Comparação de compósitos obtidos via RTM de resina epóxi e fibra de carbono com e sem descontinuidade nos tecidos

Technology is growing interest in the use of composites, due to the requirement of lighter materials and more resistant, factors essential to meet the project specifications and reduce the operational cost. In the production of high performance structural composites, considering the aerospace criteria, the domestic industry has shown interest in the process of resin transfer molding (RTM) for reproducibility and low cost. This process is suitable for producing components of polymeric composites with relatively simple geometries, consistent thicknesses, high quality finish with no size limitations. The objective of this work was machined carbon steel to make a matched-die tooling for RTM and produce two composite plates of epoxy resin and carbon fiber fabric with and without induced discontinuities, which were compared towards their impregnation with ultrasound, their properties via tensile tests and thermal analysis. In ultrasonic inspection, it was found good impregnation of the preform of both composites. In the thermal analysis it was possible to check the degradation temperature of the composites, the glass transition temperature and it was found that the composites showed no effective cure cycles, but presented good performance in the tensile test when compared with aluminum alloy 7050 T7451 . The results showed that the injection strategy was appropriate since the laminate exhibited a good quality for the proposed application

Influência do condicionamento ambiental sobre as propriedades viscoelásticas de compósitos aramida/epóxi

The increasing application of structural composites in the aerospace industry is mainly due to its low specific weight coupled with its excellent mechanical properties when in service. As a result of climatic variations that pass the aircraft is of paramount importance to study the influence of weathering on this type of material when subjected to such changes. The purpose of this work is to evaluate the mechanical behavior of specimens of kevlar fiber /epoxy matrix composites, by dynamic mechanical thermal analysis (DMA) and interlaminar shear strength tests (ILSS), after passing through three environmental conditioning: saline fog, hygrothermal and ultraviolet radiation. From the results, we concluded that the laminate was molded supplied homogeneously, not presenting problems such as porosity, delaminations or cracks inside. After a period of 625 hours of exposure to hygrothermal conditioning, we observed a 1,2% maximum of absorption of moisture. Samples subjected to the conditioning by UV irradiation (600 hours) and salt spray showed a reduction of about 24,30% and 32,30%, respectively, on the shear strength (ILSS). In DMA analysis is not observed significant changes on the glass transition temperature. However, when considering the storage modulus of the samples conditioned by UV radiation (1200 hours), salt spray and hygrothermal conditioning there is an increase of 5,34% , 7,19% and 5,57% respectively

Towards the development of fiber lasers for the 2 to 4 nanom spectral region

A growing number of applications are calling for compact laser sources operating in the mid-infrared spectral region. A review of our recent work on monolithic fiber lasers (FL) based either on the use of rare-earth fluoride fibers or on Raman gain in both fluoride and chalcogenide glass fibers is presented. Accordingly, an erbium-doped double clad fluoride glass all-FL operating in the vicinity of 3 μm is shown. In addition, we present recent results on the first demonstrations of both fluoride and chalcogenide Raman fiber lasers operating at 2.23 and 3.34 μm, respectively. It is shown that based on this approach, monolithic FLs could be developed to cover the whole 2 to 4 μm spectral band.

Obtenção e caracterização de compósitos de benzoxazina/fibra de carbono

Pós-graduação em Engenharia Mecânica - FEG