Increasing the dielectric breakdown strength of poly(ethylene terephthalate) films using a coated polyaniline layer

The dielectric strength of films made from poly(ethylene terephthalate) (PET) coated with a thin layer of polyaniline (PANI) was studied. The PANI layer was deposited on the PET films by the 'in situ' chemical polymerization method. The PANI layer of the PANI/PET films was undoped in NH4OH 0.1 M solution and re-doped with aqueous HCl solution under different pH values varying from 1 to 10. Electric breakdown measurements were performed by applying a voltage ramp and the results showed a dependence of the dielectric strength on the pH of the doping solution due to the changes in the electrical conductivity of the PANI layer. The dielectric strength of PET/PANI films treated under higher pH conditions showed an electric strength about 30% larger than the PET films, since it leads to a non-conductive PANI layer.

Polymerization of ethylene by the tris(pyrazolyl)borate titanium(IV) compound immobilized on MAO-modified silicas

The immobilization of soluble catalyst {Tp(Ms)}TiCl3 (Tp(Ms*)HB(3-mesityl-pyrazolyl)(2)(5-mesityl-pyrazolyl)(-)) on silica and MAO-modified silicas containing 4.0, 8.0 and 23.0 wt.% Al/SiO2 yields active supported catalysts for ethylene polymerization. Among the supported catalysts studied by XRF spectroscopy, higher titanium content was obtained using MAO-modified silica containing 8.0 wt.% Al/SiO2 as support. For the ethylene polymerization reactions carried out in hexane at 60degreesC using a combination of triisobutylaluminum (TiBA) and methylaluminoxane (MAO) (1:1), the activities varied between 24.4 and 113.5 kg of PE/mol [Ti] h. The highest activity is reached using MAO-modified silica containing 4.0 wt.% Al/SiO2 as support. The viscosity-average molecular weights ((M) over bar (v)) of the PE's produced with the supported catalysts varying from 1.44 to 9.94 x 10(5) g/mol with melting temperatures in the range of 125-140degreesC. The use of other Lewis acid cocatalysts, including TiBA, diethylaluminium chloride (DEAC), and trimethylaluminum (TMA) resulted also in the formation of active catalysts for ethylene polymerization. However, the activities are lower than that one using a combination of TiBA and MAO. The viscosity-average molecular weights (R,) of PE's are influenced by varying the cocatalysts as well as the Al/Ti molar ratio. The supported catalyst generated in situ under ethylene atmosphere is roughly four times more active than supported one containing 4.0 wt.% Al/SiO2. (C) 2003 Elsevier B.V. All rights reserved.

Highly selective nickel ethylene oligomerization catalysts based on sterically hindered tris(pyrazolyl)borate ligands

The reaction of TlTp' (Tp' = HB(3-mesitylpyrazolyl)(3)(-) (Tp(Ms)), HB(3-mesitylpyrazolyl)(2)(5-mesitylpyrazolyl)(-) (Tp(Ms)*)) with NiCl(2).6H(2)O affords Tp(Ms)NiCl (1) and Tp(Ms)*NiCl (2) in good yield. The compound 2 undergoes an isomerization process to form [{Tp(Ms)**}NiCl](2) (3) (Tp(Ms)** = HB(5-mesitylpyrazolyl)(2)(3-mesitylpyrazolyl)(-)) in 68% yield. Treatment of the tris(pyrazolyl)-borate nickel compounds 1 and 2 with alkylaluminum cocatalysts such as methylalumoxane (MAO) and trimethylaluminum (TMA) in toluene generates active catalysts for ethylene oligomerization. The compound 1 shows turnover frequencies in the range of (2.2-43.1) x 10(3) h(-1). Oligomerization reaction conditions can be adjusted that lead to selectivities as high as 81% for butene-1.

Thermal and photochemical stability of poly(vinyl alcohol)/modified lignin blends

A kraft lignin derivative (KLD) obtained by reaction with p-aminobenzoic acid/phthalic anhydride was blended with poly(vinyl alcohol) (PVA) by solution casting from DMSO. PVA and PVA/KLD films were exposed to ultraviolet radiation (24, 48, and 96 h) and analyzed by thermogravimetry (TG), differential scanning calorimetry (DSC), infrared spectroscopy (FTIR), hydrogen nuclear magnetic resonance (H-1 NMR) spectroscopy, and scanning electron microscopy (SEM). PVA films show a loss of thermal stability due to irradiation. PVA/KLD reveals greater thermal stability than PVA and an increase in thermal stability after irradiation. These results suggest that the incorporation of KLD into PVA provides a gain in thermal and photochemical stability. FTIR, H-1 NMR, DSC, and TG results obtained for the blends suggest that intermolecular interactions between PVA and KLD chains are present. SEM micrographs revealed blend miscibility for a KLD blend content of up to 15 wt%, as observed at magnification of 1000 times. (c) 2005 Elsevier Ltd. All rights reserved.

Effect of Different Solvent Ratios (Water/Ethylene Glycol) on the Growth Process of CaMoO4 Crystals and Their Optical Properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and characterization of cellulose acetate produced from recycled newspaper

In this work, the viability of recycling newspaper for producing cellulose acetate was tested. Newspaper recycling is extremely important not only for the environment preservation, but also from the economical point of view of aggregating value to this residue. Cellulose acetate was produced from a homogeneous acetylation, and then characterized by FTIR, DSC and TGA. Acetylation times were 48 h for as received newspaper (CA48) and 24 h for delignified newspaper (CA24), resulting in cellulose diacetate (DS = 1.98 +/- 0.22) for CA48 and cellulose triacetate (DS = 2.79 +/- 0.02) for CA24, respectively. Membranes of these materials were produced and characterized according to the previously mentioned techniques and by measurements of water vapor flux, which were compared to membranes of nanofiltration SG from Osmonix (R). Results showed that independently of a purification step, it is possible to produce cellulose acetate membranes through the chemical recycling of newspaper and that membrane CA24 presents thermal stability comparable to membranes produced of commercial cellulose acetate. (C) 2007 Elsevier Ltd. All rights reserved.

Controlled fluorination of a-C:F:H films by PECVD of ethylene-hexafluorobenzene mixtures

Highly fluorinated plasma polymers are chemically inert,acid resistant and have low friction coefficients, thereby being useful in chemical laboratories and for tribological applications. Here we report the plasma polymerization of ethylene-hexafluorobenzene mixtures by PECVD. The principal parameter of interest is the proportion of C(6)F(6) in the feed, R(F). Films were analyzed using near-normal and grazing-angle Infrared Reflection Absorption Spectroscopy (IRRAS), the latter being particularly useful for detecting modes not usually observed at near-normal incidence. The presence of CH and CF(x) (x=1 to 2) groups was thus confirmed in films deposited with R(F)>= 40%. Depending on R(F) IRRAS also revealed the presence of -CH(x) (x=1 to 3) -C=C, -C=O and phenyl rings. Deconvolution of C is spectra obtained by X-ray Photoelectron Spectroscopy (XPS) confirmed the presence of CH, CF and CF(2) groups in films deposited with R(F)>= 40%. Atomic ratios of F:C calculated from the XPS spectral data show that the degree of fluorination rises with increasing RF Some unbound fluorine is present in the films. Post-deposition reactions account for the presence of oxygen (similar to 5%) in the films. Surface energies, determined from contact angle measurements, fall with increasing R(F). (C) 2008 Elsevier B.V. All rights reserved.

Drug-matrix interaction of sodium diclofenac incorporated into ureasilpoly(ethylene oxide) hybrid materials

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Osteointegration of poly(L-lactic acid)PLLA and poly(L-lactic acid)PLLA/poly(ethylene oxide)PEO implants in rat tibiae

Natural or synthetic materials may be used to aid tissue repair of fracture or pathologies where there has been a loss of bone mass. Polymeric materials have been widely studied, aiming at their use in orthopaedics and aesthetic plastic surgery. Polymeric biodegradable blends formed from two or more kinds of polymers could present faster degradation rate than homopolymers. The purpose of this work was to compare the biological response of two biomaterials: poly(L-lactic acid)PLLA and poly(L-lactic acid)PLLA/poly(ethylene oxide)PEO blend. Forty four-week-old rats were divided into two groups of 20 animals, of which one group received PLLA and the other PLLA/PEO implants. In each of the animals, one of the biomaterials was implanted in the proximal epiphysis of the right tibia. Each group was divided into subgroups of 5 animals, and sacrificed 2, 4, 8 and 16 weeks after surgery, respectively. Samples were then processed for analysis by light microscopy. Newly formed bone was found around both PLLA and PLLA/PEO implants. PLLA/PEO blends had a porous morphology after immersion in a buffer solution and in vivo implantation. The proportion 50/50 PLLA/PEO blend was adequate to promote this porous morphology, which resulted in gradual bone tissue growth into the implant.

Crystallization of nordstrandite in ethylene glycol water solutions: electron microscopic studies

The present work shows the growth of nordstrandile microcrystals observed by transmission and scanning electron microscopy. Nordstrandite was synthesised from non-crystalline aluminium hydroxide reacted in 20% ethylene glycol/water solution, at room temperature. This material was characterized by TEM, SEM, SAED, XRD and EDS/TEM, during six month and revealed the formation and growth of nordstrandite. Fibrillar pseudoboehmite is the only aluminium hydroxide which could be identified during the first two weeks. The nuclei grow, from complete dissolution/recrystallization of pseudoboehmite fibrils, into platy rectangular microscrystals of nordstrandite. Some tabular microcrystals recrystallise, forming after six months only the mufti-point nordstrandite stars. This electron-optical study suggest that the star shape results from the overlapping of rectangular plates, and pseudoboehmite fibrils act as the precursor of nordstrandite crystallisation in ethylene glycol/water solution.

Role of polyethylene-graft-glycidyl methacrylate compatibilizer on the biodegradation of poly(epsilon-calprolactone)/cellulose acetate blends

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Interaction of the nonionic surfactant C12E8 with high molar mass poly(ethylene oxide) studied by dynamic light scattering and fluorescence quenching methods

Dynamic light scattering has been used to investigate ternary aqueous solutions of n-dodecyl octaoxyethylene glycol monoetber (C12E8) with high molar mass poly(ethylene oxide) (PEO). The measurements were made at 20 °C, always below the cloud point temperature (Tc) of the mixed solutions. The relaxation time distributions are bimodal at higher PEO and surfactant concentrations, owing to the preacute of free surfactant micelles, which coexist with the slower component, representing the polymer coil/micellar cluster comptex. As the surfactant concentration is increased, the apparent hydrodynamic radius (RH) of the coil becomes progressively larger. It is suggested that the complex structure consists of clusters of micelles sited within the polymer coil, as previously concluded for the PEO-C12E8-water system. However. C12E8 interacts less strongly than C12E8 with PEO; at low concentrations of surfactant the complex does not contribute significantly to the total scattered intensity. The perturbation of the PEO coil radius with C12E8 is also smaller than that in the C12E8 system. The addition of PEO strongly decreases the clouding temperature of the system, as previously observed for C12E8/PEO mixtures in solution Addition of PEO up to 0.2% to C12E8 (10 wt %) solutions doss not alter the aggregation number (Nagg) of the micelles probably because the surfactant monomers are equally partitioned as bound and unbound micelles. The critical micelle concentration (cmc), obtained from the I1/I3 ratio (a measure of the dependence of the vibronic band intensities on the pyrene probe environment), does not change when PEO is added, suggesting that for neutral polymer/surfactant systems the trends in Nagg and the cmc do not unambiguously reflect the strength of interaction.

Morphology of Nylon 6/Acrylonitrile-Butadiene-Styrene Blends Compatibilized by a Methyl Methacrylate/Maleic Anhydride Copolymer

The morphologies of nylon 6/acrylonitrile-butadiene-styrene blends compatibilized with a methyl methacrylate/maleic anhydride copolymer, with 3-20 wt % maleic anhydride, were examined by transmission electron microscopy. Some staining techniques were employed for identifying the various phases. The binary blends were immiscible and exhibited poor mechanical properties that stemmed from the unfavorable interactions among their molecular segments. This produced an unstable and coarse phase morphology and weak interfaces among the phases in the solid state. The presence of the copolymer in the blends clearly led to a more efficient dispersion of the acrylonitrile-butadiene-styrene phase and consequently optimized Izod impact properties. © 2003 Wiley Periodicals, Inc.

Electrooptic proprieties of layer-by-layer films of a azobenzene containing copolymer

The methacrylic copolymer functionalized with the azo chromophore 4-[N-ethyl-N-(2-hydroxiethyl)]-amino-2′-chloro-4-nitroazobenzene (MMADR13), in its polyelectrolyte form, can be used to fabricate thin films by the layer-by-layer (LbL) technique just if one alternates this anionic polyelectrolyte with a cationic polyelectrolyte such as poly(allylamine hydrochloride) (PAH). Since PAH does not present any particular optical functionality, the main final film feature will came from the side chain DR13 azo-chromophore group due to its large nonlinear optical properties and photoisomerization capabilities. This work reports the electrooptic activity of MMADR13/DR13 LBL films, which arises from the high hiperpolarizability about the azo side chain group.