Barium strontium titanate nanocrystalline thin films prepared by soft chemical method

Barium strontium titanate (Ba0.65Sr0.35TiO3) nanocrystalline thin films, which were produced by the soft chemical method, were crystallized at low temperature using a domestic microwave oven. A SiC susceptor were used to absorb the microwave energy and rapidly transfer the heat to the film. Low microwave power and short time have been used. The films obtained are crack-free, well-adhered, and fully crystallized. The microstructure displayed a polycrystalline nature with nanograin size. The metal-BST-metal structure of the thin films treated at 700 degrees C show food electric properties. The ferroelectric nature of the BST35 thin film was indicated by buttertly- shaped C-V curves. The capacitance-frequency curves reveal that the dielectric constant may reach a value up to 800 at 100kHz. The dissipation factor was 0.01 at 100kHz. The charge storage density as function of applied voltage graph showed that the charge storage densities are suitable for use in trench type 64 Mb ( 1-5 mu C/cm(2) and 265 Mb (2-11 mu C/cm(2)) DRAMs. (C) 2007 Elsevier Ltd. All rights reserved.

Influence of processing conditions on the thermal decomposition of SrTiO3 precursors

The present work investigates the influence of milling and calcination atmosphere on the thermal decomposition of SrTiO3 powder precursors. Both pure and neodymium-modified SrTiO3 samples were studied. Milling did not significantly influence numerical mass loss value, but reduced the number of decomposition steps, modifying the profiles of the TG and DTA curves. on the other hand, milling increases the amount of energy liberated by the system upon combustion of organic matter. It was also observed that the milling process, associated to the calcination in an oxygen atmosphere, considerably decreases the amount of organic matter and increases the final mass loss temperature.

Microtensile bond strength of a resin cement to feldpathic ceramic after different etching and silanization regimens in dry and aged conditions

Objectives. This study evaluated the durability of bond strength between resin cement and a feldspathic ceramic submitted to different etching regimens with and without silane coupling agent application.Methods. Thirty-two blocks (6.4 mm x 6.4 mm x 4.8 mm) were fabricated using a microparticulate feldspathic ceramic (Vita VM7), ultrasonically cleaned with water for 5 min and randomly divided into four groups, according to the type of etching agent and silanization method: method 1, etching with 10% hydrofluoric (HF) acid gel for I min + silanization; method 2, HF only; method 3, etching with 1.23% acidulated phosphate fluoride (APF) for 5 min + silanization; method 4, APF only. Conditioned blocks were positioned in their individual silicone molds and resin cement (Panavia F) was applied on the treated surfaces. Specimens were stored in distilled water (37 degrees C) for 24 h prior to sectioning. After sectioning the ceramic-cement blocks in x- and Y-axis with a bonded area of approximately 0.6 mm(2), the microsticks of each block were randomly divided into two storage conditions: Dry, immediate testing; TC, thermal cycling (12,000 times) + water storage for 150 d, yielding to eight experimental groups. Microtensile bond strength tests were performed in universal testing machine (cross-head speed: 1 mm/min) and failure types were noted. Data obtained (MPa) were analyzed with three-way ANOVA and Tukey's test (alpha = 0.05).Results. Significant influence of the use of silane (p < 0.0001), storage conditions (p = 0.0013) and surface treatment were observed (p = 0.0014). The highest bond strengths were achieved in both dry and thermocycled conditions when the ceramics were etched with HF acid gel and silanized (17.4 +/- 5.8 and 17.4 +/- 4.8 MPa, respectively). Silanization after HF acid gel and APT treatment increased the results dramatically (14.5 +/- 4.2-17.4 +/- 4.8 MPa) compared to non-silanized groups (2.6 +/- 0.8-8.9 +/- 3.1 MPa) where the failure type was exclusively (100%) adhesive between the cement and the ceramic.Significance. Silanization of the feldspathic ceramic surface after APF or HF acid etching increased the microtensile bond strength results significantly, with the latter providing higher results. Long-term thermocycling and water storage did not decrease the results in silanized groups. (C) 2006 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Fecundity of the crab Callinectes ornatus Ordway, 1863 (Decapoda, Brachyura, Portunidae) from the Ubatuba region, São Paulo, Brazil

The objective of the present study was to characterize the fecundity of Callinectes ornatus from the northern coast of São Paulo, Brazil. To study the fecundity and its relationships to size, brood weight, and egg size, the ovigerous females were collected at 2-month intervals for two consecutive years (January, 1991 to November, 1992) in the Ubatuba region using a fishing boat equipped with an otter-trawl type of net. After collecting, the animals were screened, bagged, labeled, and stored frozen. Only data from 38 females carrying early stage eggs were considered. In the laboratory, the specimens were thawed at room temperature, the pleopod structure with the egg mass was removed and the eggs were carefully removed from the pleopods. The samples were then fixed in 10% formalin and stored in 70% ethanol, until the time for processing. Processing followed the method of Hines (1982, 1988). Following the frequency determination of carapace width and fecundity, mean egg number, mean volume and mean dry weight of brooded egg mass were determined for each class obtained. Data were analyzed by regressions of log-log transformations for allometric plots (Y = aX(b)) of reproductive variables versus carapace width. Carapace width was one of the main factors for the determination of fecundity, which ranged 171 570 +/- 94 634 eggs, with females of the same size class presenting a wide amplitude of variation. This supports the hypothesis that portunid females present staggered spawning, possibly presenting more than one period of reproduction within one year. The present species showed lower fecundity than the remaining portunids studied, but they did show a rapid and efficient embryonic development, presumably capable of assuring reproductive success.

Effect of oxygen atmosphere on the morphology of LiTaO3 thin films prepared from polymeric precursor method

Lithium tantalate (LiTaO3) thin films with (50:50) stoichiometry were prepared using polymeric organic solution. The 5-layered films were deposited on silicon (100) substrates by spin coating method. The coated substrates were thermally treated at 500degreesC for 3 h under several oxygen atmospheres in order to study the influence of oxygen flow on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction results showed that an oxygen flow of 100 cm(3)/min leads to LiTaO3 thin films with higher crystallinity, without preferential orientation. It was observed by scanning electron microscopy (SEM) that the thickness of thin films decreases when the oxygen flow increases. The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by oxygen flow.

Optical properties of Mg doped LiNbO3 thin films grown by polymeric precursor method.

Polymeric precursor solution was used to deposit by spin-coating pure and Mg doped LiNbO3 thin films on sapphire substrates. The effects of magnesium addition on crystallinity, morphology and optical properties of the annealed films were investigated. X-ray diffraction patterns indicate the oriented growth of the films. AFM studies show that the films are very homogeneous, dense and present smooth surfaces. The refractive index and optical losses obtained by the prism coupling method were influenced by the magnesium addition.

Effects of processing on the structure of zein/oleic acid films investigated by X-ray diffraction

Zein films plasticized with oleic acid were formed by solution casting, by the stretching of moldable resins, and by blown film extrusion. The effects of the forming process on film structure were investigated by X-ray diffraction. Wide-angle X-ray scattering (WAXS) patterns showed d-spacings at 4.5 and 10 angstrom, which were attributed to the zein alpha-helix backbone and inter-helix packing, respectively. The 4.5.angstrom d-spacing remained stable under processing while the 10 angstrom d-spacing varied with processing treatment. Small-angle X-ray scattering (SAXS) detected a long-range periodicity for the formed films but not for unprocessed zein, which suggests that the forming process-promoted film structure development is possibly aided by oleic acid. The SAXS d-spacing varied among the samples (130-238 angstrom) according to zein origin and film-forming method. X-ray scattering data suggest that the zein molecular structure resists processing but the zein supramolecular arrangements in the formed films are dependent on processing methods.

Microstructural and optical characterization of CaWO4 and SrWO4 thin films prepared by a chemical solution method

Stoichiometric CaWO4 and SrWO4 thin films were synthesized using a chemical solution processing, the so-called polymeric precursor method. In this soft chemical method, soluble precursors such as strontium carbonate, calcium carbonate and tungstic acid, as starting materials, were mixed in an aqueous solution. The thin films were deposited on glass substrates by means of the spinning technique. The surface morphology and crystal structure of the thin films were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Nucleation stages and surface morphology evolution of the thin films on glass substrates were studied by atomic force microscopy. The films nucleate at 300 degreesC, after the coalescence of small nuclei into larger grains yielding a homogeneous dense surface. XRD characterization of these films showed that the CaWO4 and SrWO4 phases crystallize at 400 degreesC from an inorganic amorphous phase. No intermediate crystalline phase was identified. The optical properties were also studied. It was found that CaWO4 and SrWO4 thin films have an optical band gap, E-gap=5.27 and 5.78 eV, respectively, of a direct transition nature. The excellent microstructural quality and chemical homogeneity confirmed that this soft solution processing provides an inexpensive and environmentally friendly route for the preparation of CaWO4 and SrWO4 thin films. (C) 2003 Elsevier B.V. All rights reserved.

Tin-doped indium oxide nanobelts grown by carbothermal reduction method

This communication discusses the formation of doped nanobelts produced by a simple route. Tin-doped indium oxide (ITO) nanobelts were obtained by a carbothermal reduction method. The nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX) and wavelength-dispersive X-ray spectroscopy (WDX). The results show that the nanobelts have a cubic structure, are single crystalline and doped with tin and grow in the [400] direction.

Effect of drying method on the sorption isotherms and isosteric heat of persimmon pulp powder

Moisture equilibrium data of persimmon pulp powders with 50% maltodextrin (dry basis) obtained with different drying methods were determined at 20, 30, 40 and 50 degrees C. The spray-dryer gave a dry product with a higher adsorption capacity than the other methods. The vacuum- and freeze-dried products had the same adsorption capacity. The highest isosteric heat of sorption was observed for powders produced by spray-drying. The isokinetic temperature (T(B)) calculated for persimmon pulp powder obtained by vacuum-, spray- and freeze-drying were 541.4 K, 616.3 K, 513.2 K, respectively. The sorption process was spontaneous and enthalpy controlled.

Synthesis, structural refinement and optical behavior of CaTiO3 powders: A comparative study of processing in different furnaces

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis, ferroelectric and optical properties of (Pb,Ca)TiO3 thin films by soft solution processing

Calcium modified lead titanate sol was synthesized using a soft solution processing, the so-called polymeric precursor method. In soft chemistry method, soluble precursors such as lead acetate trihydrate, calcium carbonate and titanium isopropoxide, as starting materials, were mixed in aqueous solution. Pb0.7Ca0.3TiO3 thin films were deposited on platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure, dielectric and optical properties of the thin films were investigated. The electrical measurements were conducted on metal-ferroelectric-metal (MFM) capacitors. The typical measured small signal dielectric constant and dissipation factor at a frequency of 100 kHz were 299 and 0.065, respectively, for a thin film with 230 nm thickness annealed at 600degreesC for 2 h. The remanent polarization (2P(r)) and coercive field (E-c) were 32 muC/cm(2) and 100 kV/cm, respectively. Transmission spectra were recorded and from them, refractive index, extinction coefficient, and band gap energy were calculated. Thin films exhibited good optical transmissivity, and had optical direct transitions. The present study confirms the validity of the DiDomenico model for the interband transition, with a single electronic oscillator at 6.858 eV. The optical dispersion behavior of PCT thin film was found to fit well the Sellmeir dispersion equation. The band gap energy of the thin film, annealed at 600degreesC, was 3.56 eV. The results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of PCT thin films.

Evaluation of in vitro gas production of roughages and their mixtures using the curves subtraction method

The in vitro gas production of four single roughages and their paired combinations (1:1 on dry matter basis) were evaluated. Two roughage samples (100 mg) per treatment were fermented with ruminal fluid during a 48 h incubation period. Total 48 h gas volumes of fermentation dry matter (DM), neutral detergent fiber (NDF) and soluble compounds in neutral detergent (NDS) were for sugarcane = 16.8, 11.2, 6.9 mL; sugarcane + corn silage = 20.1, 12.6, 9.1 mL; sugarcane + 60-day elephantgrass = 16.5, 17.6 mL; sugarcane + 180-day elephantgrass = 13.8, 8.2, 5.9 mL; corn silage = 18.8, 16.8, 4.7 mL; corn silage + 60-day elephantgrass = 16.3, 15.4, 2.4 mL; corn silage + 180-day elephantgrass = 16.1, 11.8, 4.2 mL; 60-day elephantgrass = 16.9, 19.0 mL and 180-day elephantgrass = fermented 10.7, 12.2 mL, respectively. The NDS gas production was not possible to estimate for sugarcane + 60-day elephantgrass, 60-day elephantgrass and 180-day elephantgrass. The present data shows that the curves subtraction method can be an option to evaluate the contribution of the soluble fractions in roughages to digestion kinetics. However, this method underestimates the NDS gas contribution when roughages are low in crude protein and soluble carbohydrates. It is advisable to directly apply the two-compartmental mathematical model to the digestion curves for roughage DM, when determining the NDS gas volume and the digestion rate. This method is more straightforward and accurate when compared to the curve subtraction method. Non-structural carbohydrates combined with fiber and protein promoted a positive associative effect in sugarcane + corn silage (50:50) mixture. Therefore, it can be concluded that the soluble fraction of roughages greatly contributes to gas production. (C) 2004 Elsevier B.V. All rights reserved.

Reflux synthesis and hydrothermal processing of ZrO2 nanopowders at low temperature

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Experimental and theoretical study of workpiece temperature when end milling hardened steels using (TiAl)N-coated and PcBN-tipped tools

The present work shows an experimental and theoretical study on heat flow when end milling, at high-speed, hardened steels applied to moulds and dies. AISI H13 and AISI D2 steels were machined with two types of ball nose end mills: coated with (TiAl)N and tipped with PcBN. The workpiece geometry was designed to simulate tool-workpiece interaction in real situations found in mould industries, in which complex surfaces and thin walls are commonly machined. The compressed and cold air cooling systems were compared to dry machining Results indicated a relatively small temperature variation, with higher range when machining AISI D2 with PcBN-tipped end mill. All cooling systems used demonstrated good capacity to remove heat from the machined surface, especially the cold air. Compressed air was the most indicated to keep workpiece at relatively stable temperature. A theoretical model was also proposed to estimate the energy transferred to the workpiece (Q) and the average convection coefficient ((h) over bar) for the cooling systems used. The model used a FEM simulation and a steepest decent method to find the best values for both variables. (c) 2007 Elsevier B.V. All rights reserved.