Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mechanochemical synthesis of lead magnesium niobate ceramics in iron media

The possibility of mechanochemical synthesis of the lead magnesium niobate (PMN) powders of the composition Pb(Mg(1/3)Nb(2/3))O(3) in iron vials was investigated. According to X-ray and energy-dispersive spectroscopy (EDS) analysis of the obtained powder mixtures, milling in iron vials resulted in incorporation of Fe and formation of PFN of composition Pb(Fe(1/2)Nb(1/2))O(3) simultaneously with formation of PMN. Relative amounts of PMN and PFN were determined based on values of Curie temperature and lattice constant of perovskite phase. Although only 1 wt pct of Fe was incorporated, a stoichiometry of the system was significantly changed, resulting in formation of pyrochlore phase and excess MgO. Single-phase perovskite was obtained when the excess of PbO and Nb(2)O(5) was added during mechanochemical synthesis. Because the dielectric properties were worse than expected, the alternative ways for improvement of dielectric properties were tried and discussed.

Screen printed barium titanate thick films prepared from mechanically activated powders

Barium titanate thick films were prepared from mechanically activated powders based on BaCO 3 and TiO 2. The thick films were screen-printed on alumina substrates electroded with Ag/Pd. The BT films were sintered at 850°C for 1 hour. The thickness was 30-75 μm depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate was investigated by SEM. The dielectric properties were measured and the results were reported.

Effect of Nb on barium titanate prepared from citrate solutions

The influence of the addition of dopants on the microstructure development and electrical properties of BaTiO3 doped with 0.2, 0.4, 0.6, 0.8 mol% of Nb and 0.01 mol% of Mn based compounds was studied. Doped barium titanate was prepared using the polymeric precursor method from citrate solutions. The powders calcined at 700°C for 4 hours were analysed by infrared (IR) spectroscopy to verify the presence of carbonates, and by X-ray diffraction (XRD) for phase formation. The phase composition, microstructure and dielectric properties show a strong dependence on the amount of added niobium.

Estudio de la adición de K+ y LiNbO3 en las propiedades finales del relaxor PMN procesado por mezcla de polvos

PMN ceramic relaxor has been investigated by several researchers and many aspects of this material, like powder morphology, phase decomposition, weight loss during sintering process, densification, between others, still are investigated. PMN powder preparation has been shown more efficient when synthesized by columbite route, however lead addition stage for the PMN powder synthesis remains problematical. Therefore, this work proposes a new association of methodologies, using columbite route and the hydroxide precipitation method. Through use of the powder mixture technique, which permitted to obtain good green and sintered densities, was possible to observe K+ y Li + dopants reduce weight loss in sintering process and change significantly the dielectric properties. Addition of LiNbO3 seeds in conformation stage, which react in a distinct way as a function of the particle size, promotes the formation of differenced grains in the ceramic bulk. Consequently, very different dielectrics properties from conventional PMN ceramic were obtained.

Structure study of donor doped barium titanate prepared from citrate solutions

Barium titanates doped with Nb5+, and Y3+, were prepared. The starting powders were synthesized from citrate solutions by the Pechini process and partial Pechini process in two steps. Sintering was performed in the range from 1310° up to 1380°C for 2 hours in air atmosphere. The structural study concerning the incorporation of Nb and Y ions in the barium titanate crystal lattice was performed by XRD, XANES and EXAFS techniques. The dielectric properties were analyzed and the relationship between properties and structure of doped barium titanate was established.

The synergistic effects of Nb/Mn and Sb/Mn on the microstructure and electrical characteristics of BaTiO3 based ceramics

The microstructure and dielectric properties of Nb-Mn or Sb-Mn codoped BaTiO3 compositions were investigated. Starting ceramics powders were prepared by Pechini method. The composites were sintered at 1310°C and 1330°C in an air atmosphere for two hours. The microstructure and compositional investigations were done with SEM equipped with EDS. Two distinguish microstructure regions are observed in Nb/0.05Mn doped BaTiO 3 ceramics sintered at low temperature. The first, large one, with grain sizes from 5-40 μm and the second region with small grain sizes from 1 to 5 μm. Sintering at higher temperature, independent of Mn content, enables to achieve a uniform microstructure with grains less than 6 μm. In Sb/Mn doped ceramics, for both sintering temperatures, bimodal microstructures with fine grained matrix and grains up to 10 μm is formed. The highest value of permittivity at room temperature and the greatest change of permittivity in function of temperature are observed in Nb/0.01Mn doped ceramics compared to the same ones in Sb/Mn doped ceramics. The greatest shift of Curie temperature towards lower temperature has been noticed in Sb/Mn BaTiO3 ceramics compared to others samples. In all investigated samples the dielectric loss after initially large values at low frequency maintains a constant value for f>3 kHz.

New developments for lignocellulosics-nanocomposites with low carbon footprint

Cellulose nanofibrils have been evaluated as reinforcement material in polymeric matrixes due to their potential to improve the mechanical, optical, and dielectric properties of these matrixes as well as its environmental positive footprint. This work describes how banana nanocellulose can be used to replace others not so friendly materials in many applications including, biomaterials, automotive industries and packaging by proved with their mechanical properties. The process used is very mild to the environment and consists of a high pressure fibrillation followed by a chemical purification which affects the fiber morphology. Many fibers characterization processes were used including microscopy techniques and X-ray diffraction to study the structure and properties of the prepared nanofibers and composites. Microscopy studies showed that the used individualization processes lead to a unique morphology of interconnected web-like structure of the fibers. © 2012 Materials Research Society.

Piezoresponse force microscopy characterization of rare-earth doped BiFeO3 thin films grown by the soft chemical method

The multiferroic behavior with ion modification using rare-earth cations on crystal structures, along with the insulating properties of BiFeO3 (BFO) thin films was investigated using piezoresponse force microscopy. Rare-earth-substituted BFO films with chemical compositions of (Bi 1.00-xRExFe1.00O3 (x=0; 0.15), RE=La and Nd were fabricated on Pt (111)/Ti/SiO2/Si substrates using a chemical solution deposition technique. A crystalline phase of tetragonal BFO was obtained by heat treatment in ambient atmosphere at 500 °C for 2 h. Ion modification using La3+ and Nd3+ cations lowered the leakage current density of the BFO films at room temperature from approximately 10-6 down to 10-8 A/cm2. The observed improved magnetism of the Nd3+ substituted BFO thin films can be related to the plate-like morphology in a nanometer scale. We observed that various types of domain behavior such as 71° and 180° domain switching, and pinned domain formation occurred. The maximum magnetoelectric coefficient in the longitudinal direction was close to 12 V/cm Oe. © 2012 Elsevier Ltd and Techna Group S.r.l.

Estudo das propriedades dielétricas e de bloqueio das monocamadas automontadas

Pós-graduação em Biotecnologia - IQ

Caracterização dielétrica de partículas nanométricas e nanoestruturadas de óxido de niobato da família tetragonal tungstênio bronze com estequiometria K'Sr IND. 2' N'b IND. 5' 'O IND. 15'

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Determinação de parâmetros ópticos de materiais por análise de Kramers-Kronig de espectros de infravermelho

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Propriedades dielétricas de cerâmicas relaxoras PMN

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo de transições de fases estruturais nos sistemas PZT e PMN-PT por espectroscopia no infravermelho e espectroscopia de impedância

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação de filmes finos ferroelétricos de SrBi2'('TA IND.1-x''NB IND.x)ÍND.2 'O IND.9' puro e dopado com tungstênio, obtidos pelo método dos precursores poliméricos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)