Evaluation of the radiopacity of calcium hydroxide- and glass-ionomer-based root canal sealers

Aim To evaluate the radiopacity of calcium hydroxide-based root canal sealers (Acroseal, Sealapex and Sealer 26), a glass-ionomer-based sealer (Activ GP Sealer) and a zinc oxide and eugenol-based sealer (Intrafill).Methodology Five disc-shaped specimens (10 x 1 mm) were fabricated from each material, according to the International Organization for Standardization (ISO) 6876/2001 standard. After setting of the materials, radiographs were taken using occlusal films and a graduated aluminum step-wedge varying from 2 to 16 mm in thickness. The dental X-ray unit (GE1000) was set at 50 Kvp, 10 mA, 18 pulses s(-1) and distance of 33.5 cm. The radiographs were digitized and the radiopacity compared with that of the aluminum step-wedge, using WIXWIN-2000 software (Gendex). Data (mm Al) were submitted to ANOVA and Tukey test.Results Intrafill was the most radiopaque material (7.67 mm Al) followed by Sealer 26 (6.33 mm Al), Sealapex (6.05 mm Al) and Acroseal (4.03 mm Al). Activ GP was the least radiopaque material (1.95 mm Al, P < 0.05).Conclusions The sealers evaluated in this study had different radiopacities. However, except for the glass-ionomer-based sealer, all materials had radiopacity values above the minimum recommended by the ISO standard.

Biocompatibility of a resin-modified glass-ionomer cement applied as pulp capping in human teeth

Purpose: to evaluate the human pulp response following pulp capping with calcium hydroxide (CI-I, Group 1), and the resin-modified glass-ionomer Vitrebond (VIT, Group 2). Materials and Methods: Intact teeth with no cavity preparation were used as control Group (ICG, Group 3). Buccal Class V cavities were prepared in 34 sound human premolars. After exposing the pulps, the pulp capping materials were applied and the cavities were Filled using Clearfil Liner Bond 2 bonding agent and Z100 resin-based composite. The teeth were extracted after 5, 30, and from 120 to 300 days, fixed in 10% buffered formalin solution, and prepared according to routine histological techniques. 6-mu m sections were stained with hematoxylin and eosin, Masson's trichrome, or Brown gr Brenn technique for bacterial observation. Results: At 5 days, CH caused a large zone of coagulation necrosis, the mononuclear inflammatory reaction underneath the necrotic zone was slight to moderate. VIT caused a moderate to intense inflammatory pulp response with a large necrotic zone. A number of congested venules associated with plasma extravasation and neutrophilic infiltration was observed. Over time, only CH allowed pulp repair and complete dentin bridging around the pulp exposure site. VIT components displaced into the pulp tissue triggered a persistent inflammatory reaction which appeared to be associated with a lack of dentin bridge formation. After 30 days a few histological sections showed a number of bacteria on the lateral dentin walls. In these samples the pulp response was similar to those samples with no microleakage. VIT was more irritating to pulp tissue than CH, which allowed pulp repair associated with dentin bridge formation. These results suggested that VIT is not an appropriate dental material to be used in direct pulp capping for mechanically exposed human pulps.

In vitro cytotoxicity and in vivo-biocompatibility of contemporary resin-modified glass-ionomer cements

Objectives. To evaluate the effects of current resin-modified glass-ionomer cements (RMGICs) applied on culture of cells or implanted into subcutaneous tissue of rats.Methods. Experiment 1 - Thirty round-shaped samples of every RMGICs: Rely X Luting Cement (RL), Vitremer (VM), and Vitrebond (VB) were placed into wells with 1.1 mL of culture medium (DMEM), and incubated for 24,48 or 72 h. The extracts from every sample were applied on the MDPC-23 cells. Fresh DMEM was used as control group. The MTT assay was carried out for mitochondrial respiration. Experiment 2 - Fifty-four polyethylene tubes filled with the experimental materials were implanted into the dorsal subcutaneous tissue of rats. At 7, 30, and 90 days the animals were killed and the biopsies were processed for histological evaluation.Results. Experiment 1 - Both time of elution and material significantly influenced cell respiratory activity. in general, the extracts obtained at 24 h were less cytotoxic than 48 and 72 h incubation. The cytotoxic effect of VM and RL were not statistically different (P < 0.05) for the 24-hour period. VB showed the highest cytotoxic effect. Experiment 2 - All RMGICs elicited at 7 days a moderate to intense inflammatory reaction which decreased over time. However, connective healing occurred for most of samples at 90-day evaluation.Significance. Glass-ionomer cements may cause noticeable inflammatory response when in direct contact to connective tissue. The toxic effects of this kind of soluble material depend on the amount of components released in the aqueous environment. (C) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Tissue response to experimental dental cements prepared from a modified power glass composition

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Glass transition temperature of hard chairside reline materials after post-polymerisation treatments

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Conventional and Resin-modified Glass-Ionomer Liner on Dentin Adhesive Interface of Class I Cavity Walls After Thermocycling

Objective: The aim of this in vitro study was to analyze the effect of glass-ionomer cement as a liner on the dentin/resin adhesive interface of lateral walls of occlusal restorations after thermocycling.Materials and Methods: Occlusal cavities were prepared in 60 human molars, divided into six groups: no liner (1 and 4); glass-ionomer cement (GIC, Ketac Molar Easymix, 3M ESPE) (2 and 5); and resin-modified glass-ionomer cement (RMGIC, Vitrebond, 3M ESPE) (3 and 6). Resin composite (Filtek Z250, 3M ESPE) was placed after application of an adhesive system (Adper Single Bond 2, 3M ESPE) that was mixed with a fluorescent reagent (Rhodamine B) to allow confocal microscopy analysis. Specimens of groups 4, 5 and 6 were thermocycled (5 degrees C-55 degrees C) with a dwell time of 30 seconds for 5000 cycles. After this period, teeth were sectioned in approximately 0.8-mm slices. One slice of each tooth was randomly selected for confocal microscopy analysis. The other slices were sectioned into 0.8 nun x 0.8 mm beams, which were submitted to microtensile testing (MPa). Data were analyzed using two-way ANOVA and Tukey test (p < 0.05).Results: There was no detectedstatistical difference on bond strength among groups (alpha < 0.05). Confocal microscopy analysis showed a higher mean gap size in group 4(12.5 mu m) and a higher percentage of marginal gaps in the thermocycled groups. The RNIGIC liner groups showed the lowest percentage of marginal gaps.Conclusions: Lining with RMGIC resulted in less gap formation at the dentin/resin adhesive interface after artificial aging. RMGIC or GIC liners did not alter the microtensile bond strength of adhesive system/resin composite to dentin on the lateral walls of Class I restorations.

Analysis of surface roughness of glass-ionomer cements and compomer

The purpose of this study was to evaluate the surface roughness of two glass-ionomer cements (Vitremer and Chelon-Fil), and one compomer (Dyract) when submitted to different finishing/polishing procedures at different times. A hundred 80-sample discs were made of each material and randomly divided into six finishing/polishing groups: mylar strip (control); Sof-Lex discs; diamond burs; diamond burs/Sof-Lex discs; 30-fluted carbide bur; 30-fluted carbide bur/Sof-Lex discs. These procedures were carried out immediately after preparation of the samples, after 24 and 168 h. Average surface roughness (Ra) was measured with a profilometer and the values were compared using anova (P < 0.05). The smoothest surface for all materials was obtained when cured in contact with the mylar strip. All other tested products increased surface roughness of restorative materials, but Sof-lex discs lead to better results. The worst results were verified with diamond burs. The finishing/polishing procedures, when performed immediately, can improve the roughness of glass-ionomer cements but not of the compomer tested.

Factors affecting on bond strength of glass fiber post cemented with different resin cements to root canal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Customized fiber glass posts. Fatigue and fracture resistance

Purpose: To evaluate the root fracture strength of human single-rooted premolars restored with customized fiberglass post-core systems after fatigue simulation. Methods: 40 human premolars had their crowns cut and the root length was standardized to 13 mm. The teeth were endodontically treated and embedded in acrylic resin. The specimens were distributed into four groups (n=10) according to the restorative material used: prefabricated fiber post (PFP), PFP+accessory fiber posts (PFPa), PFP+unidirectional fiberglass (PFPf), and unidirectional fiberglass customized post (CP). All posts were luted using resin cement and the cores were built up with a resin composite. The samples were stored for 24 hours at 37 degrees C and 100% relative humidity and then submitted to mechanical cycling. The specimens were then compressive-loaded in a universal testing machine at a crosshead speed of 0.5 mm/minute until fracture. The failure patterns were analyzed and classified. Data was submitted to one-way ANOVA and Tukey's test (alpha= 0.05). Results: The mean values of maximum load (N) were: PFP - 811.4 +/- 124.3; PFPa - 729.2 +/- 157.2; PFPf - 747.5 +/- 204.7; CP - 762.4 +/- 110. Statistical differences were not observed among the groups. All groups showed favorable restorable failures. Fiberglass customized post did not show improved fracture resistance or differences in failure patterns when compared to prefabricated glass fiber posts. (Am J Dent 2012;25:35-38).

Determination of the properties of an experimental glass polyalkenoate cement prepared from niobium silicate powder containing fluoride

Objectives. The purpose of this paper is to modify the conventional calcium fluoro-aluminosilicate glass, which is used in the formation of glass ionomer cements (CIGs) by the niobium addition and to study the properties of GICs obtained.Materials and methods. Sol-gel process was used to prepare the powder at lower temperature than fusion method. Glass-ceramic powder obtained in this way was used to prepare the GICs. The properties such as working and setting times, microhardness and diametral tensile strength were evaluated for the experimental GICs and a commercial luting cement.Results. The ideal powder:liquid (P:L) ratio determined to prepare the experimental GICs was equal to 1:1. The cements prepared using this ratio showed working and setting times similar to the commercial GICs. in mechanical tests it was observed that microhardness and diametral tensile strength of the experimental GICs decreased significantly with the reduction of P:L ratio. on the other hand, the results obtained in microhardness tests indicated that the presence of niobium was a positive factor.Significance. The chemical process allows the development of glass-ceramic powder at 600 degrees C which is the goal of the present paper. It was concluded that GICs containing niobium might be used in dental applications and these results encourage further researches on other compositions. (c) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of 0.05% sodium fluoride solutions on microhardness of resin-modified glass ionomer cements

This study aimed to evaluate the influence of fluoride-containing mouthrinse solutions (Fluorgard and Oral B) on the superficial microhardness of two resin-modified glass ionomer cements (Vitremer and Fuji II LC). Fifteen discs-shaped specimens of each glass ionomer cement (0 10 mm; 2 mm thick) were prepared, thereby forming two groups. After 24-hour storage in artificial saliva, the microhardness was measure and the data were recorded. Next, each group was divided into three subgroups (n = 5), according to the solution to be immersed in. Control specimens were kept in artificial saliva along the whole experiment. The test specimens were kept in mouthrinse solution for 30 days. Vickers surface microhardness was analyzed at predetermined evaluation periods: 24 h, 48 h, 7, 14, 21 and 30 days after specimens' preparation. Data were subjected to three-way ANOVA and to Tukey test (p < 0.05). A better behavior of Fuji II LC was observed and Fluorgard affected most the characteristics of the tested materials. It may be concluded that fluoride-containing solutions influenced the tested characteristics of materials, mainly of Vitremer.

Effect of Airborne-Particle Abrasion and Mechanico-Thermal Cycling on the Flexural Strength of Glass Ceramic Fused to Gold or Cobalt-Chromium Alloy

Purpose: To evaluate the effect of airborne-particle abrasion and mechanico-thermal cycling on the flexural strength of a ceramic fused to cobalt-chromium alloy or gold alloy.Materials and Methods: Metallic bars (n = 120) were made (25 mm x 3 mm x 0.5 mm): 60 with gold alloy and 60 with Co-Cr. At the central area of the bars (8 mm x 3 mm), a layer of opaque ceramic and then two layers of glass ceramic (Vita VM13, Vita Zahnfabrick) were fired onto it (thickness: 1 mm). Ten specimens from each alloy group were randomly allocated to a surface treatment [(tungsten bur or air-particle abrasion (APA) with Al(2)O(3) at 10 mm or 20 mm away)] and mechanico-thermal cycling (no cycling or mechanically loaded 20,000 cycles; 10 N distilled water at 37 degrees C and then thermocycled 3000 cycles; 5 degrees C to 55 degrees C, dwell time 30 seconds) combination. Those specimens that did not undergo mechanico-thermal cyclingwere stored inwater (37 degrees C) for 24 hours. Bond strength was measured using a three-point bend test, according to ISO 9693. After the flexural strength test, failure types were noted. The data were analyzed using three factor-ANOVA and Tukey's test (alpha = 0.05).Results: There were no significant differences between the flexural bond strength of gold and Co-Cr groups (42.64 +/- 8.25 and 43.39 +/- 10.89 MPa, respectively). APA 10 and 20 mm away surface treatment (45.86 +/- 9.31 and 46.38 +/- 8.89 MPa, respectively) had similar mean flexural strength values, and both had significantly higher bond strength than tungsten bur treatment (36.81 +/- 7.60 MPa). Mechanico-thermal cycling decreased the mean flexural strength values significantly for all six alloy-surface treatment combinations tested when compared to the control groups. The failure type was adhesive in the metal/ceramic interface for specimens surface treated only with the tungsten bur, and mixed for specimens surface treated with APA 10 and 20 mm.Conclusions: Considering the levels adopted in this study, the alloy did not affect the bond strength; APA with Al(2)O(3) at 10 and 20 mm improved the flexural bond strength between ceramics and alloys used, and the mechanico-thermal cycling of metal-ceramic specimens resulted in a decrease of bond strength.