Bond strength of resin modified glass ionomer cement to primary dentin after cutting with different bur types and dentin conditioning

The aim of this in vitro study was to evaluate the effect of different bur types and acid etching protocols on the shear bond strength (SBS) of a resin modified glass ionomer cement (RM-GIC) to primary dentin. Forty-eight clinically sound human primary molars were selected and randomly assigned to four groups (n=12). In G1, the lingual surface of the teeth was cut with a carbide bur until a 2.0-mm-diameter dentin area was exposed, followed by the application of RM-GIC (Vitremer - 3M/ESPE) prepared according to the manufacturer's instructions. The specimens of G2, received the same treatment of G1, however the dentin was conditioned with phosphoric acid. In groups G3 and G4 the same procedures of G1 and G2 were conducted respectively, nevertheless dentin cutting was made with a diamond bur. The specimens were stored in distilled water at 37 degrees C for 24h, and then tested in a universal testing machine. SBS. data were submitted to 2-way ANOVA (= 5%) and indicated that SBS values of RM-GIC bonded to primary dentin cut with different burs were not statistically different, but the specimens that were conditioned with phosphoric acid presented SBS values significantly higher that those without conditioning. To observe micromorphologic characteristics of the effects of dentin surface cut by diamond or carbide rotary instruments and conditioners treatment, some specimens were examined by scanning electron microscopy. Smear layer was present in all specimens regardless of the type of rotary instrument used for dentin cutting, and specimens etched with phosphoric acid presented more effective removal of smear layer. It was concluded that SBS of a RM-GIC to primary dentin was affected by the acid conditioning but the bur type had no influence.

Evaluation of a double-setting alpha-tricalcium phosphate cement in eviscerated rabbit eyes

Purpose: To evaluate the macroscopy, microstructure, and tissue reaction of a double-setting a-tricalcium phosphate bone cement used as an intraocular implant in rabbits.Methods: the internal and external surface of the double-setting a-tricalcium phosphate implant was analyzed macroscopically and by scanning electron microscopy. Twelve New Zealand rabbits received 12-mm implants made of double-setting alpha-tricalcium phosphate cement after unilateral evisceration. Clinical evaluation was performed daily for the first 15 days after surgery and at 15-day intervals until the end of the study period. For histopathologic analysis, 3 animals per experimental period were submitted to enucleation at 15, 45, 90, and 180 days.Results: on gross inspection, the external surface of the implant was solid, smooth, and compact. The microarchitecture was characterized by the formation of columns of hexagonal crystals with interconnecting channels forming micropores. No wound dehiscence, signs of infection, or implant extrusion were observed in any animal throughout the study period. Histologic examination revealed the formation of fibrovascular tissue surrounding the implants, and there were signs of minimal integration of the surface limiting the fibrocellular cap with the space previously occupied by the implant.Conclusions: the double-setting alpha-tricalcium phosphate implant behaved as an inert and nonintegratable material. The lack of incorporation of this material by fibrovascular tissue is related to its characteristics of compactness and high resistance.

Effects of different treatments on purity of silica from soluble sodium silicate

Noncrystalline silica was obtained with low iron, sodium, and nitrate ions concentrations from soluble sodium silicate (water glass) and nitric acid solution. Extractions with nitric acid solution and/or deionized water and/or dialysis were carried out to eliminate soluble metal ions. Products were dried in a microwave oven and characterized by chemical analysis, XRD, and IR. Dialysis seems to be the best treatment for the elimination of sodium and nitrate ions. Silica purified by nitric acid and water extractions followed by dialysis yields the purest silica sample.