Effect of thermocycling on bond strength and elasticity of 4 long-term soft denture liners

Statement of problem. Two problems found in prostheses with soft liners are bond failure to the acrylic resin base and loss of elasticity due to material aging.Purpose. This in vitro study evaluated the effect of thermocycling on the bond strength and elasticity of 4 long-term soft denture liners to acrylic resin bases.Material and methods. Four soft lining materials (Molloplast-B, Flexor, Permasoft, and Pro Tech) and 2 acrylic resins (Classico, and Lucitone 199) were processed for testing according to manufacturers' instructions. Twenty rectangular specimens (10 X 10-mm(2) cross-sectional area) and twenty cylinder specimens (12.7-mm diameter X 19.0-mm height) for each liner/resin combination were used for the tensile and deformation tests, respectively. Specimen shape and liner thickness were standardized. Samples were divided into a test group that was thermocycled 3000 times and a control group that was stored for 24 hours in water at 37degreesC. Mean bond strength, expressed in megapascals (Wa), was determined in the tensile test with the use of a universal testing machine at a crosshead speed of 5 mm/min. Elasticity, expressed as percent of permanent deformation, was calculated with an instrument for measuring permanent deformation described in ADA/ANSI specification 18. Data from both tests were examined with 1-way analysis of variance and a Tukey test, with calculation of a Scheffe interval at a 95% confidence level.Results. In the tensile test under control conditions, Molloplast-B (1.51 +/- 0.28 MPa [mean SD]) and Pro Tech (1.44 +/- 0.27 MPa) liners had higher bond strength values than the others (P < .05). With regard to the permanent deformation test, the lowest values were observed for Molloplast-B (0.48% +/- 0.19%) and Flexor (0.44% +/- 0.14%) (P < .05). Under thermocycling conditions, the highest bond strength occurred with Molloplast-B (1.37 +/- 0.24 MPa) (P < .05) With regard to the deformation test, Flexor (0.46% +/- 0.13%) and Molloplast-B (0.44% +/- 0.17%) liners had lower deformation values than the others (P < .05).Conclusion. The results of this in vitro study indicated that bond strength and permanent deformity values of the 4 soft denture liners tested varied according to their chemical composition. These tests are not completely valid for application to dental restorations because the forces they encounter are more closely related to shear and tear. However, the above protocol serves as a good method of investigation to evaluate differences between thermocycled and control groups.

Relationship between Candida and nocturnal denture wear: quantitative study

The purpose of this study was to evaluate the relationship between Candida and denture wear during the night. Twenty-four edentulous volunteers were randomly divided into two groups. Group I (GI, n = 11) was composed of volunteers who wore their complete dentures day and night and Group H (GII, n = 13) was composed of volunteers who wore their complete dentures only during the day. Three examination periods were performed for both groups. In GI, the first examination (A) was carried out after overnight denture wearing. Subsequent examinations were conducted after one (B) and seven nights (C) without denture use during sleep. In GII, the first (A) was done without previous use during sleep, and the following were carried out after one (B) and seven nights (C) of overnight denture wearing. Total un-stimulated saliva was collected in a sterile container and cultured in duplicate inside Petri dishes. The values of colony forming units (CFU mL(-1) +/- s.d.) were obtained: GI A - 10.1 x 10(3) +/- 1.2 x 10(4), B - 2.0 x 10(3) +/- 2.6 x 10(3), and C - 2.6 x 10(3) +/- 5.9 x 10(3) and GII: A - 0.4 x 10(3) +/- 0.6 x 10(3), B - 9.4 x 10(3) +/- 17.7 x 10(3) and C - 6.3 x 10(3) +/- 15.3 x 10(3). The mean counts for Candida sp. were expressed as log (CFU + 1) mL(-1) and statistical significance of differences among groups was tested by ANOVA (alpha = 0.05). Multiple comparisons were performed according to Bonferroni test and indicated significant differences between A-B and A-C, but not between B and C for both groups. It was concluded that there is a significant relationship between continuous denture wear and Candida sp.

Biocompatibility of denture base acrylic resins evaluated M culture of L929 cells. Effect of polymerisation cycle and postpoymerisation treatments

Objective: the purpose of this study was to evaluate the effect of two post-polymerisation treatments and different cycles of polymerisation on the cytotoxicity of two denture base resins.Materials and methods: the resins tested were Lucitone 550 and QC 20. Discs of resins were fabricated following the manufacturer's instructions. Lucitone 550 was processed by long cycle or short cycle. The resin QC 20 was processed by reverse cycle or normal cycle. The specimens were divided into groups: (i) post-polymerised in microwave for 3 min at 500 W; (ii) post-polymerised in water-bath at 55 degrees C for 60 min and (iii) without post-polymerisation. Eluates were prepared by placing three discs into a sterile glass vial with 9 ml of Eagle's medium and incubated at 37 degrees C for 24 hours. L929 cells were seeded into 96 3 well culture plates and DNA synthesis was assessed by H-thymidine incorporation assay.Results: the results were submitted to two-way ANOVA and Tukey HSD test. QC 20 specimens polymerised by the normal cycle and submitted to microwave post-polymerisation were graded as moderately cytotoxic. Similar results were observed for Lucitone 550 processed by long cycle without post-polymerisation. The other experimental groups were graded as not cytotoxic. After water-bath post-polymerisation, specimens of Lucitone 550 processed by long cycle produced significantly lower inhibition of DNA synthesis than the other groups.Conclusion: the long cycle increased the cytotoxicity of Lucitone 550 and water-bath post-polymerisation reduced the cytotoxicity of Lucitone 550 processed by long cycle.

Comparison of accuracy between compression- and injection-molded complete dentures

Statement of problem. A clinically significant incisal pin opening may occur after processing complete dentures if a compression molding technique is used. To recover the proper vertical dimension of occlusion, a time-consuming occlusal adjustment is necessary that often destroys the anatomy of the artificial teeth. A new injection molding process claims to produce dentures that require few, if any, occlusal adjustments in the laboratory after processing.Purpose. This laboratory study compared incisal pin opening, dimensional accuracy, and laboratory working time for dentures fabricated by this new injection system with dentures constructed by the conventional compression molding technique.Material and methods. Two groups of 6 maxillary and 6 mandibular dentures were evaluated as follows: group 1 (control), Lucitone 199, compression molded with a long cure cycle; and group 2, Lucitone 199, injection molded with a long cure. Incisal pin opening was measured with a micrometer immediately after deflasking. A computerized coordinate measuring machine was used to measure dimensional accuracy of 3-dimensional variations in selected positions of artificial teeth in 4 stages of denture fabrication. Analysis of variance (ANOVA) and t tests were performed to compare the groups.Results. A significant difference was found in pin opening between groups (t test). Horizontal dimensional changes evaluated with repeated measures ANOVA revealed no significant differences between groups. However, analysis of vertical dimensional changes disclosed significant differences between the groups. There was no appreciable difference in laboratory working time for flasking and molding denture bases between the injection and compression molding techniques when polymethyl methacrylate resin was used.Conclusion. The injection molding method produced a significantly smaller incisal pin opening over the standard compression molding technique. The injection molding technique, using polymethyl methacrylate, was a more accurate method for processing dentures. There were no appreciable differences in laboratory working time between the injection and compression molding techniques.

Effects of chemical disinfectants on the transverse strength of denture base acrylic resins

The disinfection of dental prostheses by immersion in a chemical solution should be capable of rapid inactivation of pathogenic microorganisms, without causing any adverse effect on the denture base resins. This study evaluated the effect of disinfection immersion on the transverse strength of two heat-cured resins. The denture base resins (Lucitone 550 and QC 20) were polymerized according to the manufacturers' instructions. After polymerization, the specimens were polished, and then stored in water at 37 degreesC for 50 +/- 2 h prior immersion in one of the following solutions for 10 min: 4% chlorhexidine, 1% sodium hypochlorite and 3.78% sodium perborate. The specimens were submitted to disinfection twice, simulating when dentures come from the patient and before being returned to the patient. Ten specimens were made for each group. The transverse strength was evaluated by a 3-point bend test. The flexural strength of the two denture base acrylic resins evaluated remained unaffected after immersion in the three solutions evaluated. In general, the QC 20 resin specimens exhibited lower transverse strength than the Lucitone 550 resin specimens, regardless of immersion solutions.

Effect of denture fabrication and wear on closest speaking space and interocclusal distance during deglutition

Statement of problem. The accuracy of assessing maxillomandibular relationships for trial bases and dentures using phonetic and swallowing methods has not been compared to that observed with definitive prostheses. Thus, there is no evidence to prove whether measurements obtained through such methods remain the same after adaptation to dentures.Purpose. This study investigated changes in the closest speaking space, interocclusal rest space, and interocclusal distance during deglutition in edentulous patients during and after complete denture treatment.Material and methods. Eighteen edentulous subjects participated in this study and measurements were performed after 7 Intervals of time: (1) with occlusion rims and record bases following creation of the maxillomandibular relationship record, (2) with trial dentures, (3) at Insertion of definitive complete dentures, (4) 1 week, (5) 2 weeks, (6) 1 month, and (7) 3 months after insertion. Recordings of interocclusal distances were made with a mandibular kinesiograph. Closest speaking space was measured during the pronunciation of the word 'seis'. The distance between postural rest position and centric occlusion, or interocclusal rest space, was measured using a kinesiograph. Interocclusal distance during deglutition was tested by recording the closest mandibular position recorded during swallowing of 20 mL of water. Data were analyzed using repeated-measure ANOVA, followed by the Student-Newman-Keuls test (alpha=.05).Results. A significant (P <.01)reduction in the mean closest speaking space was found when it was evaluated using occlusion rims and record bases (4.6 mm) compared with other stages (3.0 to 3.4 mm). No significant differences were found in mean interocclusal rest space and interocclusal distance during deglutition among the time periods evaluated.Conclusions. The presence of occlusion rims can influence mandibular position during pronunciation of the /s/ sound. The arrangement of artificial teeth changes the closest speaking space. However, rest position and deglutition were not affected, either during denture fabrication or short-term use.

Effect of microwave sterilization and water storage on the Vickers hardness of acrylic resin denture teeth

Statement of problem. Acrylic resin denture teeth soften upon immersion in water, and the heating generated during microwave sterilization may enhance this process.Purpose. Six brands of acrylic resin denture teeth were investigated with respect to the effect of microwave sterilization and water immersion on Vickers hardness (VHN).Material and Methods. The acrylic resin denture teeth (Dentron [D], Vipi Dent Plus [V], Postaris [P], Biolux [B], Trilux [T], and Artiplus [A]) were embedded in heat-polymerized acrylic resin within polyvinylchloride tubes. For each brand, the occlusal surfaces of 32 identical acrylic resin denture posterior teeth were ground flat with 1500-grit silicon carbide paper and polished on a wet polishing wheel with a slurry of tin oxide. Hardness tests were performed after polishing (control group, C) after polishing followed by 2 cycles of microwave sterilization at 650 W for 6 minutes (MwS group), after polishing followed by 90-day immersion in water (90-day Wim group), and after polishing followed by 90-day storage in water and 2 cycles of microwave sterilization (90-day Wim + MwS group). For each specimen, 8 hardness measurements were made and the mean was calculated. Data were analyzed with a 2-way analysis of variance followed by the Bonferroni procedure to determine any significance between pairs of mean values (alpha=.01).Results: Mircrowave sterilization of specimens significantly decreased (P <.001) the hardness of the acrylic resin denture tooth specimens P (17.8 to 16.6 VHN, V (18.3 to 15.8 VHN), T (17.4 to 15.3 VHN), B (16.8 to 15.7 VHN), and A (17.3 to 15.7 VHN). For all acrylic resin denture teeth, no significant differences in hardness were found between the groups Mws, 90-day Wim, and 90-day Wim + MwS, with the exception of the 90-day Wim + MwS tooth A specimens (14.4 VHN), which demonstrated significant lower mean values (P <.001) than the 90-day Wim (15.8 VHN) and MwS (15.7 VHN) specimens.Conclusions. For specimens immersed in water for 90 days, 2 cycles of microwave sterilization had no effect on the hardness of most of the acrylic resin denture teeth.

Composite occlusal surfaces for acrylic resin denture teeth

Acrylic resin denture teeth often exhibit rapid occlusal wear, which may lead to a loss of chewing efficiency and a loss of vertical dimension of occlusion. The use of metal occlusal surfaces on the acrylic resin denture teeth will minimize occlusal wear. Several articles have described methods to construct metal occlusal surfaces; however, these methods are time-consuming, costly, and sometimes considered to be unesthetic. These methods also require that the patient be without the prosthesis for the time necessary to perform the laboratory procedures. This article presents a quick, simple, and relatively inexpensive procedure for construction of composite occlusal surfaces on complete and partial dentures.

Biofilm microbial communities of denture stomatitis

Introduction: Denture stomatitis is a common lesion that affects denture wearers. Its multifactorial etiology seems to depend on a complex and poorly characterized biofilm. The purpose of this study was to assess the composition of the microbial biofilm obtained from complete denture wearers with and without denture stomatitis using culture-independent methods.Methods: Samples were collected from healthy denture wearers and from patients with denture stomatitis. Libraries comprising about 600 cloned 16S ribosomal DNA (rDNA) bacterial sequences and 192 cloned eukaryotic internal transcribed spacer (ITS) region sequences, obtained by polymerase chain reactions, were analyzed.Results: The partial 16S rDNA sequences revealed a total of 82 bacterial species identified in healthy subjects and patients with denture stomatitis. Twenty-seven bacterial species were detected in both biofilms, 29 species were exclusively present in patients with denture stomatitis, and 26 were found only in healthy subjects. Analysis of the ITS region revealed the presence of Candida sp. in both biofilms.Conclusion: The results revealed the extent of the microbial flora, suggesting the existence of distinct biofilms in healthy subjects and in patients with denture stomatitis.

Changes in occlusal vertical dimension in microwave processing of complete dentures.

This study investigated the effect of different microwave curing cycles on the changes in occlusal vertical dimension of complete dentures. Four test groups with 12 maxillary dentures each were evaluated. Groups 1, 2 and 3 were polymerized with different cycles by microwave radiation and Group 4 was the control and cured by water bath. The average pin opening for all groups was less than 0.5 mm. There was no significant difference between the groups polymerized by the microwave method and the control group. However, analyses of the vertical dimension changes showed statistically significant differences between groups 2 (0.276 +/- 0.141 mm) and 3 (0.496 +/- 0.220 mm).

Histomorphometric evaluation of a threaded, sandblasted, acid-etched implant retrieved from a human lower jaw: A case report

The purpose of this study was to histomorphometrically evaluate the bone-to-implant contact and bone area around a titanium implant retrieved from a human lower jaw. A screw-shaped titanium implant (sandblasted and acid-etched surface) was removed from a 68-year-old male after having been in function for 40 months because of a fracture of the abutment screw. Following the implant removal, an undecalcified section was obtained. The histomorphometric analysis showed a rate of 75.40% of bone-to-implant contact and 89.30% of bone area filling within the limits of the implant threads. The surrounding bone healed in a well-organized pattern and could not be differentiated from the anginal alveolus. The histologic evidence showed a high degree of osseointegration in a threaded, sandblasted, and acid-etched implant retrieved from a human lower jaw after functional loading for 40 months. Copyright © 2005 by Lippincott Williams & Wilkins.

Intercommissural width in 4 racial groups as a guide for the selection of maxillary anterior teeth in complete dentures

Purpose: To determine whether intercommissural width is a reliable guide for the selection of maxillary denture teeth width. Materials and Methods: Casts were made of 160 subjects from 4 different racial groups. Locations of intercommissural width landmarks (the corners of the mouth) were made on the subjects and transferred to the casts. The distances between the corners of the mouth and the distal of the canines were measured on the casts and compared. Results: A weak correlation was found between the distal of the canines and the distance between the corners of the mouth in the 4 racial groups. Conclusion: The use of the corners of the mouth for the selection of artificial teeth is generally inaccurate.

Effectiveness of microwave irradiation on the disinfection of complete dentures

Purpose: The purpose of this study was to evaluate the effectiveness of microwave irradiation on the disinfection of simulated complete dentures. Materials and Methods: Eighty dentures were fabricated in a standardized procedure and subjected to ethylene oxide sterilization. The dentures were individually inoculated (10 7 cfu/mL) with tryptic soy broth (TSB) media containing one of the tested microorganisms (Candida albicans, Streptoccus aureus, Bacillus subtilis, and Pseudomonas aeruginosa). After 48 hours of incubation at 37°C, 40 dentures were individually immersed in 200 mL of water and submitted to microwave irradiation at 650 W for 6 minutes. Forty nonirradiated dentures were used as positive controls. Replicate aliquots (25 μL) of suspensions were plated at dilutions of 10 -3 to 10 -6 on plates of selective media appropriate for each organism. All plates were incubated at 37°C for 48 hours. TSB beakers with the microwaved dentures were incubated at 37°C for 7 more days. After incubation, the number of colony-forming units was counted and the data were statistically analyzed by Kruskal-Wallis test (α = .05). Results: No evidence of growth was observed at 48 hours for S aureus, B subtilis, and C albicans. Dentures contaminated with P aeruginosa showed small growth on 2 plates. After 7 days incubation at 37°C, no growth was visible in the TSB beakers of S aureus and C albicans. Turbidity was observed in 3 broth beakers, 2 from P aeruginosa and 1 from B subtilis. Conclusion: Microwave irradiation for 6 minutes at 650 W produced sterilization of complete dentures contaminated with S aureus and C albicans and disinfection of those contaminated with P aeruginosa and B subtilis.

Effect of microwave disinfection procedures on torsional bond strengths of two hard chairside denture reline materials

Purpose: This study evaluated the potential effects of denture base resin water storage time and an effective denture disinfection method (microwave irradiation at 650 W for 6 minutes) on the torsional bond strength between two hard chairside reline resins (GC Reline and New Truliner) and one heat-polymerizing denture base acrylic resin (Lucitone 199). Materials and Methods: Cylindrical (30 x 3.9 mm) denture base specimens (n = 160) were stored in water at 37°C (2 or 30 days) before bonding. A section (3.0 mm) was removed from the center of the specimens, surfaces prepared, and the reline materials packed into the space. After polymerization, specimens were divided into four groups (n = 10): Group 1 (G1) - tests performed after bonding; Group 2 (G2) - specimens immersed in water (200 ml) and irradiated twice (650 W for 6 minutes); Group 3 (G3) - specimens irradiated daily until seven cycles of disinfection; Group 4 (G4) - specimens immersed in water (37°C) for 7 days. Specimens were submitted to a torsional test (0.1 Nm/min), and the torsional strengths (MPa) and the mode of failure were recorded. Data from each reline material were analyzed by a two-way analysis of variance, followed by Neuman-Keuls test (p = 0.05). Results: For both Lucitone 199 water storage periods, before bonding to GC Reline resin, the mean torsional strengths of G2 (2 days - 138 MPa; 30 days - 132 MPa), G3 (2 days - 126 MPa; 30 days - 130 MPa), and G4 (2 days - 130 MPa; 30 days - 137 MPa) were significantly higher (p < 0.05) than G1 (2 days - 108 MPa; 30 days - 115 MPa). Similar results were found for Lucitone 199 specimens bonded to New Truliner resin, with G1 specimens (2 days - 73 MPa; 30 days - 71 MPa) exhibiting significantly lower mean torsional bond strength (p < 0.05) than G2 (2 day - 86 MPa; 30 days - 90 MPa), G3 (2 days - 82 MPa; 30 days - 82 MPa), and G4 specimens (2 days - 78 MPa; 30 days - 79 MPa). The adhesion of both materials was not affected by water storage time of Lucitone 199 (p > 0.05). GC reline showed a mixed mode of failure (adhesive/cohesive) and New Truliner failed adhesively. Conclusions: Up to seven microwave disinfection cycles did not decrease the torsional bond strengths between the hard reline resins, GC Reline and New Truliner to the denture base resin Lucitone 199. The effect of additional disinfection cycles on reline material may be clinically significant and requires further study. Copyright © 2006 by The American College of Prosthodontists.

The effect of water immersion on the shear bond strength between chairside reline and denture base acrylic resins: Basic science research

Purpose: The effect of water immersion on the shear bond strength (SBS) between 1 heat-polymerizing acrylic resin (Lucitone 550-L) and 4 autopolymerizing reline resins (Kooliner-K, New Truliner-N, Tokuso Rebase Fast-T, Ufi Gel Hard-U) was investigated. Specimens relined with resin L were also evaluated. Materials and Methods: One hundred sixty cylinders (20 × 20 mm) of L denture base resin were processed, and the reline resins were packed on the prepared bonding surfaces using a split-mold (3.5 × 5.0 mm). Shear tests (0.5 mm/min) were performed on the specimens (n = 8) after polymerization (control), and after immersion in water at 37°C for 7, 90, and 180 days. All fractured surfaces were examined by scanning electron microscopy (SEM) to calculate the percentage of cohesive fracture (PCF). Shear data were analyzed with 2-way ANOVA and Tukey's test; Kruskall-Wallis test was used to analyze PCF data (α = 0.05). Results: After 90 days water immersion, an increase in the mean SBS was observed for U (11.13 to 16.53 MPa; p < 0.001) and T (9.08 to 13.24 MPa, p = 0.035), whereas resin L showed a decrease (21.74 MPa to 14.96 MPa; p < 0.001). The SBS of resins K (8.44 MPa) and N (7.98 MPa) remained unaffected. The mean PCF was lower than 32.6% for K, N, and T, and higher than 65.6% for U and L. Conclusions: Long-term water immersion did not adversely affect the bond of materials K, N, T, and U and decreased the values of resin L. Materials L and U failed cohesively, and K, N, and T failed adhesively. © 2007 by The American College of Prosthodontists.