Evaluation of marginal microleakage in Class II cavities: Effect of microhylolrid, flowable, and compactable resins

Objective: the goal of the present study was to evaluate the microleakage on the cementum/dentin and enamel surfaces in Class 11 restorations, using different kinds of resin composite (microhybrid, flowable, and compactable). Method and materials: Forty human caries-free molars were extracted and selected. Eighty Class 11 standardized cavities were made in the cervical wall at the cementoenamel junction (CEJ) and at the mesial and distal surfaces. The teeth were divided into four groups: G1 - adhesive system + microhybrid resin composite Z100; G2 - adhesive system + compactable resin composite Prodigy Condensable; G3 - adhesive system + flowable resin composite Revolution + Z1 00 resin composite; G4 - adhesive system + Revolution fluid resin + compactable resin composite Prodigy Condensable. The adhesive system used in this study was Scotchbond Multi-Purpose Plus. The specimens were thermocycled in baths of 5degreesC and 55degreesC for 1,000 cycles and immersed in 50% silver nitrate solution. The specimens then were sectioned and evaluated on degree of dye penetration. Results: the results were evaluated using the nonparametric Kruskall-Wallis test, which showed a statistically significant difference between groups G1 and G4, G2 and G4, and G3 and G4. Conclusions: None of the materials was able to eliminate the marginal microleakage at the cervical wall; the application of a low-viscosity resin composite combined with a compactable resin composite significantly decreased the microleakage.

Influence of Er,Cr: YSGG laser on bond strength of self-adhesive resin cement

The purpose of this study was to investigate the bond strength of fiber post previously laser treated root canals. Forty single-rooted bovine teeth were endodontically treated, randomly and equally divided into two main groups according to the type of pretreatment: G1: 2.5% NaOCl (control group); and G2: Er,Cr:YSGG laser. Each group was further subdivided into 2 groups based on the category of adhesive systems/ luting materials used: a: an etch-and-rinse resin cement (Single Bond/RelyX ARC; 3M ESPE), and b: a self-adhesive resin cement (Rely X Unicem; 3M ESPE). Three 1.5 mm thick slabs were obtained per root and the push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. Data were analyzed by ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. Analysis of variance showed no statistically significant difference (p > 0.05) among the groups G1a (25.44 ± 2.35) and G1b (23.62 ± 3.48), G2a (11.77 ± 2.67) and G2b (9.93 ± 3.37). Fractures were observed at the interface between the dentin and the resin in all groups. The Er,Cr:YSGG laser irradiation did not influence on the bond strength of the resin cements and the etch-and-rinse resin cement had better results on bond strength than self-adhesive resin cement.

Fracture resistance of bleached teeth restored with different procedures

This study evaluated the fracture resistance of teeth submitted to internal bleaching and restored with different non-metallic post. Eighty mandibular incisors were endodontically treated and randomly divided in 10 groups (n = 8): G1- restored with composite resin (CR), G2- CR + fiber-reinforced composite post (FRC, Everstick post, Sticktech) cemented with resin cement self-etch adhesive (RCS, Panavia F 2.0, Kuraray), G3- CR + FRC + self-adhesive resin cement (SRC, Breeze, Pentral Clinical), G4- CR+ glass fiber post (GF, Exacto Post, Angelus) + RCS, G5- CR + GF + SRC. The G6 to G10 were bleached with hydrogen peroxide (HP) and restored with the same restorative procedures used for G1 to G5, respectively. After 7 days storage in artificial saliva, the specimens were submitted to the compressive strength test (N) at 0.5 mm/min cross-head speed and the failure pattern was identified as either reparable (failure showed until 2 mm below the cement-enamel junction) or irreparable (the failure showed <2 mm or more below the cement-enamel). Data were analyzed by ANOVA and Tukey test (α = 0.05). No significant difference (p < 0.05) was found among G1 to G10. The results suggest that intracoronal bleaching did not significantly weaken the teeth and the failure patterns were predominately reparable for all groups. The non-metallic posts in these teeth did not improve fracture resistance.

Oral Hygiene Indirect Instruction and Periodic Reinforcements: Effects on Index Plaque in Schoolchildren

The aim of this study was to evaluate the effectiveness of the indirect instruction and the influence of the periodic reinforcement on the plaque index in schoolchildren. Forty schoolchildren aged from 7 to 9 years old were selected from a public school. After determining the initial O'Leary Plaque Index all schoolchildren were submitted to a program for oral hygiene through indirect instruction - "The Smiling Robot". The schoolchildren were divided into 2 groups: with and without motivation reinforcement. The index plaque exam was performed in both groups after 30, 60 and 90 days of the educational program. Comparing the groups, the plaque index decreasing could be observed in the group with reinforcement with statistically significant difference. For the group with reinforcement, statistically significant difference among the evaluations was found. For the group without reinforcement, significant decrease in the plaque index was found after 30 days when compared to the first, third and fourth evaluations. The indirect instruction with "The Smiling Robot "promoted a positive initial impact on the decrease of plaque index in the schoolchildren. The periodic reinforcements showed snore suitable results and significant reduction of the plaque index in the course of the evaluations.

Root Canal Area Increase Promoted by the EndoSequence and ProTaper Systems: Comparison by Computed Tomography

Introduction: The aim of this study was to compare the increase of the root canal area after instrumentation with EndoSequence or ProTaper rotary systems. Methods: Twenty-two mesial root canals from mandibular molars were instrumented. Teeth were mounted on a base, numbered, and divided into 2 groups; teeth from 1-11 (PT group) were instrumented by using the ProTaper system, and teeth from 12-22 (ES group) were instrumented by using the EndoSequence system. Cone beam computed tomography was performed on all teeth before and after instrumentation. Measurements at 3,5, and 7 mm as well as differences in instrument performance were statistically compared by the Student t test at 5% significance level. Results: Both systems increased significantly the root canal area (P < .05) at all levels. Comparison between the rotary systems showed significantly greater increase (P < .05) for EndoSequence at 3 mm, with no statistically significant difference (P < .05) at the other levels. Conclusions: Both rotary systems increased significantly the root canal area. (J Endod 2010;36:1179-1182)

The effects of canal preparation and filling on the incidence of dentinal defects

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of the Light-Curing Unit, Storage Time and Shade of a Dental Composite Resin on the Fluorescence

The aim of this study was to determine the influence of three light-curing units, storage times and colors of the dental composite resin on the fluorescence. The specimens (diameter 10.0 +/- 0.1 mm, thickness 1.0 +/- 0.1 mm) were made using a stainless steel mold. The mold was filled with the microhybrid composite resin and a polyethylene film covered each side of the mold. After this, a glass slide was placed on the top of the mold. To standardize the top surface of the specimens a circular weight (1 kg) with an orifice to pass the light tip of the LCU was placed on the top surface and photo-activated during 40 s. Five specimens were made for each group. The groups were divided into 9 groups following the LCUs (one QTH and two LEDs), storage times (immediately after curing, 24 hours, 7 and 30 days) and colors (shades: A(2)E, A(2)D, and TC) of the composite resin. After photo-activation, the specimens were storage in artificial saliva during the storage times proposed to each group at 37 C and 100% humidity. The analysis of variance (ANOVA) and Tukey's post-hoc tests showed no significant difference between storage times (immediately, 24 hours and 30 days) (P > 0.05). The means of fluorescence had difference significant to color and light-curing unit used to all period of storage (P < 0.05). The colors had difference significant between them (shades: A2D < A2E < TC) (P < 0.05). The Ultraled (LED) and Ultralux (QTH) when used the TC shade showed higher than Radii (LED), however to A2E shade and A2D shade any difference were found (P > 0.05).

Effect of temporary cements on the shear bond strength of luting cements

Objective: The purpose of this study was to evaluate, by shear bond strength (SBS) testing, the influence of different types of temporary cements on the final cementation using conventional and self-etching resin-based luting cements. Material and Methods: Forty human teeth divided in two halves were assigned to 8 groups (n=10): I and V (no temporary cementation); II and VI: Ca(OH)(2)-based cement; III and VII: zinc oxide (ZO)based cement; IV and VIII: ZO-eugenol (ZOE)-based cement. Final cementation was done with RelyX ARC cement (groups I to IV) and RelyX Unicem cement (groups V to VIII). Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. Results: Means were (MPa): I - 3.80 (+/- 1.481); II - 5.24 (+/- 2.297); III - 6.98 (+/- 1.885); IV - 6.54 (+/- 1.459); V - 5.22 (+/- 2.465); VI - 4.48 (+/- 1.705); VII - 6.29 (+/- 2.280); VIII - 2.47 (+/- 2.076). Comparison of the groups that had the same temporary cementation (Groups II and VI; III and VII; IV and VIII) showed statistically significant difference (p<0.001) only between Groups IV and VIII, in which ZOE-based cements were used. The use of either Ca(OH) 2 based (Groups II and VI) or ZO-based (Groups III and VII) cements showed no statistically significant difference (p>0.05) for the different luting cements (RelyX (TM) ARC and RelyX (TM) Unicem). The groups that had no temporary cementation (Groups I and V) did not differ significantly from each other either (p>0.05). Conclusion: When temporary cementation was done with ZO- or ZOE-based cements and final cementation was done with RelyX ARC, there was an increase in the SBS compared to the control. In the groups cemented with RelyX Unicem, however, the use of a ZOE-based temporary cement affected negatively the SBS of the luting agent used for final cementation.

Bond strength of an adhesive system irradiated with Nd : YAG laser in dentin treated with Er : YAG laser

The purpose of this in vitro study was to verify through micro tensile bond test the bond strength of an adhesive system irradiated with Nd:YAG laser in dentine previously treated with Er:YAG laser. Twenty caries free extracted human third molars were used. The teeth were divided in four experimental groups (n = 5): (G1) control group; (G2) irradiation of the adhesive system with the Nd:YAG laser; (G3) dentin treatment with Er:YAG laser; (G4) dentin treatment with Er:YAG laser followed by the irradiation of the adhesive system with Nd:YAG laser. The Er:YAG laser fluency parameter for the dentin treatment was of 60 J/cm(2). ne adhesive system was irradiated with the Nd:YAG laser with fluency of 100 J/cm(2). Dental restorations were performed with Adper Single Bond 2/Z250. One tooth from each group was prepared for the evaluation of the adhesive interface under SEM and bond failure tests were also performed and evaluated. The statistical analysis showed statistical significant difference between the groups G1 and G3, G1 and G4, G2 and G3, and G2 and G4; and similarity between the groups G1 and G2, and G3 and G4. The adhesive failures were predominant in all the experimental groups. The SEM analysis showed an adhesive interface with features confirming the results of the mechanical tests. The Nd:YAG laser on the adhesive system did not influence the bond strength in dentin treated or not with the Er:YAG laser.

Efeitos de dois procedimentos educacionais sobre os sintomas musculoesqueléticos em trabalhadores administrativos

Objective: To investigate the effect of applying two educational programs (one using a self-instructional approach and the other using a traditional approach similar to educational workshops), on the perceived frequency of musculoskeletal symptoms. Methods: A quasi-experimental study was conducted in 94 office workers in a public company. The participants were divided into three groups through simple randomized sampling with no replacement, The first group (32 employees) underwent a traditional/workshop program, the second (28) used a self-instructional manual and the third (34) was a Control Group. The frequency of musculoskeletal symptoms was measured by means of the Nordic Musculoskeletal Questionnaire, at the beginning of the program and 30 days after its completion. The statistical analysis consisted of descriptive statistics, a nonparametric analysis of variance technique for a repeated measure model in three independent groups and the Goodman test. Results: From the data collected in pre and post-test comparisons, it was observed that the traditional/workshop educational program significantly reduced the frequency of musculoskeletal symptoms over the final seven days. For the self-instructional manual group and control group, no difference was observed in the frequency of musculoskeletal symptoms, Conclusions: It could be concluded that the interventions. particularly the traditional approach using educational workshops, had a positive effect on the individuals' actions. Despite the complexity of some of the preventive measures needed, there was a reduction in musculoskeletal symptoms of the participants during work.

Aldosterone is not Involved in the Ventricular Remodeling Process Induced by Tobacco Smoke Exposure

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)