Preparation and characterization of ceria nanospheres by microwave-hydrothermal method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation of CeO2 by a simple microwave-hydrothermal method

Cerium carbonate hydroxide (orthorhombic Ce(OH)CO3) hexagonal-shaped microplates were synthesized by a simple and fast microwave-hydrothermal method at 150 degrees C for 30 min. Cerium nitrate, urea and cetyltrimethylammonium bromide were used as precursors. Ceria (cubic CeO2) rhombus-shape was obtained by a thermal decomposition oxidation process at 500 degrees C for 1 h using as- synthesized Ce(OH)CO3. The products were characterized by X-ray powder diffraction, field-emission scanning electron microscopy, thermogravimetric analysis and Fourier transformed infrared spectroscopy. The use of microwave-hydrothermal method allowed to obtain cerium compounds at low temperature and shorter time compared to other synthesis methods. (C) 2008 Elsevier B.V. All rights reserved.

Microwave-assisted hydrothermal synthesis of nanocrystalline SnO powders

Tin oxide (SnO) powders were obtained by the microwave-assisted hydrothermal synthesis technique using SnCl2 center dot 2H(2)O as a precursor. By changing the hydrothermal processing time, temperature, the type of mineralizing agent (NaOH, KOH or NH4 OH) and its concentration, SnO crystals having different sizes and morphologies could be achieved. The powders were characterized by X-ray diffraction (X-ray), Field Emission Scanning Electron Microscopy (FE-SEM), High Resolution Transmission Electron Microscopy (HR-TEM) and Selected Area Electron Diffraction (SAED). The results showed that plate-like form is the characteristic morphology of growth and the TEM analyses indicate the growth direction as (200). (c) 2007 Elsevier B.V. All rights reserved.

In2O3 microcrystals obtained from rapid calcination in domestic microwave oven

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

BaMoO(4) powders processed in domestic microwave-hydrothermal: Synthesis, characterization and photoluminescence at room temperature

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Morphology and Photoluminescence of HfO2 Obtained by Microwave-Hydrothermal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Relationship between Crystal Shape, Photoluminescence, and Local Structure in SrTiO3 Synthesized by Microwave-Assisted Hydrothermal Method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Changes in occlusal vertical dimension in microwave processing of complete dentures.

This study investigated the effect of different microwave curing cycles on the changes in occlusal vertical dimension of complete dentures. Four test groups with 12 maxillary dentures each were evaluated. Groups 1, 2 and 3 were polymerized with different cycles by microwave radiation and Group 4 was the control and cured by water bath. The average pin opening for all groups was less than 0.5 mm. There was no significant difference between the groups polymerized by the microwave method and the control group. However, analyses of the vertical dimension changes showed statistically significant differences between groups 2 (0.276 +/- 0.141 mm) and 3 (0.496 +/- 0.220 mm).

Effectiveness of Microwave Sterilization on Three Hard Chairside Reline Resins

Purpose: The aim of this study was to evaluate the effectiveness of microwave irradiation sterilization on hard chairside reline resins. Materials and Methods: Specimens of three reline resins (Kooliner, Tokuso Rebase, and Ufi Gel Hard) were fabricated and subjected to ethylene oxide sterilization. The specimens were then individually inoculated (107 cfu/mL) with Tryptic Soy Broth media containing one of the tested microorganisms (C albicans, S aureus, B subtilis, and P aeruginosa). After 48 hours at 37°C, the samples were vortexed for 1 minute and allowed to stand for 9 minutes, followed by a short vortex to resuspend any organisms present. After inoculation, 40 specimens of each material were immersed in 200 mL of water and subjected to microwave irradiation at 650 W for 6 minutes. Forty non-irradiated specimens were used as positive controls. Replicate specimens (25 μL) of suspension were plated at dilutions of 10-3 to 10-6 on plates of selective media appropriate for each organism. All plates were incubated at 37°C for 48 hours. After incubation, colonies were counted, and the data were statistically analyzed by the Kruskal-Wallis test. Twelve specimens of each material were prepared for SEM. Results: All immersed specimens showed consistent sterilization of all the individual organisms after microwave irradiation. SEM examination indicated an alteration in cell morphology after microwave irradiation. Conclusion: Microwave sterilization for 6 minutes at 650 W proved to be effective for the sterilization of hard chairside reline resins.

Cytotoxicity of denture base resins: Effect of water bath and microwave postpolymerization heat treatments

Purpose: This study compared the effect of two postpolymerization heat treatments on the cytotoxicity of three denture base resins on L929 cells using 3H-thymidine incorporation and MTT assays. Materials and Methods: Sample disks of Lucitone 550, QC 20, and Acron MC resins were fabricated under aseptic conditions and stored in distilled water at 37°C for 48 hours. Specimens were then divided into three groups: (1) heat treated in microwave oven for 3 minutes at 500 W; (2) heat treated in water bath at 55°C for 60 minutes; and (3) no heat treatment. Eluates were prepared by placing three disks into a sterile glass vial with 9 mL of Eagle's medium and incubating at 37°C for 24 hours. The cytotoxic effect from the eluates was evaluated using the 3H-thymidine incorporation and MTT assays, which reflect DNA synthesis levels and cell metabolism, respectively. Results: The components leached from the resins were cytotoxic to L929 cells when 3H- thymidine incorporation assay was employed. In contrast, eluates from all resins revealed noncytotoxic effects as measured by MTT assay. For both MTT assay and 3H-thymidine incorporation, the heat treatments did not decrease the cytotoxicity of the materials tested. Conclusion: Resins were graded by 3H-thymidine incorporation assay as slightly cytotoxic and by MTT assay as noncytotoxic. Cytotoxicity of the denture base materials was not influenced by microwave or water bath heat treatment.

Effect of microwave treatments on dimensional accuracy of maxillary acrylic resin denture base

Microwave energy has been used as an alternative method for disinfection and sterilization of dental prostheses. This study evaluated the influence of microwave treatment on dimensional accuracy along the posterior palatal border of maxillary acrylic resin denture bases processed by water-bath curing. Thirty maxillary acrylic bases (3-mm-thick) were made on cast models with Clássico acrylic resin using routine technique. After polymerization and cooling, the sets were deflasked and the bases were stored in water for 30 days. Thereafter, the specimens were assigned to 3 groups (n=10), as follows: group I (control) was not submitted to any disinfection cycle; group II was submitted to microwave disinfection for 3 min at 500 W; and in group III microwaving was done for 10 min at 604 W. The acrylic bases were fixed on their respective casts with instant adhesive (Super Bonder®) and the base/cast sets were sectioned transversally in the posterior palatal zone. The existence of gaps between the casts and acrylic bases was assessed using a profile projector at 5 points. No statistically significant differences were observed between the control group and group II. However, group III differed statistically from the others (p<0.05). Treatment in microwave oven at 604 W for 10 min produced the greatest discrepancies in the adaptation of maxillary acrylic resin denture bases to the stone casts.

Densification of Mn-doped tin oxide films by conventional heating and microwave heating treatment

Mn(II) doped SnO2 thin films used for shielding fluoride glasses against corrosion were investigated by x-ray absorption spectroscopy (EXAFS and XANE)S at the Sn and Mn K-edges. The effect of firing treatment on the densification of the films was studied. It has been evidenced a partial change of Mn valence from 2.3 to 2.6 upon heating which is attributed to a change of ratios of two Mn sites: grafted divalent Mn ions at the surface of SnO 2 nanocrystallites and trivalent Mn ions embedded into a substitutional solid solution with Sn. © Physica Scripta 2005.

Cytotoxicity of hard chairside reline resins: Effect of microwave irradiation and water bath postpolymerization treatments

Purpose: To evaluate the influence of water bath and microwave postpolymerization treatments on the cytotoxicity of 6 hard reline acrylic resins. Materials and Methods: The materials tested were Tokuso Rebase Fast (TR), Ufi Gel Hard (UGH), Duraliner II (D), Kooliner (K), New Truliner (NT), and Light Liner (LL). LL resin was additionally tested with an air-barrier coating (LLABC). Nine disks of each material (10 × 1 mm) were made and divided into 3 groups: group 1 (no postpolymerization treatment); group 2 (postpolymerization in microwave oven); group 3 (postpolymerization in water bath at 55°C for 10 minutes). L929 cells were cultured in 96-well plates and incubated for 24 hours in Eagle's medium. Eluates prepared from the disks or medium without disks (control) replaced the medium. Cytotoxicity was assessed by both dehydrogenase succinic activity (MTT) assay and incorporation of radioactive 3H-thymidine assay. Tests were carried out in quadruplicate and repeated twice. Differences between groups were determined by analysis of variance with Tukey multiple-comparison intervals (α = .05). Results: For MTT assay, the postpolymerization treatments had no effect on the cytotoxicity of all materials (P > .05). For 3H-thymidine assay, the postpolymerization treatments significantly decreased the cytotoxicity of UGH (P < .05). The cytotoxicity of K, NT, LL, and LLABC increased after microwave irradiation (P < .05). TR, NT, and LLABC showed an increase in cytotoxicity after water bath (P < .05). Conclusion: When assessed by MTT assay, the cytotoxicity of the materials was not affected by postpolymerization treatments. 3H-Thymidine assay showed that the cytotoxicity of the resins was not improved by the postpolymerization treatments, with the exception of UGH.

Effectiveness of microwave irradiation on the disinfection of complete dentures

Purpose: The purpose of this study was to evaluate the effectiveness of microwave irradiation on the disinfection of simulated complete dentures. Materials and Methods: Eighty dentures were fabricated in a standardized procedure and subjected to ethylene oxide sterilization. The dentures were individually inoculated (10 7 cfu/mL) with tryptic soy broth (TSB) media containing one of the tested microorganisms (Candida albicans, Streptoccus aureus, Bacillus subtilis, and Pseudomonas aeruginosa). After 48 hours of incubation at 37°C, 40 dentures were individually immersed in 200 mL of water and submitted to microwave irradiation at 650 W for 6 minutes. Forty nonirradiated dentures were used as positive controls. Replicate aliquots (25 μL) of suspensions were plated at dilutions of 10 -3 to 10 -6 on plates of selective media appropriate for each organism. All plates were incubated at 37°C for 48 hours. TSB beakers with the microwaved dentures were incubated at 37°C for 7 more days. After incubation, the number of colony-forming units was counted and the data were statistically analyzed by Kruskal-Wallis test (α = .05). Results: No evidence of growth was observed at 48 hours for S aureus, B subtilis, and C albicans. Dentures contaminated with P aeruginosa showed small growth on 2 plates. After 7 days incubation at 37°C, no growth was visible in the TSB beakers of S aureus and C albicans. Turbidity was observed in 3 broth beakers, 2 from P aeruginosa and 1 from B subtilis. Conclusion: Microwave irradiation for 6 minutes at 650 W produced sterilization of complete dentures contaminated with S aureus and C albicans and disinfection of those contaminated with P aeruginosa and B subtilis.

Effect of microwave disinfection procedures on torsional bond strengths of two hard chairside denture reline materials

Purpose: This study evaluated the potential effects of denture base resin water storage time and an effective denture disinfection method (microwave irradiation at 650 W for 6 minutes) on the torsional bond strength between two hard chairside reline resins (GC Reline and New Truliner) and one heat-polymerizing denture base acrylic resin (Lucitone 199). Materials and Methods: Cylindrical (30 x 3.9 mm) denture base specimens (n = 160) were stored in water at 37°C (2 or 30 days) before bonding. A section (3.0 mm) was removed from the center of the specimens, surfaces prepared, and the reline materials packed into the space. After polymerization, specimens were divided into four groups (n = 10): Group 1 (G1) - tests performed after bonding; Group 2 (G2) - specimens immersed in water (200 ml) and irradiated twice (650 W for 6 minutes); Group 3 (G3) - specimens irradiated daily until seven cycles of disinfection; Group 4 (G4) - specimens immersed in water (37°C) for 7 days. Specimens were submitted to a torsional test (0.1 Nm/min), and the torsional strengths (MPa) and the mode of failure were recorded. Data from each reline material were analyzed by a two-way analysis of variance, followed by Neuman-Keuls test (p = 0.05). Results: For both Lucitone 199 water storage periods, before bonding to GC Reline resin, the mean torsional strengths of G2 (2 days - 138 MPa; 30 days - 132 MPa), G3 (2 days - 126 MPa; 30 days - 130 MPa), and G4 (2 days - 130 MPa; 30 days - 137 MPa) were significantly higher (p < 0.05) than G1 (2 days - 108 MPa; 30 days - 115 MPa). Similar results were found for Lucitone 199 specimens bonded to New Truliner resin, with G1 specimens (2 days - 73 MPa; 30 days - 71 MPa) exhibiting significantly lower mean torsional bond strength (p < 0.05) than G2 (2 day - 86 MPa; 30 days - 90 MPa), G3 (2 days - 82 MPa; 30 days - 82 MPa), and G4 specimens (2 days - 78 MPa; 30 days - 79 MPa). The adhesion of both materials was not affected by water storage time of Lucitone 199 (p > 0.05). GC reline showed a mixed mode of failure (adhesive/cohesive) and New Truliner failed adhesively. Conclusions: Up to seven microwave disinfection cycles did not decrease the torsional bond strengths between the hard reline resins, GC Reline and New Truliner to the denture base resin Lucitone 199. The effect of additional disinfection cycles on reline material may be clinically significant and requires further study. Copyright © 2006 by The American College of Prosthodontists.