Response of the pulp of dogs to capping with mineral trioxide aggregate or a calcium hydroxide cement

This study was conducted to observe the response of dogs' dental pulp to mineral trioxide aggregate (MTA) and a calcium hydroxide cement when used as pulp capping materials. After the pulps of 30 teeth were exposed, they were capped with either MTA or a calcium hydroxide cement. Histological analysis was performed 2 months after treatment. Results showed a healing process with complete tubular dentin bridge formation and no inflammation in any of the pulps capped with MTA. on the other hand, only five specimens from the calcium hydroxide cement group formed a complete dentin bridge. In this experimental group, pulp inflammation was observed in all but three cases. In conclusion, MTA exhibited better results than the calcium hydroxide cement for the capping of the pulp in dogs.

Development of an experimental glass ionomer cement containing niobium and fluoride

Glass ionomer cements (GICs) are currently used for various dental applications such as luting cements or as restorative materials. The calcium fluoro-alumino-silicate system is the basis for degradable glasses used to obtain the GICs. The purpose of the present paper is to add niobium to conventional glass system because according to previous papers niobium addition improves the chemical resistance and the mechanical properties of glasses. Therefore, the GICs prepared from these glasses would result in cements with higher chemical and mechanical resistance. The niobium fluoride powders were prepared using the sol-gel process and were characterized by X-ray diffraction, differential thermal analysis (DTA) and Al-27 and Si-29 MAS NMR. The results obtained by XRD showed that the powders prepared by this method are glass-ceramic. In the DTA curve was detected the presence of T-g and T-c temperatures. The analysis of MAS NMR spectra indicated that the framework of the powders is formed by SiO4 and AlO4 linked tetrahedra which are essential structures to yield the cements. Thus, we concluded that niobium fluoride silicate powders can be used in the preparation of GICs. (c) 2005 Elsevier B.V. All rights reserved.

Bond strength of resin modified glass ionomer cement to primary dentin after cutting with different bur types and dentin conditioning

The aim of this in vitro study was to evaluate the effect of different bur types and acid etching protocols on the shear bond strength (SBS) of a resin modified glass ionomer cement (RM-GIC) to primary dentin. Forty-eight clinically sound human primary molars were selected and randomly assigned to four groups (n=12). In G1, the lingual surface of the teeth was cut with a carbide bur until a 2.0-mm-diameter dentin area was exposed, followed by the application of RM-GIC (Vitremer - 3M/ESPE) prepared according to the manufacturer's instructions. The specimens of G2, received the same treatment of G1, however the dentin was conditioned with phosphoric acid. In groups G3 and G4 the same procedures of G1 and G2 were conducted respectively, nevertheless dentin cutting was made with a diamond bur. The specimens were stored in distilled water at 37 degrees C for 24h, and then tested in a universal testing machine. SBS. data were submitted to 2-way ANOVA (= 5%) and indicated that SBS values of RM-GIC bonded to primary dentin cut with different burs were not statistically different, but the specimens that were conditioned with phosphoric acid presented SBS values significantly higher that those without conditioning. To observe micromorphologic characteristics of the effects of dentin surface cut by diamond or carbide rotary instruments and conditioners treatment, some specimens were examined by scanning electron microscopy. Smear layer was present in all specimens regardless of the type of rotary instrument used for dentin cutting, and specimens etched with phosphoric acid presented more effective removal of smear layer. It was concluded that SBS of a RM-GIC to primary dentin was affected by the acid conditioning but the bur type had no influence.

Evaluation of a double-setting alpha-tricalcium phosphate cement in eviscerated rabbit eyes

Purpose: To evaluate the macroscopy, microstructure, and tissue reaction of a double-setting a-tricalcium phosphate bone cement used as an intraocular implant in rabbits.Methods: the internal and external surface of the double-setting a-tricalcium phosphate implant was analyzed macroscopically and by scanning electron microscopy. Twelve New Zealand rabbits received 12-mm implants made of double-setting alpha-tricalcium phosphate cement after unilateral evisceration. Clinical evaluation was performed daily for the first 15 days after surgery and at 15-day intervals until the end of the study period. For histopathologic analysis, 3 animals per experimental period were submitted to enucleation at 15, 45, 90, and 180 days.Results: on gross inspection, the external surface of the implant was solid, smooth, and compact. The microarchitecture was characterized by the formation of columns of hexagonal crystals with interconnecting channels forming micropores. No wound dehiscence, signs of infection, or implant extrusion were observed in any animal throughout the study period. Histologic examination revealed the formation of fibrovascular tissue surrounding the implants, and there were signs of minimal integration of the surface limiting the fibrocellular cap with the space previously occupied by the implant.Conclusions: the double-setting alpha-tricalcium phosphate implant behaved as an inert and nonintegratable material. The lack of incorporation of this material by fibrovascular tissue is related to its characteristics of compactness and high resistance.