Continuous and gradual photo-activation methods: influence on degree of conversion and crosslink density of composite resins

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Bond strength of Epiphany (TM) Sealer combined with different adhesive systems photo-activated with LED and QTH

The Epiphany (TM) Sealer is a new dual-curing resin-based sealer and has been introduced as an alternative to gutta-percha and traditional root canal sealers. The canal filling is claimed to create a seal with the dentinal tubules within the root canal system producing a 'monoblock' effect between the sealer and dentinal tubules. Therefore, considering the possibility to incorporate the others adhesive systems, it is important to study the bond strength of the resulting cement. Forty-eight root mandibular canines were sectioned 8-mm below CEJ. The dentine discs were prepared using a tapered diamond bur and irrigated with 1% NaOCl and 17% EDTA. Previous the application Epiphany (TM) Sealer, the Epiphany (TM) Primer, AdheSE, and One Up Bond F were applied to the root canal walls. The LED and QTH (Quartz Tungsten Halogen) were used to photo-activation during 45 s with power density of 400 and 720 mW/cm(2), respectively. The specimens were performed on a universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The force was recorded and the debonding values were used to calculate Push-out bond strength. The analysis of variance (ANOVA) and Tukey's post-hoc tests showed significant statistical differences (P < 0.05) to Epiphany (TM) Sealer/Epiphany (TM) Primer/QTH and EpiphanyTM Sealer/AdheSE/QTH, which had the highest mean values of bond strength. The efficiency of resin-based filling materials are dependent the type of light curing unit used including the power density, the polymerization characteristics of these resin-based filling materials, depending on the primer/adhesive used.

Effects of Surface Hydration and Application Method on the Bond Strength of Self-Etching Adhesives to Dentin

The effect of application methods and dentin hydration on the bond strength of three self-etching adhesives (SEA) were evaluated; 195 extracted bovine incisors were used. The buccal surface was ground in order to expose the dentin, which remained 2-mm minimum thickness, measured by a thickness meter through an opening on the lingual surface. Adper Single Bond 2 (TM) was used for the control group. The SEA were applied following two modes of application: passive or active and two hydration states of the dentin surface-dry and wet. After light-curing, composite buildups were made using Grandio (TM) composite. The specimens were sectioned and tested with a microtensile bond strength test. The application method and the hydration state resulted in statistical differences (p = 0.000) making the values of active application for mu TBS to dentin higher than passive application. The wet surfaces showed higher mu TBS to dentin ratios than dry surfaces. There were no statistical differences in mu TBS among the SEA tested but there were differences regarding to control group.

Microdureza de resinas em função da cor e luz halógena

O objetivo desse trabalho foi avaliar a influência da intensidade da luz e cor de uma resina composta no grau de dureza Knoop. Corpos-de-prova foram confeccionados utilizando-se matrizes de poliéster envoltas por um anel de cobre, contendo uma cavidade padronizada de 6 mm de diâmetro por 2 mm de espessura. Estas cavidades foram preenchidas com resina composta selecionada, Fill Magic - Vigodent, com as cores A3, B3, C3, D3 e I, fotopolimerizadas através de um fotopolimerizador Elipar, calibrado para produzir 3 intensidades de luz diferentes: 450 mW/cm², 800 mW/cm² e uma intensidade de luz crescente de 100 a 800 mW/cm². Foram confeccionados 90 corpos-de-prova em que o tempo de exposição da resina à luz halógena foi de 40 s. As amostras foram armazenadas em tubos de ensaio com água destilada a 37 ± 1ºC. Após este período, foram realizados os testes de dureza Knoop na região de superfície e fundo. Os resultados mostraram que houve diferença estatística em relação a intensidade de luz, entretanto em relação a cor, não houve diferença estatística. Os autores concluíram que a cor do compósito não influencia a dureza Knoop e que a intensidade progressiva promoveu os melhores resultados de dureza Knoop.

Effect of radiotherapy on the radiopacity and flexural strength of a composite resin.

The aim of this study was to evaluate the effect of radiotherapy on the radiopacity and flexural strength of composite resin. Forty Z250 composite resin specimens were polymerized using a halogen light-curing unit and divided into 5 groups, in accordance with the radiotherapy dose: G1- without irradiation, G2- 30 Gy, G3- 40 Gy, G4- 50 Gy and GS- 60 Gy Digital images were obtained using a GE 100 X-ray. Radiopacity values were obtained with the Digora digital imaging system and the flexural strength was evaluated with an EMIC universal testing machine. Data were submitted to ANOVA and Tukey 's test. G1 presented the highest radiopacity value, followed by G3, G5, G4 and G2. For flexural strength, G1 presented the lowest value, followed by G2, G5, G3 and G4. Differences were no significant (p>0.05). The commonly used dosage of radiotherapy treatment, did not cause alteration in the radiopacity and flexural strength of resin-based composites.

Influência da fotopolimerização e da cor da resina composta na microdureza

Objective: To study the influence of color opacity and light-curing systems (halogen light vs blue LED) on the microhardness of a composite resin. Methods: Esthet-X composite resin (Dentsply), shades A2 and A2-O, was inserted in a stainless steel matrix (5 mm diameter and 2 mm deep) and was light cured for 40 seconds with a halogen light source (XL 3000; 3M/ESPE) or a blue LED (Optilight LD II; Gnatus). Eight groups of 15 specimens each were formed, and were further divided according to the light-curing systems, the exposed area (base and surface), and the opacity of the composite resin, producing 120 specimens. The specimens were next stored in distilled water for 24 hours, embedded in a chemically activated acrylic resin, then subjected to finishing and polishing with sandpaper and felt discs. Microhardness was measured with a Vickers Digital Microhardness meter, with a 50 g load for 30 seconds. The obtained microhardness means were analyzed by ANOVA and Tukey's multiple-comparison test at 5% significance level. Results: The surface microhardness was always greater than the base microhardness, regardless of the light-curing source. The halogen light lamp produced significantly higher composite resin microhardness means than the blue LED (57.61 vs. 42.53 HV) (p<0.05). Statistically significant differences (p<0.05) were obtained between the microhardness means for the different composite opacities; lowest microhardness in depth was produced by the A2-O shade. Conclusion: Composite resin opacity as well as the light-curing system influenced the microhardness of the material.

Bond strength of a composite resin to an adhesive luting cement

This study evaluated the influence of surface treatment on the shear bond strength of a composite resin (CR), previously submitted to the application of a temporary cement (TC), to an adhesive luting cement. Eight-four CR cylinders (5 mm diameter and 3 mm high) were fabricated and embedded in acrylic resin. The sets were divided into 6 groups (G1 to G6) (n=12). Groups 2 to 6 received a coat of TC. After 24 h, TC was removed and the CR surfaces received the following treatments: G2: ethanol; G3: rotary brush and pumice; G4: air-abrasion; G5: air-abrasion and adhesive system; G6: air-abrasion, acid etching and adhesive system. G1 (control) did not receive TC or any surface treatment. The sets were adapted to a matrix and received an increment of an adhesive luting cement. The specimens were subjected to the shear bond strength test. ANOVA and Tukey's tests showed that G3 (8.53 MPa) and G4 (8.63 MPa) differed significantly (p=0.001) from G1 (13.34 MPa). The highest mean shear bond strength values were found in G5 (14.78 MPa) and G6 (15.86 MPa). Air-abrasion of CR surface associated with an adhesive system provided an effective bond of the CR to the adhesive luting cement, regardless the pre-treatment with the phosphoric acid.

The effects of exposure time on the surface microhardness of three dual-cured dental resin cements

This study evaluated the exposure time of light-curing of the polymers used for cementation on microhardness test in different storage times. The polymers (specifically called resin cements) were RelyX ARC, RelyX U100, and SET. Five specimens of each group were prepared and photo-polymerized with exposure times of 20 s and 180 s, using a LED polymerization unit with wavelength of 440 ~ 480 nm and light output was consistently 1,500 mW/cm2. The Vickers hardness test was performed in a MMT-3 Microhardness Tester. Data were submitted to ANOVA and Tukey's test (α = 0.05). The values of RelyX ARC showed statistically significant difference to groups with light exposure when considering only chemical cure (p < 0.05). The groups with light exposure (20 s and 180 s) showed no significant difference between them (p > 0.05). The RelyX U100 cured only chemically showed statistically significant difference between 48 h and 7 days (p < 0.05). The SET resin cement showed no significant difference to groups without light exposure for all storage times (p > 0.05). The values of hardening of the dual-cured resin cements improved after setting by light and chemical activation demonstrating the importance of light curing. © 2011 by the authors.

Degree of conversion of polymer-matrix composite assessed by FTIR analysis

Aims and objectives: The behavior of polymer-matrix composite is dependent on the degree of conversion. The aim of this study was to evaluate the degree of conversion of two resin cements following storage at 37°C immediately, 24 and 48 hours, and 7 days after light-curing by FTIR analysis. Materials and methods: The specimens were made in a metallic mold and cured with blue LED with power density of 500 mW/cm2 for 30 seconds. The specimens were pulverized, pressed with KBr and analyzed with FTIR following storage times. Statistical analysis used: ANOVA (two-way) and Tukey's post hoc. Results: To the polymer-matrix composites between 24 and 48 hours does not show a significant increase (p > 0.05), however, the highest values were found after 7 days. Conclusion: The polymer-matrix composites used in this study showed similarity on the degree of conversion and increased of according to the time of storage.

Hipomineralização molar incisivo em escolares de Botelhos, Minas Gerais, Brasil

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação de LEDs de alta intensidade quanto à eficiência de polimerização de resina composta e variação de temperatura na dentina bovina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da microdureza superficial da resina composta fotopolimerizada por aparelho de luz halógena e de diodo(LED) em função de opacidade e ação do flúor fosfato acidulado

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência do sistema de cimentação adesiva e da fonte de luz fotoativadora na resistência à extrusão de pinos de fibra de vidro

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência da temperatura sobre a microdureza de uma resina composta fotoativada com luz halógena e Leds

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)