experimental acetazolamide (AZ)-based pastes in the subcutaneous tissue of rats. Both pastes contained AZ as the main component in similar concentration. The vehicle in experimental paste 1 was saline, while experimental paste 2 was prepared with propylene glycol. Sixty polyethylene tubes were sealed at one end with gutta-percha (GP), which served as a control. Half of the tubes were flled with paste 1 and half with paste 2. The tubes were implanted in the subcutaneous tissue of 15 rats, being 4 tubes for each animal. The animals were killed 7, 15 and 45 days after surgery and the specimens were processed in laboratory. The histological sections were stained with hematoxylin and eosin and were analyzed by light microscopy. Scores were assigned to level of infammatory process: 1- none; 2- mild; 3- moderate; 4- severe. The data were analyzed statistically by the Kruskal-Wallis test (p≤0.05). Paste 1 produced an infammatory process at 7 days. However, the intensity of this infammation decreased with time and was nearly absent at 45 days. No statistically signifcant difference (p>0.05) was observed between the control (GP) and paste 1. However, paste 2 produced infammatory response at all study periods and differed signifcantly (p<0.05) from the control. In conclusion, in the present study, the experimental AZ-based paste 1 was considered as biocompatible as the control matrial (GP), while experimental paste 2 was irritating to rat subcutaneous tissue.

Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures

This paper presents results from stress cracking (SC) tests performed in both fresh and exposed high density polyethylene (HDPE) geomembranes (GM). The HDPE GMs were exposed to ultraviolet radiation, thermal aging (air oven) and tested for chemical compatibility with sodium hydroxide. Stress cracking tests in both fresh and degraded samples were performed in accordance to ASTM D5397: Notched Constant Tensile Load Test (NCTL) and Single Point-Notched Constant Tensile Load Test (SP-NCTL). The results of the NCTL showed that the geomembrane degradation process can be considered to be a catalyst for the phenomenon of SC because it caused a 50% to 60% reduction in stress crack resistance. The most resistance reduction was observed for the sample under chemical compatibility with sodium hydroxide. For the SP-NCTL, the results showed that the samples maintain the same trend verified in the NCTL. The largest resistance reduction was evidenced in samples undergoing ultraviolet degradation. © 2012 ejge.

Thermo-gravimetric analysis (TGA) after different exposures of high density polyethylene (HDPE) and poly vinyl chloride (PVC) geomembranes

This paper presents the results of thermogravimetric analysis (TGA) tests in PVC (1.0; 2.0 mm) and HDPE (0.8; 2.5 mm) geomembranes exposed to weathering and leachate after 30 months. The aim of this paper is the comparison of fresh and exposed samples to assess the degradation process concerning the total loss of mass of geomembranes. The exposure was conducted in accordance with the recommendations of ASTM standards. The TGA tests were carried out according to ASTM D6370 and E2105. Results show, for instance, that for PVC geomembrane the largest reductions of plasticizers occurred for samples exposed to weathering. The loss of plasticizers after the exposure contributed to the decrease of deformation and consequent increase in stiffness. TGA tests shows to be a valuable tool to control the quality of the materials. © 2012 ejge.

Degree of conversion of polymer-matrix composite assessed by FTIR analysis

Aims and objectives: The behavior of polymer-matrix composite is dependent on the degree of conversion. The aim of this study was to evaluate the degree of conversion of two resin cements following storage at 37°C immediately, 24 and 48 hours, and 7 days after light-curing by FTIR analysis. Materials and methods: The specimens were made in a metallic mold and cured with blue LED with power density of 500 mW/cm2 for 30 seconds. The specimens were pulverized, pressed with KBr and analyzed with FTIR following storage times. Statistical analysis used: ANOVA (two-way) and Tukey's post hoc. Results: To the polymer-matrix composites between 24 and 48 hours does not show a significant increase (p > 0.05), however, the highest values were found after 7 days. Conclusion: The polymer-matrix composites used in this study showed similarity on the degree of conversion and increased of according to the time of storage.

Solid-state hydrolysis of postconsumer polyethylene terephthalate after plasma treatment

Plasma treatments were applied on the surface of postconsumer polyethylene terephthalate (PET) bottles to increase their wettability and hasten the subsequent hydrolysis process. Sixty-four treatments were tested by varying plasma composition (oxygen and air), power (25-130 W), pressure (50-200 mTorr), and time (1 and 5 min). The best treatment was the one applied in air plasma at 130 W and 50 mTorr for 5 min, as it provided the lowest contact angle, 9.4°. Samples of PET before and after the optimized plasma condition were subjected to hydrolysis at 205°C. Although the treatment changed only a thin surface layer, its influence was evident up to relatively high conversion rates, as the treated samples presented more than 40% higher conversion rates than the untreated ones after 2 h of reaction. Infrared spectroscopy showed that the terephthalic acid obtained from 99% of depolymerization was similar to the commercial product used in PET synthesis. © 2012 Wiley Periodicals, Inc.

Characterization of high density polyethylene (HDPE) reinforced with banana peel fibers

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The use of NaOCl in combination with CHX produces cytotoxic product

Objectives: The combination of sodium hypochlorite (NaOCl) and chlorhexidine (CHX) yields a precipitate potentially toxic (PPT). The aim of this study was to evaluate the tissue response to implanted polyethylene tubes filled with PPT-soaked fibrin sponge. Methods: Forty rats received four polyethylene tubes each; each tube was filled with fibrin sponge soaked by 2.5 % NaOCl, 2.0 % CHX, PPT (2.5 % NaOCl plus 2.0 % CHX), or not soaked (control). The observation time points were 7, 15, 30, 60, and 90 days. At each time point, eight animals were killed, and the tubes and surrounding tissues were removed, fixed, and prepared for light microscopic analysis by performing glycol methacrylate embedding, serial cutting into 3-μm sections, and hematoxylin-eosin staining. Qualitative and quantitative evaluations of the reactions were performed. Results were statistically analyzed by Kruskal-Wallis test (p < 0.05). Results: All chemical solutions caused moderate reactions at 7 days. On day 30, PPT group was more cytotoxic than the control group and the CHX group (p < 0.05). On days 15 and 60, PPT group was more cytotoxic than the control group (p < 0.05). On day 90, there was no statistically significant difference between the different groups. Conclusion: PPT is more cytotoxic than NaOCl and CHX alone, particularly in the short term. Clinical significance: Protocols which suggest the use of CHX and NaOCl must be revised because this mixture produces cytotoxic product. © 2013 Springer-Verlag Berlin Heidelberg.

Avaliação da biocompatibilidade e citotoxicidade dos cimentos: Endo-CPM-Sealer, Sealapex e Ângelus MTA

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of Meteorological Elements and Lettuce (lactuca Sativa, L.) Yield Related to Geographic Orientation of Polyethylene Greenhouses

O experimento foi realizado na área experimental do Departamento de Engenharia Rural da Faculdade de Ciências Agronômicas – Unesp/Botucatu, Estado de São Paulo, em duas estufas dispostas em diferentes orientações geográficas, Leste/Oeste e Norte/Sul. A alface (Lactuva sativa L.) cv. Elisa foi cultivada em ambas estufas, sendo semeada em 05/05/99, transplantada em 29/05/99 e colhida em 31/06/99. Utilizou-se tensiômetros para monitorar o potencial de água no solo para realizar o manejo do sistema de irrigação por gotejamento. Microevaporímetros eqüidistantes de 3 m e colocados em 3 alturas, 0.50, 1.00 e 1.50 m, termohigrógrafos e tanques Classe “A” foram instalados nas duas estufas. Através de análise geoestatística, não se observou dependência espacial nem variabilidade espacial da evaporação nas duas estufas. Entretanto, a altura dos evaporímetros apresentou diferenças significativas: a evaporação à altura de 1.50 foi menor que nas outras duas.As médias de temperatura, umidade relativa e déficit de pressão de vapor do arnão diferiram estatisticamente entre as estufas e o ambiente externo. Os valores médios de evaporação de água no tanque Classe A instalado fora das estufas diferiram estatisticamente quando comparados com os instalados no interior das estufas, porém, entre as orientações não se constatou diferença significativa. Pôde-se verificar que não houve diferença significativa das características agronômicas da alface em ambas orientações estudadas. No entanto, houve diferença significativa para essas características entre os canteiros no interior das mesmas, havendo variância espacial para os dados de matéria fresca apenas na estufa N/S.

Cross linked Poly (4-Vinylpyridine-Ethylene Glycol Dimethacrylate) Used for Preconcentration of Cd(II) and its Determination by Flow Injection Flame Atomic Absorption Spectrometry