Study of the growth process of in situ polyaniline deposited films

Polyaniline (PAni) thin films were deposited onto BK7 glass substrates using the in situ deposition technique. The control of the time and the aniline concentration in the PAni polymerization reaction on the film deposition allowed us to prepare films with different thickness, down to similar to 25 nm. The film growth process was monitored by measuring the UV-vis spectra and the AFM height profiles of the film surface. The curves of adsorption kinetics were analyzed with the Avrami's model, yielding an exponent it n = 3, thus indicating nucleation of spheroids at the initial stages of polymerization that grow through a diffusion process. AFM images of the surface height profiles corroborate this hypothesis, with spheroids growing with no preferred orientation during the in situ deposition. (C) 2007 Elsevier B.V. All rights reserved.

A study on X-ray irradiation of composite polyaniline LB films

Composite Langmuir-Blodgett (LB) films from polyaniline and cadmium stearate have been irradiated with ionizing X-rays for various exposure times. In the initial stages of X-ray irradiation the absorption peak at 580 nm of an as-deposited film was seen to decrease with a concomitant increase in the absorption in the long wavelength region (700-1100 nm). Upon prolonging the irradiation, the absorption maximum shifted to 800 nm with the LB film color changing to green, characteristic of acid doped polyaniline. The changes in the Fourier transform infrared (FTIR) spectra upon irradiation are also similar to those observed upon acid doping of polyaniline. When compared with acid doping, two major differences were observed for the LB films exposed to X-rays. First, the packing order of the cadmium stearate domains in the composite LB films - as observed by X-ray diffraction - is not affected by the X-ray irradiation. In addition, no significant increase in the DC conductivity was noted after the X-ray exposure whereas similar LB films have their conductivity increased by an order of magnitude upon acid doping. These differences may be explained by considering that the inter-domain contribution to the conductivity is increased by the acid doping because the insulating cadmium stearate domains are destroyed, which does not occur with the X-ray irradiation. (C) 1998 Elsevier B.V. S.A. All rights reserved.

Temperature dependence of photoinduced birefringence in mixed Langmuir-Blodgett (LB) films of azobenzene-containing polymers

The temperature dependence of photoinduced birefringence was investigated for mixed Langmuir-Blodgett (LB) films from the homopolymer poly[4'-[[2-(methacryloyloxy)ethyl]ethyl-amino]-2-chloro-4-nitroazobenzene] (HPDR13) and cadmium stearate (Cdst) and from the copolymer 4-[N-ethyl-N-(2-hydroxyethyl)]amino-2'-chloro-4'-nitroazobenzene (MMA-DR13) and CdSt. Birefringence was achieved by impinging a linearly polarized light on the LB films. The maximum birefringence achieved decreased with temperature as thermal relaxation of the chromophores was facilitated. The buildup curves for birefringence were fitted with biexponential functions representing distinctly different mechanisms with time constants. The first, fast process is thermally activated and may be represented by an Arrhenius process. The decay of birefringence after switching off the laser source was described by a Kohlraush-Williams-Watts (KWW) function, consistent with a distribution of relaxation times for the polymer system. Activation energies were obtained from Arrhenius plots of the rate constant of the exponential functions and KWW function, which showed that the buildup of birefringence was very similar for the two polymer systems. The decay, however, was slower for the LB film from MMA-DR13/CdSt. (C) 2002 Published by Elsevier B.V. Ltd.

Preparation, characterization and taste sensing properties of Langmuir-Blodgett Films from mixtures of polyaniline and a ruthenium complex

Langmuir-Blodgett (LB) films from a ruthenium complex, mer-[RuCl3(dppb)(py)] (dppb = PPh2(CH2)(4)PPh2; py = pyridine) (Rupy), and from mixtures with varied amounts of polyaniline (PANi) were fabricated. Molecular-level interactions between the two components are investigated by surface potential, dc conductivity and Raman spectroscopy measurements, particularly for the mixed film with 10% of Rupy. For the latter, the better miscibility led to an interaction with Rupy inducing a decrease in the conducting state of PANi, as observed in the Raman spectra and conductivity measurement. The interaction causes the final film properties to depend on the concentration of Rupy, and this was exploited to produce a sensor array made up of sensing units consisting of 11-layer LB films from pure PANi, pure Rupy and mixtures with 10 and 30% of Rupy. It is shown that the combination of only four non-specific sensing units allows one to distinguish the basic tastes detected by biological systems, viz. saltiness, sweetness, sourness and bitterness, at the muM level. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

Indium tin oxide films prepared via wet chemical route

In this work, indium tin oxide (ITO) films were prepared using a wet chemical route, the Pechini method. This consists of a polyesterification reaction between an alpha-hydroxicarboxylate complex (indium citrate and tin citrate) with a polyalcohol (ethylene glycol) followed by a post annealing at 500 degrees C. A 10 at.% of doping of Sn4+ ions into an In2O3 matrix was successfully achieved through this method. In order to characterize the structure, the morphology as well as the optical and electrical properties of the produced ITO films, they were analyzed using different experimental techniques. The obtained films are highly transparent, exhibiting transmittance of about 85% at 550 nm. They are crystalline with a preferred orientation of [222]. Microscopy discloses that the films are composed of grains of 30 nm average size and 0.63 nm RMS roughness. The films' measured resistivity, mobility and charge carrier concentration were 5.8 x 10(-3) Omega cm, 2.9 cm(2)/V s and -3.5 x 10(20)/cm(3), respectively. While the low mobility value can be related to the small grain size, the charge carrier concentration value can be explained in terms of the high oxygen concentration level resulting from the thermal treatment process performed in air. The experimental conditions are being refined to improve the electrical characteristics of the films while good optical, chemical, structural and morphological qualities already achieved are maintained. (C) 2007 Elsevier B.V. All rights reserved.

Morphological characterization of Langmuir-Blodgett films from polyaniline and a ruthenium complex (Rupy): influence of the relative concentration of Rupy

We report on the use of dynamic scale theory and fractal analyses in a study of the growth stages of Langmuir-Blodgett (LB) films of polyaniline and a neutral biphosphinic ruthenium complex, namely mer-[ RuCl3 (dppb)(py)] (dppb = 1,4-bis(diphenylphosphine) buthane, py = pyridine), Rupy. The LB films were deposited onto indium-tin-oxide substrates and characterized with atomic force microscopy. From the granular morphology exhibited by the films one could infer growth processes inside and outside the grains. Growth outside was found to follow the Kardar-Parisi-Zhang model, with fractal dimensions of about 2.7. As one would expect, inside the grains the morphology is close to a Euclidian surface with fractal dimension of about 2.

Influence of ionic interactions on the photoinduced Birefringence of poly[1-[4-(3-carboxy-4 hydroxyphenylazo) benzene sulfonamido]-1 2-ethanediyl, sodium salt] films

Electrostatic interactions govern most properties of polyelectrolyte films, as in the photoinduced bire-fringence of azo-containing polymers. In this paper we report a systematic investigation of optical storage characteristics of cast and layer-by-layer (LbL) films of poly[1 -[4-(3-carboxy-4 hydroxypheny-lazo) benzene sulfonamido]-1,2-ethanediyl, sodium salt] (PAZO). Birefringence was photoinduced faster in PAZO cast films prepared at high pHs, with the characteristic writing times decreasing almost linearly with the pH in the range between 4 and 9. This was attributed to an increased free volume for the azochromophores with the enhanced electrostatic repulsion in PAZO charged to a greater extent. In contrast, in LbL films of PAZO alternated with poly(allylamine hydrochloride) (PAH), the electrostatic interactions between the oppositely charged polymers hampered photoisomerization and molecular rearrangement, thus leading to a slower writing kinetics for highly charged PAH or PAZO.

Synthesis and some properties of hybrid gels of titanium oxide containing europium (III)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Electrical characterization of in situ polymerized polyaniline thin films

The alternating conductivity, sigma*(f) = sigma'(f) + i sigma ''(f), of in situ polymerized polyaniline thin films doped with hydrochloric acid, deposited on top of an interdigitated gold line array previously deposited on glass substrates, were measured in the frequency (f) range between 0.1 Hz to 10 MHz and in the temperature range from 100 to 430 K. The results for sigma'(f) are typical of a disordered solid material: for frequencies lower than a certain hopping frequency gamma(hop), log[sigma'(f)] is frequency-independent rising almost linearly for in logf > gamma(hop). A master curve was thus obtained by plotting the real component of the conductivity using normalized scales sigma'(f)/sigma(dc) and f/gamma(hop) which is indicative of a single process operating in the whole frequency range. An expression encompassing the conduction through a disordered structure taken from previous random free energy barrier model for hopping carriers, as well a dielectric function to represent the capacitive behavior of the PAni was employed to fit the experimental results. The dielectric constant and activation energy for hopping carriers were obtained as function of the polymer doping level. (c) 2007 Elsevier B.V. All rights reserved.

Charge distribution and calcium affinity of sulfated alpha-L-galactans from ascidians. Comparison between linear and highly branched polymers

Calcium binding and charge distribution on highly branched and linear sulfated L-galactans from ascidians have been studied using a metallochromic indicator and conductimetric titrations. The distance between charged groups of the linear and highly branched galactans does not vary despite their marked differences in sulfate/total sugar molar ratios. These results indicate that the sulfated L-galactose units are concentrated in the central polysaccharide core and not intercalated among non-sulfated units. This inference is consistent with the chemical studies of these galactans. Surprisingly, calcium affinity increases with increasing amounts of non-sulfated sugar branches in the molecule. Thus, calcium binding in these polymers is not a simple function of availability of anion binding sites but a more complex calcium-polysaccharide interaction. (C) 1998 Elsevier B.V. Ltd. All rights reserved.

Structural, microstructural, and transport properties of highly oriented LaNiO3 thin films deposited on SrTiO3(100) single crystal

Electrical conductive textured LaNiO3/SrTiO3 (100) thin films were successfully produced by the polymeric precursor method. A comparison between features of these films of LaNiO3 (LNO) when heat treated in a conventional furnace (CF) and in a domestic microwave (MW) oven is presented. The x-ray diffraction data indicated good crystallinity and a structural orientation along the (h00) direction for both films. The surface images obtained by atomic force microscopy revealed similar roughness values, whereas films LNO-MW present slightly smaller average grain size (similar to 80 nm) than those observed for LNO-CF (60-150 nm). These grain size values were in good agreement with those evaluated from the x-ray data. The transport properties have been studied by temperature dependence of the electrical resistivity rho(T) which revealed for both films a metallic behavior in the entire temperature range studied. The behavior of rho(T) was investigated, allowing to a discussion of the transport mechanisms in these films. (C) 2007 American Institute of Physics.

The evolution of arsenic excess induced by thermal annealing in arsenic-rich Ga1-xAsx films

The evolution of As excess in As-rich Ga1-xAsx films is analyzed for distinct As concentrations and different annealing temperatures. Initially the samples are amorphous and crystallize partially after thermal annealing. The formation of both amorphous and crystalline As clusters is examined by micro-Raman and X-ray diffraction analysis. When highly and moderately unbalanced materials are compared, differences are clearly observed concerning the crystallization temperature and the migration kinetics of the As excess. These differences are explained by the fort-nation of As precipitates around the GaAs crystallites in the moderately unbalanced material, contrasting with the migration of the As excess to the film surface in the highly unbalanced material.

Increasing the dielectric breakdown strength of poly(ethylene terephthalate) films using a coated polyaniline layer

The dielectric strength of films made from poly(ethylene terephthalate) (PET) coated with a thin layer of polyaniline (PANI) was studied. The PANI layer was deposited on the PET films by the 'in situ' chemical polymerization method. The PANI layer of the PANI/PET films was undoped in NH4OH 0.1 M solution and re-doped with aqueous HCl solution under different pH values varying from 1 to 10. Electric breakdown measurements were performed by applying a voltage ramp and the results showed a dependence of the dielectric strength on the pH of the doping solution due to the changes in the electrical conductivity of the PANI layer. The dielectric strength of PET/PANI films treated under higher pH conditions showed an electric strength about 30% larger than the PET films, since it leads to a non-conductive PANI layer.

Improvement of the corrosion resistance of polysiloxane hybrid coatings by cerium doping

Polysiloxane hybrid films were deposited on stainless steel by dip-coating using a sol prepared by hydrolytic co-polycondensation of tetraethoxysilane (TEOS) and 3-methacryloxy propyltrimethoxysilane (MPTS), followed by radical polymerization of methacrylic moieties. The TEOS/MPTS ratio was chosen equal to 2 and the Ce/Si ratio varied between 0.01 and 0.1. The effects of cerium concentration and valence (Ce(III) and Ce (IV)) on the structural features of polysiloxane films were studied by X-ray photoelectron spectroscopy (XPS) and (29)Si nuclear magnetic resonance (NMR). The corrosion protection of stainless steel by the hybrid coatings was investigated by XPS, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves, after immersion in saline and acid solutions. The NMR results have shown for Ce(IV) doped films a high degree of polycondensation of up to 89%. Electrochemical analysis has evidenced that hybrid films with the lowest Ce concentration act as an efficient diffusion barrier by increasing the corrosion resistance and reducing the current densities up to 3 orders of magnitude compared to bare stainless steel. The analysis of structural effects induced by Ce(III) and Ce(IV) species, performed by XPS, indicates that the improved corrosion protection of Ce(IV) doped films might be mainly related to the enhanced polymerization of siloxane groups. (C) 2010 Elsevier B.V. All rights reserved.

Development of Novel Guava Puree Films Containing Chitosan Nanoparticles

One of the overall goals of industries is to use packages that do not cause environmental problems at disposal time, but that have the same properties as the conventional ones. The goal of this study is to synthesize edible films based on hydroxypropyl methylcellulose (HPMC) with guava puree and chitosan (CS) nanoparticles. This was divided into two stages, the first is the synthesis of chitosan nanoparticles and the second is the production of the films. For the nanoparticles, average size and zeta potential measurements were performed. The characterizations of mechanical and thermal properties, solubility and water vapor permeability tests were conducted in the films. It was observed that when the nanoparticles were added to HPMC and guava puree films, they improved their mechanical and thermal properties, as well as decreased the films solubility and permeability. The potential application of the films prepared would be in edible films with flavor and odor to extend the shelf life of products.