Bond strength of resin modified glass ionomer cement to primary dentin after cutting with different bur types and dentin conditioning

The aim of this in vitro study was to evaluate the effect of different bur types and acid etching protocols on the shear bond strength (SBS) of a resin modified glass ionomer cement (RM-GIC) to primary dentin. Forty-eight clinically sound human primary molars were selected and randomly assigned to four groups (n=12). In G1, the lingual surface of the teeth was cut with a carbide bur until a 2.0-mm-diameter dentin area was exposed, followed by the application of RM-GIC (Vitremer - 3M/ESPE) prepared according to the manufacturer's instructions. The specimens of G2, received the same treatment of G1, however the dentin was conditioned with phosphoric acid. In groups G3 and G4 the same procedures of G1 and G2 were conducted respectively, nevertheless dentin cutting was made with a diamond bur. The specimens were stored in distilled water at 37 degrees C for 24h, and then tested in a universal testing machine. SBS. data were submitted to 2-way ANOVA (= 5%) and indicated that SBS values of RM-GIC bonded to primary dentin cut with different burs were not statistically different, but the specimens that were conditioned with phosphoric acid presented SBS values significantly higher that those without conditioning. To observe micromorphologic characteristics of the effects of dentin surface cut by diamond or carbide rotary instruments and conditioners treatment, some specimens were examined by scanning electron microscopy. Smear layer was present in all specimens regardless of the type of rotary instrument used for dentin cutting, and specimens etched with phosphoric acid presented more effective removal of smear layer. It was concluded that SBS of a RM-GIC to primary dentin was affected by the acid conditioning but the bur type had no influence.

Comparison of two bond strength testing methodologies for bilayered all-ceramics

Objectives. This study compared the shear bond strength (SBS) and microtensile (MTBS) testing methodologies for core and veneering ceramics in four types of all-ceramic systems.Methods. Four different ceramic veneer/core combinations, three of which were feldspathic and the other a fluor-apatite to their respectively corresponding cores, namely leucitereinforced ceramic ((IPS)Empress, Ivoclar), low leucite-reinforced ceramic (Finesse, Ceramco), glass-infiltrated alumina (In-Ceram Alumina, Vita) and lithium disilicate ((IPS)Empress 2, Ivoclar) were used for SBS and MTBS tests. Ceramic cores (N = 40, n = 10/group for SBS test method, N=5blocks/group for MTBS test method) were fabricated according to the manufacturers' instructions (for SBS: thickness, 3 mm; diameter, 5 mm and for MTBS: 10 mm x 10 mm x 2 mm) and ultrasonically cleaned. The veneering ceramics (thickness: 2 mm) were vibrated and condensed in stainless steel moulds and fired onto the core ceramic materials. After trying the specimens in the mould for minor adjustments, they were again ultrasonically cleaned and embedded in PMMA. The specimens were stored in distilled water at 37 degrees C for 1 week and bond strength tests were performed in universal testing machines (cross-head speed: 1mm/min). The bond strengths (MPa +/- S.D.) and modes of failures were recorded.Results. Significant difference between the two test methods and all-ceramic types were observed (P < 0.05) (2-way ANOVA, Tukey's test and Bonferroni). The mean SBS values for veneering ceramic to lithium disilicate was significantly higher (41 +/- 8 MPa) than those to low leucite (28 +/- 4 MPa), glass-infiltrated (26 +/- 4 MPa) and leucite-reinforced (23 +/- 3 MPa) ceramics, while the mean MTBS for low leucite ceramic was significantly higher (15 +/- 2 MPa) than those of leucite (12 +/- 2 MPa), glass-infiltrated (9 +/- 1 MPa) and lithium disilicate ceramic (9 +/- 1 MPa) (ANOVA, P < 0.05).Significance. Both the testing methodology and the differences in chemical compositions of the core and veneering ceramics influenced the bond strength between the core and veneering ceramic in bilayered all-ceramic systems. (c) 2006 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Evaluation of shear bond strength at the interface of two porcelains and pure titanium injected into the casting mold at three different temperatures

Statement of problem. Titanium has physical and mechanical properties, which have led to its increased use in dental prostheses despite casting difficulties due to high melting point and formation of oxide layers which affect the metal-ceramic bond strength.Purpose. This in vitro study evaluated the shear bond strength of the interface of 2 dental porcelains and pure titanium injected into a mold at 3 different temperatures.Material and methods. Using commercially pure (cp) titanium bars (Titanium, Grade I) melted at 1668degreesC and cast at mold temperatures of 430degreesC, 700degreesC or 900degreesC, 60 specimens were machined to 4 x 4 mm, with a base of 5 x 1 mm. The 4-mm surfaces were airborne-particle abraded with 100 mum aluminum oxide before applying and firing the bonding agent and evaluating the 2 porcelains (Triceram/Triline ti and Vita Titankeramik). Ten specimens were prepared for each temperature and porcelain combination Shear bond testing was performed in a universal testing machine, with a 500-kg load cell and crosshead speed of 0.5 mm/min. The specimens were loaded until failure. The interfaces of representative fractured specimens of each temperature were examined with a scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). Data for shear bond strength (MPa) were statistically analyzed by 2-way ANOVA and the Tukey test (alpha = .05).Results. The results showed significant differences for the metal/porcelain interaction effect (P = .0464). There were no significant differences for the 2 porcelains (P = .4250). The Tukey test showed a significant difference between the pair cp Ti 430degreesC Triceram and cp Ti 900degreesC Triceram, with respective mean values and SDs of 59.74 +/- 11.62 and 34.03 +/- 10.35 MPa.Conclusion. Triceram porcelain showed a bond strength decrease with an increase in the mold temperature for casting titanium. The highest bond strength for Vita porcelain and the best metal-ceramic interface observed with the SEM were found with the mold temperature of 700degreesC.

Effect of mechanical cycling on the push-out bond strength of fiber posts adhesively bonded to human root dentin

This study evaluated the effect of mechanical cycling on the bond strength of fiber posts bonded to root dentin. The hypotheses examined were that bond strength is not changed after fatigue testing and bond strength does not present vast variations according to the type of fiber post. Sixty crownless, single-rooted human teeth were endodontically treated, with the space prepared at 12 mm. Thirty specimens received a quartz fiber post (Q-FRC (DT Light-Post), and the remaining 30 specimens received a glass fiber post (G-FRC) (FRC Postec Plus). All the posts were resin luted (All Bond+Duolink), and each specimen was embedded in a cylinder with epoxy resin. The specimens were divided into six groups: G1-Q-FRC+no cycling, G2- Q-FRC+20,000 cycles (load: 50N, angle of 45 degrees; frequency: 8Hz); G3- Q-FRC+2,000,000 cycles; G4- G-FRC+no cycling; G5- G-FRC+20,000 cycles; G6- GFRC+2,000,000 cycles. The specimens were cut perpendicular to their long axis, forming 2-mm thick disc-samples, which were submitted to the push-out test. ANOVA (alpha=.05) revealed that: (a) QFRC (7.1 +/- 2.2MPa) and G-FRC (6.9 +/- 2.1MPa) were statistically similar (p=0.665); (b) the no cycling groups (7.0 +/- 2.4MPa), 20,000 cycles groups (7.0 +/- 2.1MPa) and 2,000,000 cycles groups (7.0 +/- 2.0MPa) were statistically similar (p=0.996). It concluded that mechanical cycling did not affect the bond strength of two fiber posts bonded to dentin.

Influence of cross-head speed on resin-dentin shear bond strength

Objective: To evaluate the influence of different cross-head speeds on shear bond strength test on the dentin surface.Methods: One hundred and twenty extracted bovine incisors were embedded in polystyrene resin. The specimens were prepared by wet grinding with 320-, 400- and 600-grit Al2O3 paper exposing dentin. After the application of the adhesive system Single Bond (3M) to etched dentin, the composite resin Z-100 (3M) was applied and light cured. The specimens were randomly assigned to four groups (n = 30). The shear bond strength tests were performed with an EMIC DL 500 universal testing machine at four different cross-head speeds: 0.50 (A); 0.75 (B); 1.00 (C); and 5.00 mm/min (D).Results: the mean values of shear bond strength in MPa (SD) were: A, 11.78 (3.91); B, 11.82 (4.78); C, 16.32 (6.45); D, 15.46 (5.94). The data were analyzed with one-way ANOVA and Tukey's test (alpha = 0.05). The results indicated that A = B < C = D. The fracture pattern was evaluated by visual analysis in a stereomicroscope (25 x). The percentage of fractures that occurred at the adhesive interface were: A, 92.5%; B, 91.6%; C, 70.0%; D, 47.0%. The Student's t-test to percentages ( = 0.05) indicated that there were no significant differences among A, B and C; A and B differed from D, and there was no significant difference between C and D.Significance: Different cross-head speeds may influence the shear bond strength and the fracture pattern in dentin substrate. Shear bond strength using cross-head speeds of 0.50 and 0.75 mm/min should be preferred. (C) 2001 Academy of Dental Materials. published by Elsevier B.V. Ltd. All rights reserved.