Synthesis, structural refinement and optical behavior of CaTiO3 powders: A comparative study of processing in different furnaces

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Hierarchical Assembly of CaMoO4 Nano-Octahedrons and Their Photoluminescence Properties

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Controlled fluorination of a-C:F:H films by PECVD of ethylene-hexafluorobenzene mixtures

Highly fluorinated plasma polymers are chemically inert,acid resistant and have low friction coefficients, thereby being useful in chemical laboratories and for tribological applications. Here we report the plasma polymerization of ethylene-hexafluorobenzene mixtures by PECVD. The principal parameter of interest is the proportion of C(6)F(6) in the feed, R(F). Films were analyzed using near-normal and grazing-angle Infrared Reflection Absorption Spectroscopy (IRRAS), the latter being particularly useful for detecting modes not usually observed at near-normal incidence. The presence of CH and CF(x) (x=1 to 2) groups was thus confirmed in films deposited with R(F)>= 40%. Depending on R(F) IRRAS also revealed the presence of -CH(x) (x=1 to 3) -C=C, -C=O and phenyl rings. Deconvolution of C is spectra obtained by X-ray Photoelectron Spectroscopy (XPS) confirmed the presence of CH, CF and CF(2) groups in films deposited with R(F)>= 40%. Atomic ratios of F:C calculated from the XPS spectral data show that the degree of fluorination rises with increasing RF Some unbound fluorine is present in the films. Post-deposition reactions account for the presence of oxygen (similar to 5%) in the films. Surface energies, determined from contact angle measurements, fall with increasing R(F). (C) 2008 Elsevier B.V. All rights reserved.

Study of the annealing temperature effect on the structural and luminescent properties of SrWO4:Eu phosphors prepared by a non-hydrolytic sol-gel process

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microstructure, dielectric properties and optical band gap control on the photoluminescence behavior of Ba[Zr0.25Ti0.75]O-3 thin films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A new processing method of CaZn2(OH)(6)center dot 2H(2)O powders: Photoluminescence and growth mechanism

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Thin films prepared from tungstate glass matrix

Vitreous samples containing high concentrations of WO3 (above 40% M) have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. These films were characterized by X-ray diffraction (XRD), perfilometry, X-ray energy dispersion spectroscopy (EDS), M-Lines and UV-vis absorption spectroscopy. In this work, experimental parameters were established to obtain stable thin films showing a chemical composition close to the glass precursor composition and with a high concentration of WO3. These amorphous thin films of about 4 mu m in thickness exhibit a deep blue coloration but they can be bleached by thermal treatment near the glass transition temperature. Such bleached films show several guided modes in the visible region and have a high refractive index. Controlled crystallization was realized and thus it was possible to obtain WO3 microcrystals in the amorphous phase. (C) 2007 Elsevier B.V. All rights reserved.

CALCULATION of MAGNETODONOR STATES IN InP and POLARON EFFECTS

Far-infrared transitions in polar semiconductors are known to be affected by the presence of shallow donor impurities, external magnetic fields and the electron-LO-phonon interaction. We calculate the magnetodonor states in indium phosphide by a diagonalization procedure, and introduce the electron-phonon interaction by the Frohlich term. The main effects of this perturbation are calculated by a multi-level version of the Wigner-Brillouin theory. We determine the transition energies, from the ground state to excited states, and find good qualitative agreement with recently reported absorption-spectroscopy measurements in the 100-800 cm(-1) range, with applied magnetic fields up to 30 T. Our calculations suggest that experimental peak splittings in the 400-450 cm(-1) range are due to the electron-phonon interaction.

Developments in hot-filament metal oxide deposition (HFMOD)

Hot-filament metal oxide deposition (HFMOD) is a variant of conventional hot-filament chemical vapor deposition (HFCVD) recently developed in our laboratory and successfully used to obtain high-quality, uniform films of MOx WOx and VOx. The method employs the controlled oxidation of a filament of a transition metal heated to 1000 degrees C or more in a rarefied oxygen atmosphere (typically, of about 1 Pa). Metal oxide vapor formed on the surface of the filament is transported a few centimetres to deposit on a suitable substrate. Key system parameters include the choice of filament material and diameter, the applied current and the partial pressures of oxygen in the chamber. Relatively high film deposition rates, such as 31 nm min(-1) for MoOx, are obtained. The film stoichiometry depends on the exact deposition conditions. MoOx films, for example, present a mixture of MoO2 and MoO3 phases, as revealed by XPS. As determined by Li+ intercalation using an electrochemical cell, these films also show a colouration efficiency of 19.5 cm(2) C-1 at a wavelength of 700 nm. MOx and WOx films are promising in applications involving electrochromism and characteristics of their colouring/bleaching cycles are presented. The chemical composition and structure of VOx films examined using IRRAS (infrared reflection-absorption spectroscopy), RBS (Rutherford backscattering spectrometry) and XPS (X-ray photoelectron spectrometry) are also presented. (c) 2007 Elsevier B.V. All rights reserved.

Characterization of Si : O : C : H films fabricated using electron emission enhanced chemical vapour deposition

Silicon-based polymers and oxides may be formed when vapours of oxygen-containing organosilicone compounds are exposed to energetic electrons drawn from a hot filament by a bias potential applied to a second electrode in a controlled atmosphere in a vacuum chamber. As little deposition occurs in the absence of the bias potential, electron impact fragmentation is the key mechanism in film fabrication using electron-emission enhanced chemical vapour deposition (EEECVD). The feasibility of depositing amorphous hydrogenated carbon films also containing silicon from plasmas of tetramethylsilane or hexamethyldisiloxane has already been shown. In this work, we report the deposition of diverse films from plasmas of tetraethoxysilane (TEOS)-argon mixtures and the characterization of the materials obtained. The effects of changes in the substrate holder bias (Vs) and of the proportion of TEOS in the mixture (XT) on the chemical structure of the films are examined by infrared-reflection absorption spectroscopy (IRRAS) at near-normal and oblique incidence using unpolarised and p-polarised, light, respectively. The latter is particularly useful in detecting vibrational modes not observed when using conventional near-normal incidence. Elemental analyses of the film were carried out by X-ray photoelectron spectroscopy (XPS), which was also useful in complementary structural investigations. In addition, the dependencies of the deposition rate on Vs and XT are presented. (c) 2007 Elsevier B.V. All rights reserved.

Structure and optical properties of [Ba1-xY2x/3](Zr0.25Ti0.75)O-3 powders

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and photoluminescence behavior of Bi4Ti3O12 powders obtained by the complex polymerization method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Photoluminescent behavior of BaWO4 powders processed in microwave-hydrothermal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

(Sr,Tm)ZrO3 powders prepared by the polymeric precursor method: Synthesis, optical properties and morphological characteristics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Novel SrTi1-xFexO3 nanocubes synthesized by microwave-assisted hydrothermal method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)