Structural characterization of Ti-15Mo alloy used as biomaterial by Rietveld method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Synthesis and characterization of Fe(III)-doped ceramic membranes of titanium dioxide and its application in photoelectrocatalysis of a textile dye

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Obtaining of Nanoapatite in Ti-7.5Mo Surface After Nanotube Growth

Titanium and their alloys have been used for biomedical applications due their excellent mechanical properties, corrosion resistance and biocompatibility. However, they are considered bioinerts materials because when they are inserted into the human body they are cannot form a chemical bond with bone. In several studies, the authors have attempted to modify their characteristic with treatments that changes the material surface. The purpose of this work was to evaluate obtaining of nanoapatite after growing of the nanotubes in surface of Ti-7.5Mo alloy. Alloy was obtained from c.p. titanium and molibdenium by using an arc-melting furnace. Ingots were submitted to heat treatment and they were cold worked by swaging. Nanotubes were processed using anodic oxidation of alloy in electrolyte solution. Surfaces were investigated using scanning electron microscope (SEM), FEG-SEM and thin-film x-ray diffraction. The results indicate that nanoapatite coating could form on surface of Ti-7.5Mo experimental alloy after nanotubes growth.

Growth of Calcium Phosphate Using Chemically Treated Titanium Oxide Nanotubes

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Production of a low young modulus titanium alloy by powder metallurgy

Titanium alloys have several advantages over ferrous and non-ferrous metallic materials, such as high strengthto-weight ratio and excellent corrosion resistance. A blended elemental titanium powder metallurgy process has been developed to offer low cost commercial products. The process employs hydride-dehydride (HDH) powders as raw material. In this work, results of the Ti-35Nb alloy sintering are presented. This alloy due to its lower modulus of elasticity and high biocompatibility is a promising candidate for aerospace and medical use. Samples were produced by mixing of initial metallic powders followed by uniaxial and cold isostatic pressing with subsequent densification by isochronal sintering between 900 up to 1600 °C, in vacuum. Sintering behavior was studied by means of microscopy and density. Sintered samples were characterized for phase composition, microstructure and microhardness by X-ray diffraction, scanning electron microscopy and Vickers indentation, respectively. Samples sintered at high temperatures display a fine plate-like alpha structure and intergranular beta. A few remaining pores are still found and density above 90% for specimens sintered in temperatures over 1500 °C is reached.

Structural Evaluation of Mechanically Alloyed and Heat-Treated Ti-25at-%Si Powders

This work discusses on the structural evaluation of mechanically alloyed and heat-treated Ti-25at%Si powders. The milling process was conducted in a planetary ball mill using stainless steel balls/vials, 200 rpm and ball-to-powder weight ratio of 5:1, whereas the heat treatment was conducted under Ar atmosphere at 1100 C for 4 h. Samples were characterized by X-ray diffraction, differential scanning calorimetry, scanning electron microscopy and energy dispersive spectrometry. The Si peaks disappeared after milling for 30h, indicating that the Si atoms were dissolved into the Ti lattice in order to form an extended solid solution. The Ti peaks were broadened and their intensities reduced for longer milling times whereas a halo was formed in Ti-25Si powders milled for 200h suggesting that an amorphous structure was achieved. The crystallite size was decreased with increasing milling times. A large Ti3Si amount was found in mechanically alloyed Ti-25at%Si powders after heating at 1100 degrees C for 4h.

Surface characterization of Ti-7.5Mo alloy modified by biomimetic method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of WC-10%Co-4%Cr coating on the Ti-6Al-4V alloy fatigue strength

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Wear resistance of experimental titanium alloys for dental applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Three-Dimensional Characterization of Pores in Ti-6Al-4V Alloy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural Evaluation of Mechanically Alloyed (67-x)Ti-xZr-22Si-11B Powders

The present work reports on the structural evaluation of mechanically alloyed Ti-xZr-22Si-11B (x = 5, 7, 10, 15 and 20 at-%) powders. Milled powders and hot-pressed alloys were characterized by X-ray diffraction, electron scanning microscopy, and electron dispersive spectrometry. The Si and B atoms were preferentially dissolved into the Ti and Zr lattices during ball milling of Ti-xZr-22Si-11B (x = 7, 10, 15 and 20 at-%) powders, and extended solid solutions were achieved. The displacement of Ti peaks was more pronounced to the direction of lower diffraction angles with increasing Zr amounts in mechanically alloyed Ti-Zr-Si-B powders, indicating that the Zr atoms were also dissolved into the Ti lattice.

Surface Corrosion of Ti-16Si-4B Powder Alloy Implanted With Nitrogen by Plasma-Based Technique

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Fatigue fracture behavior of Ti-6Al-4V PVD coated

Fatigue, corrosion and wear resistance are important parameters in aircraft components development as landing gear. High strength/weight ratio and effective corrosion resistance make of titanium alloys an alternative choice to replace steel and aluminum alloys. However, titanium alloys have poor tribological properties, which reduce devices performance under friction. PVD coatings tribological systems has been increased due to their attractive mechanical properties as low environmental impact, low friction coefficient, low wear rate and hardness up to 2000 HV.In this study the influence of TiN deposited by PVD on the fatigue strength of Ti-6Al-4V alloy was evaluated. Comparison of fatigue strength of coated specimens and base material shows also a decrease when parts are coated. It was observed that the influence is more significant in high cycle fatigue tests. Scanning electron microscopy technique (SEM) was used to observe crack origin sites and fracture features. (C) 2010 Published by Elsevier Ltd.

Fatigue behavior of PVD coated Ti-6Al-4V alloy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Microstructural Characterization of Ti-6Al-7Nb Alloy After Severe Plastic Deformation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)