Effect of microwave treatments on dimensional accuracy of maxillary acrylic resin denture base

Microwave energy has been used as an alternative method for disinfection and sterilization of dental prostheses. This study evaluated the influence of microwave treatment on dimensional accuracy along the posterior palatal border of maxillary acrylic resin denture bases processed by water-bath curing. Thirty maxillary acrylic bases (3-mm-thick) were made on cast models with Clássico acrylic resin using routine technique. After polymerization and cooling, the sets were deflasked and the bases were stored in water for 30 days. Thereafter, the specimens were assigned to 3 groups (n=10), as follows: group I (control) was not submitted to any disinfection cycle; group II was submitted to microwave disinfection for 3 min at 500 W; and in group III microwaving was done for 10 min at 604 W. The acrylic bases were fixed on their respective casts with instant adhesive (Super Bonder®) and the base/cast sets were sectioned transversally in the posterior palatal zone. The existence of gaps between the casts and acrylic bases was assessed using a profile projector at 5 points. No statistically significant differences were observed between the control group and group II. However, group III differed statistically from the others (p<0.05). Treatment in microwave oven at 604 W for 10 min produced the greatest discrepancies in the adaptation of maxillary acrylic resin denture bases to the stone casts.

Restoration of severely decayed primary incisors using indirect composite resin restoration technique

Caries of primary incisors is a common problem in paediatric dentistry in some countries. The restoration of primary incisors which have been severely damaged by early childhood caries or trauma is also a difficult challenge for clinicians. This case report describes an indirect technique for the restoration of primary anterior teeth using composite resin reinforced with a fibreglass post. Over a one-year period, the crowns have demonstrated good retention and aesthetic results. The restorations were provided in two short chair-side sections, with satisfactory patient cooperation. © 2005 BSPD and IAPD.

Puncture wounds by driftwood catfish during bucket baths: Local habits of riverside people and fish natural history in the Amazon

Objective. - To assess the prevalence of stings by small spiny driftwood catfish (carataí) of the genus Centromochlus (Auchenipteridae) accidentally caught in buckets during bucket bathing by riverside people along the Brazilian Amazon and to determine the probability of catching specimens of these fish during random throws of a bucket into the river. Methods. - We interviewed 27 adult residents living at the confluence of the Negro and Solimões rivers in Brazil regarding whether or not they had ever been stung by driftwood catfish while bucket bathing. To assess the likelihood of catching catfish in bathing buckets, we randomly threw a typical plastic bucket used for bathing in 4 series of 10 throws into the river at dusk or night around a floating house. Results. - Seventeen of the 27 subjects (63%) reported being injured by driftwood catfish during bucket bathing. Three individuals (17.6%) had been injured 2 to 3 times, totaling 23 puncture accidents. All stings occurred at dusk or early night. In the 4 series of 10 bucket throws, we caught 3 driftwood catfish (in 1 series we did not catch any fish). Thus, the chance of catching a driftwood catfish in a single bucket throw at dusk was slightly less than 10%. Conclusions. - The prevalence of stings by driftwood catfish to people bucket bathing in this section of the Brazilian Amazon is high, partly because of the relatively high chances of catching these small catfish during random throws of a bathing bucket into the river.

Weight loss and surface roughness of hard chairside reline resins after toothbrushing: Influence of postpolymerization treatments

Purpose: To evaluate the effect of 2 postpolymerization treatments on toothbrushing wear (weight loss) and surface roughness of 3 autopolymerized reline resins-Duraliner II (D) (Reliance Dental), Kooliner (K) (Coe Laboratories), and Tokuso Rebase Fast (T) (Tokuyama Dental)-and 1 heat-polymerized resin, Lucitone 550 (L) (Dentsply International). Materials and Methods: Specimens (40 x 10 x 2mm) of each material (n = 24) were prepared and divided into 3 groups: control (no postpolymerization treatment); water bath (immersion in water at 55°C); and microwave (microwave irradiation). Specimens were dried until constant weight was achieved and the surface roughness (Ra) was measured. Tests were performed in a toothbrush machine using 20,000 strokes of brushing at a weight of 200 g, with the specimens immersed in 1:1 dentifrice/water slurry. Specimens were reconditioned to constant weight and the weight loss (mg) and surface roughness were evaluated. Data were analyzed by 2-way analysis of variance and followed by Tukey test (α = .05). Results: In the control group, the weight loss of materials D and T was lower (P < .05) than that of L. No differences among materials were found after postpolymerization treatments (P > .05). The weight loss of material T (control = 0.5 mg) was significantly increased (P < .05) after postpolymerization treatments (water bath = 1.9 mg; microwave = 1.8 mg). For materials K and T, the toothbrushed surface roughness was higher (P < .05) after microwave and waterbath postpolymerization treatments. Material L showed increased surface roughness after microwave postpolymerization treatment. Conclusion: The toothbrushing wear resistance of L was not superior to the reline resins. The postpolymerization treatments did not improve the toothbrushing wear resistance of the materials and produced an increased surface roughness for materials L, K, and T.

Effect of post-polymerization heat treatments on the cytotoxicity of two denture base acrylic resins

Introduction: Most denture base acrylic resins have polymethylmethacrylate in their composition. Several authors have discussed the polymerization process involved in converting monomer into polymer because adequate polymerization is a crucial factor in optimizing the physical properties and biocompatibility of denture base acrylic resins. To ensure the safety of these materials, in vitro cytotoxicity assays have been developed as preliminary screening tests to evaluate material biocompatibility. 3H-thymidine incorporation test, which measures the number of cells synthesizing DNA, is one of the biological assays suggested for cytotoxicity testing. Aim: The purpose of this study was to investigate, using 3H-thymidine incorporation test, the effect of microwave and water-bath post-polymerization heat treatments on the cytotoxicity of two denture base acrylic resins. Materials and Methods: Nine disc-shaped specimens (10 x 1 mm) of each denture base resin (Lucitone 550 and QC 20) were prepared according to the manufacturers' recommendations and stored in distilled water at 37°C for 48 h. The specimens were assigned to 3 groups: 1) post-polymerization in a microwave oven for 3 min at 500 W; 2) post-polymerization in water-bath at 55°C for 60 min; and 3) without post-polymerization. For preparation of eluates, 3 discs were placed into a sterile glass vial with 9 mL of Eagle's medium and incubated at 37°C for 24 h. The cytotoxic effect of the eluates was evaluated by 3H-thymidine incorporation. Results: The results showed that the components leached from the resins were cytotoxic to L929 cells, except for the specimens heat treated in water bath (p<0.05). Compared to the group with no heat treatment, water-bath decreased the cytotoxicity of the denture base acrylic resins. Conclusion: The in vitro cytotoxicity of the tested denture base materials was not influenced by microwave post-polymerization heat treatment.

Dynamic behavior of cluster observables for the 2d Ising model

We present results of our numerical study of the critical dynamics of percolation observables for the two-dimensional Ising model. We consider the (Monte Carlo) short-time evolution of the system with small initial magnetization and heat-bath dynamics. We find qualitatively different dynamic behaviors for the magnetization M and for Ω, the so-called strength of the percolating cluster, which is the order parameter of the percolation transition. More precisely, we obtain a (leading) exponential form for Ω as a function of the Monte Carlo time t, to be compared with the power-law increase encountered for M at short times. Our results suggest that, although the descriptions in terms of magnetic or percolation order parameters may be equivalent in the equilibrium regime, greater care must be taken to interpret percolation observables at short times.

Degree of conversion and molecular weight of one denture base and three reline resins submitted post-polymerization treatments

The effect of post-polymerization treatments (MW-microwave irradiatron and WB-water-bath) on the degree of conversion (DC) of three reline resins (Ufi Gel hard-U, Kooliner-K, and Tokuso Rebase Fast-T) and one denture base resin (Lucitone 550-L), submitted to two polymerization cycles (LS-short and LL-long), was evaluated by using FT-Raman spectroscopy (n = 5). The molecular weight (Mw) of the powder of all materials and of K polymerized specimens (control; MW; and WB; n = 3) was analyzed using GPC. DC data were analyzed using Kruskal-Wallis test (α = .05). For control specimens, there were no significant differences between U (68%) and LL (77%) and among LL, K (81%), and T (84%). LS (92%) had the highest DC (P<0.05). Only material K exhibited an increased DC after WB (P<0.05). All powders had Mw from 4.0 × 105 to 6.5 × 105 and narrow Mw distributions (2.1 to 3.6). Polymerization and post-polymerization produced K specimens with Mw similar to that of K powder.

Effect of a post-polymerization treatments on the flexural strength and vickers hardness of reline and acrylic denture base resins

This study evaluated the effect of water-bath and microwave post-polymerization treatments on the flexural strength and Vickers hardness of four autopolymerizing reline resins (Duraliner II-D, Kooliner-K, Tokuso Rebase Fast-TR and Ufi Gel Hard C-UGH) and one heat-polymerized acrylic resin (Lucitone 550-L), processed using two polymerization cycles (short cycle - 90 minutes at 73°C and 100°C for 30 minutes; and long cycle - 9 hours at 71°C). For each material, thirty specimens (64 x 10 x 3.3 mm) were made and divided into 3 groups (n=10). Specimens were tested after: processing (control group); water-bath at 55°C for 10 minutes (reline materials) or 60 minutes (L); and microwave irradiation. Flexural strength tests were performed at a crosshead speed of 5 mm/min using a three-point bending device with a span of 50 mm. The flexural strengths values were calculated in MPa. One fragment of each specimen was submitted to Vickers hardness test. Data were analyzed by 2-way ANOVA followed by Tukey's HSD test (α=0.05). L microwaved specimens (short cycle) exhibited significantly higher flexural strength means than its respective control group (p<0.05). Water-bath promoted a significant increase (p<0.05) in flexural strength of K and L (long cycle). The hardness of the tested materials was not influenced by the post-polymerization treatments. Post-polymerization treatments could be used to improve the flexural strength of some materials tested.

Microwave-induced fast decalcification of rat bone for electron microscopic analysis: An ultrastructural and cytochemical study

Bone decalcification is a time-consuming process. It takes weeks and preservation of the tissue structure depends on the quality and velocity of the demineralization process. In the present study, a decalcification methodology was adapted using microwaving to accelerate the decalcification of rat bone for electron microscopic analysis. The ultrastructure of the bone decalcified by microwave energy was observed. Wistar rats were perfused with paraformaldehyde and maxillary segments were removed and fixed in glutaraldehyde. Half of specimens were decalcified by conventional treatment with immersion in Warshawsky solution at 4oC during 45 days, and the other half of specimens were placed into the beaker with 20 mL of the Warshawsky solution in ice bath and thereafter submitted to irradiation in a domestic microwave oven (700 maximum power) during 20 s/350 W/±37°C. In the first day, the specimens were irradiated 9 times and stored at 40°C overnight. In the second day, the specimens were irradiated 20 times changing the solution and the ice after each bath. After decalcification, some specimens were postfixed in osmium tetroxide and others in osmium tetroxide and potassium pyroantimonate. The specimens were observed under transmission electron microscopy. The results showed an increase in the decalcification rate in the specimens activated by microwaving and a reduction of total experiment time from 45 days in the conventional method to 48 hours in the microwave-aided method.

Influence of microwave polymerization method and thickness on porosity of acrylic resin

Purpose: This study evaluated the influence of polymerization cycle and thickness of maxillary complete denture bases on the porosity of acrylic resin. Materials and Methods: Two heat-activated denture base resins - one conventional (Clássico) and one designed for microwave polymerization (Onda-Cryl) - were used. Four groups were established, according to polymerization cycles: A (Onda-Cryl, short microwave cycle), B (Onda-Cryl, long microwave cycle), C (Onda-Cryl, manufacturing microwave cycle), and T (Clássico, water bath). Porosity was evaluated for different thicknesses (2.0, 3.5, and 5.0 mm; thicknesses I, II, and III, respectively) by measurement of the specimen volume before and after its immersion in water. The percent porosity data were submitted to Kruskal-Wallis for comparison among the groups. Results: The Kruskal-Wallis test detected that the combinations of the different cycles and thicknesses showed significant differences, and the mean ranks of percent porosity showed differences only in the thinnest (2.0 mm) microwave-polymerized specimens (A = 53.55, B = 40.80, and C = 90.70). Thickness did not affect the results for cycle T (I = 96.15, II = 70.20, and III = 82.70), because porosity values were similar in the three thicknesses. Conclusions: Microwave polymerization cycles and the specimen thickness of acrylic resin influenced porosity. Porosity differences were not observed in the polymerized resin bases in the water bath cycle for any thickness. © 2007 by The American College of Prosthodontists.

Território e ambiente institutional: O arranjo produtivo local (APL) bordados de Ibitinga-SP

This study shows the importance of the institutional environment in which the local productive arrangements are entered. It shows that the specifics of each case are historical knowledge fundamental to the studies of APLs. It also shows that in areas of traditional sectors with intensive use of labor, low innovative capacity and low barriers to entry, relations that historically will be developing between firms, workers and market can be considered strong constraints of the trajectory of success or failure. The case study is a set of companies producing textiles and confecciones (products of bed, table and bath) located in the municipality of Ibitinga-SP, of great importance in the region, the high generation of employment and income. It is the study of a particular case in the context of studies on local productive arrangements (APLs), because it serves to highlight the importance of the institutional environment as a prerequisite to overcome the difficulties and consolidation of APLs.

Influence of storage period and effect of different brands of acrylic resin on the dimensional accuracy of the maxillary denture base

The aim of this study was to evaluate the dimensional changes of denture bases made from different resins after different storage periods. For this purpose, 25 sets of plaster models/resin bases were prepared using 4 acrylic resins submitted to two types of polymerization: 1- QC-20 submitted to polymerization by microwave energy; 2- QC-20 submitted to polymerization by water hot bath; 3- Vipi Cril submitted to polymerization by water hot bath; 4- Vipi Wave submitted to polymerization by microwave energy; and 5- Onda Cryl submitted to polymerization by microwave energy. After polymerization, the specimens were sectioned for accuracy readings using a comparison microscope. Readings were taken at 3 points: the crests of the right (A) and left (B) ridges, and the median region of the palate, in 4 different periods. The data obtained were submitted to two-way ANOVA and Tukey's test at 5% significance level. The greatest distortions were found in the posterior palatal region of the base (M), with statistically significant difference (p<0.05) for the studied resins. All acrylic resins presented dimensional changes and the storage period influenced these alterations.

Efeito de um quelante de cálcio, um detergente e da lecitina de soja sobre a qualidade do sêmen caprino congelado-descongelado

The aim of this paper was verifying the effect of the Equex STM Paste and EDTA addition to a Tris-egg yolk extender, on the postthaw goat sperm viability. Nine semen samples of two adult goats were collected by artificial vagina and cryopreserved. It was also objective of this study, to evaluate the utilization of a soybean lecithin based commercial extender (Bioexcell® - IMV, L'Aigle, French) for the goat semen freezing. They were formed five experimental groups: TRIS; TRIS+EDTA; TRIS+EQUEX; TRIS+EDTA+EQUEX e Bioexcell. After evaluation, the semen was diluted in the five extenders and packed in 0.25mL straws with 100 million of motile spermatozoa. The samples were cooled at 0,46°C/min to 5°C, submitted at 75min of equilibration time and frozen in liquid nitrogen vapour. The thawing was accomplished in 37°C water bath for 50s. There were no differences (P>0,05) on the means of post-thaw total and progressive sperm motility among the groups TRIS, TRIS+EQUEX and TRIS+EQUEX+EDTA. The Bioexcell group obtained the least (P<0,05) percentage of post-thawing total and progressive sperm motility. After the thermotolerance test, it was observed the greatest (P<0,05) rates of total and progressive sperm motility in the Equex STM groups (TRIS+EQUEX and TRIS+EQUEX+EDTA). Thus, it can be affirmed that the Equex addition promotes better maintenance rates in the pos-thaw sperm viability, when compared with the extenders that did not contain it.

Shear bond strength of orthodontic brackets bonded using halogen light and light-emitting diode at different debond times

The aim of this in vitro study was to compare the photoactivation effects of QTH (Quartz-Tungsten-Halogen) and LED (Light-Emitting Diode) on the SBS (Shear Bond Strength) of orthodontic brackets at different debond times. Seventy-two bovine lower incisors were randomly divided into two groups according to the photoactivation system used (QTH or LED). The enamel surfaces were conditioned with Transbond self-etching primer, and APC (Adhesive Pre-Coated) brackets were used in all specimens. Group I was cured with QTH for 20 s and Group II with LED for 10 s. Both groups were subdivided according to the different experimental times after bonding (immediately, 24 h and 7 days). The specimens were tested for SBS and the enamel surfaces were analyzed according to the Adhesive Remnant Index (ARI). The statistical analysis included the Tukey's test to evaluate the main effects of photoactivation and debond time on SBS. The Chi-square test was used to compare the ARI values found for each group, and no statistically significant difference was observed. The debond time of 7 days for QTH photoactivation showed statistically greater values of SBS when compared to the immediate and 24 h periods. There was no statistically significant difference between the QTH and LED groups immediately and after the 24 h period. In conclusion, bonding orthodontic brackets with LED photoactivation for 10 s is suggested because it requires a reduced clinical chair time.

Evaluation of a new intraoral paralleling device for creating guiding planes: A pilot study

Aim: The aim of the study was to assess the accuracy of a new intraoral paralleling device for creating proximal guiding planes for removable partial dental prostheses. Methods and Materials: Thirty gypsum casts were divided into two groups in which the proximal surfaces of selected teeth were prepared using either a surveying device (Group 1) or the new ParalAB paralleling device (Group 2). In each cast guiding planes were prepared on the distal surface of the maxillary left canine (A), on the mesial and distal surfaces of the maxillary left second molar (B and C), and on the distal surface of the maxillary right canine (D). Each prepared surface formed an angle related to the occlusal plane that was measured five times and averaged by one operator using a tridimensional coordinate machine. Results: The mean guiding plane angles (± standard deviation) for the prepared surfaces were A=91.82° (±0.48°, B=90.47° (±0.47°, C=90.21° (±0.76°, and D=90.50° (±0.73°) for the dental surveyor (Group 1) and A=92.18° (±0.87°), B=90.90° (±0.85°), C=90.07° (±0.92°), and D=90.66° (±0.76°) for the ParalAB paralleling device (Group 2). A two-way ANOVA, Tukey's, and Levène's tests (at p<0.05) revealed statistically significant differences among surfaces prepared by both groups and that one surface Conclusions: The ParalAB device was able to prepare parallel surfaces and despite significant difference between groups, the ParalAB presented a small deviation from absolute parallelism and can be considered a valid method to transfer guide plans in the fabrication of removable partial dentures. Clinical Significance: The preparation of suitable guiding planes on abutment teeth during the fabrication of removable partial dentures is dependent on the ability of the operator and requires considerable chair time. When multiple teeth are involved, achieving parallelism between abutment surfaces can be technically challenging, especially in posterior regions of the mouth. The ParalAB prototype intraoral paralleling device can aid the clinician during the preparation of accurate guiding planes with a minimum degree of occlusal divergence. © 2010 Seer Publishing LLC.