Propriedades estruturais e espectroscópicas de WO3 e WO3:Eu3+

Used as catalysts even in organic and inorganic molecules, as additives on catalysts, electrochromic films on smart windows the tungsten trioxide have been largely studied on the lasts decades, but there is just a few about it's luminescence. Using as precursors nitric acid and sodium tungstate the tungsten trioxide were been prepared thru wet process then treating on thermic and hydrothermal treatments. Where been evaluated the effects of methodology, nitric acid concentration, duration and temperature of treatments. The samples were characterized by X-ray diffraction (XRD), Raman scattering spectroscopy (RSS), Fourier transformed infrared spectroscopy, photoluminescence spectroscopy (PLS) and X-ray excited optical luminescence (XEOL). Hydrated phases of tungsten trioxide were obtained through hydrothermal treatments and the non-hydrated phases occur with thermic treatments. The acid concentration has the ability to determine the major phase formed as well the temperature determine the hydratation of the product. With lower temperatures dihydrate phase were preferable formed and with the rise of temperature, the water molecules were lost up to the fractionary hydratation and then the non-hydrated phase with higher temperatures depending on the atmosphere used on the thermal treatment. Doping the system with europium ions even substituting tungsten or in the interstices of the matrix were not been successful, as well the XEOL spectroscopy intensity were null and quite low for ultraviolet and visible excitation photoluminescence because of oxygen defect levels localized into the prohibited band.

Rare earth centers properties and electron trapping in SnO2 thin films produced by sol-gel route

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Filmes de titânio-silício preparados por spin e dip-coating

The conditions for the preparation of luminescent materials, consisting of Eu3+ ions entrapped in a titanium matrix, in the forma of a thin film, using the sol-gel process, are described. The films were obtained from sols prepared with TEOS and TEOT, in the presence of acetylacetone as the hidrolysis-retarding agent, using the dip-coating and spin-coating techniques. The influence of these techniques on the films based on titanium and silicon are presented. The Eu3+ was used as a luminescent probe. The films have been characterized by luminescence, reflection and transmittance. The thickness of the films could be related to the preparation procedure. Transparent thin films have been prepared by dip-coating technique.

Nanocomposites materials generated from a spray

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Eletrodo de pasta de carbono em minicavidade de contato sólido

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural and optical properties of GdAlO3:RE3+ (RE = Eu or Tb) prepared by the Pechini method for application as X-ray phosphors

In this work, GdAlO3:RE3+ (RE = Eu or Tb) was successfully prepared by the Pechini method at lower temperatures when compared to others methods as solid-state synthesis and sol-gel process. In accordance to the XRD data, the fully crystalline single-phase GdAlO3 could be obtained at 900 degrees C. The differential thermal analysis (DTA) shows a crystallization peak at 850 degrees C. The samples are composed by monocrystalline particles (50-120 nm) exhibiting the formation of aggregates among them, which indicates the beginning of the sinterization process. This feature indicates a strong tendency to the formation of aggregates, which is a suitable ability for the close-packing of particles, and hence a potential application in X-ray intensifying screens. Luminescence measurements indicate Gd3+ -> RE3+ energy transfer. The Eu3+ emission spectra exhibit all the characteristics D-5(0) -> F-7(j) transitions and the observed profile suggests that RE3+ ions occupy at least one site without center of symmetry. For terbium-doped samples, the D-5(3) -> F-7(j) (blue emission) and D-5(4) -> F-7(j) (green emission) transitions were observed and the ratio between them may depend on the Tb3+ content due to cross-relaxation processes. (C) 2009 Elsevier B.V. All rights reserved.

Aluminoxane-epoxi-siloxane hybrids waveguides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Coordenação local do Eu(III) em híbridos orgânicos/inorgânicos emissores de luz branca

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure and crystallization of lanthanum fluorozirconate glasses

Glasses with compositions (1-x)ZrF4-xLnF(3), 0.2 less than or equal to x less than or equal to 0.4 and Ln = La or La, Eu have been synthesized and investigated using differential scanning calorimetry, X-ray diffraction, Raman scattering and Eu3+ optical spectroscopy. Single-phase polycrystalline lanthanum fluorozirconates with Zr/Ln ratio equal to 1, 2 and 3 have been investigated using the same techniques for comparison. The crystalline phases LnZrF(7), LnZr(2)F(11), LT-LnZr(3)F(15) (orthorhombic) and HT-LnZr(3)F(15) (trigonal) have been characterized in the recrystallized glasses and in samples spontaneously crystallized from the melt. Another phase has also been observed but remains undefined, the Raman scattering spectra of the vitreous samples are related to the vibration modes of [ZrF6] isolated octahedra, and of [ZrF7] and [ZrF8] structural units with bridging fluorine ions. The Eu3+ fluorescence data are related to a predominant local environment of the lanthanide ions in the glasses similar to that of the lanthanide in LnZrF(7).

Pechini's solution as precursor for Eu(III)-containing ZnO films

The flat-panel-display's (FPD) market and demand for highly efficient and colored luminescent films have been growing quickly. In this work, thin films were obtained from Pechini's solution by dip-coating. The green films were thermally treated at 873 K in order to get ZnO:Eu 1 at% thin film. A Schott(R) glass plate hydrothermally treated was used as substrate. The films have a mosaic shaped feature that was observed by optical microscopy. That feature is a result of substrate thermal treatment. The film deposition decreases the substrate transmittance in the visible range. When the F-7(0) -->L-5(6) (392nm) Eu3+ transition is excited, it is possible to detect emission from D-5(0) --> F-7(J) (J = 1, 2, 3 and 4) transitions. The D-5(0) --> F-7(2) transition is also observed by using ZnO excitation wavelengths indicating energy transfer from ZnO to Eu3+ ion. (C) 2003 Elsevier B.V. (USA). All rights reserved.

Structure of redispersible SnO2 nanoparticles

Suspensions of undoped SnO2 nanoparticles and containing Eu3+ ions were prepared by a sol-gel procedure. Using the classical synthesis method ( precipitation), the particles tend to grow by a coarsening process in order to minimize the surface free energy. This effect can strongly be reduced by the addition of an amide and surfactant during the synthesis, which decreases the surface free energy of the colloidal particles. These additives promote the formation of powders composed of very small primary particles formed by a crystallite of 10 Angstrom, and exhibit good redispersion properties. The local and long order structures of the redispersible powder were studied by X-rays absorption spectroscopy at Sn L-I edge and X-rays diffraction, respectively. The structure of the colloidal aggregates in suspension was investigated by small angle X-rays scattering (SAXS). SAXS results indicate the sol are composed by a polidisperse system of hard spheres resulting of agglomeration of the primary particles and their size increasing by agglomeration for progressively higher Eu3+ content.

Clustering of rare earth in glasses, aluminum effect: experiments and modeling

Luminescent spectra of Eu3+-doped sol-gel glasses have been analyzed during the densification process and compared according to the presence or not of aluminum as a codoping ion. A transition temperature from hydrated to dehydroxyled environments has been found different for doped and codoped samples. However, only slight modifications have been displayed from luminescence measurements beyond this transition. To support the experimental analysis, molecular dynamics simulations have been performed to model the doped and codoped glass structures. Despite no evidence of rare earth clustering reduction due to aluminum has been found, the modeled structures have shown that the luminescent ions are mainly located in aluminum-rich domains. The synthesis of both experimental and numerical analyses has lead us to interpret the aluminum effect as responsible for differences in structure of the luminescent sites rather than for an effective dispersion of the rare earth ions. (C) 2004 Elsevier B.V. All rights reserved.

Synthesis and photoluminescence study of La1.8Eu0.2O3 coating on nanometric alpha-Al2O3

In this work the La1.8Eu0.2O3 coating on nanometric alpha-alumina, alpha-Al2O3@La1.8Eu0.2O3, was prepared for the first time by a soft chemical method. The powder was heat-treated at 100, 400, 800 and 1200 degrees C for 2 h. X-ray powder diffraction patterns (XRD), transmission electronic microscopy (TEM), emission and excitation spectra, as well as Eu3+, lifetime were used to characterize the material and to follow the changes in structure as the heating temperature increases. The Eu3+ luminescence data revealed the characteristic transitions D-5(0) --> F-7(J) (J = 0, 1 and 3) of Eu3+ at around 580, 591 and 613 nm, respectively, when the powders were excited by 393 nm. The red color of the samples changed to yellow when the powder was annealed at 1200 degrees C. The decrease in the (D-5(0) --> F-7(2))/(D-5(0) --> F-7(1)) ratio from around 5.0 for samples heated at lower temperatures to 3.1 for samples annealed at 1200 degrees C is consistent with a higher symmetry of the Eu3+ at higher temperature. The excitation spectra of the samples also confirms this change by the presence of a more intense and broad band at around 317 nm, instead of the presence of the characteristic peak at 393 mn, which corresponds to the F-7(0) --> L-5(6) transition of the Eu3+. The lifetimes of the D-5(0) --> F-7(2) transition of Eu3+ for the samples heat-treated at 100, 400, 800 and 1200 degrees C was evaluated as 0.57, 0.72, 0.43 and 0.31 ms, respectively. (C) 2006 Elsevier Ltd. All fights reserved.

Crystal structures and luminescence properties of La3Zr4F25 and alpha-LaZr3F15

During a study of the LaF3-ZrF4 system, both La3Zr4F25 and alpha-LaZr3F15 compounds have been evidenced. Their crystal structures have been determined from single-crystal X-ray diffraction data. La3Zr4F25 crystallises in the cubic system with a= 12.384 Angstrom and I (4) over bar 3d space group (no. 220). Its crystal structure is built up of (ZrF6)(2-) octahedra and (LaF8)(5-) dodecahedra sharing corners. The low temperature form, alpha, of LaZr3F15 is orthorhombic (space group Pmmn, no. 59) with a = 15.721 Angstrom, b = 16.299 Angstrom, c= 8.438 Angstrom. Its structure is built of corner-sharing tricaped trigonal prisms surrounding the La3+ ions and both octahedra and monocapped trigonal prisms encompassing the Zr4+ ions. This structure is characterised by dynamically disordered (ZrF6)(2-) complex anions.The Eu3+ luminescence properties of these phases have been investigated and are discussed in relationship with their crystal structures.

Time-resolved spectroscopy studies of Gd2SiO5 : Ce3+ from spherical particles

This paper reports on time-resolved emission and excitation spectra measurement studies of Gd2SiO5:Ce3+ in powder or pellet samples, from spherical particles, in order to assign the Ce3+ ion transitions into two different symmetry sites. Samples were obtained from solid-state reaction of the spherical particles oxides, SiO2 and Gd2O3:Ce3+. From time-resolved spectroscopy measurements Ce3+ ion transitions occupying the two different gadolinium crystallographic sites in Gd2SiO5 were separated and assigned. (C) 2002 Elsevier B.V. B.V. All rights reserved.