Influence of the Light-Curing Unit, Storage Time and Shade of a Dental Composite Resin on the Fluorescence

The aim of this study was to determine the influence of three light-curing units, storage times and colors of the dental composite resin on the fluorescence. The specimens (diameter 10.0 +/- 0.1 mm, thickness 1.0 +/- 0.1 mm) were made using a stainless steel mold. The mold was filled with the microhybrid composite resin and a polyethylene film covered each side of the mold. After this, a glass slide was placed on the top of the mold. To standardize the top surface of the specimens a circular weight (1 kg) with an orifice to pass the light tip of the LCU was placed on the top surface and photo-activated during 40 s. Five specimens were made for each group. The groups were divided into 9 groups following the LCUs (one QTH and two LEDs), storage times (immediately after curing, 24 hours, 7 and 30 days) and colors (shades: A(2)E, A(2)D, and TC) of the composite resin. After photo-activation, the specimens were storage in artificial saliva during the storage times proposed to each group at 37 C and 100% humidity. The analysis of variance (ANOVA) and Tukey's post-hoc tests showed no significant difference between storage times (immediately, 24 hours and 30 days) (P > 0.05). The means of fluorescence had difference significant to color and light-curing unit used to all period of storage (P < 0.05). The colors had difference significant between them (shades: A2D < A2E < TC) (P < 0.05). The Ultraled (LED) and Ultralux (QTH) when used the TC shade showed higher than Radii (LED), however to A2E shade and A2D shade any difference were found (P > 0.05).

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS).Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM).Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM.Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

Low-Level Laser Therapy and Calcitonin in Bone Repair: Densitometric Analysis

The aim of this work was to evaluate the association of low-level laser therapy (LLLT, 830 nm) and calcitonin in bone repair considering that bone healing remains a challenge to health professionals. Calcitonin has antiosteoclastic action and LLLT is a treatment that uses low-level lasers or light-emitting diodes to alter cellular function. Both are used to improve bone healing. Densitometry is a clinical noninvasive valuable tool used to evaluate bone mineral density (BMD). Sixty male rats were submitted to bone defect with a trephine bur, randomly divided into four groups of 15 animals each: control (C); synthetic salmon calcitonin (Ca); LLLT (La); LLLT combined with calcitonin (LaCa). Animals from Ca and LaCa received 2UI/Kg synthetic salmon calcitonin intramuscularly on alternate days after surgery. Animals from groups La and LaCa were treated with infrared LLLT (830 nm, 10mW, 20 J/cm(2), 6 s, contact mode). Five animals from each group were euthanized 7, 14, and 21 days after surgery and bone defects were analyzed by densitometry. Statistical analysis showed a significant difference in BMD values in LaCa group at 7 and 21 days (P = 0, 005). The results of the densitometric study showed that LLLT (830 nm) combined with calcitonin improved bone repair.

Marginal leakage in Class V cavities pretreated with different laser energy densities

The purpose of the present study was to evaluate in vitro the degree of marginal leakage in Class V cavities involving the cementoenamel junction. Cavities were 4 rum wide and 2 mm deep. The specimens received dentin pretreatment (37% phosphoric acid) followed by the Single Bond (3M) adhesive system application. The 40 specimens were then divided into four groups: Group I (control); Group 2 (Nd:YAG laser at 120 mJ/pulse, frequency of 10 Hz, power of 1.2 W); Group 3 (Nd:YAG laser at 140 mJ/pulse, frequency of 10 Hz, power of 1.4 W); Group 4 (Nd:YAG laser at 160 mJ/pulse, frequency of 10 Hz, power of 1.6 W). The cavities were restored with Z100 composite resin (3M) and light cured at 300-600 mW/cm(2) light intensity. Specimens were thermocycled to 500 cycles from 2-50 degrees C. After that, they were dried and sealed with nail varnish, respecting 1 mm around the restorations, and immersed in 0.5% methylene blue solution for 4 h. After this period, the teeth were rinsed, dried, sectioned, and analyzed in a stereoscopic loupe. The highest leakage scores were considered for each specimen. The results were statistically analyzed by the analysis of variance (ANOVA) Kruskal-Wallis test to the 5% level. For both the enamel and cementum, there was a decrease in marginal leakage with the application of laser energy; no significant differences were observed for Groups 2, 3, and 4. The results also showed a smaller tendency to marginal leakage on the cementum than on the enamel.

The Effectiveness of Low-Intensity Red Laser for Activating a Bleaching Gel and Its Effect in Temperature of the Bleaching Gel and the Dental Pulp

Statement of the Problem: The effectiveness of low-intensity red laser for activating a bleaching gel and its effect in pulp temperature was not investigated in dental literature. Purpose: The objective of this study was to assess the effectiveness of low-intensity red laser for activating a bleaching gel, as well as its effect in temperature of the bleaching gel and the dental pulp. Materials and Methods: Forty extracted bovine teeth were immersed in a solution of coffee 14 days for darkening. The initial colors were recorded by spectrophotometric analysis. The specimens were randomly distributed into two groups (N = 20): the control, which did not receive light and the experimental group that received light from an appliance fitted with three red light-emitting laser diodes (? = 660 nm). A green-colored, 35% H2O2based bleaching gel was applied for 30 minutes, and changed three times. After bleaching, the colors were again measured to obtain the L*a*b* values. Color variation was calculated (?E) and the data submitted to the non-paired t-test (5%). To assess temperature, 10 human incisors were prepared, in which one thermocouple was placed on the bleaching gel applied on the surface of the teeth and another inside the pulp chamber. Results: There was a significant difference between the groups (p = 0.016), and the experimental group presented a significantly higher mean variation (7.21 +/- 2.76) in comparison with the control group (5.37 +/- 1.76). There was an increase in pulp temperature, but it was not sufficient to cause damage to the pulp. Conclusion: Bleaching gel activation with low-intensity red laser was capable of increasing the effectiveness of bleaching treatment and did not increase pulp temperature to levels deleterious to the pulp. CLINICAL SIGNIFICANCE The application of a low-intensity red laser was effective for activating a bleaching gel with green dye, without any deleterious increases in pulpal temperature. (J Esthet Restor Dent 24:126134, 2012)

Enhanced multiwavelength holographic profilometry by laser mode selection

A method for improving the accuracy of surface shape measurement by multiwavelength holography is presented. In our holographic setup, a Bi12TiO20 photorefractive crystal was the holographic recording medium, and a multimode diode laser emitting in the red region was the light source in a two-wave mixing scheme. on employing such lasers the resulting holographic image appears covered with interference fringes corresponding to the object relief, and the interferogram spatial frequency is proportional to the diode laser's free spectral range (FSR). Our method consists in increasing the effective free spectral range of the laser by positioning a Fabry-Perot etalon at the laser output for mode selection. As larger effective values of the laser FSR were achieved, higher-spatial-frequency interferograms were obtained and therefore more sensitive and accurate measurements were performed. The quantitative evaluation of the interferograms was made through the phase-stepping technique, and the phase map unwrapping was carried out through the cellular-automata method. For a given surface, shape measurements with different interferogram spatial frequencies were performed and compared with respect to measurement noise and visual inspection. (c) 2007 Society of Photo-Optical Instrumentation Engineers.

Non-Hermitian multichannel theory of ultracold collisions modified by intense light fields tuned to the red of the trapping transition

We develop a systematic scheme to treat binary collisions between ultracold atoms in the presence of a strong laser field, tuned to the red of the trapping transition. We assume that the Rabi frequency is much less than the spacing between adjacent bound-state resonances, In this approach we neglect fine and hyperfine structures, but consider fully the three-dimensional aspects of the scattering process, up to the partial d wave. We apply the scheme to calculate the S matrix elements up to the second order in the ratio between the Rabi frequency and the laser detuning, We also obtain, fur this simplified multichannel model, the asymmetric line shapes of photoassociation spectroscopy, and the modification of the scattering length due to the light field at low, but finite, entrance kinetic energy. We emphasize that the present calculations can be generalized to treat more realistic models, and suggest how to carry out a thorough numerical comparison to this semianalytic theory. [S1050-2947(98)04902-6].

Estudo Comparativo de Juntas Soldadas a TIG e Laser Empregando-se Ti com Pureza Comercial Utilizado em Prótese sobre Implantes

Welding in the dentistry has been used for great part of the specialized dentist-surgeons in the implants area to solve prosthesis supported by implant adaptation problems. The development of new equipments Laser and TIG allowed a larger use of these processes in the prosthesis production. In this work, it was studied welded joints made by Laser and TIG, using commercial purity titanium, cpTi, applied in prosthesis supported by implants. The weld characterizations were carried out by light microscopy, EDS_elementary mapping, microhardness and tensile test. Through metallographic characterization, the weld bead presented a martensitic microstructure in the Laser welding process, originated from shear provoked by deformations in the lattice. This caused structural changes of the transformed area, which determines a fine plate-like morphology. In the weld bead from TIG, besides presenting higher hardness, was observed formation of Widmansttaten structure, which is characteristic of a geometric model, resulted of new phase formation along of the crystallographic plans. The martensitic structure is more refined than Widmansttaten structure, due to the high-speed cooling (10(3)degrees C/s) imposed by the Laser process.

Comparative ablation rate from a Er : YAG laser on enamel and dentin of primary and permanent teeth

This study was conducted to analyze the ablation rate and micromorphological aspects of microcavities in enamel and dentin of primary and permanent teeth using a Er:YAG laser system. Micromorphological evaluation has been performed in terms of permanent teeth; however, little information about Er: YAG laser interaction with primary teeth can be found in the literature. Because children have been the most beneficiary patients with laser therapy in our offices, it is extremely necessary to compare the effects of this kind of laser system on the enamel and dentin of permanent and primary teeth. In this study, we used eleven intact primary anterior exfoliated teeth and six extracted permanent molar teeth. We used a commercial laser system: a Er: YAG Twin Light laser system (Fotona Medical Lasers, Slovenia) at 2940 nm, changing average energy levels per pulse ( 100, 200, 300, and 400 mJ) producing 48 microcavities in enamel and dentin of primary and permanent teeth. Primary teeth are more easily ablated than are permanent teeth, when related to enamel or dentin. However, while this laser system is capable of slowly revealing the enamel's microstructure, in dentin only the lowest laser energies permit this kind of observation, more easily decomposing the original tissue aspect, when related to primary or permanent teeth. Statistically, the only different factor at the 5% level was an energy per pulse of 400 mJ, confirming the results found in SEM. Our results showed that dentin in both primary and permanent teeth is less resistant to Er: YAG laser ablation; this fact is easily observed under SEM observation and through the ablation rate evaluation.

Laser weld: microstructure and corrosion study of Ag-Pd-Au-Cu alloy of the dental application

The laser Welding process was introduced into dentistry by the end of the 1980s, resulting on a great impulse to that area with the development of cheaper and smaller equipment, using simpler technique. This allowed greater use of that process on the confection of prostheses compared to the brazing process since the heat source for that process is a concentrated light beam of high power, which minimizes distortion problems on the prosthetic pieces. Ag-Pd-Au-Cu alloy used on the confection of dental implant prostheses was observed before and after subjection to the laser welding process. The microstructure was analyzed with the. use of optic microscopy and the corrosion resistance was studied by the traditional electrochemical techniques and by electrochemical impedance, under environmental conditions simulating the aggressiveness found in the mouth cavity. A structural change was detected on the weld area, which presented a refined microstructure deriving from the high-speed cooling. The base metal out of the weld area presented a fusion coarse microstructure. The electrochemical essays showed differences on the potentiodynamic polarization behavior in both weld and metal base areas, indicating superior corrosion resistance in the weld area. The impedance spectra were characterized by capacitive distorted components, presenting linear impedance in the low frequencies area. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Microleakage and nanoleakage: Influence of laser in cavity preparation and dentin pretreatment

Objective: the purpose of this study was to verify if the application of the Nd:YAG laser following pretreatment of dentin with adhesive systems that were not light cured in class V cavities and were prepared with Er:YAG laser would promote better sealing of the gingival margins when compared to cavities prepared the conventional way. Background Data: Previous studies had shown that the pretreatment of dentin with laser irradiation after the application of an adhesive system is efficient in achieving higher shear bond and tensile bond strength. Materials and Methods: Er:YAG laser (Kavo-Key, Germany) with 350 mJ, 4 Hz, and 116.7 J/cm(2) was used for cavity preparation. The conventional preparation was made with diamond bur mounted in high-speed turbine. Dentin treatment was accomplished using an Nd:YAG laser (Pulse Master 1000, ADT. USA) at 60 mJ, 10 Hz, and 74.65/cm(2) following application of the adhesive system. The cavities were stored with Single Bond/Z100 and Prime & Bond NT/TPH. Eighty bovine incisors were used, and class V preparations were done at buccal and lingual surfaces divided into eight groups: (1) Er:YAG preparation + Prime & Bond NT + TPH; (2) Er:YAG preparation + Single Bond + Z100; (3) Er:YAG preparation + Single Bond + Nd:YAG + Z100; (4) Er:YAG preparation + Prime & Bond NT + Nd:YAG + TPH; (5) conventional preparation + Prime & Bond NT + TPH; (6) conventional preparation + Single Bond + Z100; (7) conventional preparation + Single Bond + Nd:YAG + Z100; (8) conventional preparation + Prime & Bond NT + Nd:YAG + TPH. All specimens were thermocycled for 300 full cycles between 5 degreesC +/- 2 degreesC and 55 degreesC +/- 2 degreesC (dwell time of 30 sec), and stored in 50% silver nitrate solution for 24 h soaked in photodeveloping solution and exposed to fluorescent light for 6 h. After this procedure, the specimens were sectioned longitudinally in 3 portions and the extension of microleakage at the gingival wall was determined following a criteria ranging from 0 to 4 using scanning electron microscopy (SEM). The medium portion sectioned of each specimen was polished and prepared for nanoleakage avaliation by SEM. Results: Kruskall-Wallis and Miller statistical tests determined that group 3 presented less microleakage and nanoleakage. Conclusion: Application of the Nd:YAG laser following pretreatment of dentin with adhesive Single Bond non-photocured Single Bond adhesive in cavities prepared with Er:YAG promote better sealing of the gingival margins.

Multiwavelength visible and white light generation by upconversion emission in Ho/Tm/Yb triply doped fluorogermanate glass-ceramic

Energy transfer excited multiwavelength visible upconversion emission and white light generation is described in a single sample of PbGeO(3)-PbF(2)-CdF(2) glass-ceramic triply doped With Ho/Tm/Yb under single infrared laser excitation. Blue (475 nm), green (540 mn), and red (650 nm), upconversion luminescence signals are generated, and the emissions are assigned, respectively, to thulium ((1)G(4)-(3)H(6)), and holmium ((5)S(2);(5)F(4)) -> (5)I(8), (5)F(5) -> (5)I(8)) ions transitions, both excited via successive energy transfers from ytterbium ions. It is experimentally shown that with a proper combination of the rare earth ions contents, white light may be produced, with the simultaneous generation of fluorescence with controllable intensities at the wavelengths of the three primary colours in a single sample and using a single near-infrared excitation source.

Orthodontic brackets removal under shear and tensile bond strength resistance tests - a comparative test between light sources

We have investigated if a new LEDs system has enough efficient energy to promote efficient shear and tensile bonding strength resistance under standardized tests. LEDs 470 +/- 10 nm can be used to photocure composite during bracket fixation. Advantages considering resistance to tensile and shear bonding strength when these systems were used are necessary to justify their clinical use. Forty eight human extracted premolars teeth and two light sources were selected, one halogen lamp and a LEDs system. Brackets for premolar were bonded through composite resin. Samples were submitted to standardized tests. A comparison between used sources under shear bonding strength test, obtained similar results; however, tensile bonding test showed distinct results: a statistical difference at a level of 1% between exposure times (40 and 60 seconds) and even to an interaction between light source and exposure time. The best result was obtained with halogen lamp use by 60 seconds, even during re-bonding; however LEDs system can be used for bonding and re-bonding brackets if power density could be increased.

A randomised clinical trial of the effect of low-level laser therapy for perineal pain and healing after episiotomy: A pilot study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Antimicrobial photodynamic action on dentin using a light-emitting diode light source