Effect of surface treatments on the shear bond strength of luting cements to Y-TZP ceramic

Statement of problem Because zirconia is a glass-free material, alternative surface treatments such as airborne-particle abrasion or silica coating should be used for long-term bonding. However, these surface treatments in combination with different bonding agents and luting cements have not yet been studied. Purpose The purpose of the study was to evaluate the effect of surface treatments on the shear bond strength (SBS) of luting cements to Y-TZP ceramic. Material and methods Zirconia disks (N=240) were airborne-particle abraded with the following particles (n=48): 50 μm Al2O3; 120 μm Al2O3; 30 μm silica-coated Al2O3 (Rocatec Soft); 120 μm Al2O3+110 μm silica-coated Al2O3 (Rocatec Plus); and Rocatec Plus. After silanization of the zirconia surface, composite resin disks were bonded with (n=12) RelyX Luting 2; RelyX ARC; RelyX U100; and Panavia F. The bonded specimens were thermocycled (10 000 cycles) and tested for SBS. Failure mode was determined with a stereomicroscope (×20). The morphology and elemental composition of airborne-particle abraded surfaces were evaluated with scanning electron microscopy (×500) and energy-dispersive x-ray spectroscopy (×50). Results Surface treatments, cements, and their interaction were significant (P<.001). For RelyX ARC, Rocatec Soft and Rocatec Plus provided the highest SBS. In general, surface treatments did not influence the SBS of RelyX U100 and Panavia F. Regardless of the cement, no significant difference was found between 50 μm and 120 μm Al2O3 particles, between Rocatec Soft and Rocatec Plus, or between Rocatec Plus and 120 μm Al2O3 particles+Rocatec Plus. All groups showed adhesive failures. Different particle sizes provided differences in morphological patterns. The elemental composition comprised Al and Al/Si for alumina and silica-abraded zirconia. Conclusions Particle size did not influence the SBS of the groups abraded exclusively with alumina or silica-coated particles. RelyX ARC was more surface-treatment dependent than RelyX U100 or Panavia F.

Confiabilidade de coroas com infraestrutura em zircônia sob fadiga deslizante: efeito do tipo de tratamento interno para cimentação

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of thermocycling effect on the bond strength between an aluminous ceramic and a resin cement

This study evaluated the effect of thermocycling on the bond strength between Procera AllCeram (Nobel-Biocare) and a resin cement (Panavia F, Kuraray CO). Nine ceramic blocks with dimensions of 5x6x6mm were conditioned at one face with Rocatec System (Espe). After, they were luted with Panavia F to composite resin blocks (Clearfil AP-X, Kuraray CO). The nine groups formed by ceramic, cement and composite resin were split up obtaining 75 samples with dimensions of 12x1x1mm and adhesive surface presenting 1mm2±0.1mm2 of area. The samples were divided into 3 groups (n=25): G1 - 14 days in distilled water at 37ºC; G2 – 6,000 cycles in water (5ºC - 55ºC – 30s); G3 – 12,000 cycles in water (5ºC - 55ºC – 30s). The samples were tested in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. Data were analyzed by ANOVA and Tukey tests. The results indicated that mean values of rupture tension (MPa) of G1 (10.71 ± 3.54) did not differ statistically (p <5%) from G2 (9.01 ± 3.90), however there was statistical difference between G1 and G3 (7.28 ± 3.00). It was concluded that thermocycling significantly reduced the bond strength values when samples were submitted to 12,000 cycles.

Resistência de união entre um cimento resinoso e uma cerâmica aluminizada submetida a diferentes tratamentos de superfície

Pós-graduação em Odontologia Restauradora - ICT