Cu0.5Zn0.5Fe2O4 ferrite for application as a soft magnetic material

This work involved the synthesis and characterization of Cu0.5Zn0.5Fe2O4 ferrite powders prepared by combustion reaction for use as soft magnetic materials. The powders were characterized by nitrogen adsorption (BET), XRD, Rietveld refinement, SEM, TEM and magnetic measures. The results indicate that the combustion reaction yielded crystalline powders containing spinel ferrite as the primary phase and traces of Fe2O3 as secondary phase. The crystallite size and lattice microdeformation calculated from Rietveld refinements were 36 and 0.24 nm, respectively. The micrographic analysis revealed particles smaller than 100 nm and fine particle agglomerates. The particles were approximately spherical and their size, calculated by TEM, was 29 nm. The magnetic parameters indicated that the Cu-Zn ferrite powders presented closed hysteresis loops and soft magnetic properties. © (2012) Trans Tech Publications, Switzerland.

Influence of convergence angle of tooth preparation on the fracture resistance of Y-TZP-based all-ceramic restorations

Objective: To investigate the influence of the convergence angle of tooth preparation on the fracture load of Y-TZP-based ceramic (YZ-Vita YZ) substructure (SB) veneered with a feldspathic porcelain (VM9-Vita VM9). Methods: Finite element stress analysis (FEA) was performed to examine the stress distribution of the system. Eighty YZ SB were fabricated using a CAD-CAM system and divided into four groups (n = 20), according to the total occlusal convergence (TOC) angle: G6-6° TOC; G12-12° TOC; G20-20° TOC; and G20MOD-20° TOC with modified SB. All SB were veneered with VM9, cemented in a fiber reinforced epoxy resin die, and loaded to failure. Half of the specimens from each group (n = 10) were cyclic fatigued (106 cycles) before testing. Failure analysis was performed to determine the fracture origin. Data were statistically analyzed using Anova and Tukey's tests (α = 0.05). Results: The greatest mean load to fracture value was found for the G20MOD, which was predicted by the FEA. Cyclic fatigue did not significantly affect the load of fracture. Catastrophic failure originating from the internal occlusal surface of the SB was the predominant failure mode, except for G20MOD. Significance: The YZ-VM9 restorations resisted greater compression load than the usual physiological occlusal load, regardless of the TOC angle of preparations. Yet, the G20MOD design produced the best performance among the experimental conditions evaluated. © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Fault current limiter using transformer and modular device of YBCO coated conductor

In this work, we report on the evaluation of a superconducting fault current limiter (SFCL). It is consisted of a modular superconducting device combined with a short-circuited transformer with a primary copper winding connected in series to the power line and the secondary side short-circuited by the superconducting device. The basic idea is adding a magnetic component to contribute to the current limitation by the impedance reflected to the line after transition of the superconducting device. The evaluation tests were performed with a prospective current up to 2 kA, with the short-circuited transformer of 2.5 kVA, 220 V/660 V connected to a test facility of 100 kVA power capacity. The resistive SFCL using a modular superconducting device was tested without degradation for a prospective fault current of 1.8 kA, achieving the limiting factor 2.78; the voltage achieved 282 V corresponding to an electric field of 11 V/m. The test performed with the combined SFCL (xsuperconducting device + transformer) using series and toroidal transformers showed current limiting factor of 3.1 and 2 times, respectively. The test results of the combined SFCL with short-circuited transformer showed undesirable influence of the transformer impedance, resulting in reduction of the fault current level. © 2002-2011 IEEE.

Synthesis, characterization and thermal behavior of solid state compounds of heavy trivalent lanthanide succinates

Solid-state Ln-L compounds, where Ln stands for heavy trivalent lanthanides or yttrium(III) (Tb-Lu, Y) and L is succinate, have been synthesized. Simultaneous thermogravimetry and differential thermal analysis (TG-DTA), differential scanning calorimetry (DSC), infrared spectroscopy, TG-DTA coupled to FTIR, elemental analysis, X-ray powder diffractometry and complexometry were used to characterize and study the thermal behavior of these compounds. For the terbium to thulium and yttrium compounds, the dehydration, as well the thermal decomposition of the anhydrous compound occurs in two consecutive steps, while ytterbium and lutetium the dehydration occurs in a single step. The results also led to information about the ligand's denticity, thermal stability and thermal decomposition of these compounds. © 2013 Elsevier B.V.

Mechanical properties of vulcanized natural rubber nanocomposites containing functional ceramic nanoparticles

Rubber nanocomposites containing different concentrations of ferroelectric and paramagnetic nanoparticles were fabricated. Nanostructures of ferroelectric potassium strontium niobate and paramagnetic nickel-zinc ferrite were synthesized using a modified polyol method. The nanoparticle characterization was carried out by transmission electron microscopy and X-ray diffraction, showing that the materials were produced with nanometer dimensions, specific crystallinity and microstrain. Mechanical tests such as hardness type Shore A, stress-strain and compression resistance were performed. They showed that increasing the concentration of nanoparticles enhance the rigidity of vulcanized films of natural rubber and this change is more pronounce for the nanocomposites formed with ferrite nanoparticles, likely due to the effect of its morphological and surface properties. © 2013 by American Scientific Publishers.

Properties of individual YBCO layers in a two-layered design for energy-efficient digital data cables

We are developing two-layered Yttrium Barium Copper Oxide (YBCO) thin film structures for energy efficient data links for superconducting electronics and present the results of their property measurements. High temperature superconductors (HTS) are advantageous for the implementation of energy-efficient cables interconnecting low temperature superconductor-based circuits and other cryogenic electronics circuits at higher temperature stages. The advantages of the HTS cables come from their low loss and low dispersion properties, allowing ballistic transfer of low power signals with very high bandwidth, low heat conduction and negligible inter-line crosstalk. The microstrip line cable geometry for typical materials is a two-layered film, in which the two superconducting layers are separated by an insulation layer with a minimized permittivity. We have made a proof of concept design of two YBCO films grown by pulsed laser deposition and then assembled into a sandwich with uniform insulating interlayer of tens of micrometers thick. We report on results obtained from such systems assembled in different ways. Structural and electromagnetic properties have been examined on individual films and on the corresponding sandwich composite. © 2013 IEEE.

Development and characterization of a new bio-nanocomposite (bio-NCP) for diagnosis and treatment of breast cancer

Breast cancer is a public health problem throughout the world. Moreover, breast cancer cells have a great affinity for hydroxyapatite, leading to a high occurrence of bone metastasis. In this work we developed a bio-nanocomposite (bio-NCP) in order to use such affinity in the diagnosis and treatment of breast cancer. The bio-NCP consists of magnetic nanoparticles of Mn and Zn ferrite inside a polymeric coating (chitosan) modified with nanocrystals of apatite. The materials were characterized with synchrotron X-ray Powder Diffraction (XPD), Time-of-Flight Neutron Powder Diffraction (NPD), Fourier Transformed Infra-red Spectroscopy (FTIR), Scanning Electron Microscopy (SEM) and magnetic measurement with a Physical Property Measurement System (PPMS). We obtained ferrite nanoparticles with a high inversion degree of the spinel structure regarding the Fe and Mn, but with all the Zn in the A site. The coating of such nanoparticles with chitosan had no notable effects to the ferrite microstructure. In addition, the polymeric surface can be easily modified with apatite nanocrystals since the hydration of the bio-NCP during synthesis can be controlled. The resulting bio-NCP presents a spherical shape with a narrow size distribution and high magnetic response at room temperature and is a very promising material for early diagnosis of breast cancer and its treatment. © 2013 Elsevier B.V.

MICROSTRUCTURAL CHARACTERIZATION OF DUAL AND MULTIPHASE STEELS APPLIED TO AUTOMOTIVE INDUSTRY

TRIP (Transformation Induced Plasticity) and DP (Dual-Phase) steels are written in a new series of steels which present excellent mechanical properties. As for microstructure aspect, TRIP steels consist on a ferrite matrix with a second phase dispersion of other constituents, such as bainite, martensite and retained austenite, while dual-phase steels consist on martensite dispersion in a ferrite matrix. In order to identify the different microconstituents present in these materials, microstructure characterization techniques by optical microscopy (using different etchants: LePera, Heat-Tinting and Nital) and scanning electron microscopy were carried out. This being so, microstructures were correlated with mechanical properties of materials, determined by means of tensile tests. It is concluded that steels assisted by TRIP effect have a strength and elongation relation higher than the dual-phase one. With microstructure characterization, it was observed phases present in these materials microstructure.

The effect of an Er,Cr:YSGG laser on external adaptation of healthy and decayed cavities

The aim of this study was to evaluate the influence of chlorhexidine and Er, Cr:YSGG laser irradiation on the bond strength and external adaptation in mixed healthy and caries-affected class V cavities before and after thermal cycling. Thirty-six cavity preparations were made in mixed class V buccal human molars, half of them being artificially caries-induced. Any remaining affected dentin was removed from the cavity with a round burr at low speed. The teeth were divided into six groups, according to cleaning agent for both healthy and caries-induced dentin: no treatment, chlorhexidine and erbium, chromium-doped: yttrium, scandium, gallium, garnet (Er,Cr:YSGG) laser irradiation. A Filtek P90 (3M ESPE, St Paul, MN, USA) silorane adhesive restorative system was used. The specimens were subjected to 5000 thermal cycles (5-55 degrees C 60 min). Epoxy replicas were obtained to characterize the external adaptation under scanning electron microscopy. The average percentages of non-continuous margins were 5.41% and 6.49% in enamel dentin before thermal cycling and 25% and 33.7% after thermal cycling, respectively. The caries-affected and laser irradiated cavities showed higher non-continuous margins. Thermal cycling was able to raise the percentage of non-continuous margin for all groups. Chlorhexidine did not affect the marginal adaptation results, and the Er,Cr:YSGG laser irradiation showed significantly worse results compared with the control group.

Bonding of Y-TZP to Dentin: Effects of Y-TZP Surface Conditioning, Resin Cement Type, and Aging

Purpose: To evaluate the effects of two surface treatments, aging, and two resin cements on shear bond strength between dentin and yttrium-stabilized tetragonal zirconia polycrystal ceramic (Y-TZP).Materials and Methods: Eighty human molars were embedded in acrylic resin and sectioned 3 mm below the occlusal plane. These teeth and 80 cylindrical Y-TZP specimens (height, 4 mm; diameter, 3.4 mm) were divided into eight groups (n=10) using the following factors: Y-TZP surface treatment (Vi: low-fusing porcelain [vitrification] + hydrofluoric acid etching + silanization or Si: tribochemical silicatization); cementation strategies (PF: Pan avia or CC: Clearfil); and storage (nonaging or aging). Bonding surfaces of 40 Y-TZP specimens received Vi treatment, and the rest received Si treatment. Half of the ceramic-tooth assemblies were cemented with Panavia, the rest with Clearfil. Shear tests were executed using 0.4-mm-thick wire at 0.5 mm/min. Data were analyzed by three-way analysis of variance and Tukey test (alpha=0.05). Fractures were analyzed.Results: Y-TZP surface treatments did not affect bond strength (p=0.762, Vi = Si), while resin cements (p<0.001, Panavia > Clearfil) and aging (p=0.006, nonaging > aging) showed a significant effect. Most failures were in adhesive at dentin-cement interfaces; no failure occurred between zirconia and cement.Conclusion: When Y-TZP ceramic is bonded to dentin, the weakest interface is that between dentin and resin cement. The resin cement/Y-TZP interface was less susceptible to failures, owing to Y-TZP surface treatments.

Experimental evidence of enhanced ferroelectricity in Ca doped BiFeO3

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

MICROSTRUCTURAL CHARACTERIZATION OF CP STEEL USED IN AUTOMOTIVE INDUSTRY

This study aims to characterize the microstructure of the complex phase steel (CP). Using the conventional and colored metallographic analysis with 3% Nital etchant, sodium metabisulfite 10% and LePera. Techniques were applied in this work of optical microscopy, using, besides the lighting in bright field, dark field illumination of the reverse contrast in bright field illumination, the method of polarized light, which generates colorful contrast, providing a complementary identification phases present in the microstructure, and the system by differential interference contrast (DIC). The results obtained by metallography CP indicates that the steel has a microstructure composed of ferrite, retained austenite, bainite and martensite and precipitates arranged in a refined and complex morphology. Besides bright field illumination others' optical microscopy's techniques such as dark field illumination were applied.

Second Phase Precipitation in Ultrafine-grained Ferrite Steel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of laser beam energy on the pulsed Nd:YAG laser welding of thin sheet corrosion resistant materials

The aim of this study was to value the possibility to join, for pulsed Nd:YAG laser welding, thin foils lap joints for sealing components in corrosive environment. Experimental investigations were carried out using a pulsed neodymium: yttrium aluminum garnet laser weld to examine the influence of the pulse energy in the characteristics of the weld fillet. The pulse energy was varied from 1.0 to 2.5 J at increments of 0.25 J with a 4 ms pulse duration. The base materials used for this study were AISI 316L stainless steel and Ni-based alloys foils with 100 mu m thickness. The welds were analyzed by electronic and optical microscopy, tensile shear tests and micro hardness. The results indicate that pulse energy control is of considerable importance to thin foil weld quality because it can generate good mechanical properties and reduce discontinuities in weld joints. The ultimate tensile strength of the welded joints increased at first and then decreased as the pulse energy increased. In all the specimens, fracture occurred in the top foil heat-affected zone next to the fusion line. The microhardness was almost uniform across the parent metal, HAZ and weld metal. A slight increase in the fusion zone and heat-affected zone compared to those measured in the base metal was observed. This is related to the microstructural refinement in the fusion zone, induced by rapid cooling of the laser welding. The process appeared to be very sensitive to the gap between couples.

Reassessment of the potential applications of Eu3+-doped Y2O3 photoluminescent material in ceramic powder form

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)