Improvement of the chemical resistance of zirconium fluoride glasses coated with a Tiron (R) modified tin oxide layer prepared by the sol-gel process

In order to improve the chemical resistance of zirconium fluoride glass a protective transparent SnO2 layer was deposited by the solgel dip-coating process in the presence of Tiron (R) as particle surface modifier agent. After water immersion for different periods of time, both coated and non-coated fluoride glasses were analyzed by scanning electron microscopy, mass loss evaluation, infrared spectroscopy and X-ray photoelectron spectroscopy. In contrast to the effects occurring for non-coated glass, where the surface undergoes a rapid selective dissolution of the most soluble species, the results for the SnO2-coated glass showed that the filling of the film nanopores by dissolved glass material results in a hermetic barrier protecting the glass surface. The selective glass dissolution was confirmed by liquid chromatography measurements of the etching solution after each exposure time. (c) 2006 Elsevier B.V. All rights reserved.

Femtosecond nonlinear optical properties of tellurite glasses

The third-order nonlinear optical properties of tellurite glasses with different compositions were investigated in the femtosecond regime at 810 nm. Using the I-scan technique, positive nonlinear refractive indices of similar to 10(-15) cm(2)/W were measured. The authors also determined that nonlinear absorption was negligible for all studied samples. This result, added to their good chemical stability, indicates that tellurite glasses are promising materials for ultrafast photonic applications. (c) 2006 American Institute of Physics.

Nucleation and growth of mullite whiskers from lanthanum-doped aluminosilicate melts

Nucleation and growth of mullite whiskers in the La2O3-Al2O3-SiO2 system were investigated in the 1500degrees-1700degreesC temperature range. A differential thermal analysis (DTA) showed that the mullitization temperature decreases from 1350degreesC to 1240degreesC as a result of lanthania doping. In the temperature range of 1250-1500degreesC, most of the mullite grains have an Al2O3/SiO2 = 1.5 composition throughout the ceramic body; however, from 1400degreesC upward, the number of anisotropic grains with the Al2O3/SiO2 = 1.3 composition begins to increase. The concentration of alumina in the composition of the grain-boundary phase decreases as firing temperatures increase. At temperatures > 1500degreesC, alumina grains and whiskers grow on the internal and external surfaces of the ceramic body with the characteristic Al2O3/SiO2 = 1.3 composition. Removal of the mullite whisker layer by acid attack revealed an alumina-rich, rosace-like patterned microstructure correlated with the process of whisker nucleation and growth. In the early stages, whisker growth rates were found to be near 60 mum/h. Experimental evidence pointed to nucleation inside the thin glass layer on the external surface.

SiO2-PbF2-CdF2 glasses and glass ceramics

Lead-Cadmium fluorosilicate stable glasses were prepared and the vitreous domain region determined in the composition diagram. Characteristic temperatures were obtained from thermal analysis and the structural studies performed illustrate clearly the role played by lead atoms in the glasses crystallization behavior and the glass-forming ability of cadmium atoms. The occurrence of either a cubic lead fluoride or a lead-cadmium fluoride solid solution in crystallizing samples was found to be dependent on Er3+ doping. The optically active ions were found to concentrate in the crystalline phase and in fact play the role of nucleating agent as suggested from X-ray diffraction and EXAFS measurements. (C) 2002 Elsevier B.V. Ltd. All rights reserved.

4f-4f intensities of the Tm3+ ions in fluoroindate glasses: the influence of third-order effects through odd intensity parameters

In this work an analysis of the phenomenological Omega(lambda) intensity parameters for the Tm3+ ion in fluoroindate glass is made using the standard Judd-Ofelt theory, and a modified oscillator strength taking into account odd-order contributions is utilized. Different sets of phenomenological intensity parameters Omega(lambda) (lambda=1,2,3,4,5,6) are discussed. The set of better quality is used to analyze the influence of third-order effects through odd intensity parameters in the new approximation. Fluoroindate glasses of compositions (40-x)InF3-20ZnF(2)-20SrF(2)-16BaF(2)-2GdF(3)-2NaF-xTmF(3) with x=1, 2 and 3 mol% were prepared, and the absorption spectra at room temperature in the spectral range from 300 to 2500 nm were obtained. The experimental oscillator strengths determined from the area under the absorption band are compared to the calculated ones. (C) 1998 Elsevier B.V. S.A.

Spectroscopic properties of Er3+ in oxysulfide glasses

Er3+ -containing gallium-lanthanum oxysulfide glasses have been prepared from Ga2O3 and La2S3 in a sulfur/argon reactive atmosphere. The samples have been characterized by absorption and emission spectroscopy and IR emission kinetics. Er3+ electronic transition intensities have been analyzed in the light of the Judd-Ofelt formalism, and quantum efficiencies evaluated for the Er3+ emission at 1.5 and 2.7 mum. The results so obtained suggest that these glasses display favorable properties concerning IR optical applications. (C) 2002 Elsevier B.V. B.V. All rights reserved.

CRYSTALLINE FRAGMENTS IN GLASSES

The nature of tetrahedral molecular fragments is investigated in SiSe2 glasses using the molecular-dynamics method. The glass consists of both edge-sharing (ES) and corner-sharing tetrahedra. The ES tetrahedra are the building blocks of chain-like-molecular fragments. The two-edge-sharing tetrahedra are the nucleus, and corner-sharing configurations provide connecting hinges between fragments. Statistics of rings and fragments reveals that threefold and eightfold rings are most abundant, chainlike fragments that are typically 10-15 angstrom long occur mostly in eightfold rings, and the longest fragments occur in elevenfold rings.

Evaluation of laser level populations of erbium-doped glasses

A simulation of erbium-doped glass systems, which provides population density for the excited states involved in the 1.5 mu m and also for 2.7 mu m emissions when pumped around 980 nm, is presented. To describe the diode pump laser processes, a theoretical model based in a coupled system of differential rate equations was developed. The approach used and the obtained spectroscopic parameters are discussed. The materials under study are two oxide glasses, lead fluoroborate (PbO-PbF2-B2O3), and heavy metal oxide (Bi2O3 PbO-Ga2O3) and a fluoride glass (ZrF4-BaF2-LaF3-AlF3-NaF), all of them doped with Er3+. (c) 2006 Elsevier B.V. All rights reserved.

Above bandgap induced photoexpansion and photobleaching in Ga-Ge-S based glasses

Photoexpansion and photobleaching effects have been examined in glass compositions Ga10Ge25S65 and Ga5Ge25As5S65. Such compositions are promising for optical storage and planar waveguide applications. To evaluate the photoinduced effect, samples were exposed to 351 nm light, varying power density (3-10 W/cm(2)) and exposure time (0-120 min). The exposed areas have been analyzed using atomic force microscopy (AFM) and an expansion of 800 nm is observed for composition Ga10Ge25S65 exposed during 120 min and 5 W/cm(2) power density. The optical absorption edge measured by a spectrophotometer indicates a blue shift (80 nm) after illumination in the composition Ga10Ge25S65. The morphology was examined using a scanning electron microscopy (SEM). The chemical compositions measured using a energy dispersive analyzer (EDX) indicate an increase of the number of sulfur atoms in the irradiated area. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Glasses in the SbPO4-WO3 system

Glasses in the binary system (100 - x)SbPO4-xWO3 (20 <= x <= 60, x in mol%) have been prepared and characterized. Differential thermal analysis (DTA) shows that the glass transition temperature, T-g increases from 412 degrees C, for samples containing 20 mol% of WO3 to 481 degrees C observed for glass containing 60 mol%. Sample containing 40 mol% in WO3 were observed to be the most stable against devitrification. The structural organization of the glasses has been studied by using Fourier transform infra-red (FTIR), Raman, P-31 Magic angle spinning (MAS) and spin echo nuclear magnetic resonance (NMR) spectroscopies. Results suggest two distinct networks comprising the glass structure, one with high SbPO4 content and the other characteristic of the highest WO3 content samples. The glasses present photochromic properties. Colour changes are observed for samples after exposure to ultraviolet or visible laser light. XANES, at L-1 absorption edge of tungsten, suggests partial reduction from W6+ to W5+ species during the laser irradiation. The photochromic effects and the colour changes, promoted by laser excitation, are reversible and easily removed by heat for during 1 h at 150 degrees C. Subsequent 'write/erase' cycles can be done without degradation of the glasses. (C) 2007 Elsevier B.V. All rights reserved.

XPS study on water corrosion of fluorzirconate glasses and their protection by a layer of surface modified tin dioxide nanoparticles

The surface corrosion process associated with the hydrolysis of fluorozirconate glass, Z-BLAN (53ZrF(4), 20BaF(2), 20NaF, 4LaF(2), 3AlF(3)), and the corrosion protection efficiency of a nanocrystalline transparent SnO2 layer were investigated by X-ray photoelectron spectroscopy. The tin oxide film was deposited by the sol-gel dip-coating process in the presence of Tiron(R) as particle surface modifier agent. The chemical bonding structure and composition of the surface region of coated and non-coated ZBLAN were studied before water contact and after different immersion periods (5-30 min). In contrast to the effects occurring for non-coated glass, where the surface undergoes a rapid selective dissolution of the most soluble species inducing the formation of a new surface phase consisting of stable zirconium oxyfluoride, barium fluoride and lanthanum fluoride species, the results for the SnO2-coated glass showed that the hydrolytic attack induces a filling of the film nanopores by dissolved glass material and the formation of tin oxylluoride and zirconium oxyfluoride species. This process results in a modified film, which acts as a hermetic diffusion barrier protecting efficiently the glass surface. (C) 2006 Elsevier B.V. All rights reserved.

Temperature and wavelength dependence of the thermo-optical properties of tellurite and chalcogenide glasses

The refractive index and the temperature coefficient of the optical path length change of tellurite (80TeO(2):20Li(2)O) and chalcogenide glasses (72.5Ga(2)S(3):27.5La(2)O(3)) were determined as a function of temperature (up to 150 degrees C) and wavelength (in the range between 454 and 632.8 nm). The tellurite glass exhibits the usual refractive index dispersion in the wavelength range analyzed, while anomalous refractive index dispersion was observed for the chalcogenide glass between 454 and 530 nm. The dispersion parameters were determined by means of the single-effective oscillator model. In addition, a strong dependence of the temperature coefficient of the optical path length on the photon energy and temperature was found for the chalcogenide glass. The latter was correlated to the shift of the optical band gap (or electronic edge) with temperature, which was interpreted by the electron-phonon interaction model. (C) 2007 American Institute of Physics.

Structural studies of NaPO3-MoO3 glasses by solid-state nuclear magnetic resonance and raman spectroscopy

Vitreous samples were prepared in the (100 - x)% NaPO3-x% MoO3 (0 <= x <= 70) glass-forming system by a modified melt method that allowed good optical quality samples to be obtained. The structural evolution of the vitreous network was monitored as a function of composition by differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FT-IR), Raman scattering, and solid-state nuclear magnetic resonance (NMR) for P-31, Na-23, and Mo-95 nuclei. Addition of MoO3 to the NaPO3 glass melt leads to a pronounced increase in the glass transition temperatures up to x = 45, suggesting a significant increase in network connectivity. For this same composition range, vibrational spectra suggest that the Mo6+ ions are bonded to some nonbridging oxygen atoms (Mo-O- or Mo=O bonded species). Mo-O-Mo bond formation occurs only at MoO3 contents exceeding x = 45. P-31 magic-angle spinning (MAS) NMR spectra, supported by two-dimensional J-resolved spectroscopy, allow a clear distinction between species having two, one, and zero P-O-P linkages. These sites are denoted as Q(2Mo)((2)), Q(1Mo)((2)), and Q(0Mo)((2)), respectively. For x < 0.45, the populations of these sites can be described along the lines of a binary model, according to which each unit of MoO3 converts two Q(nMo)((2)) sites into two Q((n+1)Mo)((2)) sites (n = 0, 1). This structural model is consistent with the presence of tetrahedral Mo(=O)(2)(O-1/2)(2) environments. Indeed, Mo-95 NMR data suggest that the majority of the molybdenum species are four-coordinated. However, the presence of additional six-coordinate molybdenum in the MAS NMR spectra indicates that the structure of these glasses may be more complicated and may additionally involve sharing of network modifier oxide between the network formers phosphorus and molybdenum. This latter hypothesis is further supported by Na-23{P-31} rotational echo double resonance (REDOR) data, which clearly reveal that the magnetic dipole-dipole interactions between P-31 and Na-23 are increasingly diminished with increasing molybdenum content. The partial transfer of modifier from the phosphate to the molybdate network former implies a partial repolymerization of the phosphate species, resulting in the formation of Q(nMo)((3)) species and accounting for the observed increase in the glass transition temperature with increasing MoO3 content that is observed in the composition range 0 <= x <= 45. Glasses with MoO3 contents beyond x = 45 show decreased thermal and crystallization stability. Their structure is characterized by isolated phosphate species [most likely of the P(OMo)(4) type] and molybdenum oxide clusters with a large extent of Mo-O-Mo connectivity.

Totally visible transparent chloro-sulphide glasses based on Ga2S3-GeS2-CsCI

In this paper, the influence on optical properties of alkali halides such as CsCl in a covalent glassy matrix has been investigated. Chalcogenide glasses belonging to the (GeS2)-(Ga2S3)-CsCI system with high ratio of CsCl present an entire transparency in the visible range. These glasses maintain good transmission up to 12 mu m. Furthermore, the thermo-mechanical properties and the glass hygroscopicity have been investigated as function of the CsCl amount. This new generation of glasses presents a great interest for optical application. They could be used both for passive applications (multi-spectral imaging) and active applications for rare-earth doping due to their good transmission in the visible range, increasing optical pumping possibilities.

Conductivity and F-19 NMR in PbGeO3-PbF2-CdF2 glasses and glass-ceramics

The temperature dependence of the electrical conductivity and the F-19 nuclear magnetic resonance (NMR) of PbGeO3-PbF2CdF, glasses and glass ceramics are investigated. The measured conductivity values of the glasses are above 10(-5) Skin at 500 K, and increase with increasing lead fluoride content. Activation energies extracted from the conductivity data are in the range 0.59-0.73 eV. Results are consistent with the hypothesis that in these oxyfluoride glasses lead fluoride rich clusters are dispersed in a metagermanate based matrix providing increasing mobility pathways for conducting ions. The conductivity of a sample of the glass ceramic of composition (mol%) 60PbGeO(3-)20PbF(2)-20CdF(2) was found to be smaller than that in the corresponding glass, suggesting that there are poor ionic conducting regions in the interface between the nanometer sized crystals. The temperature dependence of the F-19 relaxation times, measured in the range 100-800 K, exhibit the qualitative features associated with high fluorine mobility in both, glass and glass ceramics materials. We suggest that de-convolution of the spin-lattice relaxation rates observed in the glass ceramics shows that the observed high temperature rate maximum is associated with the diffusional motions of the fluorine ions in beta-PbF2 crystals. (c) 2005 Elsevier B.V. All rights reserved.