Microwave-assisted hydrothermal synthesis of NiO-Ce1-XEuxO2-δ powders for fuel cell catalytic anodes

CeO2-based materials doped with rare earth (TR +3) can be used as alternative to traditional NiO-YSZ anodes in solid oxide fuel cells as they have higher ionic conductivity and lower ohmic losses compared to YSZ. Moreover, they allow fuel cell operation at lower temperatures (500-800°C). In the anode composition, the concentration of NiO acting as catalyst in YSZ provides high electrical conductivity and high electrochemical activity of reactions, promoting internal reform in the cell. In this work, NiO - Ce1-xEuxO2-δ compounds (x = 0.1, 0.2 and 0.3) have been synthesized by microwave-assisted hydrothermal method. The materials were characterized by TG, XRD, TPR and SEM-FEG techniques. The refinement of data obtained by X-ray diffraction showed the presence of ceria doped with europium crystallized in a cubic phase with fluorite structure, in addition to the presence of NiO. The microwave-assisted hydrothermal method showed significant reduction in the average particle size and good mass control of phase compositions compared to other chemical synthesis techniques.

Parameters optimization of heat treatment for obtaining luminescent PZT powders

Low crystalline PZT powder samples were successfully synthesized using polymeric precursor method and slow decomposition steps. The polymeric resin precursor was thermal treated in a muffle type oven varying the temperature from 250 °C to 700 °C and the time from 3 to 24 hours in order to investigate the order/disorder mechanism toward the amorphous powders. Powder samples with low crystalline phases were obtained at lower temperatures and long time of thermal treatment, demonstrating a kinetic dependence for organic removal and a thermodynamic barrier for crystallization processes. Through XRD and FTIR spectroscopy characterizations the long time thermal treated samples showed to be composed of the solid solution of metal oxides in absent of organic matter, originating broad XRD peaks profiles and no carbonaceous bands in FTIR spectra. A Photoluminescence characterization showed that the peak emission is higher for disordered and homogeneous phases, which only can be reached through the long time of thermal treatment.

Influence of the preparation route on the structural, morphological and spectroscopic properties of SrTiO3 and SrTiO3:eu3+ powders

This research shows the influence of the synthesis route in the structural and morphological characteristics as well as in the luminescent properties of doped with europium and pure SrTiO3 (STO) powders prepared by microwave assisted hydrothermal synthesis, MWH, and by the polymeric precursor method, PPM. The XRD at room temperature of the STO powders nominally pure obtained by PPM at 700°C for 3 hours, as well as by the MWH at 190°C by 30 minutes present all the reflection peaks for the cubic perovskite structure (JCPDS-ICDD 35-734). The morphology varies according to the synthesis route. The particles of pure STO obtained by PPM presents morphology in the form of plates and the morphology of the particles synthesized by MWH is spherical with approximately 150 nm. The photoluminescent analysis shows for pure STO wide bands associated with the transition of charge transfer from the titanates group (TiO3)2- that are centered on 450 nm. In both preparation methods the emission bands obtained in the composites spectra were found to be asymmetric and low intense. However, in the case of the STO prepared by the PPM a bigger FWHM of the band can be observed. The excitation of the samples was done using a laser (Coherent Innova) with wavelength of 350 nm.

Photocatalytic decomposition of rhodamine-B using scandium and silver-modified TiO2 Powders

Semiconductor-mediated photocatalytic oxidation is an interesting method for water decontamination and a specially modified TiO2 is said to be a promising material. This study verified that the synthesis of 1wt%Ag modified-Sc0.01Ti0.99O1.995 powder samples prepared by Polymeric Precursor Method is capable of forming a mixture of anatase-rutile phase with high photocatalytic performance. This kind of material is found to have a lower bandgap compared to the TiO2-anatase commercial powders, which can be associated to an innovative hybrid modification. The simultaneous insertion of scandium in order to generate a p-type semiconductor and a metallic silver nanophase acting as an electron trapper demonstrated being capable of enhancing the degradation of rhodamine B compared to the commercial TiO2. In spite of the different thermal treatments or phase amounts, the hybrid modified powder samples showed higher photocatalytic activity than the commercial ones.

Influence of alternative drying aids on water sorption of spray dried mango mix powders: a thermodynamic approach

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Rietveld refinement and optical properties of SrWO4:Eu3+ powders prepared by the non-hydrolytic sol-gel method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

A joint experimental and theoretical study on the electronic structure and photoluminescence properties of Al-2(WO4)(3) powders

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The modification of structural and optical properties of nano- and submicron ZnO powders by variation of solvothermal syntheses conditions

Nano- (30-60 nm) and submicron (100-350 nm) ZnO particles were synthesized using solvothermal method at 200 degrees C from an ethanolic solution of zinc acetate dihydrate, applying different reaction conditions, i.e., pH value of precursor and time of the reaction. The X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), UV-vis diffuse reflectance (DR), Raman spectroscopy, and photoluminescence (PL) spectroscopy have been employed for characterization of synthesized ZnO powders. It was shown that the structural, morphological, and optical properties are largely determined by reaction conditions during solvothermal synthesis. The particle crystallinity improves with the decrease of pH value and/or the increase of time of the reaction. The Raman and PL spectra analyses indicate that the oxygen interstitials are dominant intrinsic defects in solvothermally synthesized ZnO powders. It was observed that concentration of defects in wurtzite ZnO crystal lattices slightly changes with the variation of pH value of the precursor and time of the solvothermal reaction. The correlation between structural ordering and defect structure of particles and corresponding growth processes was discussed.

Al2O3 obtained through resistive evaporation for use as insulating layer in transparent field effect transistor

Alumina thin films have been obtained by resistive evaporation of Al layer, followed by thermal oxidation achieved by annealing in appropriate atmosphere (air or O-2-rich), with variation of annealing time and temperature. Optical and structural properties of the investigated films reveal that the temperature of 550 degrees C is responsible for fair oxidation. Results of surface electrical resistivity, Raman and infrared spectroscopies are in good agreement with this finding. X-ray and Raman data also suggest the crystallization of Si nuclei at glass substrate-alumina interface, which would come from the soda-lime glass used as substrate. The main goal in this work is the deposition of alumina on top of SnO2 to build a transparent field-effect transistor. Some microscopy results of the assembled SnO2/Al2O3 heterostructure are also shown.

Heterojunction between Al2O3 and SnO2 thin films for application in transparent FET

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Properties of glass-ceramics obtained from crystallization of the SiO2-Al2O3-MgO-Li2O system with addition of ZrO2

This paper presents the study results with glass-ceramics obtained from base glass (MgO-Al2O3- SiO2-Li2O system) with addition of ZrO2 as nucleating agent. The glass was melted at 1650 degrees C for 3 h and at a heating rate of 10 degrees C/min. The molten glass was poured into a graphite mold to obtain monolithic samples and also in water in order to obtain particulate material. Such material was grinded and then pressed by both uniaxial and isostatic pressing methods before being sintered. Both the monolithic and pressed samples were performed under two different conditions of heat treatment so that their nucleation and crystallization occurred. In the first one, the samples were heated to 1100 degrees C with a heating rate of 10 degrees C/min. In the second one, there was an initial heating rate of 10 degrees C/min up to 780 degrees C, which was kept for 5 minutes. After that, the samples were heated to 1100 degrees C at a heating rate of 1 degrees C/min. Microhardness analyses showed that base glass presented values around 7.0 GPa. The glass-ceramics obtained from the powder sintering showed microhardness values lower than those obtained from monolithic samples. The highest hardness values were observed in the samples which were treated with two heating rates, whose values were around 9.2 +/- 0.5 GPa. Moreover, the glass-ceramics which were produced with an only heating rate, presented values around 7.1 +/- 0.2 GPa, very close to those observed in the base glass.

Structural characterization of Li-MN doped powders prepared by Pechini's method

Pechini's method has been successfully used to prepare Li-doped MgNb2O6(MN) at short time and low temperature. It consists in the preparation of metal citrate solution, which is polymerized at 250°C to form a high viscous resin. This resin was burned in a box type furnace at 400°C/2h and ground in a mortar. Successive steps of calcination up to 900°C were used to form a crystalline precursor. SEM, DTA and XRD were used to characterize the powders. MN precursor powders containing from 0.1 to 5.0 mol% of LiNbO3 additive was prepared aiming better dielectric properties and microstructural characteristics of the PMN prepared from columbite route. SEM analysis showed that particles increased by sintering, forming large agglomerates. The surface area is also substantially reduced with the increase in additive amount above 1.0 mol%. In XRD pattern of the precursor material with 5.0 mol% of additive was observed the LiNbO3 phase of trigonal structure. XRD data were used for Rietveld refinement and a decrease in microstrain and pronounced increase in crystallite size with the increase of LiNbO3 were observed. It is in agreement with the particle morphologies observed by SEM analysis.

Photocatalytic decomposition of rhodamine-b using scandium and silver-modified TiO2 powders

Semiconductor-mediated photocatalytic oxidation is an interesting method for water decontamination and a specially modified TiO2 is said to be a promising material. This study verified that the synthesis of 1wt%Ag modified-Sc0.01Ti0.99O1.995 powder samples prepared by Polymeric Precursor Method is capable of forming a mixture of anatase-rutile phase with high photocatalytic performance. This kind of material is found to have a lower bandgap compared to the TiO2-anatase commercial powders, which can be associated to an innovative hybrid modification. The simultaneous insertion of scandium in order to generate a p-type semiconductor and a metallic silver nanophase acting as an electron trapper demonstrated being capable of enhancing the degradation of rhodamine B compared to the commercial TiO2. In spite of the different thermal treatments or phase amounts, the hybrid modified powder samples showed higher photocatalytic activity than the commercial ones.

Al2O3 Obtained through resistive evaporation for use as insulating layer in transparent field effect transistor

Alumina thin films have been obtained by resistive evaporation of Al layer, followed by thermal oxidation achieved by annealing in appropriate atmosphere (air or O2-rich), with variation of annealing time and temperature. Optical and structural properties of the investigated films reveal that the temperature of 550°C is responsible for fair oxidation. Results of surface electrical resistivity, Raman and infrared spectroscopies are in good agreement with this finding. X-ray and Raman data also suggest the crystallization of Si nuclei at glass substrate-alumina interface, which would come from the soda-lime glass used as substrate. The main goal in this work is the deposition of alumina on top of SnO2 to build a transparent field-effect transistor. Some microscopy results of the assembled SnO2/Al2O3 heterostructure are also shown.

Tribocorrosion behaviour of hot pressed CoCrMo−Al2O3 composites for biomedical applications

Alumina/alumina wear couple can lower the wear rates and thus metallic ion releasing on load bearing metallic implant materials. However, the low fracture toughness of ceramics is still a major concern. Therefore, the present study aims to process and to triboelectrochemically characterise the 5 and 10 vol.-%Al2O3 reinforced CoCrMo matrix composites. Corrosion and tribocorrosion behaviour of the composites were investigated in 8 g L−1 NaCl solution at body temperature. Corroded and worn surfaces were investigated by a field emission gun scanning electron microscope equipped with energy dispersive X-ray spectroscopy. After tribocorrosion experiments, wear rates were calculated using a profilometer. Results suggest that Al2O3 particle addition decreased the tendency of CoCrMo alloy to corrosion under both static and tribocorrosion conditions. However, no significant influence on the corrosion and wear rates was observed in composites mainly due to increased porosity and insufficient matrix/reinforcement bonding.