Diametral tensile strength of dual-curing resin cements submitted exclusively to autopolymerization.

OBJECTIVES: To evaluate, at different times, the diametral tensile strength (DTS) of dual-curing resin cements that were not photopolymerized. METHOD AND MATERIALS: Equal amounts of base and catalyst pastes of Panavia F (Kuraray), Variolink II (Vivadent), Rely X (3M ESPE), and Enforce (Dentsply) were mixed and inserted into cylindrical molds (4 x 2 mm) (n = 10). Cements were not photopolymerized. DTS test was performed in a testing machine at 30 minutes, 1 hour, 24 hours, and 7 days. The specimens were stored in light-proof containers with distilled water at 37 degrees C until the time of assay. An autopolymerizing resin cement (Cement-It, Jeneric Pentron) and a zinc phosphate cement served as controls. One-way analysis of variance (ANOVA) and Tukey test were performed separately for each cement and for each time (P <.05). RESULTS: All cements showed an increase in DTS when tested at 1 and 24 hours. Tests at 24 hours and 7 days revealed no statistically significant differences. In all groups, the zinc phosphate cement had the lowest DTS mean values (2.1 MPa, 3.6 MPa, 6.5 MPa, and 6.9 MPa), while Cement-It (35.1 MPa, 33.6 MPa, 46.9 MPa, and 46.3 MPa) and Enforce (31.9 MPa, 31.7 MPa, 43.4 MPa, and 47.6 MPa) presented the highest DTS mean values. CONCLUSION: All cements presented maximal strength at 24 hours. The dual-curing resin cements, even when nonphotopolymerized, demonstrated higher DTS than the zinc phosphate cement and similar or lower values than the autopolymerizing resin cement.

Changes on degree of conversion of dual-cure luting light-cured with blue LED

The indirect adhesive procedures constitute recently a substantial portion of contemporary esthetic restorative treatments. The resin cements have been used to bond tooth substrate and restorative materials. Due to recently introduction of the self-bonding resin luting cement based on a new monomer, filler and initiation technology has become important to study the degree of conversion of these new materials. In the present work the polymerization reaction and the filler content of dual-cured dental resin cements were studied by means of infra-red spectroscopy (FT-IR) and thermogravimetry (TG). Twenty specimens were made in a metallic mold (8 mm diameter × 1 mm thick) from each of 2 cements, Panavia® F2.0 (Kuraray) and RelyX™ Unicem Applicap (3M/ESPE). Each specimen was cured with blue LED with power density of 500 mW/cm 2 for 30 s. Immediately after curing, 24 and 48 h, and 7 days DC was determined. For each time interval 5 specimens were pulverized, pressed with KBr and analyzed with FT-IR. The TG measurements were performed in Netzsch TG 209 under oxygen atmosphere and heating rate of 10°C/min from 25 to 700°C. A two-way ANOVA showed DC (%) mean values statistically significance differences between two cements (p < 0.05). The Tukey's test showed no significant difference only for the 24 and 48 h after light irradiation for both resin cements (p > 0.05). The Relx-Y™ Unicem mean values were significantly higher than Panavia® F 2.0. The degree of conversion means values increasing with the storage time and the filler content showed similar for both resin cements. © 2009 Pleiades Publishing, Ltd.

In vitro lingual bracket evaluation of indirect bonding with plasma arc, LED and halogen light

Authors - Magno AFF, Martins RP, Vaz LG, Martins LP Objectives - Evaluate the shear bond strength (SBS) and the adhesive remnant index (ARI) of indirect bonded lingual brackets using xenon plasma arc light, light-emitting diode (LED) and conventional quartz-tungsten-halogen light. Material and Methods - Lingual brackets were bonded indirectly to 60 premolars divided to three groups according to the curing light used: Group 1, plasma arc for 6 s; Group 2, LED for 10 s; and Group 3, halogen light for 40 s. After bonding, the specimens were subjected to a shear force until debonding. The debonding pattern was assessed and classified according to the ARI scores. The mean shear bond strengths were accessed by anova followed by the Student-Newman-Keuls test for multiple comparisons. ARI scores were assessed using the chi-square test. Results - The three groups showed significant differences (p < 0.001), with the averages of group 1 < group 2 < group 3. Groups showed no differences regarding ARI scores. Conclusion - Bonding lingual brackets indirectly with plasma arc, during 60% of the time used for the LED, produced lower SBS than obtained with the latter. Using LED during 25% of the time of the halogen light produced lower SBS than obtained with the latter. These differences did not influence the debonding pattern and are clinically acceptable according to the literature. © 2010 John Wiley & Sons A/S.

Evaluation of tooth color after bleachingwith and without light-activation

Purpose: The use of different light sources as an adjunct to in-office bleaching has been questioned. Thus, the aim of this study was to evaluate the color changes of teeth after application of bleaching techniques with different products, with and without activation by a LED-laser system. Methods: Twenty-four bovine teeth surfaces were submitted to three bleaching techniques with two commercially available 35% hydrogen peroxide bleaching agents (n=8). The specimens were immersed in red wine for 48 h at 37°C and submitted to the bleaching techniques. Color changes were measured before and after staining as well as immediately after and 24 h after the bleaching treatments, with two different methods of color evaluation, software ScanWhite V1.1 and intra-oral spectrophotometer (Vita Easyshade). Data were analyzed by ANOVA and Kruskal-Wallis test. Results: The statistical analysis showed that there was no statistically significant difference at 5% of significance level between the different groups, independently of the evaluation time, evaluation methods or the use of LED-laser systems. Conclusion: The results suggested that the use of light in the bleaching techniques did not influence the color changes. Copyright: © 2011 Roberto et al.

Evaluation of degree of conversion and hardness of dental composites photoactivated with different light guide tips

Objective: The aim of this study was to evaluate the degree of conversion and hardness of different composite resins, photo-activated for 40 s with two different light guide tips, fiber optic and polymer. Methods: Five specimens were made for each group evaluated. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm-1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm-1. The Vickers hardness measurements were performed in a universal testing machine. A 50 gf load was used and the indenter with a dwell time of 30 seconds. The degree of conversion and hardness mean values were analyzed separately by ANOVA and Tukey's test, with a significance level set at 5%. Results: The mean values of degree of conversion for the polymer and fiber optic light guide tip were statistically different (P<.001). The hardness mean values were statistically different among the light guide tips (P<.001), but also there was difference between top and bottom surfaces (P<.001). Conclusions: The results showed that the resins photo-activated with the fiber optic light guide tip promoted higher values for degree of conversion and hardness.

Avaliação da microdureza de quatro cimentos resinosos duais fotopolimerizados através da interposição de diferentes materiais: estudo in vitro

Pós-graduação em Odontologia Restauradora - ICT

Teachers Formation in Higher Education: Some Aspects under the Light of Education-Work Relations

This text is mainly aimed to address essential aspects of teacher formation in the light of education-work relations in the higher education, from our systematic experience in higher education teaching, particularly teaching and research in the field of Didactics discipline. This formulation is justified considering our concern in seeking to situate this discussion in the context of bringing together knowledge areas and the field of teaching knowledge. Still, our choice to develop such an approach in the light of work-education relationship is due to the belief about the possibilities of seeking to overcome the requirements imposed by capitalism to our educational system, within the possible contradictions of these relationships. In this context the teachers’ formation in higher education gains social and strategic importance, taking on the task of forming individuals of “action-reflection-action” in a society established historically based on the social relations which settle in the light of capital’s multiple determinations. It appears that, in this sense, the major confrontations have been given within the discussions about what to prioritize or combine in the list of criteria and content for teacher’s formation. In Didactic, we seek to emphasize discussions that we consider with a philosophical background, referring to the orientation of teaching practice in knowledge of contemporary ideological struggle; socio-historical, referring to the possibility of formation of disciplines, among them Didactic, and curriculums and references to support its guidance in the process of teacher’s formation. This context of discussion is based on the concrete teaching practice with a view to transformation and to search for new syntheses in terms of knowledge and in terms of historical reality. Then therefore, our methodological approach grounded in the dimensions of the same unit: historical materialism as posture, method and as praxis.

Changes in irradiance and energy density in relation to different curing distances

The present study aimed to assess the influence of curing distance on the loss of irradiance and power density of four curing light devices. The behavior in terms of power density of four different dental curing devices was analyzed (Valo, Elipar 2, Radii-Cal, and Optilux-401) using three different distances of photopolymerization (0 mm, 4 mm, and 8 mm). All devices had their power density measured using a MARC simulator. Ten measurements were made per device at each distance. The total amount of energy delivered and the required curing time to achieve 16 J/cm2 of energy was also calculated. Data were statistically analyzed with one-way analysis of variance and Tukey’s tests (p < 0.05). The curing distance significantly interfered with the loss of power density for all curing light devices, with the farthest distance generating the lowest power density and consequently the longer time to achieve an energy density of 16 J/cm2 (p < 0.01). Comparison of devices showed that Valo, in extra power mode, showed the best results at all distances, followed by Valo in high power mode, Valo in standard mode, Elipar 2, Radii-Cal, and Optilux-401 halogen lamp (p < 0.01). These findings indicate that all curing lights induced a significant loss of irradiance and total energy when the light was emitted farther from the probe. The Valo device in extra power mode showed the highest power density and the shortest time to achieve an energy density of 16 J/cm2 at all curing distances.

Composite resin color stability: influence of light sources and immersion media

This study evaluated the influence of light sources and immersion media on the color stability of a nanofilled composite resin. Conventional halogen, high-power-density halogen and high-power-density light-emitting diode (LED) units were used. There were 4 immersion media: coffee, tea, Coke® and artificial saliva. A total of 180 specimens (10 mm x 2 mm) were prepared, immersed in artificial saliva for 24 h at 37±1ºC, and had their initial color measured with a spectrophotometer according to the CIELab system. Then, the specimens were immersed in the 4 media during 60 days. Data from the color change and luminosity were collected and subjected to statistical analysis by the Kruskall-Wallis test (p<0.05). For immersion time, the data were subjected to two-way ANOVA test and Fisher's test (p<0.05). High-power-density LED (ΔE=1.91) promoted similar color stability of the composite resin to that of the tested halogen curing units (Jet Lite 4000 plus--ΔE=2.05; XL 3000--ΔE=2.28). Coffee (ΔE=8.40; ΔL=-5.21) showed the highest influence on color stability of the studied composite resin. There was no significant difference in color stability regardless of the light sources, and coffee was the immersion medium that promoted the highest color changes on the tested composite resin.

The effect of blue light on periodontal biofilm growth in vitro

We have previously shown that blue light eliminates the black-pigmented oral bacteria Porphyromonas gingivalis, Prevotella intermedia, Prevotella nigrescens, and Prevotella melaninogenica. In the present study, the in vitro photosensitivity of the above black-pigmented microorganisms and four Fusobacteria species (Fusobacterium nucleatum ss. nucleatum, F. nucleatum ss. vincentii, F. nucleatum ss. polymorphum, Fusobacterium periodonticum) was investigated in pure cultures and human dental plaque suspensions. We also tested the hypothesis that phototargeting the above eight key periodontopathogens in plaque-derived biofilms in vitro would control growth within the dental biofilm environment. Cultures of the eight bacteria were exposed to blue light at 455 nm with power density of 80 mW/cm(2) and energy fluence of 4.8 J/cm(2). High-performance liquid chromatography (HPLC) analysis of bacteria was performed to demonstrate the presence and amounts of porphyrin molecules within microorganisms. Suspensions of human dental plaque bacteria were also exposed once to blue light at 455 nm with power density of 50 mW/cm(2) and energy fluence of 12 J/cm(2). Microbial biofilms developed from the same plaque were exposed to 455 nm blue light at 50 mW/cm(2) once daily for 4 min (12 J/cm(2)) over a period of 3 days (4 exposures) in order to investigate the cumulative action of phototherapy on the eight photosensitive pathogens as well as on biofilm growth. Bacterial growth was evaluated using the colony-forming unit (CFU) assay. The selective phototargeting of pathogens was studied using whole genomic probes in the checkerboard DNA-DNA format. In cultures, all eight species showed significant growth reduction (p < 0.05). HPLC demonstrated various porphyrin patterns and amounts of porphyrins in bacteria. Following phototherapy, the mean survival fractions were reduced by 28.5 and 48.2 % in plaque suspensions and biofilms, respectively, (p < 0.05). DNA probe analysis showed significant reduction in relative abundances of the eight bacteria as a group in plaque suspensions and biofilms. The cumulative blue light treatment suppressed biofilm growth in vitro. This may introduce a new avenue of prophylactic treatment for periodontal diseases.

Composite resin color stability: influence of light sources and immersion media

This study evaluated the influence of light sources and immersion media on the color stability of a nanofilled composite resin. Conventional halogen, high-power-density halogen and high-power-density light-emitting diode (LED) units were used. There were 4 immersion media: coffee, tea, Coke® and artificial saliva. A total of 180 specimens (10 mm x 2 mm) were prepared, immersed in artificial saliva for 24 h at 37±1ºC, and had their initial color measured with a spectrophotometer according to the CIELab system. Then, the specimens were immersed in the 4 media during 60 days. Data from the color change and luminosity were collected and subjected to statistical analysis by the Kruskall-Wallis test (p<0.05). For immersion time, the data were subjected to two-way ANOVA test and Fisher's test (p<0.05). High-power-density LED (ΔE=1.91) promoted similar color stability of the composite resin to that of the tested halogen curing units (Jet Lite 4000 plus--ΔE=2.05; XL 3000--ΔE=2.28). Coffee (ΔE=8.40; ΔL=-5.21) showed the highest influence on color stability of the studied composite resin. There was no significant difference in color stability regardless of the light sources, and coffee was the immersion medium that promoted the highest color changes on the tested composite resin.