Study of the thermomechanical and electrical properties of conducting composites containing natural rubber and carbon black

This work describes the preparation and characterization of composite materials obtained by the combination of natural rubber (NR) and carbon black (CB) in different percentages, aiming to improve their mechanical properties, processability, and electrical conductivity, aiming future applications as transducer in pressure sensors. The composites NR/CB were characterized through optical microscopy (OM), DC conductivity, thermal analysis using differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMA), thermogravimetry (TGA), and stress-strain test. The electrical conductivity varied between 10(-9) and 10 S m(-1), depending on the percentage of CB in the composite. Furthermore, a linear (and reversible) dependence of the conductivity on the applied pressure between 0 and 1.6 MPa was observed for the sample with containing 80 wt % of NR and 20% of CB. (C) 2007 Wiley Periodicals, Inc.

Influence of strains and defects on ferroelectric and dielectric properties of thin-film barium-strontium titanates

Pristine, W and Mn 1% doped Ba(0.6)Sr(0.4)TiO(3) epitaxial thin films grown on the LaAlO(3) substrate were deposited by pulsed laser deposition (PLD). Dielectric and ferroelectric properties were determined by the capacitance measurements and X-ray diffraction was used to determine both residual elastic strains and defect-related inhomogeneous strains-by analyzing diffraction line shifts and line broadening, respectively. We found that both elastic and inhomogeneous strains are affected by doping. This strain correlates with the change in Curie-Weiss temperature and can qualitatively explain changes in dielectric loss. To explain the experimental findings, we model the dielectric and ferroelectric properties of interest in the framework of the Landau-Ginzburg-Devonshire thermodynamic theory. As expected, an, elastic-strain contribution due to the epilayer-substrate misfit has an important influence on the free-energy. However, additional terms that correspond to the defect-related inhomogeneous strain had to be introduced to fully explain the measurements.

Effects of powder preparation and sintering procedure on microstructure and dielectric properties of PLZT ceramics

PLZT ceramics belong to one of the very important groups of functional materials that make a basis for the production of a large range of electronic devices. The microstructure and properties of ceramics depend on the powder preparation and thermal processing conditions. Various techniques have been used to obtain chemically homogeneous and fine starting powders. PLZT powders have been prepared by two different production routes: by a modified Pechini method, using a polymeric precursor method (PMM) and by a partial oxalate method. A two-step sintering process, including a hot pressing, was carried out at 1100 and 1200degreesC Distinct phases obtained during the sintering process have been investigated by SEM and EDS techniques and dielectric properties such as permittivity and dielectric loss were measured in a frequency range from 1 to 20 kHz.. A significant difference in microstructure and dielectric properties, depending on powder origin and sintering procedure, has been noticed.

Structural and surface properties of thermally prepared Ti/RhxTi(1-x)Oy electrodes: I - influence of preparation parameters

Electrodes of RhxTi(1-x) O-y nominal composition were prepared by thermal decomposition of the chloride or nitrate precursor salts dissolved in strongly acidic medium and applied by brush to both sides of a Tidegrees support. A systematic study of the influence of calcination temperature and time as well as oxygen flux was conducted. The coatings were characterised by SEM, EDAX, XRD, open circuit potential measurements and cyclic voltammetry (CV). Visible-ultraviolet spectrophotometry was employed to identify the chemical form of the precursor in solution while thermogravimetric analysis (TGA) was used to assess the decomposition temperature ranges. Optimisation of the coating preparation parameters showed coatings obtained from [Rh(H2O)(6)](NO3)(3) precursor dissolved in HNO3 1:2 (v/v) and fired at 430 degreesC for 2 h in a 5 1 min (-1) oxygen stream-furnished stable electrodes having the highest electrochemically active surface area. (C) 2002 Elsevier B.V. Ltd. All rights reserved.

Synthesis, structure and redox properties of an unexpected trinuclear copper(II) complex with aspartame: [Cu(apm)(2)Cu(mu-N,O : O '-apm)(2)(H2O)Cu(apm)(2)(H2O)]center dot 5H(2)O

Structural, magnetic and spectroscopic data of a new trinuclear copper(II) complex with the ligand aspartame (apm) are described. [Cu(apm)(2)CU(mu-N,O:O'-apm)(2)(H2O)Cu(apm)(2)(H2O)]-5H(2)O crystallizes in the triclinic system, space group P1 (#1) with a = 7.3300(1) angstrom, b = 15.6840(1) angstrom, c = 21.5280(1) angstrom, alpha = 93.02(1)degrees, beta = 93.21 (1)degrees, gamma = 92.66(1)degrees and Z = 1. Aspartame coordinates to Cu(II) through the carboxylate and beta-amino groups. The carboxylate groups of the two central ligands act as bidentate bridges in a syn-anti conformation while the carboxylate groups of the four peripheral ligands are monodentate in a syn conformation. The central copper ion is in a distorted square pyramidal geometry with the apical position being occupied by one oxygen atom of the water molecule. The two terminal copper(II) atoms are coordinated to the ligands in the same position but their coordination sphere differs from each other due to the fact that one copper atom has a water molecule in an apical position leading to an octahedral coordination sphere while the other copper atom is exclusively coordinated to aspartame ligands forming a distorted square pyramidal coordination sphere. Thermal analysis is consistent with the X-ray structure. EPR spectra and CV curves indicate a rupture of the trinuclear framework when this complex is dissolved in ethanol or DMF, forming a mononuclear species, with a tetragonal structure. (c) 2005 Elsevier B.V. All rights reserved.

Hardness and elastic modulus of carbon-germanium alloys

This work reports on the mechanical properties of germanium-rich amorphous carbon-germanium alloys prepared by RF sputtering of a germanium/graphite target under an argon/hydrogen atmosphere. Nano-hardness, elastic modulus and stress were investigated as a function of the carbon content. The stress, which is reduced by the incorporation of carbon, was related to the film structure and to the difference in the Ge-Ge and Ge-C bond length. Contrary to what was expected, the hardness and elastic modulus of the alloys are lower than the corresponding values for pure amorphous hydrogenated germanium film, which in turn has both properties also smaller than those of crystalline germanium. These properties are analyzed in terms of the structural properties of the films. (C) 2001 Elsevier B.V. B.V All rights reserved.

Effect of presence of an acid catalyst on structure and properties of iron-doped siloxane-polyoxyethylene nanocomposites prepared by sol-gel

In this work we investigate the effect of hydrochloric acid (HC) addition on the structure and thermal and magnetic properties of iron-doped siloxane-polyoxyethylene (POE) hybrids prepared by the sol-gel route. X-ray powder diffraction (XRD) and X-ray absorption near edge structure (XANES) results reveal the dominance of ferrihydrite nanoparticles and a mixture of this phase with FeCl4- species in the hybrid prepared without and with HCl, respectively. Thermal analysis reveals the existence of two crystalline polymeric phases in the hybrid prepared with HCl whereas hybrids prepared without HCl are amorphous. The 105 and 60 Angstrom sized ferrihydrite nanoparticles were detected by SAXS analysis of the composite prepared without and with HCl, respectively. The magnetic results suggest that in both samples antiferromagnetic nanoparticles coexist with small clusters/isolated ions. In the sample without HCl addition, larger particles dominate the magnetic behavior, while the opposite occurs for the sample prepared using HCl catalyst. (C) 2004 Elsevier B.V. All rights reserved.

Effect of high hydrostatic pressure processing on rheological and textural properties of probiotic low-fat yogurt fermented by different starter cultures

The effect of milk processing on rheological and textural properties of probiotic low-fat yogurt (fermented by two different starter cultures) was studied. Skim milk fortified with skim milk powder was subjected to three treatments: (1) thermal treatment at 85C for 30 min; (2) high hydrostatic pressure (HHP) at 676 MPa for 5 min; and (3) combined treatments of HHP (676 MPa for 5 min) and heat (85C for 30 min). The processed milk was fermented using two different starter cultures containing Streptococcus thermophilus, Lactobacillus delbrueckii ssp. bulgaricus, Lactobacillus acidophilus and Bifidobacterium longum at inoculation rates of 0.1 and 0.2%. Rheological parameters were determined and a texture profile analysis was carried out. Yogurts presented different rheological behaviors according to the treatment used, which could be attributed to structural phenomena. The combined HHP and heat treatment of milks resulted in yogurt gels with higher consistency index values than gels obtained from thermally treated milk. The type of starter culture and inoculation rate, providing different fermentation pathways, also affected the consistency index and textural properties significantly. The combined HHP and heat treatment of milks before fermentation, and an inoculation rate of 0.1% (for both cultures), led to desirable rheological and textural properties in yogurt, which presented a creamy and thick consistency that does not require the addition of stabilizers.

Dielectric and fatigue properties of Pb(Zr0.53Ti0.47)O-3 thin films prepared from oxide precursors method

Fatigue is an important problem to be considered if a ferroelectric film is used for non-volatile memory devices. In this phenomena, the remanent polarization and coercive field properties degrades in cycles which increase in hysteresis loops. The reasons have been attributed to different mechanisms such as a large voltage applied on ferroelectric film in every reading process in Ferroelectric Random Access Memory (FeRAM) or memories for digital storage in computer, grain size effects and others. The aim of this work is to investigate the influence of the crystallization kinetics on dielectric and ferroelectric properties of the Pb(Zr0.53Ti0.47)O-3 thin films prepared by an alternative chemical method. Films were crystallized in air on Pt/Ti/SiO2/Si substrates at 700 degrees C for 1 hour, in conventional thermal annealing (CTA), and at 700 degrees C for 1 min and 700 degrees C 5 min, using a rapid thermal annealing (RTA) process. Final films were crack free and presented an average of 750 nm in thickness. Dielectric properties were studied in the frequency range of 100 Hz - 1 MHz. All films showed a dielectric dispersion at low frequency. Ferroelectric properties were measured from hysteresis loops at 10 kHz. The obtained remanent polarization (P-r) and coercive field (E-c) were 3.7 mu C/cm(2) and 71.9 kV/cm respectively for film crystallized by CTA while in films crystallized by RTA these parameters were essentially the same. In the fatigue process, the P, value decreased to 14% from the initial value after 1.3 x 10(9) switching cycles, for film by CTA, while for film crystallized by RTA for 5 min, P, decreased to 47% from initial value after 1.7 x 10(9) switching cycles.

Influence of temperature on the dielectric and ferroelectric properties of bismuth titanate thin films obtained by the polymeric precursor method

The (1 1 7) and (0 0 1 0)-oriented Bi4Ti3O12 thin films were fabricated on Pt/Ti/SiO2/Si substrates by using a polymeric precursor solution under appropriate crystallization conditions. Atomic force microscopy and scanning electron microscopy showed relatively large grains, which is typical for this system. The capacitance dependence on voltage is strongly non-linear, confirming the ferroelectric properties of the films resulting from the domain switching. The (1 1 7)-oriented films exhibited a higher remanent polarization (23.7 μ C cm(-2)) than the (0 0 1 0)-oriented films (11.8 μ C cm(-2)). Fatigue tests revealed that the temperature of thermal treatment and degree of orientation affect the performance of the device. © 2005 Elsevier B.V. All rights reserved.

Er(3+) doped phosphoniobate glasses and planar waveguides: structural and optical properties

Phosphoniobate glasses with composition (mol%) (100-x) NaPO(3)-xNb(2)O(5) ( x varying from 11 to 33) were prepared and characterized by means of thermal analysis, Fourier transform infrared spectroscopy, Raman scattering and (31)P nuclear magnetic resonance. The addition of Nb(2)O(5) to the polyphosphate base glass leads to depolymerization of the metaphosphate structure. Different colors were observed and assigned as indicating the presence of Nb(4+) ions, as confirmed by electron paramagnetic resonance measurements. The color was observed to depend on the glass composition and melting temperature as well. Er(3+) containing samples were also prepared. Strong emission in the 1550 nm region was observed. The Er(3+4)I(15/2) emission quantum efficiency was observed to be 90% and the quenching concentration was observed to be 1.1 mol%( 1.45 x 10(20) ions cm(-3)). Planar waveguides were prepared by Na(+)-K(+)-Ag(+) ion exchange with Er(3+) containing samples. Optical parameters of the waveguides were measured at 632.8, 543.5 and 1550 nm by the prism coupling technique as a function of the ion exchange time and Ag(+) concentration. The optimized planar waveguides show a diffusion depth of 5.9 mu m and one propagating mode at 1550 nm.

Rietveld refinement, microstructure, conductivity and impedance properties of Ba[Zr0.25Ti0.75]O-3 ceramic

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Ceramic raw materials from the State of Maranhao, Brazil. Part 1: chemical and mineralogical characterization and technological properties of clays from Sao Luis, Rosario, Pinheiro and Mirinzal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Barrier and Mechanical Properties of Clay-Reinforced Polymeric Nanocomposites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Fermi acceleration and scaling properties of a time dependent oval billiard

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)