219 resultados para Fluoroindate glasses (FIG)


Relevância:

20.00% 20.00%

Publicador:

Resumo:

Luminescent spectra of Eu3+-doped sol-gel glasses have been analyzed during the densification process and compared according to the presence or not of aluminum as a codoping ion. A transition temperature from hydrated to dehydroxyled environments has been found different for doped and codoped samples. However, only slight modifications have been displayed from luminescence measurements beyond this transition. To support the experimental analysis, molecular dynamics simulations have been performed to model the doped and codoped glass structures. Despite no evidence of rare earth clustering reduction due to aluminum has been found, the modeled structures have shown that the luminescent ions are mainly located in aluminum-rich domains. The synthesis of both experimental and numerical analyses has lead us to interpret the aluminum effect as responsible for differences in structure of the luminescent sites rather than for an effective dispersion of the rare earth ions. (C) 2004 Elsevier B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Vitreous samples were prepared in the NaPO(3)-BaF(2)WO(3) ternary system with high WO(3) concentrations. These glasses exhibit a strong absorption in the visible due to the presence of reduced tungsten species and the use of oxidizing species is required. The couple Sb(2)O(3)/NaNO(3) was introduced in the composition and allowed to obtain transparent glasses. These oxidized samples were illuminated by visible laser radiation and showed an efficient volumetric photochromic effect. The photosensitive effect appeared as a dark spot throughout the entire volume of the glasses. The effect was investigated by several techniques such as, U-V-visible absorption, Raman and XANES at the L(1) and L(3) tungsten absorption edges. The results suggest a photoreduction of tungsten atoms without structural changes of the viteous network. Finally, the photochromic effect can be erased by thermal treatment at 200 degrees C for a few minutes. (C) 2007 Published by Elsevier B.V.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

In this work the quantitative theoretical treatment for two beam mode mismatched thermal lens spectrometry is applied to investigate the thermo-optical properties of chalcohalide (chalcolgenides and halides mixture) glasses. For the three kinds of glass studied the thermal diffusivity varied between 2.5 and 2.7 x 10(-3) cm(2) s(-1). Using these results and supposing Dulong-Petit specific heats we estimated the thermal conductivity and temperature ratio of optical path length (ds/dT) and temperature coefficient of refractive index (dn/dT). All samples had positive ds/dT(similar to 3.3 x 10(-6) K-1) and negative dn/dT (similar to -26 x 10(-6) K-1). The difference between these parameters and the change of signal are consequences of the expansion coefficient (13 x 10(-6) K-1) and refractive index (n similar to 2.6) of chalcohalides. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Changes occurring in absorption coefficients when glasses in the SbPO4-WO3 binary system were irradiated by light, at the edge of the absorption band, were measured in real time. These glasses present good thermal and optical properties and photoinduced changes in the absorption coefficients are reversible by heat treatment around 150 degrees C. Subsequent recording/erasing cycles could be made without sample degradation. The sensitivity of the induced optical changes was studied for different wavelengths, light powers and energy of light dose exposures, and for different compositions of the glasses. The changes in the absorption coefficients of the glass samples were accompanied by a color change from yellow to blue, and were also characterized by visible spectroscopy. The color changes occurred through the entire volume of the glass (similar to 2 mm thickness) for the Ar-ion laser lines at the edge of the absorption band. (c) 2006 Elsevier B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

The top faces of float glass samples were exposed to vapors resulting from the decomposition of KNO3 at 565 degrees C for up to 32 h. X-ray dispersive spectra (EDS) show that K+ ions migrate into the glass. The K+ concentration profile was obtained and its diffusion coefficient was calculated by the Boltzmann-Matano technique. The mean diffusion coefficient was approximately 10 X 10(-11) cm(2) s(-1). It was observed that the refractive index and the Vickers hardness decrease with the depth (after the removal of successive layers), and their profiles were thus obtained. These profiles enabled the calculation of the diffusion coefficient of K+ through the Boltzmann-Matano technique, with mean results ranging between 6 x 10(-11) and 30 x 10(-11) cm(2) s(-1). (c) 2006 Elsevier B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

We report on a metastable light-induced volume expansion in Ge25+xGa10-xS65 glasses under irradiation with band gap (UV) light, which can result in recording of relief gratings on their surface in the case of irradiation with two interfering beams. We propose a mechanism for the expansion, which is based on the light-induced change in the polarizability of secondary (van der Waals type) bonds and the effect of this change on primary (covalent type) bonds of the glass. The effect is suggested to be due to an interference of electrons, which belong to a chalcogen atom and participate in the formation of secondary and primary bonds, respectively. We suggest that a minimum point of the Lennard-Jones potential, which corresponds to the equilibrium position of a chalcogen atom is shifted in the course of irradiation to a larger interatomic distance. This shift causes a volume expansion and allows a diffusion of chalcogen atoms into the irradiated area. We show that light-induced polymerization of the glass network is an important attribute of the light-induced volume expansion.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

In this work, we present an approach for neutron fluence measurements based on natural thorium thin films and natural uranium-doped glasses calibrated through natural uranium thin films to be used for dating with the Fission-Track Method (FTM). This neutron dosimetry approach allows the employment of FTM even when dating is carried out using low neutron themalization facilities. Besides, it makes possible the determination of the Th/U ratio of the mineral to be dated. Durango apatite which is often employed in FTM as an age standard was analyzed. This apatite presented a fairly high Th/U ratio, 29.9 +/- 1.7. Th fissions were 18%, 12% and 10% of the total for irradiations where thermal to fast neutron flux ratios were 2.4, 4.4 and 5,2, respectively. These results show that Th fission must be considered for this apatite, when not well-thermalized irradiation facilities are used. The ratio between spontaneous and induced track length, L(S)/L(1), close to 0.89, indicates a certain amount of rejuvenation of the age of Durango apatite. Therefore, its apparent age should be corrected, the application of a technique based on track-length measurements produced a corrected age of 29.7 +/- 1.1 Ma, consistent with the independent reference age of this apatite (31.4 +/- 0.5 Ma). This result represents a support for viability of the neutron dosimetry approach studied in this work for FTM.(C) 2002 Elsevier B.V. B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

The optical nonlinearity of tungstate fluorophosphate glasses, synthesized in the NaPO3-BaF2-WO3 system, was investigated through experiments based on the third-order susceptibility, chi((3)). Nonlinear (NL) refraction and NL absorption measurements in the picosecond regime were performed using the Z-scan technique at 532 nm. NL refractive index, n(2)proportional toRe chi((3)), ranging from 0.4x10(-14) cm(2)/W to 0.6x10(-14) cm(2)/W were determined. The two-photon absorption coefficient, alpha(2)proportional toIm chi((3)), for excitation at 532 nm, vary from 0.3 to 0.5 cm/GW. Light induced birefringence experiments performed in the femtosecond regime indicate that the response time of the nonlinearity at 800 nm is faster than 100 fs. The experiments show that chi((3)) is enhanced when the WO3 concentration increases and this behavior is attributed to the hyperpolarizabilities associated to W-O bonds. (C) 2004 American Institute of Physics.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Tin oxide nanoparticles prepared by an aqueous sol-gel method were deposited by dip-coating on fluorozirconate glass, ZBLAN (53%ZrF4-20%BaF2-4%LaF3-3%AlF3-20%NaF) to improve its resistance against wet corrosion. The aqueous leaching of uncoated and SnO2-coated fluorozirconate glass was studied by X-ray photoemission spectroscopy (XPS) and it was shown that even an ultra thin tin dioxide film provides good protection of the glass surface against the bulk propagation of the hydrolytic attack.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

The surface corrosion process associated with the hydrolysis of fluorozirconate glass, ZBLAN (53ZrF(4), 20BaF(2), 20NaF, 4LaF(2), 3AlF(3)) was investigated using X-ray photoelectron spectroscopy (XPS), grazing-incidence small angle X-ray scattering (GISAXS), X-ray reflectivity (XRR) and scanning electron microscopy (SEM). After a short exposure period (25 min) of the glass surface to deionized water the XPS data indicate an increase of the oxygen content accompanied by a decrease of fluorine concentration. The analysis of the chemical bonding structure identified the predominant surface reaction products as zirconium hydroxyfluoride and oxyfluoride species. The second most abundant glass component, bariumfluoride, remains almost unaffected by oxygen, while sodium fluoride is completely removed from the attacked surface region. The detected structural and compositional changes are related to the selective dissolution of the glass components leading to the formation of a new surface phase. This process is accompanied by a visible surface roughening caused by reprecipitated species, observed by SEM. The modification of the glass surface is responsible for an increase of the GISAXS intensity. The scattering was attributed to nanovoids formed at the surface region of the glass with an average size of 2.4 +/- 0.05 nm. (C) 2004 Elsevier B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

X-ray absorption spectroscopy was used to study the local environment of tungsten atoms in NaPO3-BaF2,-WO3 glasses and the results were compared with crystalline references Na2WO4 and WO3. XANES measurements at the W-L-1 edge allowed to determine a distorted octahedral environment of tungsten atoms in these glasses similar to the local order of tungsten in monoclinic WO3. Extended X-ray absorption fine structure (EXAFS) has been used as a local probe to monitor the effect of WO3 concentration on the tungsten environment. Based on an analysis of the EXAFS data, we proposed a three-shell model of oxygen atoms around tungsten as in monoclinic WO3. With increasing WO3 concentration, it was found that R-2 decreases from 1.96 to 1.92 angstrom whereas R-3 increases from 2.07 to 2.12 angstrom. (c) 2005 Elsevier B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Vitreous samples were prepared in the (100 2 x) NaPO3-x WO3 (0 <= x <= 70) glass forming system using conventional melting-quenching methods. The structural evolution of the vitreous network was monitored as a function of composition by thermal analysis, Raman spectroscopy and high resolution one- and two-dimensional P-31 solid state NMR. Addition of WO3 to the NaPO3 glass melt leads to a pronounced increase in the glass transition temperatures, suggesting a significant increase in network connectivity. At the same time Raman spectra indicate that up to about 30 mol% WO3 the tungsten atoms are linked to some non-bridging oxygen atoms (W-O- or W=O bonded species), suggesting that the network modifier sodium oxide is shared to some extent between both network formers. W-O- W bond formation occurs only at WO3 contents exceeding 30 mol%. P-31 magic angle spinning (MAS)-NMR spectra, supported by two-dimensional J-resolved spectroscopy, allow a clear distinction between species having two, one, and zero P-O-P linkages. The possible formation of some anionic tungsten sites suggested from the Raman data implies an average increase in the degree of polymerization for the phosphorus species, which would result in diminished P-31/Na-23 interactions. This prediction is indeed confirmed by P-31{Na-23} and Na-23{P-31} rotational echo double resonance (REDOR) NMR results, which indicate that successive addition of WO3 to NaPO3 glass significantly diminishes the strength of phosphorus-sodium dipole-dipole couplings.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

The deactivation of the two lowest excited states of Ho3+ was investigated in Ho3+ singly doped and Ho3+, Pr3+-codoped fluoride (ZBLAN) glasses. We establish that 0.1-0.3 mol % Pr3+ can efficiently deactivate the first excited (I-5(7)) state of Ho3+ while causing a small reduction of similar to 40% of the initial population of the second excited (I-5(6)) state. The net effect introduced by the Pr3+ ion deactivation of the Ho3+ ion is the fast recovery of the ground state of Ho3+. The Burshstein model parameters relevant to the Ho3+-> Pr3+ energy transfer processes were determined using a least squares fit to the measured luminescence decay. The energy transfer upconversion and cross relaxation parameters for 1948, 1151, and 532 nm excitations of singly Ho3+-doped ZBLAN were determined. Using the energy transfer rate parameters we determine from the measured luminescence, a rate equation model for 650 nm excitation of Ho3+-doped and Ho3+, Pr3+-doped ZBLAN glasses was developed. The rate equations were solved numerically and the population inversion between the I-5(6) and the I-5(7) excited states of Ho3+ was calculated to examine the beneficial effects on the gain associated with Pr3+ codoping. (c) 2007 American Institute of Physics.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

In this work the technique of X-ray reflectometry was applied to study zirconiumsulfate films deposited by sol-gel dip-coating process on a borosilicate glass surface. The influence of withdrawal speed and temperature of thermal treatment on the film structure are analyzed. The thermal evolution of the density and thickness of the film was compared with these properties measured for a monolithic xerogel by helium picnometry and thermomechanical analysis. The fitting of experimental curves by classical reflectivity model showed the presence of an additional layer at the top surface of the coating. Layer thickness increases with increase of withdrawal speed in agreement with the Landau-Levich model. The apparent and real densities are similar for coatings fired below 400 degrees C, which shows that the films are free of pores. The shrinkage during firing is anisotropic, occurring essentially perpendicular to the coating surface. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Relevância:

20.00% 20.00%

Publicador:

Resumo:

Binary tellurite-based glasses in the TeO2-PbO system were prepared and its structure investigated by means of Raman Scattering and X-ray Absorption Spectroscopy. Both spectroscopies indicate strong modifications of the first coordination shell around tellurium atoms when the PbO content increases revealing for lead its glassy network modifier role. Also, Pb L-3-edge EXAFS measurements reveal this structural role played by lead atoms, but the presence of a medium range order contribution indicates that lead also participates to the glassy network formation. (C) 2001 Elsevier B.V. Ltd. All rights reserved.