Structural and electrochemical properties of LiCoO2 prepared by combustion synthesis

LiCoO2 powders were prepared by combustion synthesis, using metallic nitrates as the oxidant and metal sources and urea as fuel. A small amount of the LiCoO2 phase was obtained directly from the combustion reaction, however, a heat treatment was necessary for the phase crystallization. The heat treatment was performed at the temperature range from 400 up to 700 degreesC for 12 h. The powders were characterized by X-ray diffraction (XRD), X ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and specific surface area values were obtained by BET isotherms. Composite electrodes were prepared using a mixture of LiCoO2, carbon black and poly(vinylidene fluoride) (PVDF) in the 85:10:5% w/w ratio. The electrochemical behavior of these composites was evaluated in ethylene carbonate/dimethylcarbonate solution, using lithium perchlorate as supporting electrolyte. Cyclic voltammograms showed one reversible redox process at 4.0/3.85 V and one irreversible redox process at 3.3 V for the LiCoO2 obtained after a post-heat treatment at 400 and 500 degreesC.Raman spectroscopy showed the possible presence of LiCoO2 with cubic structure for the material obtained at 400 and 500 degreesC. This result is in agreement with X-ray data with structural refinement for the LiCoO2 powders obtained at different temperatures using the Rietveld method. Data from this method showed the coexistence of cubic LiCoO2 (spinel) and rhombohedral (layered) structures when LiCoO2 was obtained at lower temperatures (400 and 500 degreesC). The single rhombohedral structure for LiCoO2 was obtained after post-heat treatment at 600 degreesC. The maximum energy capacity in the first discharge was 136 mA g(-1) for the composite electrode based on LiCoO2 obtained after heat treatment at 700 degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Dynamical Elastic Moduli of the Ti-13Nb-13Zr biomaterial alloy by mechanical spectroscopy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural characterization of Ti-15Mo alloy used as biomaterial by Rietveld method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Nanoindentation mechanical properties characterization of glassy polymeric carbon treated with ion beam

Phenolic resins when heat treated in inert atmosphere up to 1000 degreesC become glassy polymeric carbon (GPC), a chemically inert and biocompatible material useful for medical applications, such as in the manufacture of heart valves and prosthetic devices. In earlier work we have shown that ion bombardment can modify the surface of GPC, increasing its roughness. The enhanced roughness, which depends on the species, energy and fluence of the ion beam, can improve the biocompatibility of GPC prosthetic artifacts. In this work, ion bombardment was used to make a layer of implanted ions under the surface to avoid the propagation of microcracks in regions where cardiac valves should have pins for fixation of the leaflets. GPC samples prepared at 700 and 1500 degreesC were bombarded with ions of silicon. carbon, oxygen and gold at energies of 5, 6, 8 and 10 MeV, respectively, and fluences between 1.0 x 10(13) and 1.0 x 10(16) ions/cm(2). Nanoindentation hardness characterization was used to compare bombarded with non-bombarded samples prepared at temperatures up to 2500 degreesC. The results with samples not bombarded showed that the hardness of GPC increases strongly with the heat treatment temperature. Comparison with ion bombarded samples shows that the hardness changes according to the ion used, the energy and fluence. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Obtaining of Nanoapatite in Ti-7.5Mo Surface After Nanotube Growth

Titanium and their alloys have been used for biomedical applications due their excellent mechanical properties, corrosion resistance and biocompatibility. However, they are considered bioinerts materials because when they are inserted into the human body they are cannot form a chemical bond with bone. In several studies, the authors have attempted to modify their characteristic with treatments that changes the material surface. The purpose of this work was to evaluate obtaining of nanoapatite after growing of the nanotubes in surface of Ti-7.5Mo alloy. Alloy was obtained from c.p. titanium and molibdenium by using an arc-melting furnace. Ingots were submitted to heat treatment and they were cold worked by swaging. Nanotubes were processed using anodic oxidation of alloy in electrolyte solution. Surfaces were investigated using scanning electron microscope (SEM), FEG-SEM and thin-film x-ray diffraction. The results indicate that nanoapatite coating could form on surface of Ti-7.5Mo experimental alloy after nanotubes growth.

Growth of Calcium Phosphate Using Chemically Treated Titanium Oxide Nanotubes

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

A metallurgical study of aluminium alloys used as aircraft components

The effects of heat treatment on morphologies and microstructures of Al 2024 and Al 7050 alloys, used as aircraft components, were studied by metallographic techniques. Light microscopy (LM) and quantitative image analysis were used to characterize the precipitate dispersion and morphology for these alloys. The application of the scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) combined techniques for studying these multiphase systems makes it possible to distinguish and quantify the different phases in the surface structure. Xray diffraction also permitted a qualitative comparison of the structures before and after heat treatments.

Caracterização mecânica e microestrutural de um aço baixo carbono microligado com estrutura multifásica

Neste trabalho foi realizada a caracterização mecânica e microestrutural de um aço microligado com estrutura multifásica. Foi aplicado tratamento térmico pré-determinado, objetivando a formação de uma microestrutura multifásica no material. Na caracterização microestrutural foram utilizados ataques químicos à base de metabissulfito de sódio e ácido pícrico, enquanto a caracterização mecânica foi realizada através de ensaios de tração. Os resultados demonstram o elevado potencial dos aços multifásicos em aplicações que necessitem de valores superiores de resistência e ductilidade, pois tanto para temperatura isotérmica de 400ºC quanto para 350ºC houve um ganho no limite de resistência à tração ficando em torno de 786MPa e 773MPa respectivamente, representando um aumento de 15,5% e 13,6% com relação ao material fornecido.

Surface characterization of Ti-7.5Mo alloy modified by biomimetic method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal and mechanical behaviour of sisal/phenolic composites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Fatigue Strength of X45CrSi93 stainless steel applied as internal combustion engine valves

Stainless steels are used to intake and exhaust valves production applied as internal combustion engines. In general valves are requested to support cyclic stresses applied due to opening and closing processes during the operation. The objective of this research is to study the influence on the axial fatigue strength of the resulting microstructure after heat treatment at the martensitic X45CrSi93 steel, combined with different surface treatments as hard chrome-plating, nitride and grinding. It was verified a significant increase on the fatigue strength of the martensitic steel after nitriding, compared with results from the chrome-plating specimens. A slight increase in the tensile strength was also noticed on nitrided parts as a consequence of a resistance increase due to nitrogen and carbon solid solution. (C) 2011 Published by Elsevier Ltd. Selection and peer-review under responsibility of ICM11

Morphological evolution of tin oxide nanobelts after phase transition

This article reports a study of the thermal stability and morphological changes in tin oxide nanobelts grown in the orthorhombic SnO phase. The nanobelts were heat-treated in a differential scanning calorimetry (DSC) furnace at 800 degrees C for I It in argon, oxygen, or synthetic air atmospheres. The samples were then characterized by DSC, X-ray diffraction (XRD), high resolution transmission electron microscopy (HRTEM), and high resolution field emission scanning electron microscopy (FE-SEM). The results confirmed that the orthorhombic SnO phase is thermodynamically unstable, causing the belts to transform into the SnO2 phase when heat-treated. During the phase transition, if oxygen is available in the furnace atmosphere, nanofibers grow at the edge of nanobelts at about 50 degrees of the belts' growth direction, while particles grow on the belt surface in the absence of oxygen. Although the decomposition process reduces the nanobelt cell volume by 22%, most belts remain monocrystalline after the heat treatment. The results confirm that phase transition is a decomposition process, which explains the morphological changes in the belts based on metallic tin generated in the process.

Biomimetic calcium phosphate coating on Ti-7.5Mo alloy for dental application

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Histological and three-dimensional evaluation of osseointegration to nanostructured calcium phosphate-coated implants

Nanostructures on implant surfaces have been shown to enhance osseointegration; however, commonly used evaluation techniques are probably not sufficiently sensitive to fully determine the effects of this process. This study aimed to observe the osseointegration properties of nanostructured calcium phosphate (CaP)-coated implants, by using a combination of three-dimensional imaging and conventional histology. Titanium implants were coated with stable CaP nanoparticles using an immersion technique followed by heat treatment. Uncoated implants were used as the control. After topographical and chemical characterizations, implants were inserted into the rabbit femur. After 2 and 4 weeks, the samples were retrieved for micro-computed tomography and histomorphometric evaluation. Scanning electron microscopy evaluation indicated that the implant surface was modified at the nanoscale by CaP to obtain surface textured with rod-shaped structures. Relative to the control, the bone-to-implant contact for the CaP-coated implant was significantly higher at 4 weeks after the implant surgery. Further, corresponding 3-D images showed active bone formation surrounding the implant. 3-D quantification and 2-D histology demonstrated statistical correlation; moreover, 3-D quantification indicated a statistical decrease in bone density in the non-coated control implant group between 2 and 4 weeks after the surgery. The application of 3-D evaluation further clarified the temporal characteristics and biological reaction of implants in bone. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Ribonuclease production by Aspergillus species

Ribonuclease production by Aspergillus flavipes. A sulphureus and A. fischeri in semisynthetic medium, after 24-144 hours at 30 degrees C under shaking, was studied. After cultivation, the medium was separated from micelia by filtration and the resultant solution was used as enzymatic extract. The highest amount of biomass and RNase was obtained after 96 hours of cultivation. The enzymes produced by three species presented similar characteristics, with optimum temperature at 55 degrees C and two peaks of activity at pH 4.5 and 7.0. A. flavipes RNases were more sensitive to temperature: 50% of the initial activity was lost after 1 hour at 70 degrees C. After this heat treatment, RNase of A. sulphureus lost 30% of this activity and that of A. fischeri only 16%. The nucleotides released by enzimatic hydrolysis of RNA were separated by ion exchange chromatography in a AG-1X8-formiate column and identified by paper chromatography. This procedure indicated that the raw enzymatic extract of Aspergillus flavipes is able to hydrolyze RNA, releasing 3'-nucleotides monophosphate at pH 4.5 and 3' and 5'-nucleotides monophosphate at pH 7.0 and 8.5. This result suggests that this strain produces two different types of RNase, one acidic and other alcaline, with different specificities.