Low-frequency high-temperature internal friction in Ti-13Nb-13Zr alloy

Recent studies have been done to achieve biomedical alloys containing non-toxic elements and presenting low elastic moduli. It has been reported that Ti-Nb-Zr alloys rich in beta phase, especially Ti-13Nb-13Zr, have potential characteristics for substituting conventional materials such as Ti-6Al-4V, stainless steel and Co alloys. The aim of this work is to study the internal friction (IF) of Ti-13Nb-13Zr (TNZ) alloy due to the importance of the absorption impacts in orthopedic applications. The internal friction of this alloy produced by arc melting was measured using an inverted torsion pendulum with the free decay method. The measurements were performed from 77 to 700 K with heating rate of 1 K/min, in a vacuum better than 10-5 mBar. The results show a relaxation structure at high temperature strongly dependent on microstructure of the material. Qualitative discussions are presented for the experimental results, and the possibility of using the TNZ as a high damping material is briefly mentioned.

Vickers hardness of cast commercially pure titanium and Ti-6Al-4V alloy submitted to heat treatments

The purpose of this study was to evaluate the effect of heat treatments on the Vickers hardness of commercially pure titanium and Ti-6Al-4V cast alloys. Six-millimeter-diameter cylindrical specimens were cast in a Rematitan System. Commercially pure titanium and Ti-6Al-4V alloy specimens were randomly assigned to 3 groups (n=10) that received the following heat treatments: control (no heat treatment); treatment 1 (T1): heating at 750°C for 2 h; and treatment 2 (T2): annealing at 955°C for 1 h and aging at 620°C for 2 h. After heat treatments, the specimens were embedded in acrylic resin and their surface was ground and polished and hardness was measured. Vickers hardness means (VHN) and standard deviations were analyzed statistically by Kruskal-Wallis test at 5% significance level. For commercially pure titanium, Vickers hardness means of group T2 (259.90 VHN) was significantly higher than those of the other groups (control - 200.26 VHN and T1 - 202.23 VHN), which presented similar hardness means to each other (p>0.05). For Ti-6Al-4V alloy, statistically significant differences were observed among the three groups: T2 (369.08 VHN), T1 (351.94 VHN) and control (340.51 VHN) (p<0.05). The results demonstrated different hardness of CP Ti and Ti-6Al-4V when different heat treatments were used. For CP Ti, VHN means of T2 group was remarkably higher than those of control and T1 group, which showed similar VHN means to each other. For Ti-6Al-4V alloy, however, VHN means recorded for each group may be presented as follows: T2>T1>control.

Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks

Objectives: The aim of this study was to evaluate the effect of thermal and mechanical cycling alone or in combination, on the flexural strength of ceramic and metallic frameworks cast in gold alloy or titanium. Methods: Metallic frameworks (25 mm × 3 mm × 0.5 mm) (N = 96) cast in gold alloy or commercial pure titanium (Ti cp) were obtained using acrylic templates. They were airborne particle-abraded with 150 μm aluminum oxide at the central area of the frameworks (8 mm × 3 mm). Bonding agent and opaque were applied on the particle-abraded surfaces and the corresponding ceramic for each metal was fired onto them. The thickness of the ceramic layer was standardized by positioning the frameworks in a metallic template (height: 1 mm). The specimens from each ceramic-metal combination (N = 96, n = 12 per group) were randomly assigned into four experimental fatigue conditions, namely water storage at 37 °C for 24 h (control group), thermal cycling (3000 cycles, between 4 and 55 °C, dwell time: 10 s), mechanical cycling (20,000 cycles under 10 N load, immersion in distilled water at 37 °C) and, thermal and mechanical cycling. A flexural strength test was performed in a universal testing machine (crosshead speed: 1.5 mm/min). Data were statistically analyzed using two-way ANOVA and Tukey's test (α = 0.05). Results: The mean flexural strength values for the ceramic-gold alloy combination (55 ± 7.2 MPa) were significantly higher than those of the ceramic-Ti cp combination (32 ± 6.7 MPa) regardless of the fatigue conditions performed (p < 0.05). Mechanical and thermo-mechanical fatigue decreased the flexural strength results significantly for both ceramic-gold alloy (52 ± 6.6 and 53 ± 5.6 MPa, respectively) and ceramic-Ti cp combinations (29 ± 6.8 and 29 ± 6.8 MPa, respectively) compared to the control group (58 ± 7.8 and 39 ± 5.1 MPa, for gold and Ti cp, respectively) (p < 0.05) (Tukey's test). While ceramic-Ti cp combinations failed adhesively at the metal-opaque interface, gold alloy frameworks exhibited a residue of ceramic material on the surface in all experimental groups. Significance: Mechanical and thermo-mechanical fatigue conditions decreased the flexural strength values for both ceramic-gold alloy and ceramic-Ti cp combinations with the results being significantly lower for the latter in all experimental conditions. © 2007 Academy of Dental Materials.

Mechanical Property Assessment of Bone Healing around a Titanium-Zirconium Alloy Dental Implant

Background: It has been reported that titanium-zirconium alloy with 13-17% zirconium (TiZr1317) implants show higher biomechanical stability and bone area percentage relative to commercially pure titanium (cpTi) grade 4 fixtures. Purpose: This study aimed to determine whether the higher stability for TiZr1317 implants is associated with higher mechanical properties of remodeling bone in the areas around the implants. Materials and Methods: This study utilized 36 implants (n=18: TiZr1317, n=18: cpTi), which were placed in the healed ridges of the mandibular premolar and first molar of 12 mini pigs (n=3 implants/animal). After 4 weeks in vivo, the samples were retrieved, and resin-embedded histologic sections of approximately 100μm in thickness were prepared. In order to determine the nanomechanical properties, nanoindentation (n=30 tests/specimen) was performed on the bone tissue of the sections under wet conditions with maximum load of 300μN (loading rate: 60μN/s). Results: The mean (±standard deviation) elastic modulus (E) and hardness (H) for the TiZr1317 group were 2.73±0.50GPa and 0.116±0.017GPa, respectively. For the cpTi group, values were 2.68±0.51GPa and 0.110±0.017GPa for E and H, respectively. Although slightly higher mechanical properties values were observed for the TiZr1317 implants relative to the cpTi for both elastic modulus and hardness, these differences were not significant (E=p>0.75; H=p>0.59). Conclusions: The titanium-zirconium alloy used in this study presented similar degrees of nanomechanical properties to that of the cpTi implants. © 2013 Wiley Periodicals, Inc.

Titanium-35niobium alloy as a potential material for biomedical implants: in vitro study

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of Heat Treatment and Oxygen Doping on the Mechanical Properties and Biocompatibility of Titanium-Niobium Binary Alloys

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of the Oxygen on the Mechanical Properties of Ti-Mo Systems Alloys

Titanium alloys normally contain oxygen, nitrogen, or carbon as impurities, and although this concentration is low, these impurities cause changes in the mechanical properties of Ti alloys. Oxygen is a strong alpha-phase stabilizer and its addition causes solid-solution strengthening, shape memory effect, and superelasticity. The most promising alloys are those with Nb, Zr, Ta, and Mo as alloying elements. In this paper, the preparation, processing, and characterization of Ti-Mo alloys (5 and 10 wt%) used as biomaterials are presented, along with the influence of oxygen on their mechanical properties. The addition of oxygen causes an increase in the elasticity modulus of the Ti-5Mo alloy due to an increase in the alpha' phase volume fraction, which possesses a higher modulus than the alpha '' phase. Ti-10Mo possesses a mixture between alpha '' and beta phases, oxygen enters these two structures and causes a dominating effect.

Anelastic relaxation due to hydrogen in Ti-35Nb-7Zr-5Ta alloy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Oxygen Diffusion in Ti-20Mo Alloys, used as Biomaterial, Measured by Mechanical Spectroscopy

Titanium alloys are favorable implant materials for orthopedic applications, due to their desirable properties such as good corrosion resistance, low elasticity modulus, and excellent biocornpatibility. The research on titanium alloys is concentrated in the beta type, as the Ti-20Mo alloys and the addition of interstitial elements in these metals cause changes in their mechanical properties. The mechanical spectroscopy measurements have been frequently used in order to verify the behavior of these interstitials atoms in metallic alloys. This paper presents the study of oxygen diffusion in Ti-20Mo alloys using mechanical spectroscopy measurements. A thermally activated relaxation structure was observed in the sample after oxygen doping. It was associated with the interstitial diffusion of oxygen atoms in a solid solution in the alloy. The diffusion coefficient for the oxygen diffusion in the alloy was obtained by the frequency dependence of the peak temperature and by using a simple mathematical treatment of the relaxation structure and the Arrhenius law.

Diffusion of Oxygen and Nitrogen in the Ti-15Mo Alloy used for Biomedical Applications

The Ti-15Mo alloy is a promising material for use as a biomaterial because of its excellent corrosion resistance and its good combination of mechanical properties, such as fatigue, hardness, and wears resistance. This alloy has a body-centered predominantly cubic crystalline structure and the addition of interstitial atoms, such as oxygen and nitrogen, strongly alters its mechanical properties. Mechanical spectroscopy is a powerful tool to study the interaction of interstitial elements with the matrix metal or substitutional solutes, providing information such as the distribution and the concentration of interstitial elements. The objective of this paper is to study of the effects of heavy interstitial elements, such as oxygen and nitrogen, on the anelastic properties of the Ti-15Mo alloy by using mechanical spectroscopy measurements. In this study, the diffusion coefficients, pre-exponential factors, and activation energies were calculated for the oxygen in the Ti-15Mo alloy.

Structural characterization of Ti-15Mo alloy used as biomaterial by Rietveld method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Growth of Calcium Phosphate Using Chemically Treated Titanium Oxide Nanotubes

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Surface characterization of Ti-7.5Mo alloy modified by biomimetic method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of WC-10%Co-4%Cr coating on the Ti-6Al-4V alloy fatigue strength

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Three-Dimensional Characterization of Pores in Ti-6Al-4V Alloy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)