Utilização de lama vermelha para oxidação eletrolítica assistida por plasma de liga de alumínio

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Usinagem do alumínio da classe 6005 com uso de ferramenta cerâmica

The machining process is so much important in the economic world. Many machining parameters have been studied to maximize results, in terms of cost and lifetime. (decrease of cutting tool wear, improved surface finish, among others). The objective of this study is to evaluate the wear of a ceramic tool in the machining of the aluminum alloy 6005 A. The analysis of the wear of the cutting tools is very important due to its big impact on the final finishing of the piece as a whole. The evaluation took place in two stages, first it was done a detailed study of the literature of the whole machining process, where the study of the formation and swarf classification were among the most important steps in this phase. The second step consisted in the machining of the piece of aluminum 6005 A with a ceramic cutting tool constituded of aluminum oxide and magnesium oxide with silicon carbide impregnation. The swarf generated in this process was then photographed with a Zeiss optical microscope and analyzed for its size and shape. Through this comparison it was concluded that the swarf are generated shear swarfs, shaped like a tangled, fragmented and arcs connected, thus classifying the material as medium difficulty machining. Through the image analysis tool it was concluded that the parameter of lower wear was the: Vc = 500m / min, f = 0.10mm / rev and ap = 0.5mm

Torneamento da liga de alumínio da classe 6005 utilizando ferramenta cerâmica

Machining processes are one of the most important manufacturing processes in the modern world. In these processes, there are many elements which will influence in the final result of the machined part. Among them, the tools are the principal factor of the rising cost, because its global influence on the process. In aeronautical industries, this can be more evidenced due the need to machining several alloys, between them, aluminum alloys. These alloys have to demonstrate a specific surface finishing to be used in aircraft's fuselage. This kind of industry is one of the segments which is still rising in Brazil, and they are looking viable alternatives in the manufacturing processes of materials, due the need to produce more and more parts and equipment, with costs increasingly reduced. The purpose of this project is the development of a ceramic with differentiated properties. The ceramics were developed using a pre-sintering at 1200 °C, with posterior sintering at 1600°C, and subjected to dry turning process on aluminum alloy 6005. The characterizations showed that ceramics presented with toughness on the center of 1700 MPa and on the surface of 1950 MPa, density 98,5 ±0,14. g/cm³. Ceramics were grinded and faceted, according to ISO standard 1832, and subjected to turning tests in a ROMI lathe brand, model GL240M, using cutting speeds of 500, 800 and 1000 m/min with different feed rates. The machining results showed low occurrence of flank wear to all cutting speeds, and better surface finishing average values of Ra = 0,4935 μm and Rt = 8,112 μm. In general, it could be seen that the tool presents important potential to machining 6005 alloy, and that the use of correct parameters can decrease and/or eliminate subsequent processes, providing important reductions in costs related to the machining processes

Análise e comparação de orelhamento na liga AA3104 após laminação a quente

Aluminum has been widely used in the forming and manufacture of beverage cans, specific aluminum alloy AA3104, which manufacturers are increasingly demanding as to mechanical properties, quality and reducing waste. This work describes the analysis and comparison of the behavior of earing AA3104 aluminum alloy samples of final thicknesses of 1.80 and 2.10 mm. Were obtained after a hot rolling process, a total population of 86 samples for the two different thicknesses, of which 23 samples of 1.80 mm and 2.10 mm 63 samples. After removal of samples, there was a mechanical test inlay, then characterizing the earing in them. The results earing to the thicknesses of 1.80 and 2.10 mm were analyzed and compared statistically to give 7.1% and 7.4% on average, respectively, correlated with the hot rolling process variables, showing that they are statistically equal and that the process variables do not affect the end result desired, ranging from 7.0 to 7,5%

Effects of aluminum-copper alloy filtration on photon spectra, air kerma rate and image contrast

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The role of coarse intermetallics in the localized corrosion behaviour of AA 2024-T3 in low concentrated chloride media

Aluminium alloy (AA) 2024-T3 is an important engineering material due to its widespread use in the aerospace industry. However, it is very prone to localized corrosion attack in chloride containing media, which has been mainly associated to the presence of coarse intermetallics (IMs). In this work the corrosion behaviour of aluminium alloy 2024-T3 in low concentrated chloride media was investigated using microscopy and electrochemical methods. SEM observations have shown that intermetallics with the same nominal composition present heterogeneous reaction rates, and that both types of coarse IMs normally found in the AA 2024-T3 microstructure corrode. Moreover, EDS analyses have shown important compositional changes in the corroded IMs, evidencing the selective corrosion of their more active constituents and the onset of an intense oxygen peak, irrespective to the IM nature. TEM/EDS observations on non-corroded samples have evidenced the heterogeneous composition within the IMs. On the other hand, the results of the electrochemical investigations, in accordance with the SEM/EDS observations, have evidenced that IMs corrosion dominates the electrochemical response of the alloy during the first hours of immersion in the test electrolyte. © 2009 by NACE International.

Efeito dos oxi-ânions do grupo VIB sobre a corrosão aquosa das ligas Al(2024) e Al(7050) utilizadas na indústria aeronaútica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Corrosion behavior of Ti-13Nb-13Zr alloy used as a biomaterial

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Nanohardness and contact angle of Si wafers implanted with N and C and Al alloy with N by plasma ion implantation

Surfaces of silicon wafers implanted with N and C, respectively, and aluminum 5052 implanted with N alone by plasma immersion ion implantation WHO were probed by a nanoindentor and analyzed by the contact-angle method to provide information on surface nanohardness and wettability. Silicon nitride and silicon carbide are important ceramic materials for microelectronics, especially for high-temperature applications. These compounds can be synthesized by high-dose ion implantation. The nanohardness of a silicon sample implanted with 12-keV nitrogen PIII (with 3 X 10(17) cm(-2) dose) increased by 10% compared to the unimplanted sample, in layers deeper than the regions where the formation of the Si,N, compound occurred. A factor of 2.5 increase in hardness was obtained for C-implanted Si wafer at 35 keV (with 6 X 10(17) cm(-2) dose), again deeper than the SiC-rich layer, Both compounds are in the amorphous state and their hardness is much lower than that of the crystalline compounds, which require an annealing process after ion implantation. In the same targets, the contact angle increased by 65% and 35% for N- and C-implanted samples, respectively. Compared to the Si target, the nitrogen PIII-irradiated Al 5052 (wish 15 keV) showed negligible change in its hydrophobic character after ion implantation. Its near-surface nanohardness measurement showed a slight increase for doses of 1 X 10(17) cm(-2). We have been searching for an AlN layer of the order of 1000 A thick, using such a low-energy PIII process, but oxide formation during processing has precluded its synthesis. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Damping behavior of continuous fiber/metal composite materials by the free vibration method

Fiber metal laminates (FML) offer significant improvements over current available materials for aircraft structures due to their excellent mechanical characteristics and relatively low density. Non-destructive testing techniques are being used in the characterization of composite materials. Among these, vibration testing is one of the most used tools because it allows the determination of the mechanical properties. In this work, the viscoelastic properties such as elastic (E') and viscous (E) responses were obtained for aluminum 2024 alloy; carbon fiber/epoxy; glass fiber/epoxy and their hybrids aluminum 2024 alloy/carbon fiber/epoxy and aluminum 2024 alloy/glass fiber/epoxy composites. The experimental results were compared to calculated E modulus values by using the composite micromechanics approach. For all specimens studied, the experimental values showed good agreement with the theoretical values. The damping behavior, i.e. The storage modulus and the loss factor, from the aluminum 2024 alloy and fiber epoxy composites can be used to estimate the viscoelastic response of the hybrid FML. (c) 2005 Elsevier Ltd. All rights reserved.

Effect of WC-10%Co-4%Cr coating on the Ti-6Al-4V alloy fatigue strength

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading

Objectives. This study evaluated the effect of thermal- and mechanical-cycling on the shear bond strength of three low-fusing glassy matrix dental ceramics to commercial pure titanium (cpTi) when compared to conventional feldspathic ceramic fused to gold alloy.Methods. Metallic frameworks (diameter: 5 min, thickness: 4 mm) (N = 96, n = 12 per group) were cast in cpTi and gold alloy, airborne particle abraded with 150 mu m aluminum oxide. Low-fusing glassy matrix ceramics and a conventional feldspathic ceramic were fired onto the alloys (thickness: 4mm). Four experimental groups were formed; Gr1 (control group): Vita Omega 900-Au-Pd alloy; Gr2: Ticeram-cpTi; Gr3: Super Porcelain Ti-22-cpTi and G4: Vita Titankeramik-cpTi. While half of the specimens from each ceramic-metal combination were randomly tested without aging (water storage at 37 C for 24h only), the other half were first thermocycled (6000 cycles, between 5 and 55 C, dwell time: 13 s) and then mechanically loaded (20,000 cycles under SON load, immersion in distilled water at 37 C). The ceramic-alloy interfaces were loaded under shear in a universal test machine (cross-head speed: 0.5 mm/min) until failure occur-red. Failure types were noted and the interfaces of the representative fractured specimens from each group were examined with stereo microscope and scanning electron microscope (SEM). in an additional study (N = 16, n = 2 per group), energy dispersive X-ray spectroscopy (EDS) analysis was performed from ceramic-alloy interfaces. Data were analyzed using ANOVA and Tukey's test.Results. Both ceramic-metal combinations (p < 0.001) and aging conditions (p < 0,001) significantly affected the mean bond strength values. Thermal- and mechanical-cycling decreased the bond strength (MPa) results significantly for Gr3 (33.4 +/- 4.2) and Gr4 (32.1 +/- 4.8) when compared to the non-aged groups (42.9 +/- 8.9, 42.4 +/- 5.2, respectively). Gr1 was not affected significantly from aging conditions (61.3 +/- 8.4 for control, 60.7 +/- 13.7 after aging) (p > 0.05). Stereomicroscope images showed exclusively adhesive failure types at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface but with a visible dark titanium oxide layer in Groups 2-4 except Gr1 where remnants of bonder ceramic was visible. EDS analysis from the interfacial zone for cpTi-ceramic groups showed predominantly 34.5-85.1% O(2) followed by 1.1-36.7% Aland 0-36.3% Si except for Super Porcelain Ti-22 where a small quantity of Ba (1.4-8.3%), S (0.7%) and Sn (35.3%) was found. In the Au-Pd alloy-ceramic interface, 56.4-69.9% O(2) followed by 15.6-26.2% Si, 3.9-10.9% K, 2.8-6% Na, 4.4-9.6% Al and 0-0.04% Mg was observed.Significance. After thermal-cycling for 6000 times and mechanical-cycling for 20,000 times, Triceram-cpTi combination presented the least decrease among other ceramic-alloy combinations when compared to the mean bond strength results with Au-Pd alloy-Vita Omega 900 combination. (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Electrochemical studies of copper-aluminum-silver alloys in 0.5 M H2SO4

The electrochemical behavior in 0.5 M H2SO4 at 25 degreesC of a Cu-Al(9.3 wt%)-Ag(4.7 wt%) alloy submitted to different heat treatments and an annealed Cu- Al(9.7 wt%)-Ag(34.2 wt%) were studied by means of open circuit potential (E-mix) measurements, potentiodynamic polarizations and cyclic voltammetry. SEM and EDX microanalysis were used to examine the changes caused by the electrochemical perturbations. The steady state potentials observed for the studied samples were correlated in terms of the phases present in the alloys surface. The resulting E/I potentiodynamic profiles were explained in terms of the potentiodynamic behavior of pure copper and pure silver. The presence of aluminum decreased the extent of copper oxidation. In the apparent Tafel potential region, two anodic Tafel slopes were obtained: 40 mV dec(-1) in the low potential region and 130 mV dec(-1) in the high potential region, which were related with the electrochemical processes involving copper oxidation. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Investigation of the corrosion behaviour of AA 2024-T3 in low concentrated chloride media

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)