Influence of surface sealants on microleakage of composite resin restorations

Purpose: The purpose of this study was to verify the influence of surface sealants and dentin adhesive systems on the microleakage of composite restorations. Methods: Class V cavities were made on the buccal faces of 100 permanent third molars and restored with Z250. After 24 hours, they were submitted to polishing and finishing processes. The teeth were divided into groups according to the sealant agent: group 1 - Single Bond; group 2 - Opti Bond Solo Plus; group 3 - Fortify; group 4 - Fortify Plus; and group 5 - control without sealant. The analysis of immediate microleakage was performed in 10 restorations from each group, soon after the sealing. The other 10 specimens from each group were submitted to tooth-brushing and thermal cycles. The teeth were isolated and immersed in 2% methylene blue solution, washed in tap water, and sectioned in the buccolingual direction. The percentage of marginal leakage was calculated using an image analysis program, and results were submitted to analysis of variance and Tukey's test. Results: All the sealed groups demonstrated lower microleakage values compared to the control group. Group 3, sealed with Fortify, presented the lowest mean microleakage values. Conclusion: The application of surface sealants effectively decreased the microleakage in composite resin restorations.

Fatigue resistance of bovine teeth restored with resin-bonded fiber posts: Effect of post surface conditioning

This study evaluated the effect of post surface conditioning on the fatigue resistance of bovine teeth restored with resin-bonded fiber-reinforced composite (FRC). Root canals of 20 single-rooted bovine teeth (16 mm long) were prepared to 12 mm using a preparation drill of a double-tapered fiber post system. Using acrylic resin, each specimen was embedded (up to 3.0 mm from the cervical part of the specimen) in a PVC cylinder and allocated into one of two groups (n = 10) based on the post surface conditioning method: acid etching plus silanization or tribochemical silica coating (30 μm SiOx + silanization). The root canal dentin was etched (H2PO3 for 30 seconds), rinsed, and dried. A multi-step adhesive system was applied to the root dentin and the fiber posts were cemented with resin cement. The specimens were submitted to one million fatigue cycles. After fatigue testing, a score was given based on the number of fatigue cycles until fracture. All of the specimens were resistant to fatigue. No fracture of the root or the post and no loss of retention of the post were observed. The methodology and the results of this study indicate that tribochemical silica coating and acid etching performed equally well when dynamic mechanical loading was used.

Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks

Objectives: The aim of this study was to evaluate the effect of thermal and mechanical cycling alone or in combination, on the flexural strength of ceramic and metallic frameworks cast in gold alloy or titanium. Methods: Metallic frameworks (25 mm × 3 mm × 0.5 mm) (N = 96) cast in gold alloy or commercial pure titanium (Ti cp) were obtained using acrylic templates. They were airborne particle-abraded with 150 μm aluminum oxide at the central area of the frameworks (8 mm × 3 mm). Bonding agent and opaque were applied on the particle-abraded surfaces and the corresponding ceramic for each metal was fired onto them. The thickness of the ceramic layer was standardized by positioning the frameworks in a metallic template (height: 1 mm). The specimens from each ceramic-metal combination (N = 96, n = 12 per group) were randomly assigned into four experimental fatigue conditions, namely water storage at 37 °C for 24 h (control group), thermal cycling (3000 cycles, between 4 and 55 °C, dwell time: 10 s), mechanical cycling (20,000 cycles under 10 N load, immersion in distilled water at 37 °C) and, thermal and mechanical cycling. A flexural strength test was performed in a universal testing machine (crosshead speed: 1.5 mm/min). Data were statistically analyzed using two-way ANOVA and Tukey's test (α = 0.05). Results: The mean flexural strength values for the ceramic-gold alloy combination (55 ± 7.2 MPa) were significantly higher than those of the ceramic-Ti cp combination (32 ± 6.7 MPa) regardless of the fatigue conditions performed (p < 0.05). Mechanical and thermo-mechanical fatigue decreased the flexural strength results significantly for both ceramic-gold alloy (52 ± 6.6 and 53 ± 5.6 MPa, respectively) and ceramic-Ti cp combinations (29 ± 6.8 and 29 ± 6.8 MPa, respectively) compared to the control group (58 ± 7.8 and 39 ± 5.1 MPa, for gold and Ti cp, respectively) (p < 0.05) (Tukey's test). While ceramic-Ti cp combinations failed adhesively at the metal-opaque interface, gold alloy frameworks exhibited a residue of ceramic material on the surface in all experimental groups. Significance: Mechanical and thermo-mechanical fatigue conditions decreased the flexural strength values for both ceramic-gold alloy and ceramic-Ti cp combinations with the results being significantly lower for the latter in all experimental conditions. © 2007 Academy of Dental Materials.

Histological and histomorphometrical alterations of the periodontal ligament in gerbils submitted to teeth extraction

This study verified the effect of unilateral teeth extraction on the periodontal ligament in gerbils (Meriones unguiculatus). Ten adult male gerbils weighing about 50 g had induced occlusal alterations by upper left molar extractions while the other ten animals, only submitted to surgical stress, were considered as controls. The periodontal ligament was characterized by qualitative and quantitative analysis, histological description and histomorphometric quantification. Significant alterations were observed on the left side of the experimental group (P < 0.05), the hypofunctional region, when it was compared with the contralateral side and the corresponding region of the control group. Two months after occlusal alterations induced by unilateral teeth extraction, atrophic histological alterations and a decrease in the periodontal space on the ipsilateral side characterized the periodontal ligament. In this study it was possible to conclude that the gerbil can be used in experimental models attempting to correlate the periodontium's biological response to various mechanical stresses, as the periodontal ligament was shown to be highly sensitive to occlusal alterations. © 2008 The Authors.

Effect of microwave disinfection on physical and mechanical properties of acrylic resins

This study evaluated the effect of microwave energy on the hardness, impact strength and flexural strength of the Clássico, Onda-Cryl and QC-20 acrylic resins. Aluminum die were embedded in metallic or plastic flasks with type III dental stone, in accordance with the traditional packing technique. A mixing powder/liquid ratio was used according to the manufacturer's instructions. After polymerization in water batch at 74°C for 9 h, boiling water for 20 min or microwave energy at 900 W for 10 min, the specimens were deflasked after flask cooling at room temperature, and submitted to finishing. Specimens non-disinfected and disinfected by microwave irradiation were submitted to hardness, impact and flexural strength tests. Each specimen was immersed in distilled water and disinfected in a microwave oven calibrated to 650 W for 3 min. Knoop hardness test was performed with 25 g load for 10 s, impact test was carried out using the Charpy system with 40 kpcm, and 3-point bending test with a crosshead speed of 0.5 mm/min until fracture. Data were submitted to statistical analysis by ANOVA and Tukey's test (α=0.05). Disinfection by microwave energy decreased the hardness of Clássico and Onda-Cryl acrylic resins, but no effect was observed on the impact and flexural strength of all tested resins.

Adhesive cementation of zirconia posts to root dentin: Evaluation of the mechanical cycling effect

This study evaluated the effect of mechanical cycling on the bond strength of zirconia posts to root dentin. Thirty single-rooted human teeth were transversally sectioned to a length of 16 mm. The canal preparation was performed with zirconia post system drills (CosmoPost, Ivoclar) to a depth of 12 mm. For post cementation, the canals were treated with total-etch, 3-steps All-Bond 2 (Bisco), and the posts were cemented with Duolink dual resin cement (Bisco). Three groups were formed (n = 10): G1 - control, no mechanical cycling; G2 - 20,000 mechanical cycles; G3 - 2,000,000 mechanical cycles. A 1.6-mm-thick punch induced loads of 50 N, at a 45° angle to the long axis of the specimens and at a frequency of 8 Hz directly on the posts. To evaluate the bond strengths, the specimens were sectioned perpendicular to the long axis of the teeth, generating 2-mm-thick slices, approximately (5 sections per teeth), which were subjected to the push-out test in a universal testing machine at a 1 mm/min crosshead speed. The push-out bond strength was affected by the mechanical cycling (1-way ANOVA, p = .0001). The results of the control group (7.7 ± 1.3 MPa) were statistically higher than those of G2 (3.9 ± 2.2 MPa) and G3 (3.3 ± 2.3 MPa). It was concluded that the mechanical cycling damaged the bond strength of zirconia posts to root dentin.

Evaluation of dimensional change and detail reproduction in silicones for facial prostheses.

The aim of this study was to evaluate the dimensional stability and detail reproduction of two silicones used for facial prosthesis, under the influence of chemical disinfection and storage time. Twenty-eight test specimens were obtained, half made of Silastic MDX 4-4210 silicone, and the other half of Silastic 732 RTV silicone. The test specimens were divided into 4 groups: Silastic 732 RTV and Silastic MDX 4-4210, with disinfection 3 times a week with Efferdent and without disinfection. Dimensional change was analyzed using an electronic comparison microscope and detail reproduction was observed under a stereo microscope, immediately and 2 months after the test specimens were made. Once the results were obtained, an analisis of variance (ANOVA) was applied, followed by the Tukey's Test with 1% confidence. The storage time factor had a statistical influence on dimensional stability: Silastic MDX 4-4210 had less contraction than Silastic 732 RTV. Chemical disinfection did not significantly alter the dimensional stability of the materials used. Regarding detail reproduction, no alteration of values was observed in any of the materials analyzed, regardless of storage period or disinfection.

Effect of radiotherapy on the radiopacity and flexural strength of a composite resin.

The aim of this study was to evaluate the effect of radiotherapy on the radiopacity and flexural strength of composite resin. Forty Z250 composite resin specimens were polymerized using a halogen light-curing unit and divided into 5 groups, in accordance with the radiotherapy dose: G1- without irradiation, G2- 30 Gy, G3- 40 Gy, G4- 50 Gy and GS- 60 Gy Digital images were obtained using a GE 100 X-ray. Radiopacity values were obtained with the Digora digital imaging system and the flexural strength was evaluated with an EMIC universal testing machine. Data were submitted to ANOVA and Tukey 's test. G1 presented the highest radiopacity value, followed by G3, G5, G4 and G2. For flexural strength, G1 presented the lowest value, followed by G2, G5, G3 and G4. Differences were no significant (p>0.05). The commonly used dosage of radiotherapy treatment, did not cause alteration in the radiopacity and flexural strength of resin-based composites.

Comparison of resin push-out strength to root dentin of bovine- and human-teeth

Aim : To compare the push-out strength of bovine- and human-root dentin and, thus, evaluate the suitability of bovine-root dentin to substitute human-root dentin for bond strength testing. Materials and Methods : Ten single-rooted human-teeth and ten bovine incisors were prepared using a #3 bur of a fiber post system (12 mm long). The posts were duplicated with resin cement (Duolink). The root canals were treated with All Bond 2 adhesive system and the resin posts were cemented using Duolink. The specimens were cut perpendicular to their long axis, yielding disc-specimens with 1.5 mm thickness, which were submitted to a push-out test (1 mm/min). Ten bond strength values per group (n = 10) were used for statistical analysis (Student t test, a =.05). Results : Statistically significant differences were found for the bond strength values between bovine- (4.1 1.3 MPa) and human-root dentin (8.6 5.7 MPa) (P =.0001). Conclusion : The push-out strengths of bovine- and human-root dentin were statistically different.

Longitudinal bond strength evaluation using the deproteinized dentin technique

This study evaluated bond strength to dentin as a result of storage time for conventional adhesive systems (with or without collagen) that had been deproteinized with 10% sodium hypochlorite (NaOCl). For this study, 72 human molars were sectioned in a mesiodistal axial plane and embedded in acrylic resin; at that point, the vestibular and lingual surfaces were worn down with abrasive paper. Acid etching was performed for 15 seconds (using 37% phosphoric acid) and the specimens were divided into 12 groups (n = 6), depending on the adhesive system used, the dentin treatment performed, and the length of evaluation (24 hours or six months). A resin composite was inserted over the prepared area with the aid of a metal matrix. Following a mechanical shear test, fractured surfaces were analyzed by stereomicroscope and the data were submitted to ANOVA and Tukey's test. It was concluded that the dentin deproteinization treatment with 10% NaOCI improved the bond strength in five of the six groups. The bond strength after 24 hours was significantly higher than the bond strength measured after six months. Of the three adhesive systems tested in this study, DenTASTIC UNO demonstrated the lowest bond strength.

Durability of the bond strength of self-adhesive resin cements to human dentin

This study subjected two self-adhesive resin cements and two conventional resin cements to dry and aging conditions, to compare their microtensile bond strengths (MTBS) to dentin. Using four different luting systems (n = 10), 40 composite resin blocks (each 5x5x4 mm) were cemented to flat human crown dentin surfaces. The specimens were stored in water for 24 hours (37°C), at which point each specimen was sectioned along two axes to obtain beams that were divided randomly into two groups: dry samples, which were tested immediately, and samples that were subjected to accelerated aging conditions (12, 000 thermocycles followed by storage for 150 days). The μTBS results were affected significantly by the luting system used (P < 40001). Only the μTBS of Rely-X Unicem was reduced significantly after aging; the μTBS remained stable or increased for the other self-adhesive resin cement and the two conventional cements.

Evaluation of hardness and color stability in the soft lining materials after thermocycling and chemical polishing.

The aim of this study was to evaluate the Shore A hardness and color stability of two soft lining materials after thermocycling and when chemical polishing was used or omitted. Two acrylic-based soft lining materials were tested: Coe-Soft and Soft Confort, 14 specimens were made for each material. They were distributed in four groups according to the treatment performed. The specimens were thermocycled (1000 cycles) and half of the group submitted to chemical polishing (methyl methacrylate). Shore A hardness was determined and color stability was calculated by means of Commission International de l'Eclairage Lab uniform color scale using a spectrophotometer, the measurements were made immediately after deflasked, chemical polishing and thermocycling. Analysis of variance (ANOVA) and Tukey's tests were performed at p < 0.01. Color changes (deltaE) were observed after thermocycling in both soft lining materials: Soft Confort (10.60) showed significantly higher values than Coe-Soft (4.57). Coe-Soft (26.42) showed higher Shore A hardness values than Soft Confort (19.42). Chemical polishing did not influence in the color stability of both materials; however, influenced in the hardness values of Coe-Soft.

Influence of desensitizing agents on the microshear bond strength of adhesive systems to dentin.

The aim of this study was to evaluate the effect of desensitizing agents on the micro-shear bond strength of adhesive systems to dentin. Forty bovine teeth were divided into 8 groups (n=5): G1--Single Bond (SB); G2--GH.F + SB; G3-- Desensibilize + SB; G4--essensiv + SB; G5 --ingle Bond 2 (SB2); G6--H.E + SB2; G7--esensibilize + SB2; G8--Dessensiv + SB2. In all of the groups, the desensitizing agents were applied after phosphoric acid etching and before the dentin adhesive application. Z250 composite resin tubes were bonded on the treated surface. After 24 hours, the teeth were tested in a universal machine. Data were submitted to ANOVA and Tukey's test (5%). The results showed that the groups where Desensibilize and Dessensiv were applied exhibited smaller bond strength values.