Ferroelectric and optical properties of Ba0.8Sr0.2TiO3 thin film

Barium strontium titanate (Ba0.8Sr0.2TiO3) thin films have been prepared on Pt/Ti/SiO2/Si substrates using a soft solution processing. X-ray diffraction and also micro-Raman spectroscopy showed that the Ba0.8Sr0.2TiO3 thin films exhibited a tetragonal structure at room temperature. The presence of Raman active modes was clearly shown at the 299 and 725 cm(-1) peaks. The tetragonal-to-cubic phase transition in the Ba0.8Sr0.2TiO3 thin films is broadened, and suppressed at about 35 degreesC, with a maximum dielectric constant of 948 (100 kHz). Electrical measurements for the prepared Ba0.8Sr0.2TiO3 thin films showed a remnant polarization (P-r) of 6.5 muC/cm(2), a coercive field (E-c) of 41 kV/cm, and good insulating properties. The dispersion of the refractive index is interpreted in terms of a single electronic oscillator at 6.97 eV. The direct band gap energy (E-g) and the refractive index (n) are estimated to be 3.3 eV and n = 2.27-2.10, respectively. (C) 2002 American Institute of Physics.

BaTiO3 obtained through metallic stearate precursors

Metallic stearates were used as precursors to obtain BaTiO3. Barium and titanium stearate mixtures were homogenized in ball mill containing some amount of ammonium stearate. The mixture of the precursors was evaluated by simultaneous TG/ DTA and TMA, and residues from thermal decomposition were characterized by XRD and SEM. It could be verified that the residues from the thermal decomposition in both oxidant and inert atmospheres were the BaTiO3 but with characteristic morphological and crystalline aspects depending on the experimental conditions in which the mixtures of precursors were obtained. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Electrical properties of screen printed BaTiO3 thick films

The deposition of thick film pastes by screen-printing is a relatively simple and convenient method to produce thicker layers with thickness up to 100 mum. In the present work, the barium titanate thick films were prepared from mechanically activated powders based on BaC03 and TiO2. After mixing, the powders were calcined at low temperature by slow heating and cooling rates. The thick films were deposited on to Al2O3 substrates through hybrid technology. The obtained films were fired at 850 degreesC together with electrode material (silver/palladium). The electrical properties of thick films: dielectric permittivity, dielectric losses, Curie temperature, hysteresis loop were reported. The obtained BT thick films can be applied in as multilayer capacitors or in gas sensor application. (C) 2003 Elsevier Ltd. All rights reserved.

Composites PVDF-TrFE/BT used as bioactive membranes for enhancing bone regeneration

In this paper a piezoelectric composite membranes were developed for charge generator to promoter bone regeneration on defects sites. Is known that the osteogenesis process is induced by interactions between biological mechanisms and electrical phenomena. The membranes were prepared by mixing Barium Titanate (BT) powders and PVDF-TrFE (PVDF:TrFE = 60:40 mol%) on dimethylformamide medium. This precursor solution was dried and crystallized at 100degreesC for 12 hours. Composites membranes were obtained by following methods: solvent casting (SC), spincoating (SP), solvent extraction by water addition (WS) and hot pressing (HP).The microstructural analysis performed by SEM showed connectivity type 3-0 and 3-1 with high homogeneity for samples of ceramic volume fraction major than 0.50. Powder agglomerates within the polymer matrix was evidenced were observed for composites with the BT volume fraction major than 40%. The composite of ceramic fraction of 0.55 presented the best values of remanent polarization (similar to33 muC/cm(2)), but the flexibility of these composites with the larger ceramic fraction was significantly affected.For in vivo evaluation PVDF-TrFE/BT 90/10 membranes with 3cm larger were longitudinally implanted under tibiae of male rabbit. After 21 days the animals were sacrificed. By histological analyses were observed neo formed bone with a high mitotic activity. In the interface bone-membrane was evidenced a pronounced callus formation. These results encourage further applications of these membranes in bone-repair process.

Investigation of piezoelectricity in perovskite (LaFeO3): A theoretical study

In a previous report we studied theoretically the piezoelectric effect in barium titanate (BaTiO3) [O. Treu Filho, J.C. Pinheiro, R.T. Kondo, J. Mol. Struct. (THEOCHEM), 671 (2004) 71]. In this article we applied the Hartree-Fock (HF) theory in the investigation of piezoelectricity in LaFeO3. Initially, the generator coordinate HF (GCHF) method was used to build 22s14p, 30s19p13d, and 32s24p17d Gaussian basis sets for O(3p), Fe(D-5), and La(D-2) atoms. Then those basis sets were contracted to [7s6p], [13s8p6d], and [18s13p7d], respectively. The quality of the contracted basis sets in polyatomic calculations was evaluated through calculations of total and orbital energies (HOMO and HOMO-1) of (FeO1+)-Fe-2 and (LaO1+)-La-1. Finally, the contracted basis sets were supplemented with polarization and diffuse functions and used to investigate the piezoelectricity in LaFeO3. The calculated properties were dipole moment, total energy, and atomic charges and the analysis of those properties showed that covalent bonds constitute the electronic structure of [LaFCO3](2) fragment. Therefore, it is reasonable to believe that LaFeO3 does not present piezoelectric properties. (C) 2006 Elsevier B.V. All rights reserved.

Effect of the excess of bismuth on the morphology and properties of the BaBi2Ta2O9 ceramics

In this study, the effect of bismuth content on the crystal structure, morphology and electric properties of barium-bismuth-tantalate (BBT) ceramics was explored with the aid of X-ray diffraction (XRD), scanning electron microcopy (SEM), dielectric properties and ferroelectric hysteresis loops. BaBi2Ta2O9 (BBT) ceramics have been successfully prepared by the solid-state reaction. The BBT phase was crystallized at 900 degreesC for 2 h. The excess of bismuth controls the grain size, affecting the density of the material. Measurements of dieletric constant and dieletric losses confirm that the material is a ferroeletric with a Curie temperature around 77 degreesC. The dieletric constant measured at room temperature was 400, with a dielectric loss of 0.03. Both the phase-transition behaviour and ferroelectric properties, such as spontaneous polarization (P-s), showed a dependence on Bi content. (C) 2004 Elsevier B.V. All rights reserved.

Secondary phases in Nb-doped BaTiO3 ceramics

In this work, the effect of Nb2O5 addition on the microstructure of BaTiO3 was studied. From XRD diagrams, a diminution in tetragonality parameters with an increase in dopant concentration was observed. In order to determine morphology and composition of secondary phases in niobium-doped barium titanate, EDAX and SEM analyses were carried out. It was found that a concentration of dopant higher than 0.15 mol% leads to fine-grained BaTiO3 without abnormal grain growth. Otherwise, compositions of secondary phases correspond to the titanium-rich region in the BaO-TiO2 phase diagram. Besides, the titanium content in the precipitate increases with the Nb2O5 addition. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Preparation, structural and optical characterization of BaWO4 and PbWO4 thin films prepared by a chemical route

Polycrystalline BaWO4 and PbWO4 thin films having a tetragonal scheelite structure were prepared at different temperatures. Soluble precursors such as barium carbonate, lead acetate trihydrate and tungstic acid, as starting materials, were mixed in aqueous solution. The thin films were deposited on silicon, platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure of the thin films were investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffraction, and specular reflectance infrared Fourier transform spectroscopy, respectively. Nucleation stages and surface morphology evolution of thin films on silicon substrates have been studied by atomic force microscopy. XRD characterization of these films showed that BaWO4 and PbWO4 phase crystallize at 500 degreesC from an inorganic amorphous phase. FTIR spectra revealed the complete decomposition of the organic ligands at 500 degreesC and the appearance of two sharp and intense bands between 1000 and 600 cm(-1) assigned to vibrations of the antisymmetric stretches resulting from the high crystallinity of both thin films. The optical properties were also studied. It was found that BaWO4 and PbWO4 thin films have Eg = 5.78 eV and 4.20 eV, respectively, of a direct transition nature. The excellent microstructural quality and chemical homogeneity results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of BaWO4 and PbWO4 thin films. (C) 2003 Elsevier Ltd. All rights reserved.

Measurements of gunshot residues by sector field inductively coupled plasma mass spectrometry - Further studies with pistols

The most popular handgun in Brazil is the single round-barrel caliber 0.38 revolver. In recent years, however, owing to the modernization of police arms and their availability on the legal and illicit markets, pistols have become increasingly popular and currently represent about 20% of police seizures. In a previous paper we presented a novel collection method for gunshot residues (GSR) using a sampling procedure based on ethylenediamine-tetraacetic acid (EDTA) solution as a complexing agent on moistened swabs with subsequent detection using sector field-high resolution-inductively coupled plasma-mass spectrometry (SF-HR-ICP-MS). In the present paper, we discuss the capability of this methodology to identify antimony (Sb), barium (Ba) and lead (Pb) on the hands of volunteers after shot tests with 9 mm and 0.40 in. caliber pistols. Two types of munitions were tested: 9 mm Taurus and clean range. The use of a technique with high sensitivity, such as SF-HR-ICP-MS, permits the identification of low concentrations (less than 1 mu g/L) of metals in firearm residue and constitutes a powerful tool in forensic science. We also discuss the importance of the sampling procedure, including collection from a different body part than the gun hand of the suspect. Comparison of the analytical data obtained allows clear discrimination between samples from the hands of shooters and non-shooters. (C) 2007 Elsevier B.V.. All rights reserved.

Influence of Zn2+ co-doping ion on Eu3+-O2- associate luminescence in Sr2SiO4

This work reports on the study about the luminescence behavior of Eu3+-O2- associates in Sr2SiO4 doped with Eu3+, or simultaneously doped with Eu3+ and Zn2+ ions, where the Zn2+ doping ion acts as a charge compensating agent. Both Sr2SiO4:Eu3+ and Sr2SiO4:Eu3+,Zn2+ emission spectra show two types D-5(0)-->F-7(0) type transitions, one type related to Eu3+ in the Sr2+ Site, at 577 and 580 nm and the other one related to Eu3+-O2- associates, at 574 nm. Excitation spectra present two CT bands at 275 and 324 nm related to each emission center, respectively. Comparing the relative intensities between the emission spectra, the 0-->0 transition at 574 nm assigned to Eu3+-O2- associates in the Sr2SiO4:Eu3+ emission spectrum is much more intense than the same transition in the Sr2SiO4:Eu3+,Zn2+ emission spectrum. Moreover, in the Sr2SiO4:Eu3+ excitation spectrum, the intensity ratio between the CT band related to the Eu3+-O2- emission center and Eu3+ F-7-->L-5(6) transition is also larger than in the Sr2SiO4:Eu3+,Zn2+ one. Therefore, the presence of Zn2+ species provides an extra charge compensating mechanism, which decreases the formation of Eu3+-O2- associates. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Thermal properties of fluoride glasses and their gel precursors

Xerogels were prepared from zirconium, barium, aluminum, lanthanum and lithium acetates, corresponding to a Li containing ZBLA composition. The study of their thermal properties (DSC, TG/DTG, FT-IR) showed that they might be used as chemically stable precursors in the preparation of fluoride glasses. Hydrofluoric acid in solution was chosen as a mild fluorinating agent. This newly proposed technique of fluorinating allowed to obtain high quality ZBLALi glass which presents the advantage of higher thermal stability and homogeneity in comparison with the glass obtained using individual commercial fluorides.

Construction and performance of a drop cell for the nephelometric determination of sulfur dioxide

A nephelometric technique based on a liquid drop is described for the measurement of atmospheric sulfur dioxide. A 40-mul drop of barium chloride and hydrogen peroxide solution is suspended in a flowing-air sampling stream. The sulfur (IV) collected is oxidized to sulfur (VI) and finally precipitated as barium sulfate. Nephelometric detection of drop is achieved by an appropriate arrangement consisting of an optical fiber contacting the drop and a photodiode placed at 90degrees relative to the fiber. The design and characteristics of this drop-based gas sensor system are described. The analytical response, as photocurrent, is proportional to the product of the sampling period and the sulfur dioxide concentration. The detection limit is ca. 1.1 mg m(-3) for a 10-min sampling time. The present technique is fairly rapid and simple, uses a small amount of reagent and is set up with low-cost equipment, making this system economically viable. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Effects of post-annealing on the dielectric properties of Au/BaTiO3/Pt thin film capacitors

Barium titanate thin films were prepared by the polymeric precursor method and deposited onto Pt/Ti/SiO2/Si substrates. X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FT-IR) and micro-Raman spectroscopy were used to investigate the formation of the BaTiO3 perovskite phase. Afterwards, the films were submitted to post-annealing treatments in oxygen and nitrogen atmospheres at 300 degreesC for 2 h, and had their dielectric properties measured. It was observed that the electric properties of the thin films are very sensitive to the nature of the post-annealing atmosphere. This study demonstrates that post-annealing in an oxygen atmosphere increases the dielectric relaxation phenomenon and that post-annealing in a nitrogen atmosphere produces a slight dielectric relaxation. (C) 2004 Elsevier B.V All rights reserved.

XPS study on water corrosion of fluorzirconate glasses and their protection by a layer of surface modified tin dioxide nanoparticles

The surface corrosion process associated with the hydrolysis of fluorozirconate glass, Z-BLAN (53ZrF(4), 20BaF(2), 20NaF, 4LaF(2), 3AlF(3)), and the corrosion protection efficiency of a nanocrystalline transparent SnO2 layer were investigated by X-ray photoelectron spectroscopy. The tin oxide film was deposited by the sol-gel dip-coating process in the presence of Tiron(R) as particle surface modifier agent. The chemical bonding structure and composition of the surface region of coated and non-coated ZBLAN were studied before water contact and after different immersion periods (5-30 min). In contrast to the effects occurring for non-coated glass, where the surface undergoes a rapid selective dissolution of the most soluble species inducing the formation of a new surface phase consisting of stable zirconium oxyfluoride, barium fluoride and lanthanum fluoride species, the results for the SnO2-coated glass showed that the hydrolytic attack induces a filling of the film nanopores by dissolved glass material and the formation of tin oxylluoride and zirconium oxyfluoride species. This process results in a modified film, which acts as a hermetic diffusion barrier protecting efficiently the glass surface. (C) 2006 Elsevier B.V. All rights reserved.

Designing Gaussian basis sets to the theoretical study of the piezoelectric effect of perovskite (BaTiO3)

Gaussian basis sets (24s14p, 30s19p14d, and 33s21p14d for O (P-3), Ti (S-5), and Ba (S-1) atoms, respectively), are designed with the strategy of the Generator Coordinate Hartree-Fock method. The basis sets are then contracted to [6s4p], [10s5p4d], and [16s9p5d] to O, Ti, and Ba atoms, respectively, and used in calculations of total and orbital energies of (TiO+2)-Ti-1 and (BaO)-Ba-1 fragments for quality evaluation in molecular studies. For O atom, the [6s4p] basis set is enriched with d polarization function and used along with the [10s5p4d] and [16s9p5d] basis sets for the theoretical study of the piezoelectric effect of perovskite (BaTiO3). The results of this work evidence that the piezoelectric properties in BaTiO3 can be caused by electrostatic interactions. (C) 2003 Elsevier B.V. All rights reserved.