Bond strength of Epiphany (TM) Sealer combined with different adhesive systems photo-activated with LED and QTH

The Epiphany (TM) Sealer is a new dual-curing resin-based sealer and has been introduced as an alternative to gutta-percha and traditional root canal sealers. The canal filling is claimed to create a seal with the dentinal tubules within the root canal system producing a 'monoblock' effect between the sealer and dentinal tubules. Therefore, considering the possibility to incorporate the others adhesive systems, it is important to study the bond strength of the resulting cement. Forty-eight root mandibular canines were sectioned 8-mm below CEJ. The dentine discs were prepared using a tapered diamond bur and irrigated with 1% NaOCl and 17% EDTA. Previous the application Epiphany (TM) Sealer, the Epiphany (TM) Primer, AdheSE, and One Up Bond F were applied to the root canal walls. The LED and QTH (Quartz Tungsten Halogen) were used to photo-activation during 45 s with power density of 400 and 720 mW/cm(2), respectively. The specimens were performed on a universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The force was recorded and the debonding values were used to calculate Push-out bond strength. The analysis of variance (ANOVA) and Tukey's post-hoc tests showed significant statistical differences (P < 0.05) to Epiphany (TM) Sealer/Epiphany (TM) Primer/QTH and EpiphanyTM Sealer/AdheSE/QTH, which had the highest mean values of bond strength. The efficiency of resin-based filling materials are dependent the type of light curing unit used including the power density, the polymerization characteristics of these resin-based filling materials, depending on the primer/adhesive used.

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS).Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM).Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM.Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

A simplified Fermi Accelerator Model under quadratic frictional force

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Flexural Strength of Four Adhesive Fixed Dental Prostheses of Composite Resin Reinforced with Glass Fiber

Purpose: To evaluate the flexural strength of two fixed dental prosthesis (FDP) designs simulating frameworks of adhesive fixed partial prostheses, reinforced or not by glass fiber.Materials and Methods: Forty specimens, made with composite resin, were divided into 4 groups according to the framework design and the presence of fiber reinforcement: A1 - occlusal support; A2: occlusal support + glass fiber; B1: occlusal and proximal supports; B2: occlusal and proximal supports + glass fiber. The specimens were subjected to the three-point bending test, and the data were submitted to two-way ANOVA and Tukey's test (5%).Results: Group A2 (97.9 +/- 38 N) was statistically significantly different from all other experimental groups, presenting a significantly lower mean flexural strength.Conclusion: The use of glass fibers did not improve the flexural strength of composite resin, and designs with occlusal and proximal supports presented better results than designs simulating only occlusal support.

Does Adhesive Resin Application Contribute to Resin Bond Durability on Etched and Silanized Feldspathic Ceramic?

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Bonding Efficacy of New Self-etching, Self-adhesive Dual-curing Resin Cements to Dental Enamel

Purpose: This study evaluated the efficacy of the union between two new self-etching self-adhesive resin cements and enamel using the microtensile bond strength test.Materials and Methods: Buccal enamel of 80 bovine teeth was submitted to finishing and polishing with metallographic paper to a refinement of #600, in order to obtain a 5-mm(2) flat area. Blocks (2 x 4 x 4 mm) of laboratory composite resin were cemented to enamel according to different protocols: (1) untreated enamel + RelyX Unicem cement (RX group); (2) untreated enamel + Bifix SE cement (BF group); (3) enamel acid etching and application of resin adhesive Single Bond + RelyX Unicem (RXA group); (4) enamel acid etching and application of resin adhesive Solobond M + Bifix SE (BFA group). After 7 days of storage in distillated water at 37 degrees C, the blocks were sectioned for obtaining microbar specimens with an adhesive area of 1 mm(2) (n = 120). Specimens were submitted to the microtensile bond strength test at a crosshead speed of 0.5 mm/min. The results (in MPa) were analyzed statistically by ANOVA and Tu key's test.Results: Enamel pre-treatment with phosphoric acid and resin adhesive (27.9 and 30.3 for RXA and BFA groups) significantly improved (p <= 0.05) the adhesion of both cements to enamel compared to the union achieved with as-polished enamel (9.9 and 6.0 for RX and BF).Conclusion: Enamel pre-treatment with acid etching and the application of resin adhesive significantly improved the bond efficacy of both luting agents compared to the union achieved with as-polished enamel.

Effect of adhesive system type and tooth region on the bond strength to dentin

Purpose: This study evaluated the bond strength of two etch-and-rinse adhesive systems (two- and three-step) and a self-etching system to Coronal and root canal dentin.Materials and Methods: The root canals of 30 human incisors and canines were instrumented and prepared with burs. The posts used for luting were duplicated with dual resin cement (Duo-link) inside Aestheti Plus #2 molds. Thus, three groups were formed (n = 10) according to the adhesive system employed: All-Bond 2 (TE3) + resin cement post (rcp) + Duo-link (DI); One-Step Plus (TE2) + rcp + DI; Tyrian/One-Step Plus (SE) + rcp + DI. Afterwards, 8 transverse sections (1.5 mm) were cut from 4 mm above the CEJ up to 4 mm short of the root canal apex, comprising coronal and root canal dentin. The sections were submitted to push-out testing in a universal testing machine EMIC (1 mm/min). Bond strength data were analyzed with two-way repeated measures ANOVA and Tukey's test (p < 0.05).Results: The relationship between the adhesives was not the same in the different regions (p < 0.05). Comparison of the means achieved with the adhesives in each region (Tukey; p < 0.05) revealed that TE3 (mean standard deviation: 5.22 +/- 1.70) was higher than TE2 (2.60 +/- 1.74) and SE (1.68 +/- 1.85).Conclusion: Under the experimental conditions, better bonding to dentin was achieved using the three-step etch-and-rinse system, especially in the coronal region. Therefore, the traditional etch-and-rinse three-step adhesive system seems to be the best choice for teeth needing adhesive endodontic restorations.

Durability of Microtensile Bond to Nonetched and Etched Feldspar Ceramic: Self-adhesive Resin Cements vs Conventional Resin

Purpose: The objective of this study was to evaluate the effect of thermocycling (TC), self-adhesive resin cements and surface conditioning on the microtensile bond strength (mu TBS) between feldspathic ceramic blocks and resin cements.Materials and Methods: Fifty-six feldspathic ceramic blocks (10 x 7 x 5 mm) (Vita Mark II) were divided into groups according to the factors "resin cement" (3 cements) and "surface conditioning" (no conditioning or conditioning [10% hydrofluoric acid etching for 5 min + silanization]) (n = 8): group 1: conditioning+Variolink II (control group); group 2: no conditioning+Biscem; group 3: no conditioning+RelyX U100; group 4: no conditioning+Maxcem Elite; group 5: conditioning+Biscem; group 6: conditioning+RelyX U100; group 7: conditioning+Maxcem Elite. The ceramic-cement blocks were sectioned to produce non-trimmed bar specimens (adhered cross-sectional area: 1 +/- 0.1 mm(2)), which were divided into two storage conditions: dry, mu TBS immediately after cutting; TC (12,000x, 5 degrees C/55 degrees C). Statistical significance was deterimined using two-way ANOVA (7 strategies and 2 storage conditions) and the post-hoc Tukey test (p<0.05).Results: Resin cement and thermocycling affected the mu TBS significantly (p = 0.001). In the dry condition, group 5 (18 +/- 6.5 MPa) presented the lowest values of mu TBS when compared to the other groups. TC decreased the mean mu TBS values significantly (p<0.05) for all resin cements tested (9.7 +/- 2.3 to 22.1 +/- 6.3 MPa), except for the resin cement RelyX U100 (22.1 +/- 6.3 MPa). In groups 3 and 4, it was not possible to measure mu TBS, since these groups had 100% pre-test failures during sectioning. Moreover, the same occurred in group 2 after TC, where 100% failure was observed during thermocycling (spontaneous failures).Conclusion: Hydrofluoric acid etching and silanization of the feldspathic ceramic surface are essential for bonding self-adhesive resin cement to a feldspathic ceramic, regardless of the resin cement used. Non-etched ceramic is not recommended.

The adhesive system and root canal region do not influence the degree of conversion of dual resin cement

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In Vitro Antibacterial Activity of Adhesive Systems on Streptococcus Mutans

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond strengths, degree of conversion of the cement and molecular structure of the adhesive-dentine joint in fibre post restorations

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of Application Methods of Self-etching Adhesive Systems on Adhesive Bond Strength to Dentin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of Self-Etching Adhesive Systems Used in the Dental Modelling Technique on the Cohesive Strength of Composite Resin

This study evaluated the cohesive strength of composite using self-etching adhesive systems (SE) in the lubrication of instruments between layers of composite. The specimens were made by using a Teflon (R) device. SE were used at the interface to lubricate the instruments: Group 1(G1) - control group, no lubricant was used; Group 2(G2) -Futurabond (R) M; Group 3(G3) - Optibond (R) All-In-One; Group 4(G4) - Clearfil (R) SE Bond; Group 5(G5) - Futurabond (R) NR; Group 6(G6) - Adper (R) SE Plus; Group 7(G7) - One Up Bond (R) F. Specimens were submitted to the tensile test to evaluate the cohesive strength. Data were submitted to the ANOVA and Tukey tests. ANOVA showed a value of p = 0.00. The average means (SD): G2 = 11.33(+/-3.44) a, G3 = 15.36(+/-4.06) ab, G4 = 18.9(+/-4.72) bc, G7 = 19.62(+/-4.46) bc, G5 = 21.02(+/-5.09) bc, G6 = 23.39(+/-4.17) cd, and G1 = 28.49(+/-2.89) d. All SE decreased the cohesive strength of the composite, except for Adper (R) SE Plus.

Microtensile bond strengths and scanning electron microscopic evaluation of self-adhesive and self-etch resin cements to intact and etched enamel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)