The effect of water immersion on the shear bond strength between chairside reline and denture base acrylic resins: Basic science research

Purpose: The effect of water immersion on the shear bond strength (SBS) between 1 heat-polymerizing acrylic resin (Lucitone 550-L) and 4 autopolymerizing reline resins (Kooliner-K, New Truliner-N, Tokuso Rebase Fast-T, Ufi Gel Hard-U) was investigated. Specimens relined with resin L were also evaluated. Materials and Methods: One hundred sixty cylinders (20 × 20 mm) of L denture base resin were processed, and the reline resins were packed on the prepared bonding surfaces using a split-mold (3.5 × 5.0 mm). Shear tests (0.5 mm/min) were performed on the specimens (n = 8) after polymerization (control), and after immersion in water at 37°C for 7, 90, and 180 days. All fractured surfaces were examined by scanning electron microscopy (SEM) to calculate the percentage of cohesive fracture (PCF). Shear data were analyzed with 2-way ANOVA and Tukey's test; Kruskall-Wallis test was used to analyze PCF data (α = 0.05). Results: After 90 days water immersion, an increase in the mean SBS was observed for U (11.13 to 16.53 MPa; p < 0.001) and T (9.08 to 13.24 MPa, p = 0.035), whereas resin L showed a decrease (21.74 MPa to 14.96 MPa; p < 0.001). The SBS of resins K (8.44 MPa) and N (7.98 MPa) remained unaffected. The mean PCF was lower than 32.6% for K, N, and T, and higher than 65.6% for U and L. Conclusions: Long-term water immersion did not adversely affect the bond of materials K, N, T, and U and decreased the values of resin L. Materials L and U failed cohesively, and K, N, and T failed adhesively. © 2007 by The American College of Prosthodontists.

Interaction between total-etch and self-etch adhesives and conventional and self-adhesive resin cements

The aim of this study was to compare the bond strength to enamel between resin cements combined with total-etch and self-etch adhesive systems and a self-adhesive cement. Eighty bovine incisors had their buccal surface ground flat exposing a plane area in the enamel. Eighty Artglass resin cylinders measuring 3 mm in diameter and 4 mm in height were fabricated. The teeth were divided into eight groups of 10 teeth each and the resin cylinders were cemented with different adhesive systems and resin cements; G1: RelyX Unicem (self-adhesive cement); G2: H 3PO 4 + Single Bond + RelyX ARC; G3: AdheSE + Variolink II; G4: H 3PO 4 + Excite + Variolink II; G5: Xeno III + Enforce; G6: H 3PO 4 + Prime&Bond NT + Enforce; G7: Biatite Primers 1 and 2 + Bistite II DC; G8: H 3PO 4 + Bistite Primers 1 and 2 + Bistite II DC. After application of the adhesives, the cylinders were cemented according to manufacturer instructions. The specimens were submitted to 2000 thermal cycles at a temperature ranging from 5±5°C to 55±5°C, and shear bond strength was then tested at a variety of 1 mm/min. The data were analyzed by ANOVA and the Tukey's test (á=5%), obtaining a p value of 0.00. The following mean (±standard deviation) bond strength values were observed for each group: G1: 5.14(±0.99)a; G3: 16.23(±4.69)b; G7: 17.82(±3.66)b; G5: 18.48(±2.88)bc; G8: 20.15(±4.12)bc; G4: 22.85(±3.08)cd; G2: 24.96(±2.89)d; G6: 26.07(±1.69)d. Groups followed by the same letters did not differ significantly. For most of the resin cements tested, the application of adhesive systems using acid etching resulted in a higher bond strength when compared to the self-etch adhesive systems and to the self-adhesive cement.

Optimization of multipulse converters with delta and Y-differential connections

This work presents a study regarding the optimization of multipulse converters. A general expression for the connection (Δ or Y) for both 12 and 18-pulses is obtained and describes the output voltages on the secondary windings, depending on the voltage reference from the primary. These generalized expressions allows choosing different ratios between input and output voltages and as result an optimum operation point for the converter can be calculated. Considering Δ-connected converters the optimum point occurs when the magnetic core of the autotransformer processes 18% and 17% of the output power for 12 and 18-pulses, respectively. For Y-connected converters the optimum point occurs when the kVA rating is 13% and 18% for 12 and 18-pulses, respectively. Based on these results magnetic elements can be calculated and designed leading to a great weight and volume reduction and also to lower costs and losses. Finally an analysis is made to improve the kVA rating of the transformers for 12 and 18 pulses converters. © 2009 IEEE.

Lack of correlation between periodontitis and renal dysfunction in systemically healthy patients

Objectives: The aim of this study was to assess a suggested association between periodontitis and renal insufficiency by assaying kidney disease markers. Methods: Variables used to diagnose periodontitis were: (i) probing pocket depth (PPD), (ii) attachment loss (AL), (iii) bleeding on probing (BOP), (iv) plaque index (PI) and (v) extent and severity index. Blood and urine were collected from 60 apparently healthy non-smokers (men and women), consisting of a test group of 30 subjects with periodontitis (age 46±6 yrs) and a control group of 30 healthy subjects (age 43±5 yrs). Kidney function markers (urea, creatinine, uric acid and albumin contents) were measured in the serum and urine. Also, the glomerular filtration rate was estimated from creatinine clearance, from the abbreviated Modification of Diet in Renal Disease formula and from the albumin: creatinine ratio in a 24-h sample of urine. Results: It was found that the control group had a greater mean number of teeth than the test group and that the two groups also differed in PPD, AL, BOP and PI, all these variables being higher in the test group (P=0.006). For the extent and severity index of both PPD and AL, the test group had much higher medians of both extent and severity than the control group (P=0.001). With regard to kidney function, none of the markers revealed a significant difference between the control and test groups and all measured values fell within the reference intervals. Conclusions: It is proposed that severe periodontitis is not associated with any alteration in kidney function.

Comparisons between Bio-Oss® and Straumann® Bone Ceramic in immediate and staged implant placement in dogs mandible bone defects

Objective: To compare immediate and staged approach implant placement in circumferential defects treated with deproteinized bovine bone mineral (DBBM); hidroxyapatite/tricalcium phosphate (HA/TP); autogenous bone (Ab); and coagulum (Cg); upon implant stability, osseointegration and alveolar crest maintenance. Materials and methods: Six dogs underwent extractions of lower premolars, bilaterally. Twelve weeks later four bone defects (6 mm wide/4 mm long) were drilled at one side and randomly filled with DBBM; HA/TP; Ab; and Cg, respectively, and left to heal (staged approach). Eight weeks later one implant (Osseospeed™, AstraTech) was placed in experimental sites. At the same session four defects were drilled on contra-lateral side and implants were inserted immediately after biomaterials grafting (immediate approach). Animals were euthanized 8 weeks later. Implant stability was measured by resonance frequency analysis (RFA) at installation and after sacrifice. Ground sections were prepared for bone contact (BIC); bone area (BA); distance implant shoulder-bone crest (IS-C); distance implant shoulder first bone contact (IS-B); and areas occupied by soft tissue. Results: The BA and BIC were superior in the staged approach. The Cg exhibited higher BIC and BA as compared with other materials at the total implant body (P = 0.004 and 0.012, respectively). The DBBM, HA/TP and Ab groups rendered similar BA and BIC. The immediate approach resulted in less crest resorption compared to staged approach. The biomaterials did not affect the IS-C and IS-B measurements. Particles area tended to be higher in DBBM group than HA/TP (P = 0.15), while soft tissue infiltrate was higher in DBBM group when used in the immediate approach (P = 0.04). The RFA indicated gain in stability in the staged approach (P = 0.002). The correlation test between RFA vs. BIC and BA demonstrated inferior stability for DBBM group in immediate approach (P = 0.01). Conclusions: Implants placed in healed defects resulted in better stability as a consequence of higher BIC and BA. The Cg alone rendered increased BIC compared to other materials in both approaches. Immediate approach should be preferable to staged approach in terms of alveolar crest maintenance. The BIC and BA values did not vary between micro and macro-threads in this experimental model. Implants installed in sites filled with DBBM in immediate approach were less stable. © 2011 John Wiley & Sons A/S.

Durability of Adhesion between Feldspathic Ceramic and Resin Cements: Effect of Adhesive Resin, Polymerization Mode of Resin Cement, and Aging

Purpose: Adhesive cementation is an important step for restorations made of feldspathic ceramic as it increases the strength of such materials. Incorrect selection of the adhesive resin and the resin cement to adhere to the ceramic surface and their durability against aging can affect the adhesion between these materials and the clinical performance. This study evaluated the effect of adhesive resins with different pHs, resin cements with different polymerization modes, and aging on the bond strength to feldspathic ceramic. Materials and Methods: One surface of feldspathic ceramic blocks (VM7) (N = 90) (6.4 × 6.4 × 4.8 mm3) was conditioned with 10% hydrofluoric acid for 20 seconds, washed/dried, and silanized. Three adhesive resins (Scotchbond Multi-Purpose Plus [SBMP], pH: 5.6; Single Bond [SB], pH: 3.4; and Prime&Bond NT [NT], pH: 1.7) were applied on the ceramic surfaces (n = 30 per adhesive). For each adhesive group, three resin cements with different polymerization modes were applied (n = 10 per cement): photo-polymerized (Variolink II base), dual polymerized (Variolink II base + catalyst), and chemically polymerized (C&B). The bonded ceramic blocks were stored in water (37°C) for 24 hours and sectioned to produce beam specimens (cross-sectional bonded area: 1 ± 0.1 mm2). The beams of each block were randomly divided into two conditions: Dry, microtensile test immediately after cutting; TC, test was performed after thermocycling (12,000×, 5°C to 55°C) and water storage at 37°C for 150 days. Considering the three factors of the study (adhesive [3 levels], resin cement [3 levels], aging [2 levels]), 18 groups were studied. The microtensile bond strength data were analyzed using 3-way ANOVA and Tukey's post hoc test (α= 0.05). Results: Adhesive resin type (p < 0.001) and the resin cement affected the mean bond strength (p= 0.0003) (3-way ANOVA). The NT adhesive associated with the chemically polymerized resin cement in both dry (8.8 ± 6.8 MPa) and aged conditions (6.9 ± 5.9 MPa) presented statistically lower bond strength results, while the SBMP adhesive resin, regardless of the resin cement type, presented the highest results (15.4 to 18.5 and 14.3 to 18.9 MPa) in both dry and aged conditions, respectively (Tukey's test). Conclusion: Application of a low-pH adhesive resin onto a hydrofluoric acid etched and silanized feldspathic ceramic surface in combination with chemically polymerized resin cement did not deliver favorable results. The use of adhesive resin with high pH could be clinically advised for the photo-, dual-, and chemically polymerized resin cements tested. © 2012 by the American College of Prosthodontists.

Association between IL8 haplotypes and pathogen levels in chronic periodontitis

Chronic periodontitis (CP) is considered to be a multifactorial disease influenced by microbial and genetic factors. The aim of the present study was to investigate whether the genetic susceptibility to CP in individuals with the IL8 ATC/TTC haplotype is associated with subgingival levels of periodontopathogens. Sixty-five individuals, grouped according to the presence (n = 28) or absence (n = 37) of the IL8 haplotype, were evaluated. After clinical periodontal evaluation, each group was subdivided according to the presence (CP) or absence (H) of periodontitis. Four subgingival samples were obtained from CP and two samples per subject from H patients. The levels and proportions of Porphyromonas gingivalis, Tannerella forsythia, and Treponema denticola were analyzed using quantitative real-time polymerase chain reaction (q-PCR). No differences were found in the proportion of periodontopathogenic bacteria between groups with the presence or absence of the IL8 haplotype. However, in the CP groups, the levels of periodontopathogens were significantly higher in the individuals without the IL8 haplotype than in the individuals with the IL8 haplotype. These results suggest that periodontal destruction may occur in patients who are considered to be genetically susceptible to CP with a lower microbial challenge because of the presence of the IL8 ATC/TTC haplotype than in patients without this haplotype. © 2013 Springer-Verlag Berlin Heidelberg.

The relation between structural features and electrochemical activity of MnO2 nanoparticles synthesized from a polyol-made Mn 3O4 precursor

A simple hybrid synthesis processing method was developed to synthesize γ-MnO2 nanocrystalline particles. The polyol method was modified by the addition of nitric acid in order to allow the synthesizing of single-phase Mn3O4 in a large scale. In the sequence, the acid digestion technique was used to transform Mn3O4 into γ-MnO2. Structural and morphological characterization was carried out by X-ray diffractometry, Infrared and Raman spectroscopy, thermogravimetric analysis, nitrogen adsorption isotherm, scanning electron microscopy, and transmission electron microscopy. The electrochemical properties were investigated by cyclic voltammetry and galvanostatic charge-discharge measurements. The synthesized material exhibits a specific capacitance of 125.1 F g-1 at a mass loading of 0.98 mg cm-2. The relation between structural features and electrochemical activity is discussed by comparing the synthesized material with commercial electrolytic manganese dioxide. © 2013 Springer-Verlag Berlin Heidelberg.

Microtensile bond strength of resin cements to caries-affected dentin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Correlation between hand/wrist and panoramic radiographs in severe secondary hyperparathyroidism

Objectives: Hand/wrist and dental radiographs are important for osteoporosis analysis in secondary hyperparathyroidism (SHPT). This study evaluated whether a correlation exists between the effects of the disease on the hands and jaws, and investigated the association between osteoporosis progression in the hands and parathyroid hormone (PTH) levels in chronic kidney disease (CKD) patients. Materials and methods: Four panoramic radiographic parameters (mental index, mandibular cortical index, trabecular bone pattern, and calcification/resorption) and four corresponding hand/wrist radiographic parameters (metacarpal cortical thickness, phalangeal cortical index, trabecular bone pattern, and calcification/resorption) were applied to investigate possible correlation between the effects of SHPT on the jaws and hands/wrists, by Spearman's correlation coefficient. PTH levels and the hand/wrist radiographic parameters were also tested by spearman's correlation coefficient (p < 0.05). The presence of brown tumors, vascular calcifications, and acroosteolysis on the hands was also evaluated. Results: Mandibular cortical index was strongly correlated with the phalangeal cortical index (p = 0.000). Phalangeal cortical index and trabecular bone pattern of hand/wrist correlated with PTH levels (0.002 and 0.000, respectively). Brown tumors occurred in four CKD patients, while both vascular calcifications and acroosteolysis were observed in 19 patients. Conclusion: There is a significant correlation between the morphological changes caused by secondary hyperparathyroidism in hand and jaw bones. The morphological status can be assessed using the mandibular cortical index, besides the phalangeal cortical index. The latter correlates well with parathyroid hormone levels of advanced chronic kidney disease. Clinical relevance: Panoramic images reveal morphological changes in the jaw bone, indicating likewise changes in the hand/wrist in severe secondary hyperparathyroidism. The severity of the bone changes may be a reflection of the parathyroid hormone levels in advanced chronic kidney disease. © 2012 Springer-Verlag.

Cross-mating experiments detect reproductive compatibility between Triatoma sherlocki and other members of the Triatoma brasiliensis species complex

Phylogenetic approaches based on mitochondrial DNA variation (fragments of Cyt B and 16S ribosomal RNA) have revealed Triatoma sherlocki as the most recent species addition to the Triatoma brasiliensis species complex; a monophyletic group which includes T. brasiliensis, Triatoma melanica, and Triatoma juazeirensis. T. sherlocki is the most differentiated among all species of this complex: it is unable to fly, possesses longer legs than the other members, and has reddish tonality in some parts of its exochorion. We question whether these species are reproductively compatible because of this pronounced morphological differentiation, and therefore, we present a series of cross breeding experiments that test compatibility between T. sherlocki and other members of the T. brasiliensis complex. We extended our analyses to include crosses between T. sherlocki and Triatoma lenti, because the latter has been suggested as a possible member of this complex. T. sherlocki male. ×. T. lenti female pairs failed to produce hybrids. All other crosses of T. sherlocki and members of T. brasiliensis species complex, as well as backcrosses, produced viable offspring through the third generation. This study stresses the importance of searching for the features that may isolate members of the T. brasiliensis species complex. © 2013 Elsevier B.V.

Association between bone mass and functional capacity among elderly people aged 80 years and over

Objetivo:Analisar a associação entre a massa óssea e capacidade funcional de idosos com 80 anos ou mais.Métodos:A amostra foi composta por 93 idosos entre 80 e 91 anos (83,2 ± 2,5 anos), 61 mulheres (83,3 ± 2,7 anos) e 32 homens (83,1 ± 2,2 anos) da cidade de Presidente Prudente. A avaliação da massa óssea foi feita pela absorptiometria de dupla energia de raios X (DXA), na qual foram mensurados os valores de conteúdo mineral ósseo (BMC) e densidade mineral óssea (BMD) do fêmur e da coluna (L1-L4). A capacidade funcional foi avaliada por meio dos testes de velocidade para caminhar, equilíbrio estático e força de membros inferiores contidos no questionário Saúde, Bem-Estar e Envelhecimento (Sabe). As variáveis da massa óssea e capacidade funcional foram categorizadas de acordo com os valores de mediana e a pontuação obtida nos testes, respectivamente. Para tratamento estatístico fez-se o teste qui-quadrado, o software usado foi SPSS (13.0) e o nível de significância estabelecido foi de 5%.Resultados:Os idosos do sexo masculino com maior desempenho nos testes funcionais apresentaram maiores valores de BMC de fêmur comparados com os de menor desempenho, resultado não encontrado quando avaliadas as mulheres.Conclusão:Dessa forma, a massa óssea do fêmur para idosos longevos do sexo masculino está associada à capacidade funcional. A avaliação constante da massa mineral óssea e a prática de atividade física ao longo da vida seriam medidas para prevenção das quedas em idosos.

Association between pharyngeal residue and posterior oral spillage with penetration and aspiration in Stroke

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mid-infrared supercontinuum generation in a suspended-core As2S3 chalcogenide microstructured optical fiber

We demonstrate the supercontinuum (SC) generation in a suspended-core As2S3 chalcogenide microstructured optical fiber (MOF). The variation of SC is investigated by changing the fiber length, pump peak power and pump wavelength. In the case of long fibers (20 and 40 cm), the SC ranges are discontinuous and stop at the wavelengths shorter than 3500 nm, due to the absorption of fiber. In the case of short fibers (1.3 and 2.4 cm), the SC ranges are continuous and can extend to the wavelengths longer than 4 μm. The SC broadening is observed when the pump peak power increases from 0.24 to 1.32 kW at 2500 nm. The SC range increases with the pump wavelength changing from 2200 to 2600 nm, corresponding to the dispersion of As2S3 MOF from the normal to anomalous region. The SC generation is simulated by the generalized nonlinear Schrödinger equation. The simulation includes the SC difference between 1.3 and 2.4 cm long fiber by 2500 nm pumping, the variation of SC with pump peak power in 2.4 cm long fiber, and the variation of SC with pump wavelength in 1.3 cm long fiber. The simulation agrees well with the experiment.

Effect of time between adhesive application and photoactivation on adhesion and collagen exposure

Fundacao de Amparo a Pesquisa do Estado de sao Paulo (FAPESP)