Effect of Airborne-Particle Abrasion and Mechanico-Thermal Cycling on the Flexural Strength of Glass Ceramic Fused to Gold or Cobalt-Chromium Alloy

Purpose: To evaluate the effect of airborne-particle abrasion and mechanico-thermal cycling on the flexural strength of a ceramic fused to cobalt-chromium alloy or gold alloy.Materials and Methods: Metallic bars (n = 120) were made (25 mm x 3 mm x 0.5 mm): 60 with gold alloy and 60 with Co-Cr. At the central area of the bars (8 mm x 3 mm), a layer of opaque ceramic and then two layers of glass ceramic (Vita VM13, Vita Zahnfabrick) were fired onto it (thickness: 1 mm). Ten specimens from each alloy group were randomly allocated to a surface treatment [(tungsten bur or air-particle abrasion (APA) with Al(2)O(3) at 10 mm or 20 mm away)] and mechanico-thermal cycling (no cycling or mechanically loaded 20,000 cycles; 10 N distilled water at 37 degrees C and then thermocycled 3000 cycles; 5 degrees C to 55 degrees C, dwell time 30 seconds) combination. Those specimens that did not undergo mechanico-thermal cyclingwere stored inwater (37 degrees C) for 24 hours. Bond strength was measured using a three-point bend test, according to ISO 9693. After the flexural strength test, failure types were noted. The data were analyzed using three factor-ANOVA and Tukey's test (alpha = 0.05).Results: There were no significant differences between the flexural bond strength of gold and Co-Cr groups (42.64 +/- 8.25 and 43.39 +/- 10.89 MPa, respectively). APA 10 and 20 mm away surface treatment (45.86 +/- 9.31 and 46.38 +/- 8.89 MPa, respectively) had similar mean flexural strength values, and both had significantly higher bond strength than tungsten bur treatment (36.81 +/- 7.60 MPa). Mechanico-thermal cycling decreased the mean flexural strength values significantly for all six alloy-surface treatment combinations tested when compared to the control groups. The failure type was adhesive in the metal/ceramic interface for specimens surface treated only with the tungsten bur, and mixed for specimens surface treated with APA 10 and 20 mm.Conclusions: Considering the levels adopted in this study, the alloy did not affect the bond strength; APA with Al(2)O(3) at 10 and 20 mm improved the flexural bond strength between ceramics and alloys used, and the mechanico-thermal cycling of metal-ceramic specimens resulted in a decrease of bond strength.

Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading

Objectives. This study evaluated the effect of thermal- and mechanical-cycling on the shear bond strength of three low-fusing glassy matrix dental ceramics to commercial pure titanium (cpTi) when compared to conventional feldspathic ceramic fused to gold alloy.Methods. Metallic frameworks (diameter: 5 min, thickness: 4 mm) (N = 96, n = 12 per group) were cast in cpTi and gold alloy, airborne particle abraded with 150 mu m aluminum oxide. Low-fusing glassy matrix ceramics and a conventional feldspathic ceramic were fired onto the alloys (thickness: 4mm). Four experimental groups were formed; Gr1 (control group): Vita Omega 900-Au-Pd alloy; Gr2: Ticeram-cpTi; Gr3: Super Porcelain Ti-22-cpTi and G4: Vita Titankeramik-cpTi. While half of the specimens from each ceramic-metal combination were randomly tested without aging (water storage at 37 C for 24h only), the other half were first thermocycled (6000 cycles, between 5 and 55 C, dwell time: 13 s) and then mechanically loaded (20,000 cycles under SON load, immersion in distilled water at 37 C). The ceramic-alloy interfaces were loaded under shear in a universal test machine (cross-head speed: 0.5 mm/min) until failure occur-red. Failure types were noted and the interfaces of the representative fractured specimens from each group were examined with stereo microscope and scanning electron microscope (SEM). in an additional study (N = 16, n = 2 per group), energy dispersive X-ray spectroscopy (EDS) analysis was performed from ceramic-alloy interfaces. Data were analyzed using ANOVA and Tukey's test.Results. Both ceramic-metal combinations (p < 0.001) and aging conditions (p < 0,001) significantly affected the mean bond strength values. Thermal- and mechanical-cycling decreased the bond strength (MPa) results significantly for Gr3 (33.4 +/- 4.2) and Gr4 (32.1 +/- 4.8) when compared to the non-aged groups (42.9 +/- 8.9, 42.4 +/- 5.2, respectively). Gr1 was not affected significantly from aging conditions (61.3 +/- 8.4 for control, 60.7 +/- 13.7 after aging) (p > 0.05). Stereomicroscope images showed exclusively adhesive failure types at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface but with a visible dark titanium oxide layer in Groups 2-4 except Gr1 where remnants of bonder ceramic was visible. EDS analysis from the interfacial zone for cpTi-ceramic groups showed predominantly 34.5-85.1% O(2) followed by 1.1-36.7% Aland 0-36.3% Si except for Super Porcelain Ti-22 where a small quantity of Ba (1.4-8.3%), S (0.7%) and Sn (35.3%) was found. In the Au-Pd alloy-ceramic interface, 56.4-69.9% O(2) followed by 15.6-26.2% Si, 3.9-10.9% K, 2.8-6% Na, 4.4-9.6% Al and 0-0.04% Mg was observed.Significance. After thermal-cycling for 6000 times and mechanical-cycling for 20,000 times, Triceram-cpTi combination presented the least decrease among other ceramic-alloy combinations when compared to the mean bond strength results with Au-Pd alloy-Vita Omega 900 combination. (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Mechanical and thermal cycling effects on the flexural strength of glass ceramics fused to titanium

This study evaluated the effects of mechanical and thermal cycling on the flexural strength (ISO 9693) of three brands of ceramics fused to commercially pure titanium (cpTi). Metallic frameworks of 25 x 3 x 0.5 mm dimensions (N = 84) were cast in cpTi, followed by 150-mu m aluminum oxide airborne particle abrasion at a designated area of the frameworks (8 x 3 mm). Bonder and opaque ceramic were applied on the frameworks, and then the corresponding ceramic (Triceram, Super Porcelain Ti-22, Vita Titankeramik) was fired onto them (thickness: 1 mm). Half of the specimens from each ceramic-metal combination were randomly tested without aging (only water storage at 37 degrees C for 24 hours), while the other half were mechanically loaded (20,000 cycles under 10 N load, immersion in distilled water at 37 degrees C) and thermocycled (3,000 cycles, between 5-55 degrees C, dwell time of 13 seconds). After the flexural strength test, failure types were noted. Mechanical and thermal cycling decreased the mean flexural strength values significantly (p<0.05) for all the three ceramic-cpTi combinations tested when compared to the control group. In all the three groups, failure type was exclusively adhesive at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface except for a visible oxide layer.

Synthesis, spectral and thermal studies on dicarboxylate-bridged palladium(II) coordination polymers. Part II

The synthesis and thermal behavior of the new [Pd(fum)(bipy)] (n) center dot 2nH(2)O (1), [Pd(fum)(bpe)] (n) center dot nH(2)O (2) and [Pd(fum)(pz)] (n) center dot 3nH(2)O (3) {bipy = 4,4'-bipyridine, bpe = 1,2-bis(4-pyridyl)ethene and pz = pyrazine} fumarate complexes are described in this work as well their characterization by IR and (13)C CPMAS NMR spectroscopies. TG curves showed that the compounds released organic ligands and lattice water molecules in the temperature range of 46-491 A degrees C. In all the cases, metallic palladium was identified as the final residue.

Germination response of Hylocereus setaceus (Salm-Dyck ex DC: ) Ralf Bauer (Cactaceae) seeds to temperature and reduced water potentials

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal-biological aspects on the seed germination of Cucumis anguria L.: influence of the seed coat

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of addition of different hydrocolloids on pasting, thermal, and rheological properties of cassava starch

Amidos e gomas são hidrocoloides frequentemente usados em sistemas alimentícios com a finalidade de fornecer textura, umidade e mobilidade de água. A interação amido-goma em sistemas alimentícios pode alterar o inchamento do grânulo de amido e as suas propriedades de gelatinização e reológicas. Neste trabalho, o efeito da adição de goma xantana (GX), carboximetilcelulose sódica (CMC) e carragena (CAR) nas concentrações de 0,15, 0,25, 0,35 e 0,45% (p/v) sobre as propriedades de pasta, térmicas e reológicas do amido de mandioca foi estudado. O Poder de inchamento (PI) e a Microscopia Eletrônica de Varredura (MEV) dos géis de amido também foram avaliados. Os resultados obtidos mostraram que a GX apresentou forte interação com o amido, penetrando entre os grânulos e provocando aumento das viscosidades de pasta, PI, G' e G, e redução da retrogradação do amido; CMCS aumentou as viscosidades de pasta, PI, G' e G das misturas, principalmente em função da sua maior capacidade de reter água, e não por causa da interação com o amido; CAR não modificou qualquer das propriedades do amido, porque não houve nenhuma interação entre essa goma e o amido de mandioca nas concentrações usadas.

Maturation of Eugenia pyriformis seeds under different hydric and thermal conditions

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of maltodextrin on the freezing point and thermal conductivity of uvaia pulp (Eugenia piriformis Cambess)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal and mechanical properties of PVDF/PANI blends

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of varying amounts of thermal cycling on bond strength and permanent deformation of two resilient denture liners

Statement of problem. Two problems found in prostheses with resilient liners are bond failure to the acrylic resin base and increased permanent deformation due to material aging.Purpose. This in vitro study evaluated the effect of varying amounts of thermal cycling on bond strength and permanent deformation of 2 resilient denture liners bonded to an acrylic resin base.Material and methods. Plasticized acrylic resin (PermaSoft) or silicone (Softliner) resilient lining materials were processed to a heat-polymerized acrylic resin (QC-20). One hundred rectangular specimens (10 X 10-mm(2) cross-sectional area) and 100 cylindrically-shaped specimens (12.7-mm diameter X 19.0-mm height) for each liner/resin combination were used for the tensile and deformation tests, respectively. Specimen shape and liner thickness were standardized. Specimens were divided into 9 test groups (n=10) and were thermal cycled for 200, 500, 1000, 1500, 2000, 2500, 3000, 3500, and 4000 cycles. Control specimens (n=10) were stored for 24 hours in water at 37degreesC. Mean bond strength, expressed as stress at failure (MPa), was determined with a tensile test using a universal testing machine at a crosshead speed of 5 mm/min. Analysis of failure mode, expressed as a percent (%), was recorded as either cohesive, adhesive, or both, after observation. Permanent deformation, expressed as a percent (%), was determined using ADA specification no. 18. Data from both tests were examined with a 2-way analysis of variance and a Tukey test (alpha=.05).Results. For the tensile test, Softliner specimens submitted to different thermal cycling regimens demonstrated no significantly different bond strength values from the control; however, there was a significant difference between the PermaSoft control group (0.47 +/- 0.09 MPa [mean +/- SD]) and the 500 cycle group (0.46 +/- 0.07 MPa) compared to the 4000 cycle group (0.70 +/- 0.20 MPa) (P<.05). With regard to failure type, the Softliner groups presented adhesive failure (100%) regardless of specimen treatment. PermaSoft groups presented adhesive (53%), cohesive (12%), or a combined mode of failure (35%). For the deformation test, there was no significant difference among the Softliner specimens. However, a significant difference was observed between control and PermaSoft specimens after 1500 or more cycles (1.88% +/- 0.24%) (P<.05).Conclusions. This in vitro study indicated that bond strength and permanent deformation of the 2 resilient denture liners tested varied according to their chemical composition.

Health risk related to radon in a thermal spa utilizing waters from Guarani aquifer

This investigation was carried out within the Parana sedimentary basin, Brazil, involved the sampling of groundwater and air, and was realized with the purpose of evaluating the radioactivity, due to radon gas, in a thermal spa utilizing the waters from Guarani (Botucatu-Piramboia) aquifer. The results reported here provide additional information relative to that of previous studies focusing on the presence of radionuclides in the aquifer, which have mainly characterized those belonging to uranium and thorium series decay, such as the uranium isotopes (U-238 and U-234), radium isotopes (Ra-226 and Ra-228), radon daughters (Bi-214 and Pb-214) and radon (Rn-222) itself the results obtained were compared with the maximum permissible concentration limits in air and drinking water defined by international standards, such as the guidelines for drinking water quality established by the World Health Organization. The possible processes responsible for the presence of radon in the aquifer were also considered in order to evaluate the data obtained.

Simultaneous determination of As, Cu, Mn, Sb, and Se in drinking water by GRAS with transversely heated graphite atomizer and longitudinal Zeeman-effect background correction

A method has been developed for the direct and simultaneous determination of As, Cu, Mn, Sb, and Se in drinking water by electrothermal atomic absorption spectrometry (ETAAS) using a transversely heated graphite tube atomizer (THGA) with longitudinal Zeeman-effect back- ground correction. The thermal behavior of analytes during the pyrolysis and atomization stages was investigated in 0.028 mol L-1 HNO3, 0.14 mol L-1 HNO3 and 1 + 1 (v/v) diluted water using mixtures of Pd(NO3)(2) + Mg(NO3)(2) as the chemical modifier, With 5 mug Pd + 3 mug Mg as the modifier, the pyrolysis and atomization temperatures of the heating program of the atomizer were fixed at 1400degreesC and 2100degreesC, respectively, and 20 muL of the water sample (sample + 0.28 mol L-1 HNO3, 1 + 1, v/v), dispensed into the graphite tube, analytical curves were established ranging from 5.00 - 50.0 mug L-1 for As, Sb, Se; 10.0 - 100 mug L-1 for Cu; and 20.0 - 200 mug L-1 for Mn. The characteristic masses were around 39 pg As, 17 pg Cu, 60 pg Mn, 43 pg Sb, and 45 pg Se, and the lifetime of the tube was around 500 firings. The limits of detection (LOD) based on integrated absorbance (0.7 mug L-1 As, 0.2 mug L-1 Cu, 0.6 mug L-1 Mn, 0.3 mug L-1 Sb, 0.9 mug L-1 Se) exceeded the requirements of the Brazilian Food Regulations (decree # 310-ANVS from the Health Department), which established the maximum permissible level for As, Cu, Mn, Sb, and Se at 50 mug L-1, 1000 mug L-1, 2000 mug L-1, 5 mug L-1, and 50 mug L-1, respectively. The relative standard deviations (n = 12) were typically < 5.3% for As, < 0.5% for Cu, < 2.1% for Mn, < 11.7% for Sb, and < 9.2% for Se. The recoveries of As, Cu, Mn, Sb, and Se added to the mineral water samples varied from 102-111%, 91-107%, 92-109%, 89-97%, and 101-109%, respectively. Accuracy for the determination of As, Cu, Mu Sb and Se was checked using standard reference materials NIST SRM 1640 - Trace Elements in Natural Water, NIST SRM 1643d - Trace Elements in Water, and 10 mineral water samples. A paired t-test showed that the results were in agreement with the certified values of the standard reference materials at the 95% confidence level.

How do cold water biota arrive in a tropical bay near Rio de Janeiro, Brazil?

Previous ecological studies on foraminifera and ostracoda from the tropical Sepetiba Bay, located in the southern part of the State of Rio de Janeiro, Brazil, have noted the presence in this area of some cool water taxons typical of the Argentine continental platform. These studies have proposed that parcels of these temperate waters with their associated biological indicators are advected northward along the platform, penetrating into some tropical entrances of the southeast coast of Brazil. In the present study, ecological data (foraminifera, ostracoda and microbivalves), are used together with information obtained by satellite tracked drifting buoys and digital thermal imagery obtained from NOAA satellites to indicate the path taken by these high latitude species along the southern Brazilian coast to arrive in the Sepetiba Bay, near the city of Rio de Janeiro. Our general conclusion is that biotic elements native to the colder, less saline marine waters seen to the south of Brazil have been and are being advected northward along the inner part of the continental platform to about 22 degrees S. Water parcels containing this biota may, in a sporadic fashion, enter into the tropical Sepetiba Bay. The passage of meteorological fronts through the region is considered to be an important if not the principal mechanism for the sporadic entry of the cool water into the Southern Coastal Entrance of the State of Rio de Janeiro. (C) 1998 Elsevier B.V.s Ltd. All rights reserved.

Evaluation of Ir, Ru, and W as permanent modifiers for the simultaneous determination of As, Bi, Pb, Sb, and Se in natural water by electrothermal atomic absorption spectrometry

Iridium-, Ru-, and W-coated platforms were prepared by thermal treatment of the transversely heated graphite atomizer and investigated for the simultaneous determination of As, Bi, Pb, Sb, and Se in tap water by electrothermal atomic absorption spectrometry. The maximum pyrolysis temperature for As and Bi increased in a modifier sequence W < Ru < Ir. For Pb, Sb, and Se, this sequence was W < Ru, It. Calculated characteristic masses in the presence of It, Ru, and W were 35, 33, and 35 pg for As; 63, 51, and 52 pg for Bi; 50, 32, and 34 pg for Pb; 40, 35, and 31 pg for Sb; and 39, 39, and 93 pg for Se, respectively. Ruthenium was elected as the optimum modifier.Repeatability of the measurements was typically < 6%. Recoveries of As, Bi, Pb, Sb, and Se added to tap water samples varied from 79 to 109%. Accuracy was also checked by analysis of five certified reference materials (CRMs) from the National Institute of Standards and Technology (NIST1640 - Trace Elements in Natural Water; NIST 1643d Trace Elements in Water) and High Purity Standards (Trace Metals in Drinking Water Standards, lots #812708, #591107, and #710710). A paired t-test showed that the results for the CRMs were in agreement at the 95% confidence level with the certified values. The graphite tube lifetime was about 650 firings. multi-element determination is particularly challenging due to the necessity of carefully optimizing compromise conditions.Based on the considerations listed above, the aim of this paper was to evaluate the behavior of Ir, Ru, and W as permanent modifiers for the simultaneous determination of As, Bi, Pb, Sb, and Se. The performance of the proposed procedure was also verified after the ETAAS analysis of tap waters and reference materials.