Epitaxially grown LiNbO3 thin films by polymeric precursor method

LiNbO3 thin films were grown on (0001) sapphire substrates by a chemical route, using the polymeric precursor method. The overall process consists of preparing a coating solution from the Pechini process, based on metallic citrate polymerization, the precursor films, deposited by dip coating, are then heat treated to eliminate the organic material and to synthesize the phase. In this work, we studied the influence of the heat treatment on the structural and optical properties of single-layered films. Two routes were also investigated to increase the film thickness: increasing the viscosity of the coating solution and/or increasing the number of successively deposited layers. The x-ray diffraction theta -2 theta scans revealed the c-axis orientation of the single- and multilayered films and showed that efficient crystallization can be obtained at temperatures as low as 400 degreesC, the phi-scan diffraction evidenced the epitaxial growth with two in-plane variants, A microstructural study revealed that the films were crack free, homogeneous, and relatively dense. Finally, the investigation of the optical properties (optical transmittance and refractive index) confirmed the good quality of the films. These results indicate that the polymeric precursor method is a promising process to develop lithium niobate waveguides.

Real-time optical monitoring of the dip coating process

A significant part of film production by the coating industry is based on wet bench processes, where better understanding of their temporal dynamics could facilitate control and optimization. In this work, in situ laser interferometry is applied to study properties of flowing liquids and quantitatively monitor the dip coating batch process. Two oil standards Newtonian, non-volatile, with constant refractive indices and distinct flow properties - were measured under several withdrawing speeds. The dynamics of film physical thickness then depends on time as t(-1/2), and flow characterization becomes possible with high precision (linear slope uncertainty of +/-0.04%). Resulting kinematic viscosities for OP60 and OP400 are 1,17 +/- 0,03. St and 9,9 +/- 0,2 St, respectively. These results agree with nominal values, as provided by the manufacturer. For more complex films (a multi-component sol-gel Zirconyl Chloride aqueous solution) with a varying refractive index, through a direct polarimetric measurement, allowing also determination of the temporal evolution of physical thickness (uncertainty of +/- 0,007 microns) is also determined during dip coating.

Planar and UV written channel optical waveguides prepared with siloxane poly(oxyethylene)-zirconia organic-inorganic hybrids. Structure and optical properties

Organic-inorganic hybrids were prepared using ureapropyltriethoxysilane, methacryloxypropyltrimethoxysilane and acrylic acid modified zirconium(IV) n-propoxide precursors and were characterized by small angle X-ray scattering, X-ray diffraction and photoluminescence spectroscopy. The results indicate an effective interaction between the zirconium-based nanoparticles and the siliceous nanodomains that induces changes in the hybrids' emission features. Planar waveguides were obtained by spin-coating of the prepared sols on sodalime and silica substrates. Refractive index, thickness, number of propagating modes, and attenuation coefficient were measured at 543.5, 632.8 and 1550 nm by the prism coupling technique. The synergism between the two hybrid precursors resulted in monomode planar waveguides with low losses in the infrared ( from 0.6-1.1 dB cm(-1)) which also support a number of propagating modes in the visible ( losses from 0.4-1.5 dB cm(-1)). Channel waveguides were also obtained by UV photopatterning using amplitude or phase masks and propagating modes were observed at 1550 nm.

High Verdet constant Ga : S : La : O chalcogenide glasses for magneto-optical devices

The magneto-optical rotation at room temperature was measured for three Ga:S:La:O chalcogenide glasses at several laser lines in the visible. The first sample was a binary system constituted by 70 mol % Ga2S3 and 30 mol % La2O3, whereas in the second and third ones the lanthanum oxide was partially substituted by lanthanum sulfide, keeping the amount of gallium sulfide fixed. A pulsed magnetic field between 50 and 80 kG was used for the Faraday rotation measurements. The Verdet constant for one of the ternary samples was found to be as high as 0.205 min G(-1) cm(-1) at 543 nm, indicating that these chalcogenide glasses are very promising for magneto-optical applications. The data for each sample were fitted using the expected analytical expression for the magneto-optical dispersion. Measurements of the refractive index of the glasses at 632.8 nm are also reported. Data on the magneto-optical properties of two high Verdet constant, heavy-metal oxide diamagnetic glasses are also included for comparison. (C) 1999 Society of Photo-Optical Instrumentation Engineers. [S0091-3286(99)00102-6].

Relief grating induced by photo-expansion in Ga-Ge-S and Ga-Ge-As-S glasses

We report the fabrication of relief diffraction gratings recorded on a surface of photosensitive Ga10Ge25S65 and Ga5Ge25As5S65 glasses by means of interference of two UV laser beams at 351 nm. The diffraction efficiency (eta) of first diffraction order was measured. Atomic-force-microscope (AFM) was used to perform a 3D imaging analysis of the sample surface topography that shows the superposition of an imprinted grating over the topography of the glass. The change in the absorption edge and the refractive index has been evaluated and a structural approach of the relief grating on the glass surface has been discussed.

Ultrafast nonlinearity of antimony polyphosphate glasses

We report on the ultrafast nonlinearity of antimony polyphosphate glasses measured using the Kerr shutter technique. The nonlinear refractive index, n(2), was (1.1+/-0.2)x10(-14) cm(2)/W at 800 nm, and enhancement of n(2) by approximate to80% was observed by adding 10% of lead oxide in the glass composition. The full width at half-maximum of the third-order correlation signal was 150 fs, which implies a fast response of the samples (less than or equal to100 fs). Nonlinear absorption was negligible in the range of intensities used. (C) 2003 American Institute of Physics.

Reversible holographic glasses using visible lasers

Antimony based glasses have been investigated for the first time regarding the possibility of holographic data storage using visible lasers sources. Changes in both refractive index and the absorption coefficient were measured using a holographic setup. The modulation of the optical constants is reversible by heat treatment. Bragg gratings were written under visible light of an Ar laser and erased thermally.

Photosensitivity in antimony based glasses

New glass forming systems based on Sb2O3-SbPO4 has been explored. These glasses present higher thermal stability against devitrification and higher refractive index than chalcogenide glasses. Under irradiation, using Ar-laser 350nm wavelength and 50 mW power density, change on the coloration is observed. Structural and electronic modifications around Sb cations induced by such treatment have been characterized by XANES measurements at the L-Sb edges. on the one hand, XANES spectra, at the LJ edge, show a decrease of the coordination number for Sb atoms induced by exposure to light indicating a breaking of Sb-O bonds in the glassy network. on the other hand, XANES spectra, at the Lt edge, suggest a change in the oxidation state of Sb atoms. These modifications associated to the photodarkening of the glass is reversible either after a couple of days or after heating the glass at the glass transition temperature, T-g.

Changes of physical properties of glass surfaces exposed to KNO3 vapors

Modifications of glass surfaces were studied after exposure of samples to an atmosphere resulting from the decomposition of molten KNO3. The diffusion coefficient of K+ ions migrating into the surfaces of float glass and synthesized glasses doped with up to 5 wt% SnO2 was calculated by the Boltzmann-Matano technique. The Vickers hardness and the refractive index increase with exposure time. Infrared spectra show that the migration of K+ is responsible for an increase in the number of non-bridging oxygens in the exposed samples. The spectra of the synthesized glasses present evidences that their surfaces undergo crystallization during the exposure. All results lead to the conclusion that the presence of tin in the glasses hinders the diffusion of K+ ions, thus affecting the Vickers hardness, the refractive index and the infrared spectra. It is shown that the exposure method can be used as an alternative process to promote the K+ migration into glass surfaces. (c) 2006 Elsevier B.V. All rights reserved.

Brillouin scattering in planar waveguides. II. Experiments

Silica-titania planar waveguides of different thicknesses and compositions have been produced by radio-frequency sputtering and dip coating on silica substrates. Waveguides were also produced by silver exchange on a soda-lime silicate glass substrate. Brillouin scattering of the samples has been studied by coupling the exciting laser beam with a prism to different transverse-electric (TE) modes of the waveguides, and collecting the scattered light from the front surface. In multimode waveguides, the spectra depend on the m mode of excitation. For waveguides with a step index profile, two main peaks due to longitudinal phonons are present, apart from the case of the TE0 excitation, where a single peak is observed. The energy separation between the two peaks increases with the mode index. In graded-index waveguides, m-1 peaks of comparable intensities are observed. The spectra are reproduced very well by a model which considers the space distribution of the exciting field in the mode, a simple space dependence of the elasto-optic coefficients, through the value of the refraction index, and neglects the refraction of phonons. A single-fit parameter, i.e., the longitudinal sound velocity, is used to calculate as many spectra as is the number of modes in the waveguide. (C) 2003 American Institute of Physics.

Planar waveguides based on nanocrystalline and Er3+ doped SnO2

Luminescent SnO2: x%mol Er3+ (x=0.1-2.0) thin films have been spin coated on borosilicate and silica substrates from water colloidal suspensions that could be prepared containing up to 40% in weight SnO2 nanocrystalline powders. High Resolution Transmission Electron Microscopy results show the well known SnO2 cassiterite structure and nanocrystallites around 10 nm in diameter, corroborating results from X-ray diffraction. Mono and multi layers have been prepared from the stable colloidal suspensions and films thickness was observed to increase linearly, up to 200 nm, with the colloidal suspensions nanoparticles amount. Excitation and emission spectra have been measured and Er3+ ions were found to be essentially incorporated into the cassiterite structure, substituting for Sn4+, for doping concentration lower than 0.05 mol%. Er3+ ions also appear segregated at the grains surface for higher doping concentration. The optical parameters (refractive index, thickness and propagating modes) of a waveguide sample were measured at 632.8 and 543.4 nm by the prism coupling technique. A monomodal waveguide was obtained with attenuation loss of 3.5 dB/cm along a 2.5 cm optical path.

Ferroelectric and optical properties of Ba0.8Sr0.2TiO3 thin film

Barium strontium titanate (Ba0.8Sr0.2TiO3) thin films have been prepared on Pt/Ti/SiO2/Si substrates using a soft solution processing. X-ray diffraction and also micro-Raman spectroscopy showed that the Ba0.8Sr0.2TiO3 thin films exhibited a tetragonal structure at room temperature. The presence of Raman active modes was clearly shown at the 299 and 725 cm(-1) peaks. The tetragonal-to-cubic phase transition in the Ba0.8Sr0.2TiO3 thin films is broadened, and suppressed at about 35 degreesC, with a maximum dielectric constant of 948 (100 kHz). Electrical measurements for the prepared Ba0.8Sr0.2TiO3 thin films showed a remnant polarization (P-r) of 6.5 muC/cm(2), a coercive field (E-c) of 41 kV/cm, and good insulating properties. The dispersion of the refractive index is interpreted in terms of a single electronic oscillator at 6.97 eV. The direct band gap energy (E-g) and the refractive index (n) are estimated to be 3.3 eV and n = 2.27-2.10, respectively. (C) 2002 American Institute of Physics.

Optical properties of potassium niobate thin films prepared by the polymeric precursor method

Thin films of potassium niobate were deposited on MgO (100) substrates by the polymeric precursor method and annealing in static air at 600 degreesC for 20 h. The obtained films were characterized by X-ray diffraction, atomic force microscopy (AFM) and the prism coupling method. The phi-scan diffraction evidenced the growth of the films with fourfold symmetry. AFM study shows that the films are homogeneous, dense and present a smooth surface. The refractive index and optical losses were strongly influenced by the degree of crystallinity. (C) 2004 Elsevier B.V. All rights reserved.

Femtosecond nonlinear optical properties of lead-germanium oxide amorphous films

The nonlinear (NL) response of lead-germanium oxide amorphous films was investigated using a Ti:saphire laser delivering pulses of approximate to 150 fs at 800 nm. The Kerr shutter technique was employed to reveal the time response of the nonlinearity that is smaller than 150 fs. The sign and magnitude of the nonlinearity were obtained using a novel technique called thermally managed eclipse Z scan which allows the simultaneous characterization of cumulative and noncumulative NL effects. The NL refractive index of electronic origin, n(2)approximate to 2x10(-17) m(2)/W, and the NL absorption coefficient, alpha(2)approximate to 3x10(3) cm/GW, were determined. (c) 2007 American Institute of Physics.

Multi-wavelength holography in Bi12TiO20 crystals: Applications in refractometry

We present a recent development in holography with multimode, large free-spectral range (FSR) diode lasers in photorefractive sillenite crystals. A novel refractometry method based on this type of holographic recording in Bi12TiO20 (BTO) crystals is proposed. The holographic image of a prism-shaped transparent sample appears covered of interference fringes, and as the sample is properly translated, the fringes run along the holographic image. An expression providing the refractive index of the medium as a function of the sample displacement and the correspondent number of running fringes was derived. The refractive indexes of optical (BK7) glass, ethanol, hexan, cumene and aqueous solution of NaCl with different concentrations were measured in order to test the method. The obtained results are in good agreement with the ones reported in literature or measured by us using a commercial Abbe refractometre. (c) 2006 Elsevier B.V. All rights reserved.