Influence of Different Ceramics on Resin Cement Knoop Hardness Number

This study evaluated: 1) the effect of different ceramics on light attenuation that could affect microhardness, measured as the Knoop Hardness Number (KHN), of a resin cement immediately and 24 hours after polymerization and 2) the effect of different activation modes (direct light-activation, light activation through ceramics and chemical activation) on the KHN of a resin cement.Resin cement Rely X ARC (3M ESPE) specimens 5.0 mm in diameter and 1.0 nun thick were made in a Teflon mold covered with a polyester film. The cement was directly light activated for 40 seconds with an XL 2500 curing unit (3M ESPE) with 650 mW/cm(2), light activated through ceramic discs of Duceram Plus (DeguDent), Cergogold (DeguDent), IPS Empress (Ivoclar), IPS Empress 2 (Ivoclar), Procera. (NobelBiocare), In Ceram Alumina (Vita) and Cercon (DeguDent), having a 1.2 mm thickness or chemically activated without light application. The resin cement specimens were flattened, and KHN was obtained using an HMV 2 microhardness tester (Shimadzu) with a load of 50 g applied for 15 seconds 100 pin from the irradiated surface immediately and after storage at 37 degrees C for 24 hours. Ten measurements were made for each specimen, with three specimens for each group at each time. The data were submitted to ANOVA and Tukey's test (p=0.05). The KHN of the resin cement was not only affected by the mode of activation, but also by the post-activation testing time. The mean KHN of the resin cement for chemical activation and through all ceramics showed statistically significant lower values compared to direct activation immediately and at 24 hours. The KHN for 24 hours post-activation was always superior to the immediate post-activation test except with direct activation. The most opaque ceramics resulted in the lowest KHN values.

Short-term in situ/ex vivo study of the anticariogenic potential of a resin-modified glass-ionomer cement associated with adhesive systems

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of mineral trioxide aggregate and calcium hydroxide cement as pulp-capping agents in human teeth

This study evaluated the histomorphologic response of human dental pulps capped with mineral trioxide aggregate (MTA) and Ca(OH)(2) cement (CH). Pulp exposures were performed on the occlusal floor of 40 human permanent premolars. After that, the pulp was capped either with CH or MTA and restored with composite resin. After 30 and 60 days, teeth were extracted and processed for histologic exam and categorized in a histologic score system. The data were subjected to Kruskal-Wallis and Conover tests (alpha = .05). All groups performed well in terms of hard tissue bridge formation, inflammatory response, and other pulpal findings. However, a lower response of CH30 was observed for the dentin bridge formation, when compared with MTA30 and MTA60 groups. Although the pulp healing with calcium hydroxide was slower than that of MTA, both materials were successful for pulp capping in human teeth.

Short-term evaluation of the pulpo-dentin complex response to a resin-modified glass-ionomer cement and a bonding agent applied in deep cavities

Objectives. To evaluate the response of the pulpo-dentin complex following application of a resin-modified glass-ionomer cement or an adhesive system in deep cavities performed in human teeth.Methods. Deep class V cavities were prepared on the buccal surface of 26 premolars. In Group I the cavity walls (dentin) and enamel were conditioned with 32% phosphoric acid and the dentin adhesive system One Step (Bisco, Inc., Itasca, IL, USA) was applied. In Groups 2 and 3, before total etching and application of bonding agent, the cavity floor was lined with the resin-modified glass-ionomer cement-Vitrebond (3M ESPE Dental Products Division, St. Paul, MN, USA) or the calcium hydroxide cement-Dycal (control group, Dentsply, Mildford, DE, USA), respectively. The cavities were restored using light-cured Z-100 composite resin (3M ESPE). The teeth were extracted between 5 and 30 days and prepared for microscopic assessment. Serial sections were stained with H/E, Masson's trichrome, and Brown and Brenn techniques.Results. In Group 1, the inflammatory response was more evident than in Groups 2 and 3. Diffusion of dental material components across dentinal tubules was observed only in Group 1, in which the intensity of the pulp response increased as the remaining dentin thickness decreased. Bacteria were evidenced in the lateral walls of two samples (Group 2) which exhibited no inflammatory response or tissue disorganization.Conclusions. Based on the experimental conditions, it was concluded total acid etching followed by application of One Step bonding agent cannot be recommended as adequate procedures. In this clinical condition the cavity walls should be lined with a biocompatible dental material, such as Vitrebond or Dycal. 2003 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of Ultrasonic Excitation on the Porosity of Glass Ionomer Cement: A Scanning Electron Microscope Evaluation

Background: Ultrasonic excitation (US) was applied to glass ionomer cement (GIC) during early set time to increase the advantageous properties of this material. Purpose: The aim of this in vitro study was to assess the inner porosity of GIC after US. Study design: A total of 16 specimens, for each material, were prepared from high-viscosity GIC Fuji IX GP, Ketac Molar, and Ketac Molar Easymix. Half of these specimens (n = 8) received 30 s of US during the initial cement setting. After completion of the material setting, specimens were fractured and observed by scanning electronic microscopy to quantitatively assay porosity inside the material using Image J software. Results: Statistical data analysis revealed that US reduced the porosity for all tested materials (P <= 0.05). The following reductions (expressed in percentages) were achieved: Fuji IX-from 3.9% to 2.8%; Ketac Molar Easy Mix-from 4.4% to 2.6%, and Ketac Molar-from 2.4% to 1.6%. Conclusion: Under the tested conditions, US was an effective method for porosity reduction inside the material. Microsc. Res. Tech. 74:54-57, 2011. (C) 2010 Wiley-Liss, Inc.

Influences of the insertion method in glass ionomer cement porosity

The aim of this study was to evaluate the presence of porosities inside the glass ionomer cement (GIC) after different techniques of material insertion. MATERIAL and METHOD: Specimens were prepared with high-viscosity GIC Ketac Molar Easymix and divided into three groups according to the insertion method: spatula (PI), Centrix injector (CI), and low-cost syringe (LCS). The specimens were fractured and observed with scanning electronic microscopy to quantitatively evaluate porosity inside the material using Image J Software. RESULTS: Statistical analysis, ANOVA application, and Tukey test to significance level of 5%, revealed that there was no statistical difference between the groups. CONCLUSION: Although the use of LCS has not decreased the porosity of the material, this insertion method is easy, accessible, and low cost, which makes it a viable alternative of use in the ART technique and in others bucal health programs. Microsc. Res. Tech., 2012. (c) 2012 Wiley Periodicals, Inc.

Influence of the activation mode of a self-etch resin-based luting cement upon the metabolism of odontoblast-like cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mechanical and biological characterization of resin-modified glass-ionomer cement containing doxycycline hyclate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Utilization of autogenous bone, bioactive glasses, and calcium phosphate cement in surgical mandibular bone defects in Cebus apella monkeys

Purpose: the purpose of the present study was to evaluate the histologic results of bone cavities that were surgically created in the mandibles of Cebus apella monkeys and filled with autogenous bone, PerioGlas, FillerBone, or Bone Source. Materials and Methods: Surgical cavities 5 mm in diameter were prepared through both mandibular cortices in the mandibular angle region. The cavities were randomly filled, and the animals were divided into groups according to the material employed: Group 1 cavities were filled with autogenous corticocancellous bone; group 2 cavities were filled with calcium phosphate cement (BoneSource); and group 3 and group 4 cavities were filled with bioactive glass (FillerBone and PerioGlas, respectively). After 180 days the animals were sacrificed, and specimens were prepared following routine laboratory procedures for hematoxylin/eosin staining and histologic evaluation. Results: the histologic analysis showed that autogenous bone allowed total repair of the bone defects; bioactive glasses (FillerBone and PerioGlas) allowed total repair of the defects with intimate contact of the remaining granules and newly formed bone; and the cavities filled with calcium phosphate cement (BoneSource) were generally filled by connective fibrous tissue, and the material was almost totally resorbed. Discussion: the autogenous bone, FillerBone, and PerioGlas provided results similar to those in the current literature, showing that autogenous bone is the best Choice for filling critical-size defects. Synthetic implanted materials demonstrated biocompatibility, but the bioglasses demonstrated osteoconductive activity that did not occur with calcium phosphate (BoneSource). Conclusion: According to the methodology used in this study, it can be concluded that the utilization of autogenous bone and bioactive glasses permitted the repair of surgically created critical-size defects by newly formed bone; the synthetic implanted materials demonstrated biocompatibility, and the bioactive glasses demonstrated osteoconductive activity. The PerioGlas was mostly resorbed and replaced by bone and the remaining granules were in close contact with bone; the FillerBone showed many granules in contact with the newly formed bone; BoneSource did not permit repair of the critical-size defects, and the defects were generally filled by connective fibrous tissue.

Biocompatibility of a resin-modified glass-ionomer cement applied as pulp capping in human teeth

Purpose: to evaluate the human pulp response following pulp capping with calcium hydroxide (CI-I, Group 1), and the resin-modified glass-ionomer Vitrebond (VIT, Group 2). Materials and Methods: Intact teeth with no cavity preparation were used as control Group (ICG, Group 3). Buccal Class V cavities were prepared in 34 sound human premolars. After exposing the pulps, the pulp capping materials were applied and the cavities were Filled using Clearfil Liner Bond 2 bonding agent and Z100 resin-based composite. The teeth were extracted after 5, 30, and from 120 to 300 days, fixed in 10% buffered formalin solution, and prepared according to routine histological techniques. 6-mu m sections were stained with hematoxylin and eosin, Masson's trichrome, or Brown gr Brenn technique for bacterial observation. Results: At 5 days, CH caused a large zone of coagulation necrosis, the mononuclear inflammatory reaction underneath the necrotic zone was slight to moderate. VIT caused a moderate to intense inflammatory pulp response with a large necrotic zone. A number of congested venules associated with plasma extravasation and neutrophilic infiltration was observed. Over time, only CH allowed pulp repair and complete dentin bridging around the pulp exposure site. VIT components displaced into the pulp tissue triggered a persistent inflammatory reaction which appeared to be associated with a lack of dentin bridge formation. After 30 days a few histological sections showed a number of bacteria on the lateral dentin walls. In these samples the pulp response was similar to those samples with no microleakage. VIT was more irritating to pulp tissue than CH, which allowed pulp repair associated with dentin bridge formation. These results suggested that VIT is not an appropriate dental material to be used in direct pulp capping for mechanically exposed human pulps.

EFFECT of DIFFERENT AIRBORNE-PARTICLE ABRASION/BONDING AGENT COMBINATIONS on THE BOND STRENGTH of A RESIN CEMENT TO A BASE METAL ALLOY

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efficacy of Air-abrasion Technique and Additional Surface Treatment at Titanium/Resin Cement Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Er,Cr: YSGG laser on bond strength of self-adhesive resin cement

The purpose of this study was to investigate the bond strength of fiber post previously laser treated root canals. Forty single-rooted bovine teeth were endodontically treated, randomly and equally divided into two main groups according to the type of pretreatment: G1: 2.5% NaOCl (control group); and G2: Er,Cr:YSGG laser. Each group was further subdivided into 2 groups based on the category of adhesive systems/ luting materials used: a: an etch-and-rinse resin cement (Single Bond/RelyX ARC; 3M ESPE), and b: a self-adhesive resin cement (Rely X Unicem; 3M ESPE). Three 1.5 mm thick slabs were obtained per root and the push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. Data were analyzed by ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. Analysis of variance showed no statistically significant difference (p > 0.05) among the groups G1a (25.44 ± 2.35) and G1b (23.62 ± 3.48), G2a (11.77 ± 2.67) and G2b (9.93 ± 3.37). Fractures were observed at the interface between the dentin and the resin in all groups. The Er,Cr:YSGG laser irradiation did not influence on the bond strength of the resin cements and the etch-and-rinse resin cement had better results on bond strength than self-adhesive resin cement.

Persistence of endodontic methacrylate-based cement residues on dentin adhesive surface treated with different chemical removal protocols

The aim of this study was to evaluate the persistence of methacrylate-based cement residues on the dentin, after dentin surface cleaning with ethanol or acetone, with or without previous application of a dentin adhesive. Forty bovine crown fragments were obtained and the dentin surface was washed with 1.0 mL of 2.5% sodium hypochlorite (NaOCl), followed by 0.1 mL of 17% ethylenediaminetetraacetic acid application for 3 min, and final irrigation with 2.5% NaOCl. The specimens were air dried and resin-based cement was rubbed onto the dentine surface with a microbrush applicator. In 20 specimens, previously to cement, a dentin adhesive was applied in all surfaces. After 15 min, the surface was scrubbed with a cotton pellet and moistened with ethanol or acetone, compounding the following groups: G199.5% ethanol and G2acetone, without previous use of dentin adhesive; G399.5% ethanol and G4acetone, with previous use of dentin adhesive. The dentin surface was scrubbed until the cement residues could not be visually detected. Sections were then processed for scanning electron microscopy and evaluated at 500x magnification and scores were attributed to each image according to the area covered by residual sealer, and data were subjected to KruskalWallis at 5% significance. The lower residue presence was observed in G3 (P = 0.005). All surface presented cement residues when acetone was used as cleaning solution (P = 0.0005). The cleaning solutions were unable to completely remove the cement residues from both surfaces. The ethanol used after previous application of the dentin adhesive promoted the lower presence of residues.

Persistence of resinous cement residues in dentin treated with different chemical removal protocols

The aim of this study was to evaluate the persistence of resin cement residues after dentin surface cleaning with different alcohol-based solutions or an essential oil (eucalyptol). Forty bovine teeth were sectioned in order to expose pulp chamber dentin to be washed with 1.0 mL of 2.5% sodium hypochlorite (NaOCl), followed by 0.1 mL of 17% EDTA application for 3 min, and final irrigation with 2.5% NaOCl. The specimens were air dried and resin-based cement was rubbed onto the dentine surface with a microbrush applicator. After 15 min, the surface was scrubbed with a cotton pellet and moistened with different dentin cleaning solutions, compounding the following groups: G195% ethanol, G270% ethanol, G370% isopropyl alcohol, or G4eucalyptol. The dentin was scrubbed until the cement residues could not be visually detected. Sections were then processed for SEM and evaluated at x 500 magnification. Scores were attributed to each image according to the area covered by residual sealer, and data were subjected to KruskalWallis at 5% significance. Eucalyptol promoted the most adequate dentin cleaning, although no statistical difference was detected amongst the groups (P > 0.05), except between the eucalyptol and 70% ethanol groups (P < 0.05). All the evaluated dentin cleaning solutions were unable to completely remove the cement residues from the dentin surface. Microsc. Res. Tech., 2012. (C) 2012 Wiley Periodicals, Inc.