Fluoride uptake and acid resistance of enamel irradiated with Er : YAG laser

This study evaluated the resistance to demineralization and fluoride incorporation of enamel irradiated with Er:YAG. A total of 110 bovine teeth were selected and divided into eight groups: unlased, 37% phosphoric acid, and samples irradiated with the Er:YAG laser at several fluences (31.84 J/cm(2), 25.47 J/cm(2), 19.10 J/cm(2), 2.08 J/cm(2), 1.8 J/cm(2), and 0.9 J/cm(2)). The application of acidulated phosphate fluoride was performed after treatments. All samples were immersed in 2 ml of 2.0 M acetic-acetate acid solution at pH 4.5 for 8 h, and fluoride, calcium, and phosphorus ions dissolved were analyzed by atomic absorption spectrometry and spectrophotometry. The phosphoric acid and 31.84 J/cm(2) groups presented the lowest dissolution of calcium and phosphorus ions. Higher fluoride incorporation was observed on 1.8 J/cm(2) and 0.9 J/cm(2) groups. Based on these results, Er:YAG laser was able to decrease acid dissolution and increase fluoride uptake and can be a promissory alternative for preventive dentistry.

A Contribution to the Estimation of Binary Halide and Pseudo-Halide Equilibrium Constants using a Linear Extrapolation Methodology

The molar single ion activity coefficient (y(F)) of fluoride ions was determined at 25 degrees C and ionic strengths between 0.100 and 3.00 mol L(-1) NaClO(4) using an ion-selective electrode. The activity coefficient dependency on ionic strength was determined to be Phi(F) = log y(F) = 0.2315I-0.041I(2). The function Phi(F)(I), combined with functions obtained in previous work for copper (Phi(Cu)) and hydrogen (Phi(H)), allowed us to make the estimation of the stoichiometric and thermodynamic protonation constants of some halides and pseudo-halides as well as the formation constants of some pseudo-halides and fluoride 1:1 bivalent cation complexes. The calculation procedure proposed in this paper is consistent with critically-selected experimental data. It was demonstrated that it is possible to use Phi(F)(I) for predicting the thermodynamic equilibrium parameters independently of Pearson's hardness of acids and bases.

Redox Behavior of molybdenum and tungsten in phosphate glasses

In this work, vitreous samples were prepared in the binary system (100 - x)NaPO3-xMO(3) with M = Mo and W and x varying from 10 to 60. The transmittance properties in the UV, visible, and near-infrared were monitored as a function of MO3 concentration. In both cases, an increase in the amount of transition metal results in an intense and broad absorption band in the visible and near-infrared attributed to metal reduction under synthesis conditions. It was shown that this large absorption can be partially or totally removed using specific oxidizing agents or by improving synthesis parameters such as melting temperature or cooling rate of the melt. In addition, structural investigations by Raman and X-ray absorption spectroscopy suggest that reduction only occurs when the metal cation is in octahedral geometry and that the transmittance improvement is not related with any structural changes. These results were explained in terms of thermodynamic equilibrium of redox species in the melt and allowed to obtain for the first time transparent and chemically stable glasses containing high concentrations of MO3 with transition metals in octahedral geometry inside the glass network.

Structural study of thin films prepared from tungstate glass matrix by Raman and X-ray absorption spectroscopy

Thin films were prepared using glass precursors obtained in the ternary system NaPO(3)-BaF(2)-WO(3) and the binary system NaPO(3)-WO(3) with high concentrations of WO(3) (above 40% molar). Vitreous samples have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. Several structural characterizations were performed by Raman spectroscopy and X-ray Absorption Near Edge Spectroscopy (XANES) at the tungsten L(I) and L(III) absorption edges. XANES investigations showed that tungsten atoms are only sixfold coordinated (octahedral WO(6)) and that these films are free of tungstate tetrahedral units (WO(4)). In addition, Raman spectroscopy allowed identifying a break in the linear phosphate chains as the amount of WO(3) increases and the formation of P-O-W bonds in the films network indicating the intermediary behavior of WO(6) octahedra in the film network. Based on XANES data, we suggested a new attribution of several Raman absorption bands which allowed identifying the presence of W-O and W=O terminal bonds and a progressive apparition of W-O-W bridging bonds for the most WO(3) concentrated samples (above 40% molar) attributed to the formation of WO(6) clusters. (C) 2008 Elsevier B.V. All rights reserved.

Crystallization study of molybdate phosphate glasses by thermal analysis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

1.5 mu m and visible up-conversion emissions in Er3+/Yb3+ co-doped tellurite glasses and optical fibers for photonic applications

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Stabilization of fluoroindate glasses by magnesium fluoride and other heavy metal fluorides

Their extended transparency in the IR makes them attractive for use as optical fibers for CO laser power delivery and optical amplification. This paper firstly describes the spectacular stabilizing effect of MgF2 on the binary system InF3-BaF2. The investigation of the InF3-BaF2-MgF2 system led to samples up to 5mm in thickness. Further optimization of this system was achieved by incorporation of limited amounts of other fluorides and resulted in increased resistence to devitrification. The second approach of this work was concerned to the investigation of the pseudo-ternary system InF3-GdF3-GaF3 at constant concentrations of ZnF2-SrF2-BaF2-NaF. Several compositions were studied in this system. The samples presented a better thermal stability when compared to other families of fluoride glasses. Therefore, these glasses seem to be very promising for the fabrication of special optical fibers. Thermal data are reported.

Synthesis and Structural Studies of Er3+ Containing Lead Cadmium Fluoroborate Glasses and Glass-Ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Time dependence and energy-transfer mechanisms in Tm3+Ho3+ and Tm3+-Ho3+ co-doped alkali niobium tellurite glasses sensitized by Yb3+

Glass samples with the composition (mol%) 80TeO(2)-10Nb(2)O(5)-5K(2)O-5Li(2)O, stable against crystallization, were prepared containing Yb3+, Tm3+ and Ho3+. The energy transfer and energy back transfer mechanisms in samples containing 5% Yb3+-5% Tm3+ and 5% Yb3+-5% Tm3+-0.5% Ho3+ were estimated by measuring the absorption and fluorescence spectra together with the time dependence of the Yb3+ F-2(5/2) excited state. A good fit for the luminescence time evolution was obtained with the Yokota-Tanimoto's diffusion-limited model. The up-conversion fluorescence was also studied in 5% Yb-5% Tm. 5% Yb-0.5% Ho and 5% Yb-5% Tm-0.5% Ho tellurite glasses under laser excitation at 975 nm. Strong emission was observed from (1)G(4) and F-3(2) Tm3+ energy levels in all samples. The S-5(2) Ho3+ emission was observed only in Yb3+Ho3+ samples being completely quenched in Yb3+/Tm3+/Tm3+ samples. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Spectroscopic investigation of a new hybrid glass formed by the interaction between croconate ion and calcium polyphosphate

In this work, a new organic-inorganic hybrid material has been synthesized by the incorporation of croconate ion into a calcium polyphosphate coacervate. The hybrid so obtained was characterized by means of electronic and vibrational spectroscopies. The material is a homogeneous mixture described by a structural model, which includes helical chains of polyphosphate ions, where the calcium ion occupies the internal vacancies of the structure. The croconate ion appears to be occupying the regions outside the polymeric structure, surrounded by several water molecules. The electronic spectrum of the incorporated material shows a broad band peaking at the same wavelength region (363 nm) observed for the aqueous solution of croconate ion, and manifesting the Jahn-Teller effect as evidenced by the doublet structure of the band. The infrared spectrum is widely dominated by the absorption bands of the polyphosphate ion and the appearance of the carbonyl stretching band at ca. 1550 cm(-1) indicates the presence of croconate ion incorporated in the structure. The Raman spectrum of the material shows several vibrational bands related to the oxocarbon moiety; most of them are shifted in comparison with the free ion. These shifts can be understood in terms of strong hydrogen bonding interactions between water molecules and the oxocarbon moiety. The low temperature methodology proposed here can be well used in the preparation of new phosphate glasses containing organic moieties opening the route to an entirely new class of hybrid glasses. (c) 2004 Elsevier B.V All rights reserved.

Red-green-blue upconversion emission and energy-transfer between Tm3+ and Er3+ ions in tellurite glasses excited at 1.064 mu m

Red, green, and blue emission through frequency upconversion and energy-transfer processes in tellurite glasses doped with Tm3+ and Er3+ excited at 1.064 mum is investigated. The Tm3+/Er3+-codoped samples produced intense upconversion emission signals at around 480, 530, 550 and 660 nm. The 480 nm blue emission was originated from the (1)G(4)-->H-3(6) transition of the Tm3+ ions excited by a multiphoton stepwise phonon-assisted excited-state absorption process. The 5 30, 5 50 nm green and 660 mn red upconversion luminescences were identified as originating from the H-2(11/2), S-4(3/2) --> I-4(15/2) and F-4(9/2) --> I-4(15/2) transitions of the Er3+ ions, respectively, populated via efficient cross-relaxation processes and excited-state absorption. White light generation employing a single infrared excitation source is also examined. (C) 2003 Elsevier B.V. (USA). All rights reserved.

Glasses containing lutetium fluoride

Glasses containing lutetium fluoride have been prepared in the system BaF2 - SrF2 - ZnF2 - LuF3 - InF3. The composition of the phases crystalling out of these glasses suggests octahedral pre-arrangement comprising [LuF6] and [Sr(Ba)F-2 structural fragments.

Synthesis and structural investigations on TeO2-PbF2-CdF2 glasses and transparent glass-ceramics

New glasses have been prepared in the oxifluoride mixed system TeO2-PbF2-CdF2. Starting from pure TeO2 the addition of the fluorides leads to a decrease in the glasses characteristic temperatures. Also from Raman scattering results a structural evolution was observed where the number of structural units described as [TeO3] trigonal pyramids and [TeO3+1] polyhedra increases at the expense of the [TeO4] trigonal bipyramids supposed to exist in the TeO2, rich samples. Transparent glass ceramics were obtained from the glass with composition 80TeO(2)-10PbF(2)-10CdF(2), (mol%) with the PbTe3O7 crystalline phase being identified by X-ray diffraction and EXAFS measurements performed at the Te K, Cd K and Pb L-III edges. Also from Exafs measurements it is proposed that cadmium ions are preferentially surrounded by oxygen atoms although they were in a fluoride anion environment in the starting material. (C) 2002 Published by Elsevier B.V. Ltd.

Temperature investigation of infrared-to-visible frequency upconversion in erbium-doped tellurite glasses excited at 1540 nm

Temperature investigation of infrared-to-visible frequency upconversion in erbium-doped tellurite glasses excited by CW laser radiation at 1540 nm and under cryogenic temperatures is reported. Intense upconversion emission signals around 530, 550 and 660 nm corresponding to the H-2(11/2), S-4(3/2), and F-4(9/2) transitions to the I-4(15/2) ground state were generated and studied as a function of the laser intensity and temperature. The upconversion excitation mechanism of the Er3+ ions emitting energy levels was accomplished via stepwise multiphoton absorption. The green upconversion luminescence exhibited a fivefold intensity enhancement when the temperature of the sample was varied in the range between 5 and 300 K. A maximum green upconversion intensity was attained around 120 K and a steady decreasing behavior for higher temperatures up to 300 K was observed. A model based upon conventional rate equations was used to model the observed temperature evolution of the upconversion luminescence. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Infrared-to-visible frequency upconversion in Pr3+/Yb3+- and Er3+/Yb3+-codoped tellurite glasses

Upconversion luminescence and thermal effects in Pr3+/Yb3+- and Er3+/Yb3+-codoped 60TeO(2)-10GeO(2)-10K(2)O-10Li(2)O-10Nb(2)O(5) tellurite glasses excited by CW infrared radiation at 1.064 mum is reported. Generation of intense green and red fluorescence emission in Er3+/Yb3+-codoped samples and appreciable upconversion luminescence in the wavelength region of 450-680 nm in Pr3+/Yb3+-codoped samples is observed. Temperature-induced enhancement of X12 in the upconversion efficiency in Er3+/Yb3+- and X10 in the Pr3+/Yb3+-doped samples is demonstrated. (C) 2002 Elsevier B.V. B.V. All rights reserved.