Effect of different light sources on degree of conversion, hardness and plasticization of a composite

Clinical performance of composite resins depends largely on their mechanical properties,and those are influenced by several factors,such as the light-curing mode. The purpose of this study was to evaluate the influence of different light sources on degree of conversion(DC), Knoop hardness(KHN) and plasticization(P) of a composite resin. Disc-shaped specimens (5 x 2 mm) of Esthet-X(Dentsply) methacrylate-based microhybrid composite were light-cured using quartz-tungsten-halogen (QTH) Optilight Plus(Gnatus) or light-emitting diode(LED) Ultraled(Dabi Atlante) curing units at 400 and 340 mW/cm2 of irradiance, respectively. After 24 h, absorption spectra of composite were obtained using Nexus 670(Nicolet)FT-IR spectrometer in order to calculate the DC.The KHN was measured in the HMV-2000(Shimadzu) microhardness tester under 50 g loads for 15 s, and P was evaluated by percentage reductio of hardness after 24 h of alcohol storage. Data were subjected to t-Student test(alpha=0.05).QTH device showed lower P and higher KHN$ than LED (p<0.05), and no difference between the light-curing units was found for DC (p>0.05). The halogen-curing unit with higher irradiance promoted higher KHN and lower softening in alcohol than LED.

Radiografia digital para inspeção de soldas de dutos - melhor sensibilidade

The conventional radiographic technique using industrial radiographic films is with the days finishing. The Digital Radiography is taking place in several sectors, e.g., the medical, aerospace, security, automotive, etc. In addition to representing a technological trend, it has been demonstrated that digital radiography offers a series of benefits in terms of productivity, sensitivity, environmental aspects, image treatment tools, cost reduction, etc. If one weld seam to be inspected is from a serried product, as example a pipe, the best option to be implemented is the Flat Panel Detector with this equipment is possible to reduce the obtaining digital radiographic images in place of films and reducing the inspection cycle time due to its high degree of automation. In the experiments described in this paper this new technique was tested and the results were compared with those obtained by the conventional radiography. The welded specimens were prepared using the submerged-arc welding process and small artificial cracks of the most varied dimensions, present in the specimens, were used to establish a comparison of the sensitivities presented by the techniques employed After conducting several experiments, the digital method presented the highest sensitivity to the wire-type Image Quality Indicator (IQI) and in the detection of small defects, leading to the conclusion that the use of digital radiography using the flat-panel detector offers advantages over the conventional technique [1, 2]. This work was carried out based on the API 5L Edition 2004 [3] and ISO 3183 Edition 2007 [4] specifications.

Time reduction of light curing: Influence on conversion degree and microhardness of orthodontic composites

Introduction: The aim of this study was to assess the influence of curing time and power on the degree of conversion and surface microhardness of 3 orthodontic composites. Methods: One hundred eighty discs, 6 mm in diameter, were divided into 3 groups of 60 samples according to the composite used-Transbond XT (3M Unitek, Monrovia, Calif), Opal Bond MV (Ultradent, South Jordan, Utah), and Transbond Plus Color Change (3M Unitek)-and each group was further divided into 3 subgroups (n = 20). Five samples were used to measure conversion, and 15 were used to measure microhardness. A light-emitting diode curing unit with multiwavelength emission of broad light was used for curing at 3 power levels (530, 760, and 1520 mW) and 3 times (8.5, 6, and 3 seconds), always totaling 4.56 joules. Five specimens from each subgroup were ground and mixed with potassium bromide to produce 8-mm tablets to be compared with 5 others made similarly with the respective noncured composite. These were placed into a spectrometer, and software was used for analysis. A microhardness tester was used to take Knoop hardness (KHN) measurements in 15 discs of each subgroup. The data were analyzed with 2 analysis of variance tests at 2 levels. Results: Differences were found in the conversion degree of the composites cured at different times and powers (P < 0.01). The composites showed similar degrees of conversion when light cured at 8.5 seconds (80.7%) and 6 seconds (79.0%), but not at 3 seconds (75.0%). The conversion degrees of the composites were different, with group 3 (87.2%) higher than group 2 (83.5%), which was higher than group 1 (64.0%). Differences in microhardness were also found (P < 0.01), with lower microhardness at 8.5 seconds (35.2 KHN), but no difference was observed between 6 seconds (41.6 KHN) and 3 seconds (42.8 KHN). Group 3 had the highest surface microhardness (35.9 KHN) compared with group 2 (33.7 KHN) and group 1 (30.0 KHN). Conclusions: Curing time can be reduced up to 6 seconds by increasing the power, with a slight decrease in the degree of conversion at 3 seconds; the decrease has a positive effect on the surface microhardness.