Effect of tartrate content on aging and deposition condition of copper-tin electrodeposits from a non-cyanide acid bath

The effect of the presence of tartrate additive on the chemical stability of a Cu-Sn acid bath was evaluated. It was observed that this additive hinders decomposition of the Cu/Sn deposition bath with storage time, since the decrease in electrochemical efficiency was attenuated. In addition, it was observed that optimal galvanostatic deposition with or without tartrate occurs at approximately 11 mA cm(-2). However, in the presence of tartrate the deposition charge was lower, leading to lower energy consumption. SEM analysis showed that the tartrate added to the plating bath caused a marked change in the morphology of the Cu/Sn films obtained gal vanostatic ally. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Photocatalytic Degradation of Phenol by Thermal Titanium Dioxide Thin Layer Electrodes

Electrochemical processes in industrial effluents have been studied as a means to obtain higher efficiency in wastewater treatment. Heterogeneous photocatalysis appears as a low-cost alternative through the use of lower wattage lamps and thermal TiO2 films. Photocatalysis became a clean process for water treatment due to hydroxyl radicals generated on semiconductor surface. Such radicals are able to degrade several organic compounds. This study used different electrodes and analytical methods for degradation of phenol molecules to reduce treatment costs, improve efficiency, and identify compounds formed during the decomposition of phenolic molecules. Thermal growth of TiO2 film was observed on the titanium electrode in rutile form. Application of an electrical potential on the Ti/TiO2 working electrode increases efficiency in reducing concentration of phenol after photocatalytic treatment. Still, high energy radiation (UVC) showed best degradation rates in photolytic process. Different compounds formed during the degradation of phenol were also identified in the UVC-PE treatment.

Influence of rare earth doping on the structural and catalytic properties of nanostructured tin oxide

Nanoparticles of tin oxide, doped with Ce and Y, were prepared using the polymeric precursor method. The structural variations of the tin oxide nanoparticles were characterized by means of nitrogen physisorption, carbon dioxide chemisorption, X-ray diffraction, and X-ray photoelectron spectroscopy. The synthesized samples, undoped and doped with the rare earths, were used to promote the ethanol steam reforming reaction. The SnO2-based nanoparticles were shown to be active catalysts for the ethanol steam reforming. The surface properties, such as surface area, basicity/base strength distribution, and catalytic activity/selectivity, were influenced by the rare earth doping of SnO2 and also by the annealing temperatures. Doping led to chemical and micro-structural variations at the surface of the SnO2 particles. Changes in the catalytic properties of the samples, such as selectivity toward ethylene, may be ascribed to different dopings and annealing temperatures.

Morphological characterization of Langmuir-Blodgett films from polyaniline and a ruthenium complex (Rupy): influence of the relative concentration of Rupy

We report on the use of dynamic scale theory and fractal analyses in a study of the growth stages of Langmuir-Blodgett (LB) films of polyaniline and a neutral biphosphinic ruthenium complex, namely mer-[ RuCl3 (dppb)(py)] (dppb = 1,4-bis(diphenylphosphine) buthane, py = pyridine), Rupy. The LB films were deposited onto indium-tin-oxide substrates and characterized with atomic force microscopy. From the granular morphology exhibited by the films one could infer growth processes inside and outside the grains. Growth outside was found to follow the Kardar-Parisi-Zhang model, with fractal dimensions of about 2.7. As one would expect, inside the grains the morphology is close to a Euclidian surface with fractal dimension of about 2.

Influence of heat treatment on the optical properties of SnO2 : Sb thin films deposited by dip coating using aqueous solution

Antimony doped tin oxide thin films were deposited on glass by a chemical route derived from Pechini method. Particular emphasis was given to the microstructure of crystallized films. Crystalline phase formation was studied by grazing incident X-ray diffraction and by thermal analyses. Scanning electron microscopy was carried out for microstructure characterization, surface roughness was observed using scanning tunneling microscope and the optical transmittance measurements were performed in the wavelength range of 200-800 nm. (C) 2002 Kluwer Academic Publishers.

Deposition of controlled thickness ultrathin SnO2 : Sb films by spin-coating

The technological interest in transparent conductive oxide films (TCOs) has motivated several works in processing techniques, in order to obtain adequate routes to application. In this way, this work describes a new route to obtain antimony-doped tin oxide (ATO) films, based in colloidal dispersions of oxide nanocrystals. The nanoparticles were obtained by a hydrolisis method, using SnCl2 and SbCl3 in ethanolic solutions. The residual halides were removed by dyalisis, obtaining a limpid and transparent colloidal suspension. By this, the method offers the advantage of producing ultrathin films without organic contaminants. This route was employed to produce films with 5, 10, 14, and 18 mol% Sb doping, with thickness ranging from 40 to 70 nm. The physical characterization of the samples showed a uniform layer deposition, resulting in good packing density and high transmittance. A preliminar electrical study confirmed the low electrical resistivity even in the ultrathin films, in such level similar of reported data. The method described is similar in some aspects to layer-by-layer (LbL) techniques, allowing fine control of thickness and interesting properties for ultrathin films, however, with low cost when compared to similar routes.

Effect of thickness on the electrical and optical properties of Sb doped SnO2 (ATO) thin films

This work reports the preparation and characterization of (SnO2) thin films doped with 7 mol% Sb2O3. The films were prepared by the polymeric precursor method, and deposited by spin-coating, all of them were deposited on amorphous silica substrate. Then, we have studied the thickness effect on the microstrutural, optical and electric properties of these samples. The microstructural characterization was carried out by X-ray diffraction (XRD) and scanning tunneling microscopy (STM). The electrical resistivity measurements were obtained by the van der Pauw four-probe method. UV-visible spectroscopy and ellipsometry were carried out for the optical characterization. The films present nanometric grains in the order of 13 nm, and low roughness. The electrical resistivity decreased with the increase of the film thickness and the smallest measured value was 6.5 x 10(-3) Omega cm for the 988 nm thick film. The samples displayed a high transmittance value of 80% in the visible region. The obtained results show that the polymeric precursor method is effective for the TCOs manufacturing.

Density improvement of the sol-gel dip-coated SnO2 films by chemical surface modification

We compare the effect of organic (Tiron (R)) and inorganic (Mn(11)) additives on the low temperature (< 600 degrees C) densification of the sol-gel dip-coated SnO2 films. The structural and compositional properties of the samples were investigated by X-ray reflectometry (XRR), X-ray absorption spectroscopy (XAS) and X-ray photoelectron spectroscopy (XPS). The results suggest that the replacement of hydroxyl groups at the particle surface by Tiron (R) reduces the level of agglomeration of the sol, increasing the particles packing and the apparent density of the coatings. Undoped and Mn-doped films drawn from a Tiron (R) containing suspension show after firing at 500 degrees C a porosity reduction of 12 and 8.6%, respectively. The porosity decrease is less pronounced (4.3%) for the film without additives. Both XAS and XPS data show the presence of trivalent manganese. The formation of a non-homogeneous solid solution characterised by the presence of Mn(111) replacing tin atom near to the crystallite surface was evidenced by XAS. Additionally, XPS results reveal the presence of metallic Sn at the surface of films containing Tirono. (c) 2005 Elsevier Ltd. All rights reserved.

Film formation and surface growth on tin electrodes in bicarbonate solutions: an impedance spectroscopy study

The electrochemical behaviour of potentiodynamically formed thin anodic films of polycrystalline tin in aqueous sodium bicarbonate solutions (pH approximate to 8.3) were studied using cyclic voltammetry and electrochemical impedance spectroscopy. Different equivalent circuits corresponding to various potential regions were employed to account for the electrochemical processes taking place under each condition. (C) 2004 Elsevier Ltd. All rights reserved.

Effect of temperature on glass-ceramic films prepared by impregnation of commercial float glass surfaces with oxide powders under pressure

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Nanomechanical properties of glass-ceramic films obtained by pressure impregnation of oxide powders on commercial float glass surfaces

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Improved Conductivity Induced by Photodesorption in SnO2 Thin Films Grown by a Sol-Gel Dip Coating Technique

Thin films of undoped and Sb-doped SnO2 have been prepared by a sol-gel dip-coating technique. For the high doping level (2-3 mol% Sb) n-type degenerate conduction is expected, however, measurements of resistance as a function of temperature show that doped samples exhibit strong electron trapping, with capture levels at 39 and 81 meV. Heating in a vacuum and irradiation with UV monochromatic light (305 nm) improve the electrical characteristics, decreasing the carrier capture at low temperature. This suggests an oxygen related level, which can be eliminated by a photodesorption process. Absorption spectral dependence indicates an indirect bandgap transition with Eg ≅ 3.5 eV. Current-voltage characteristics indicate a thermionic emission mechanism through interfacial states.

Behavior of bromide in the photoelectrocatalytic process and bromine generation using nanoporous titanium dioxide thin-film electrodes

In this study, the photoelectrocatalytic behavior of bromide and generation of bromine using TiO2 was investigated in the separate anode and cathode reaction chambers. Our results show that the generation of bromine begins around a flatband potential of -0.34 V vs. standard calomel electrode (SCE) at pH 3.0 under UV illumination and increases with an increase in positive potential, finally reaching a steady-state concentration at 1.0 V vs. SCE. Maximum bromine formation occurs over the range of pH 4-6, decreasing sharply at conditions where the pH > 7. © 2003 Elsevier Ltd. All rights reserved.

Corrosion protection of fluorzirconate glasses coated by a layer of surface modified tin oxide nanoparticles

The protection efficiency against water corrosion of fluorozirconate glass, ZBLAN, dip-coated by nanocrystalline tin oxide film containing the organic molecule Tiron® was investigated by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). The chemical bonding structure of the surface region and morphology were studied before and after two water exposure periods of 5 and 30 min. The results of the analysis for the as-grown sample revealed a SnO1.6 phase containing carbon and sulfur, related to Tiron®, and traces of elements related to ZBLAN (Zr, F, Ba). This fact and the clear evidence of the presence of tin oxifluoride specie (SnOxF y) indicates a diffusion of the glass components into the porous coating. After water exposure, the increase of the oxygen concentration accompanied by a strong increase of Zr, F, Ba and Na content is interpreted as filling of the nanopores of the film by glass compounds. The formation of a compact protective layer is supported by the morphological changes observed by AFM. © 2005 Elsevier B.V. All rights reserved.

Biodegradability of PP/PHBV (70/30) blend films

This study aimed to investigate the biodegradation of polypropylene/ poly(hydroxybutyrate-co-hydroxyvalerate) (PP/PHBV) blend (70/30, w/w) films in soil, monitoring the evolution of CO2 using the respirometric method. The polymeric films were incubated at 28°C ± 2°C for 180 days in biometer flasks, and the sequence of biodegradation percentage was PP/PHBV (70/30) > PP, that is, 15% and 0%, respectively. Fourier transform infrared spectroscopy and X-ray diffraction measurements showed that biodegradation occurs in the blend PP/PHBV interphases. Preferentially, the microbial action occurs in the fraction of the biodegradable polymer (PHBV), and it influences the PP fraction morphology, which showed some significant changes in the monomer unit sequences and the organization of the chains. © 2013 Wiley Periodicals, Inc.