Effect of Cement Shade and Light-curing Unit on Bond Strength of a Ceramic Cemented to Dentin

Purpose: To evaluate the effect of cement shade, light-curing unit, and water storage on tensile bond strength (a) of a feldspathic ceramic resin bonded to dentin.Materials and Methods: The dentin surface of 40 molars was exposed and etched with 37% phosphoric acid, then an adhesive system was applied. Forty blocks of feldspathic ceramic (Vita VM7) were produced. The ceramic surface was etched with 10% hydrofluoric acid for 60 s, followed by the application of a silane agent and a dual-curing resin cement (Variolink II). Ceramic blocks were cemented to the treated dentin using either A3 or transparent (Tr) shade cement that was activated using either halogen or LED light for 40 s. All blocks were stored in 37 degrees C distilled water for 24 h before cutting to obtain non-trimmed bar-shaped specimens (adhesive area = 1 mm(2) +/- 0.1) for the microtensile bond strength test. The specimens were randomly grouped according to the storage time: no storage or stored for 150 days in 37 degrees C distilled water. Eight experimental groups were obtained (n = 30). The specimens were submitted to the tensile bond strength test using a universal testing machine at a crosshead speed of 1 mm/min. The data were statistically analyzed using ANOVA and Tukey's post-hoc tests (alpha = 0.05).Results: The mean bond strength values were significantly lower for the corresponding water stored groups, except for the specimens using A3 resin cement activated by halogen light. There was no significance difference in mean bond strength values among all groups after water storage.Conclusion: Water storage had a detrimental effect under most experimental conditions. For both cement shades investigated (Tr and A3) under the same storage condition, the light-curing units (QTH and LED) did not affect the mean microtensile bond strengths of resin-cemented ceramic to dentin.

Marginal leakage in Class V cavities pretreated with different laser energy densities

The purpose of the present study was to evaluate in vitro the degree of marginal leakage in Class V cavities involving the cementoenamel junction. Cavities were 4 rum wide and 2 mm deep. The specimens received dentin pretreatment (37% phosphoric acid) followed by the Single Bond (3M) adhesive system application. The 40 specimens were then divided into four groups: Group I (control); Group 2 (Nd:YAG laser at 120 mJ/pulse, frequency of 10 Hz, power of 1.2 W); Group 3 (Nd:YAG laser at 140 mJ/pulse, frequency of 10 Hz, power of 1.4 W); Group 4 (Nd:YAG laser at 160 mJ/pulse, frequency of 10 Hz, power of 1.6 W). The cavities were restored with Z100 composite resin (3M) and light cured at 300-600 mW/cm(2) light intensity. Specimens were thermocycled to 500 cycles from 2-50 degrees C. After that, they were dried and sealed with nail varnish, respecting 1 mm around the restorations, and immersed in 0.5% methylene blue solution for 4 h. After this period, the teeth were rinsed, dried, sectioned, and analyzed in a stereoscopic loupe. The highest leakage scores were considered for each specimen. The results were statistically analyzed by the analysis of variance (ANOVA) Kruskal-Wallis test to the 5% level. For both the enamel and cementum, there was a decrease in marginal leakage with the application of laser energy; no significant differences were observed for Groups 2, 3, and 4. The results also showed a smaller tendency to marginal leakage on the cementum than on the enamel.

In vitro evaluation of apical sealing in root apex treated with demineralization agents and retrofiled with mineral trioxide aggregate through marginal dye leakage

O objetivo deste estudo foi avaliar o selamento de ápices radiculares tratados com diferentes agentes desmineralizantes e retrobturados com agregado de trióxido mineral (MTA), mediante infiltração marginal por corante. Cinqüenta e seis dentes unirradiculares humanos extraídos foram instrumentados, obturados e seccionados apicalmente. Os preparos cavitários apicais foram confeccionados com pontas ultra-sônicas e os agentes desmineralizantes foram aplicados previamente à retrobturação com Pro Root MTA. Os espécimes foram divididos aleatoriamente em 4 grupos (n=14): grupo 1 (sem agente desmineralizante); grupo 2 (ácido fosfórico 35% durante 15 s); grupo 3 (solução de EDTA 17%, pH 7, durante 3 min); grupo 4 (gel de EDTA 24%, pH 7, durante 4 min). A extensão da infiltração de corante (rodamina B 2% a 37°C, por 24 h) foi avaliada em milímetros utilizando-se um estereomicroscópio. Os resultados foram analisados estatisticamente por meio de análise de variância a um critério e do teste Tukey com nível de significância de 5%. Dentre os grupos experimentais, a menor extensão de infiltração do corante foi verificada no grupo 1 (1,89 mm), seguido pelos grupos 2 (2,18 mm), 4 (2,54 mm) e 3 (2,64 mm). Não houve diferenças estatisticamente significante (p>0.05) na infiltração marginal pelo corante entre os grupos 1, 2 e 4 e os grupos 2, 3 e 4. Com base nos resultados obtidos, pode-se concluir que a aplicação de agentes desmineralizantes não pode ser recomendada quando da utilização do MTA em cirurgias parendodônticas.

In vitro evaluation of dental bleaching effectiveness using hybrid lights activation

OBJETIVO: Avaliar se fontes de luz aumentam a eficácia do peróxido de hidrogênio na técnica de clareamento profissional. METODOLOGIA: Foram empregados 60 dentes incisivos bovinos, com dimensões coronárias e radiculares padronizadas a partir do limite amelo-cementário, sendo descartada a porção lingual. Os corpos-de-prova (cp) foram limpos em ultra-som por 20 min e a dentina condicionada com H3PO4 a 38% por 15 s, sendo os (cp) imersos em solução de café solúvel a 25% por duas semanas. A dentina foi impermeabilizada com esmalte e os (cp) divididos em 5 grupos, sendo a cor inicial mensurada através do espectofotômetro-EasyShade (VITA). Todos os (cp) receberam três aplicações por 10 min do gel clareador Opalescence Xtra-Boost (Ultradent) conforme segue: Grupo 1 - controle, não recebeu fotoativação, Grupo 2 - ativado com luz halôgena, Grupo 3 - ativado com LED azul/LASER, Grupo 4 - ativado com LED verde/LASER e Grupo 5 - ativado com LED vermelho. Após o clareamento foi mensurada a variação de cor E, a*, b*e L* e as referentes à escala de cor Vita Clássico. Os dados foram submetidos à análise de variância, teste de Tukey e de Dunn (α=5%). RESULTADOS: A diferença geral da cor foi reduzida quando se empregou LED Azul e Luz Halógena, sendo que o desempenho do peróxido de hidrogênio a 38% foi intensificado dependendo da fonte de luz utilizada. A avaliação quantitativa de cor, obtida por espectrofotômetro e pela escala de cor Vita Clássico, foram coincidentes. CONCLUSÃO: O tipo de fonte de luz empregada interfere na eficácia do agente clareador.

Microtensile bond strengths and scanning electron microscopic evaluation of self-adhesive and self-etch resin cements to intact and etched enamel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of silica coating combined to a MDP-based primer on the resin bond to Y-TZP ceramic

The aim of this study was to evaluate the influence of silica coating and 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based primer applications upon the bonding durability of a MDP-based resin cement to a yttrium stabilized tetragonal zirconia (Y-TZP) ceramic. Ninety-six Y-TZP tabs were embedded in an acrylic resin (free surface for adhesion: 5 x 5 mm(2)), ground finished and randomly divided into four groups (N = 24) according to the ceramic surface conditioning: (1) cleaning with isopropanol (ALC); (2) ALC + phosphoric acid etching + MDP-based primer application (MDP-primer); (3) silica coating + 3-methacryloyloxypropyl trimethoxysilane (MPS)-based coupling agent application (SiO(2) + MPS-Sil); and (4) SiO(2) + MDP-primer. The MDP-based resin cement was applied on the treated surface using a cylindrical mold (diameter=3 mm). Half of the specimens from each surface conditioning were stored in distilled water (37 C, 24 h) before testing. Another half of the specimens were stored (90 days) and thermo-cycled (12,000x) during this period (90d/TC) before testing. A shear bond strength (SBS) test was performed at a crosshead speed of 0.5 mm/min. Two factors composed the experimental design: ceramic conditioning strategy (in four levels) and storage condition (in two levels), totaling eight groups. After 90d/TC (Tukey; p < 0.05), SiO(2) + MDP-primer (24.40 MPa) promoted the highest SBS. The ALC and MDP-primer groups debonded spontaneously during 90d/TC. Bonding values were higher and more stable in the SiO2 groups. The use of MDP-primer after silica coating increased the bond strength. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part 8: Appl Biomater 95B: 69-74, 2010.

Desenvolvimento de biocerâmicas porosas de hidroxiapatita para utilização como scaffolds para regeneração óssea

Biocerâmicas porosas tem aplicações biomédicas importantes como preenchimento de defeitos ósseos e scaffolds na engenharia de tecidos. A hidroxiapatita (HA, Ca10(PO4)6(OH)2) que apresenta semelhança química e estrutural com a fase mineral dos ossos e dos dentes, é biocompatível e osteocondutiva, e tem excelente afinidade química e biológica com os tecidos ósseos. Este trabalho teve como objetivo desenvolver biocerâmicas porosas HA para utilização como scaffold para regeneração óssea empregando-se a técnica de réplica da esponja polimérica. A pasta biocerâmica de HA foi obtida por via úmida utilizando hidróxido de cálcio [Ca(OH)2] e ácido fosfórico (H3PO4) e impregnada em esponjas de poliuretano com diferentes densidades. Tratamento térmico a 600°C por 1h foi realizado para eliminação da esponja seguido da sinterização a 1100°C por 2 horas. Os scaffolds apresentaram a HA como fase majoritária, elevada porosidade (> 70%) e poros com tamanhos variando na ordem de macro (>100μm) e microporosidade (1-20μm), sendo estes fatores adequados para a aplicação como scaffolds para regeneração óssea.

Síntese de hidroxiapatita pelo método sol-gel utilizando precursores alternativos: nitrato de cálcio e ácido fosfórico

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Determinação espectrofotométrica de ácido glicólico com ácido cromotrópico assistida por forno de microondas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal, structural and optical properties of new tungsten lead-pyrophosphate glasses

Crystalline lead-pyrophosphate precursor was prepared in aqueous solution from lead nitrate and phosphoric acid and characterized by X-ray diffraction, thermogravimetry and Raman scattering. This crystalline lead-phosphate was then used to prepare glass samples in the binary system Pb(2)P(2)O(7)-WO(3). Dependence of WO(3) content on thermal, structural and optical properties were investigated by thermal analysis (DSC), Raman spectroscopy, UV-visible and near-infrared absorption and M-Line technique to access refractive index values. Incorporation of WO(3) in the lead-pyrophosphate matrix enhances the glass transition temperature and thermal stability against devitrification, favors formation of P-O-W bonds and WO(6) clusters. In addition, optical properties are strongly modified with a redshift of the optical bandgap with WO(3) incorporation as well as an increase of the refractive index from 1.89 to 2.05 in the visible. (C) 2011 Elsevier B.V. All rights reserved.

Determinação espectrofotométrica de hexametilenotetramina (HMT) em medicamentos, utilizando ácido cromotrópico e forno de micro-ondas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A pH optode based on thymol blue: application to determination of CO2 using flow injection analysis system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Teor de fósforo e pH no bulbo molhado, com diferentes freqüências de fertirrigação, utilizando ácido fosfórico

A aplicação de fertilizantes fosfatados, tais como superfosfofato simples, superfosfofato triplo e monofosfato de amônio, via gotejamento, pode apresentar incrustações nas canalizações e obstruções de emissores. No presente trabalho, realizado na UNESP/Jaboticabal - SP, estudaram-se a distribuição do fósforo e a sua influência sobre o pH e a umidade em Latossolo Vermelho, fertirrigado durante um mês, com cinco aplicações semanais de ácido fosfórico. Utilizaram-se quatro repetições e oito tratamentos, constituídos da combinação de doses de P2O5 (0 e 50 kg ha-1) e freqüências de aplicação de 1; 3; 5 e 7 dias. Pelos resultados obtidos, observou-se que a freqüência de irrigação ou de fertirrigação não influenciou na distribuição final da umidade no bulbo molhado; aplicando-se o ácido fosfórico, o pH do solo até 30 cm do gotejador e até 40 cm em profundidade foi reduzido, atingindo valor de 3,6, e o teor de fósforo foi maior nessa mesma porção do bulbo, ultrapassando 1.500 mg dm-3. Isso permite indicar que o ácido fosfórico pode ser utilizado em irrigação localizada, com controle do pH do solo, pois sua redução influencia no desenvolvimento das culturas e, conseqüentemente, na produtividade.

OBSERVATIONS on ETCHED ENAMEL IN NON-ERUPTED DECIDUOUS MOLARS: A SCANNING ELECTRON MICROSCOPIC STUDY

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effects of a non-rinse conditioner on the enamel of primary teeth

O objetivo deste estudo in vitro foi de avaliar ao microscópio eletrônico de varredura os aspectos morfológicos do esmalte de dentes decíduos após condicionamento com ácido fosfórico a 36% ou com um agente condicionador não lavável. Foram selecionados 10 dentes decíduos anteriores esfoliados naturalmente. As amostras sofreram limpeza coronária com pasta de pedra-pomes e água, em baixa-velocidade. O condicionamento foi realizado no esmalte da face vestibular. Os espécimes foram divididos em dois grupos: G1 (n=10): condicionamento com ácido fosfórico a 36% na forma de gel - Conditioner 36 (Dentsply) durante 20 segundos, seguidos de lavagem com água durante 15 segundos; G2 (n=10): condicionamento com NRC - Non Rinse Conditioner (Dentsply) durante 20 segundos, seguidos de secagem com ar durante 15 segundos. As amostras foram desidratadas, montadas em bases metálicas e cobertas com ouro para análise ao microscópio eletrônico de varredura (Jeol JSM 6.100). A análise da eletromicrografias revelou que ambos os agentes condicionadores foram efetivos para condicionar o esmalte de dentes decíduos, causando microporosidades mas com melhor resultado quando utilizou-se o ácido fosfórico a 36% na forma de gel.