Surface conditioning of a composite used for inlay/onlay restorations: Effect on mu TBS to resin cement

Purpose: To assess the effect of the composite surface conditioning on the microtensile bond strength of a resin cement to a composite used for inlay/onlay restorations.Materials and Methods: Forty-two blocks (6 x 6 x 4 mm) of a microfilled composite (Vita VMLC) were produced and divided into 3 groups (N = 14) by composite surface conditioning methods: Gr1 - etching with 37% phosphoric acid, washing, drying, silanization; Gr2 - air abrasion with 50-Im Al203 particles, silanization; Gr3 - chairside tribochemiCal silica coating (CoJet System), silanization. Single-Bond (one-step adhesive) was applied on the conditioned surfaces and the two resin blocks treated with the same method were cemented using RelyX ARC (dual-curing resin cement). The specimens were stored for 7 days in water at 37 degrees C and then sectioned to produce nontrimmed beam samples, which were submitted to microtensile bond strength testing (mu TBS). For statistical analysis (one-way ANOVA and Tukey's test, = 0.05), the means of the beam samples from each luted specimen were calculated (n = 7).Results: mu TBS values (MPa) of Gr2 (62.0 +/- 3.9a) and Gr3 (60.5 +/- 7.9a) were statistically similar to each other and higher than Gr1 (38.2 +/- 8.9b). The analysis of the fractured surfaces revealed that all failures occurred at the adhesive zone.Conclusion: Conditioning methods with 50-Im Al203 or tribochemical silica coating allowed bonding between resin and composite that was statistically similar and stronger than conditioning with acid etching.

Contribution of the study of the styloid prominence in the posterior tympanic cavity

70 human temporal bones were analyzed with the aid of an otologic microscope. The styloid prominence was found to be extremely variable in shape, location and occurrence. Depending on the degree of development, the prominence establishes important relationships with the sinus tympani, with the fossula of the cochlear fenestra, and with the suprapyramidal recess. Serial sections were used to study the relationship of the styloid process with the facial nerve inside the bony mass of the mastoid portion of the temporal bone.

Inhibition of demineralization in vitro around amalgam restorations

Objective: The purpose of this in vitro study was to evaluate some forms of preventing or avoiding demineralization within enamel cavity walls adjacent to amalgam restorations. Method and materials: Third molar teeth were sectioned to obtain 72 specimens, divided into one control and five experimental groups: amalgam only; varnish plus amalgam; acidulated phosphate fluoride plus amalgam; adhesive amalgam; glass-ionomer cement plus amalgam; control (amalgam only, not subjected to a demineralization challenge). The experimental groups were subjected to pH and thermal cycling and then submitted to enamel hardness determinations. Results: Significant differences between the treatment groups revealed that the bonded amalgam technique offered the best resistance to demineralization. The use of cavity varnish resulted in greater mineral loss than amalgam placed alone. Conclusion: The use of an adhesive system, glass-ionomer cement, or acidulated phosphate fluoride under amalgam restorations may interfere with development of secondary caries.