Compressive fatigue in titanium dental implants submitted to fluoride ions action

The aim of this study was to assess the influence of a fluoridated medium on the mechanical properties of an internal hexagon implant-abutment set, by means of compression, mechanical cycling and metallographic characterization by scanning electronic microscopy. Five years of regular use of oral hygiene with a sodium fluoride solution content of 1500 ppm were simulated, immersing the samples in this medium for 184 hours, with the solutions being changed every 12 hours. Data were analyzed at a 95% confidence level with Fisher's exact test. After the action of fluoride ions, a negative influence occurred in the mechanical cycling test performed in a servohydraulic machine (Material Test System-810) set to a frequency of 15 Hz with 100,000 cycles and programmed to 60% of the maximum resistance of static compression test. The sets tended to fracture by compression on the screw, characterized by mixed ruptures with predominance of fragile fracture, as observed by microscopy. An evidence of corrosion by pitting on sample surfaces was found after the fluoride ions action. It may be concluded that prolonged contact with fluoride ions is harmful to the mechanical properties of commercially pure titanium structures.

Tribocorrosion behaviour of anodic treated titanium surfaces intended for dental implants

Tribocorrosion plays an important role in the lifetime of metallic implants. Once implanted, biomaterials are subjected to micro-movements in aggressive biological fluids. Titanium is widely used as an implant material because it spontaneously forms a compact and protective nanometric thick oxide layer, mainly TiO2, in ambient air. That layer provides good corrosion resistance, and very low toxicity, but its low wear resistance is a concern. In this work, an anodizing treatment was performed on commercial pure titanium to form a homogeneous thick oxide surface layer in order to provide bioactivity and improve the biological, chemical and mechanical properties. Anodizing was performed in an electrolyte containing β-glycerophosphate and calcium acetate. The influence of the calcium acetate content on the tribocorrosion behaviour of the anodized material was studied. The concentration of calcium acetate in the electrolyte was found to largely affect the crystallographic structure of the resulting oxide layer. Better tribocorrosion behaviour was noticed on increasing the calcium acetate concentration. © 2013 IOP Publishing Ltd.

Titanium-35niobium alloy as a potential material for biomedical implants: in vitro study

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Growth of Calcium Phosphate Using Chemically Treated Titanium Oxide Nanotubes

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Genotoxicity of corrosion eluates obtained from endosseous implants

Purpose: Commercially pure titanium alloys are currently used as metallic biomaterials in implantology. Corrosion phenomena appear to play a decisive role in metallic implant long-term behavior. Thus, the goal of this study was to examine the genotoxic potential of corrosion eluates obtained from dental implants using Chinese ovary hamster cells in vitro by the single-cell gel (comet) assay. This technique detects deoxyribonucleic acid strand breaks in individual cells in alkaline conditions.Materials and Methods: the materials tested included 3 dental implants commercially available. Each of the tested materials was corroded in a solution consisting of equal amounts of acetic acid and sodium chloride (0.1 M) for 1, 3, 7, 14, and 21 days. The Chinese ovary hamster cultures were then exposed to all corrosion eluates obtained from endosseous dental implants for 30 minutes at 37 degrees C.Results: None of the eluates was found to exhibit genotoxicity, regardless of the type of dental implant used.Conclusion: the results suggest that all dental implants tested in this study did not induce deoxyribonucleic acid breakage as depicted by the single-cell gel (comet) assay.

Use of a titanium device in lateral sinus floor elevation: an experimental study in monkeys

Aim: To evaluate the effect of a space-maintaining device fixed to the lateral wall of the maxillary sinus after the elevation of the sinus mucosa on bone filling of the sinus cavity. Material and methods: Immediately after the elevation of the maxillary sinus Schneiderian membrane accomplished through lateral antrostomy in four monkeys, a titanium device was affixed to the lateral sinus wall protruding into the sinus cavity to maintain the mucosa elevated without the use of grafting material. The healing of the tissue around the implants was evaluated after 3 and 6 months. Ground sections were prepared and analyzed histologically. Results: The void under the elevated sinus membrane, originally filled with the blood clot, was reduced after 3 as well as after 6 months of healing of about 56% and 40.5%, respectively. In seven out of eight cases, the devices had perforated the sinus mucosa. The formation of mineralized bone and bone marrow amounted to about 42% and 69% after 3 and 6 months, respectively. The connective tissue represented about 53% and 23% of the newly formed tissue after 3 and 6 months, respectively. Conclusions: New bone formation was found below the devices. However, shrinkage of the newly formed tissue was observed both after 3 and 6 months of healing. Hence, the space-maintaining function of the devices used in the present study has to be questioned.

Evaluation of Torque Maintenance of Abutment and Cylinder Screws With Morse Taper Implants

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Anterior Tooth Rehabilitation With Frozen Homogenous Bone Graft and Immediately Loaded Titanium Implant Using Computer-Guided Surgery

Computed tomographic scanning is a precise, noinvasive surveying technique that enables the professionals to improve the precision of implant placement by building a prototype that allows the confection of surgical guides. The authors present a clinical case of anterior tooth rehabilitation with frozen homogenous bone graft and immediately loaded titanium implant using computer-guided surgery. A multislice computed tomography was realized, and a prototype was built. All the procedures were previously realized in the prototype before started in the patient. This technique allows a better surgical planning, makes the procedures more accurate, and reduces surgery time.

Stability of cp-Ti and Ti-6Al-4V alloy for dental implants as a function of saliva pH - an electrochemical study

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

What is the role of lipopolysaccharide on the tribocorrosive behavior of titanium?

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fatigue and Fluoride Corrosion on Streptococcus mutans Adherence to Titanium-Based Implant/Component Surfaces

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Severe Dietary Magnesium Deficiency on Systemic Bone Density and Removal Torque of Osseointegrated Implants

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Argon-based atmospheric pressure plasma enhances early bone response to rough titanium surfaces

This study investigated the effect of an Argon-based atmospheric pressure plasma (APP) surface treatment operated chairside at atmospheric pressure conditions applied immediately prior to dental implant placement in a canine model. Surfaces investigated comprised: rough titanium surface (Ti) and rough titanium surface + Argon-based APP (Ti-Plasma). Surface energy was characterized by the Owens-Wendt-Rabel-Kaelble method and chemistry by X-ray photoelectron spectroscopy (XPS). Six adult beagles dogs received two plateau-root form implants (n = 1 each surface) in each radii, providing implants that remained 1 and 3 weeks in vivo. Histometric parameters assessed were bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). Statistical analysis was performed by Kruskall-Wallis (95% level of significance) and Dunn's post-hoc test. The XPS analysis showed peaks of Ti, C, and O for the Ti and Ti- Plasma surfaces. Both surfaces presented carbon primarily as hydrocarbon (C?C, C?H) with lower levels of oxidized carbon forms. The Ti-Plasma presented large increase in the Ti (+11%) and O (+16%) elements for the Ti- Plasma group along with a decrease of 23% in surface-adsorbed C content. At 1 week no difference was found in histometric parameters between groups. At 3 weeks significantly higher BIC (>300%) and mean BAFO (>30%) were observed for Ti-Plasma treated surfaces. From a morphologic standpoint, improved interaction between connective tissue was observed at 1 week, likely leading to more uniform and higher bone formation at 3 weeks for the Ti-Plasma treated implants was observed. (C) 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part A 2012.

IMPROVEMENT TO THE MARGINAL COPING FIT of COMMERCIALLY PURE TITANIUM CAST IN PHOSPHATE-BONDED INVESTMENT BY USING A SIMPLE PATTERN COATING TECHNIQUE

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Design of dental implants, influence on the osteogenesis and fixation

The fixation and the bone ingrowth at the interface of porous cylindrical implants (total porosity of 37% and average pores diameter of 480 mu m) were compared in vivo to rough cylindrical implants (R-a = 5.3 mu m), both of commercially pure titanium, made by powder metallurgy. The implants were inserted into the tibias of 20 rabbits and the animals were sacrificed 4 and 8 weeks after surgery. The percentage of bone-implant contact observed in porous implant was significantly larger than in the rough ones for all of sacrifice periods, respectively, 57% vs. 46% after 4 weeks, and 59% vs. 50% after 8 weeks. The mechanical tests showed a significant increase in the shear strength of the porous implants for the two analyzed periods, 4 and 8 weeks (14 and 20 MPa), when compared with rough ones (4 and 13 MPa). These results suggest that porous implants improve the contact at the implant-bone interface and increase the fixation to the bone, improving the osseointegration. Thus, the porous implant might be an alternative to dental implant in less favorable conditions, and appear to be better fixed to bone, offering promising alternatives.