Microwave synthesis of YAG : Eu by sol-gel methodology

Yttrium-aluminum oxides are interesting compounds and they have been extensively used as host for lasers and phosphors, due to their stable physical and chemical properties. The fabrication of yttrium-aluminum garnet (YAG) has been investigated thoroughly. Single-crystal YAG is expensive and to produce it a new way has been investigated. This process consists of modifying the methodology of reagents mixture and the process of heating them. The microwave irradiation is used to heat-treat the oxide mixture. The traditional synthesis of YAG powders occurs through the reaction of aluminum and yttrium powders at high temperatures. With this work we investigated the preparation of YAG by non-hydrolytic sol-gel route as an alternative methodology to obtain yttrium-aluminum matrix from inorganic precursors (yttrium and aluminum chloride). The preparation of the gel was carried out in an oven-dried glassware. The AlCl3, YCl3 and ethanol were reacted in reflux under argon atmosphere. Europium III chloride was added as a structural probe. The powder was dried and heat-treated in modified microwaves. The samples were pre-treated at 50 and 800 C during I h and then heated in microwaves for 30 s, 2 and 4 min. The formation process and structure of the powders were studied by means of X-ray diffraction (XRD), photoluminescence (PL) and transmission electronic microscopy (TEM). XRD presents only picks corresponding to the YAG phase and confirmed by TEM. PL date showed that the YAG phase was formed in 2 min with the samples pre-treated at 50 C. For the samples pretreated at 800 degrees C, the YAG phase appears in 30s. The excitation spectra present a maximum of 394 nm corresponding to the L-5(6) level and emission spectra of Eu III ion present bands characteristic transitions arising from the D-5(0) -> F-7(J) (J= 1, 2, 3, 4) monifolds excited at their maximum. The magnetic dipole D-5(0) -> F-7(1) transition presents more intensity than the electric dipole D-5(0) -> F-7(2) transition. This methodology showed efficiency in obtaining YAG phase. (c) 2006 Elsevier B.V. All rights reserved.

Formation of SnO2 supported porous membranes

In this work, the effect of the substrate microstructure on the formation of SnO2 membranes and of the sintering conditions on their porosity have been analysed. Samples have been prepared by colloidal suspensions cast on alumina or kaolin substrates. Supported membranes have been characterized by Hg porosimetry, MEV, XRD and N-2 adsorption-desorption isotherms. The results show that the narrower pore size distribution of alumina substrate allowed to prepare membranes more homogeneous and free of cracks than that supported on kaolin. The crystallite and pore sizes of the membranes could be controlled by adjusting the temperature of sintering, allowing materials with adequate microstructure with application for ultrafiltration process.

Structural features of phosphate and sulfate modified zirconia prepared by sol-gel route

This paper describes the effect of sulfate, phosphate and nitrate complexing ligands on the structural features of amorphous xerogels and on the crystallization of metastable zirconia phases during the xerogel-ceramic conversion. Powdered samples were prepared by a sol-gel route using zirconyl chloride precursors chemically modified by complexing ligands. The structural evolution of ZrO2 phases as function of firing temperature was analyzed by XRPD, EXAFS and P-13 NMR/MAS. The experimental results show the formation of metastable t-ZrO2 during the low firing temperature of xerogels modified by sulfate or phosphate groups. The martensitic tetragonal-monoclinic transformation occurs during desorption of sulfate groups. The largest temperature interval of stability of metastable tetragonal zirconia was observed for phosphate-modified xerogels.

Structure of SnO2 alcosols and films prepared by sol-gel dip coating

To obtain SnO2 films to be used for surface protection of fluoride glasses, a non-aqueous sol-gel route for the preparation was developed. An ethanolic SnO2 colloidal suspension was prepared by thermohydrolysis of SnCl4 solution at 70 degreesC. By using this procedure, redispersable powders with nanometer sized particles were obtained. Films were obtained by dip coating on glass and mica substrates. The structures of the ethanolic precursor suspension and films were compared to those of similar samples prepared by the classical aqueous sol-gel route. Comparative analyses performed by photon correlation spectroscopy demonstrated that the powders obtained by freeze-drying are fully redispersable either in aqueous or in alcoholic solutions at pH greater than or equal to 8. As prepared sols and redispersed colloidal suspensions have hydrodynamic radius distribution (2-14 nm) with an average size close to 7 nm. The variations in film structures with firing temperature were investigated by small-angle X-ray scattering and X-ray reflectometry. The experimental results show that the films have a two level porous structure composed of agglomerates of primary colloidal particles. The sintering of the primary particles leads to the densification of agglomerates and to the formation of inter-agglomerate spatially correlated pores. The volume fraction of intra-agglomerate pores is reduced from approximate to 50% to approximate to 30% by the precipitation of precursor salts partially hydrolyzed in ethanolic solution. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Characterization and catalytic activity of 2,6-dichlorophenyl substituted iron(III) porphyrin supported on silica gel and imidazole propyl gel

In this work we have made use of the study of the interaction between Fe(TDCPP)(+) and the axial ligands OH- and imidazole in order to help characterize the heterogenized catalysts Fe(TDCPP)SG and Fe(TDCPP)IPG through UV-VIS and EPR spectroscopies and thus, better understand their different catalytic activity in the oxidation of cyclohexane by PhIO. We have found out that in Fe(TDCPP)SG (containing 1.2 X 10(-6) mol Fe(TDCPP)(+)/g of support), the FeP bis-coordinates to silica gel through Fe-O coordination and it is high-spin (FeP)-P-III species. In Fe(TDCPP)IPG 1 (containing 1.1 X 10(-6) mol Fe(TDCPP)(+) and 2.2 X 10(-4) mol imidazole/g of support), the FeP is bis-ligated to imidazole propyl gel through Fe-imidazole coordination and using NO as a paramagnetic probe, we present evidence that Fe(TDCPP)(+) is present as a mixture of low-spin (FeP)-P-III and (FeP)-P-II species. This catalyst led to a relative low yield of cyclohexanol (25%) because the bis-coordination of the (FeP)-P-III to the support partially blocks the reaction between Fe(TDCPP)(+) and PhIO, thus leading to the formation of only a small amount of the active species Fe-IV(OP+, while the (FeP)-P-II species do not react with the oxygen donor. Increasing the amount of Fe(TDCPP)(+) and decreasing the amount of imidazole in the support led to the obtention of high-spin (FeP)-P-III EPR signals in the spectra of Fe(TDCPP)IPG 5 (containing 4.4 X 10(-6) mol Fe(TDCPP)(+) and 2.2 X 10(-5) mol imidazole/g of IPG), together with low-spin (FeP)-P-III species. This latter catalyst led to better cyclohexanol yields (67%) than Fe(TDCPP)IPG 1. Fe(TDCPP)IPG 5 was further used in a study of the optimization of its catalytic activity and in recycling experiments in the optimized conditions. Recycling oxidation reactions of Fe(TDCPP)IPG 5 led to a total turnover number of 201 and total cyclohexanol yield of 201%, which could not be attained with Fe(TDCPP)Cl in homogeneous solution (turnover = 96) due to the difficulty in recovering and reusing it.

Study of the catalytical intermediates of metalloporphyrins supported on imidazole propyl gel

In this work, the catalytic intermediates for Fe(TPP)(+), Fe(TDCPP)(+), Fe(TFPP)(+), Mn(TPP)(+) and Mn(TDCPP)(+) supported on imidazole propyl gel with PhIO were studied by UV-Vis spectrophotometry. For Fe(TPP)+ and Fe(TFPP)+ the study was also monitored by EPR spectroscopy. The active catalytic intermediate observed for FeP-IPG is the ore-iron (IV) porphyrin pi cation radical Fe-IV(O)P.+, which is evidenced by a decrease in the intensity of the Sorer band. The total re-establishment of the initial Soret band intensity for Fe(TDCPP)IPG and Fe(TFPP)IPG at the end of the reaction shows that they were completely recovered, There are advantages in following the reactions of PNO with unsubstituted Fe(TPP)(+) and Mn(TPP)(+) on IPG by UV-Vis, since they were slower and allowed to 'see' the intermediate species without spectral interference from the recovered catalyst, since they are only partially recovered. With Fe(TPP)IPG, a band at 580 nm was detected at the beginning of the reaction, indicating the possible formation of a Fe-OIPh intermediate. Supporting Mn(TPP)(+) on IPG leads to a shift of band V from 478 nm to 488 nm. In the reaction of MnP-IPG with PhIO, we observed the disappearance of the band in 488 nm and the appearance of a band in 412 nm, which corresponds to the active catalytic intermediate Mn-V(O)P as the main component, as is expected for a more efficient system. The recovery of supported catalysts observed in these experiments was further proved with the possibility of their successive recyclings in cyclohexane oxidation reactions by PhIO.

Rheological study of the thermoreversible sol-gel transition of sulfate modified zirconyl chloride aqueous sol

The sols prepared by mixing a ZrOCl2 acidified solution to a hot H2SO4 aqueous solutions were studied in order to clarify the mechanism of thermoreversible sol-gel transition observed in this system. The viscoelastic properties of these suspensions were analyzed during the sol-gel transition by dynamic rheological measurements and quasi-elastic light scattering. The rheological properties were correlated to mass fractal and nearly linear growth models, and percolation theory. The results evidence that the thermoreversible sol-gel transition in this system is due to the formation of a network of physically linked aggregates having fractal structure. The decrease of the SO42- contents in the initial solution leads to the decrease of the fractal dimensionality from 2.3 to 1.8, indicating a change of the kinetic mechanism of aggregate growth. Near the gel point these samples have the typical scaling expected from percolation theory. (C) 2004 Elsevier B.V. All rights reserved.

Density improvement of the sol-gel dip-coated SnO2 films by chemical surface modification

We compare the effect of organic (Tiron (R)) and inorganic (Mn(11)) additives on the low temperature (< 600 degrees C) densification of the sol-gel dip-coated SnO2 films. The structural and compositional properties of the samples were investigated by X-ray reflectometry (XRR), X-ray absorption spectroscopy (XAS) and X-ray photoelectron spectroscopy (XPS). The results suggest that the replacement of hydroxyl groups at the particle surface by Tiron (R) reduces the level of agglomeration of the sol, increasing the particles packing and the apparent density of the coatings. Undoped and Mn-doped films drawn from a Tiron (R) containing suspension show after firing at 500 degrees C a porosity reduction of 12 and 8.6%, respectively. The porosity decrease is less pronounced (4.3%) for the film without additives. Both XAS and XPS data show the presence of trivalent manganese. The formation of a non-homogeneous solid solution characterised by the presence of Mn(111) replacing tin atom near to the crystallite surface was evidenced by XAS. Additionally, XPS results reveal the presence of metallic Sn at the surface of films containing Tirono. (c) 2005 Elsevier Ltd. All rights reserved.

Tin oxide nanoparticle formation using a surface modifying agent

This work presents results concerning the preparation of redispersible tin oxide nanoparticles achieved by using Tiron molecule ((OH)(2)C(6)H(2) (SO(3)Na)(2)) as surface modifying agent. The adsorption isotherm measurements show that an amount of 10 wt.% of Tiron is need to recover the SnO(2) nanoparticles surface with a monolayer. These nanoparticles can be easily redispersed in tetramethyl ammonium hydroxide at pH greater than or equal to11 until a powder concentration of 12 vol.% of tin. Under these conditions, hydrodynamic particle size is about 7 nm and increases until 52 nm at pH 6 due to the aggregation phenomenon. The time evolution of the viscoelastic properties indicates that the suspensions at pH 12.5, containing 12 vol.% tin oxide and 10 wt.% of surface modifier are kinetically stable. After thermal treatment at different temperature the powder characterisation evidences that the presence of Tiron monolayer at the nanoparticles surface increases the thermal stability of the porous texture and prevent the micropore size growth. This set of results contributes to satisfy the demand for more controlled synthesis of nanoparticles with high thermal stability as required for fabrication of ultrafiltration ceramic membranes. (C) 2004 Elsevier Ltd. All rights reserved.

Thermo-Reversible Sol-Gel Transition of Surface Modified Titanium Poly Oxo Building Blocks

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermo-reversible sol-gel transition of TiO2 nanoparticles with surface modified by p-toluene sulfonic acid

In this paper an unprecedent thermo-reversible sol-gel transition for titania nanoparticles dispersed in a solution of p-toluene sulfonic acid (PTSH) in isopropanol is reported. The sol formed by the thermo-hydrolysis at 60 degrees C of titanium tetraisopropoxide (Ti((OPr)-Pr-i)(4)) reversibly changes into a turbid gel upon cooling to room temperature. Turbidimetric measurements performed for samples containing different nominal acidity ratios (A = [PTSH]/[Ti]) have evidenced that the gel transformation temperature increases from 20 to 35 degrees C as the [PTSH]/[Ti] ratio increases from 0.2 to 2.0. SAXS results indicate that the thermo-reversible gelation is associated to a reversible aggregation of a monodisperse set of titania nanoparticles with average gyration radius of approximate to 2 nm. From the different PTSH species evidenced by Raman spectroscopy and TG/DTA of dried gels we proposed that the then-no-reversible gelation in this systems is induced by the formation of a supramolecular network, in which the protonated surface of nanoparticles is interconnected through cooperative hydrogen bonds between -SO3 groups of p-toluene sulfonic acid. (C) 2009 Elsevier Ltd. All rights reserved.

Influence of viscoelastic characteristics of the colloidal suspensions on the formation of SnO2 supported membranes

SnO2 supported membranes have been prepared by sol-casting on alumina tubular substrate, using aqueous colloidal suspensions prepared by sol-gel route. The viscoelastic behaviour during sol ageing was analyzed by dinamic rheologial measurements. The complex viscosity and the storage and loss moduli have been followed during the sol-gel transition and the results have been correlated with the linear aggregates growth and the scalar percolation models. The scanning electron microscopy has evidenced that the homogeneity and thickness of the membrane depend on the sol ageing time. Crack-free and homogeneous membranes have been obtained for coated layers of 0.5μm thickness. © 1997 Trans Tech Publications.

Monolithic diphasic gels of mullite by sol-gel process under ultrasound stimulation

Diphasic gel in the mullite composition was prepared from a colloidal sol of boehmite mixed with a hydrolyzed tetraethoxisilane (TEOS) solution. The boehmite sol was obtained by peptization of a poorly crystallized or very small mean crystallite size (∼34 Å) precipitate, resulting from the reaction between solutions of aluminum sulfate and sodium hydroxide. Ultrasound was utilized in the processes of the TEOS hydrolysis and the boehmite peptization, and also for complete homogenization of the mixture to gel. The wet gel is almost clear and monolithic. The gel transparency is lost on drying, when syneresis has ended, so that the interlinked pore structure starts to empty and is recovered upon water re-absorption. Cracking closely accompanies this critical drying process. Differential thermal analysis (DTA) and X-ray diffraction (XRD) show that the solid structure of the gel is composed of an amorphous silica phase, as a matrix, and a colloidal sized crystalline phase of boehmite. Upon heat treatment, the boehmite phase within the gel closely follows the same transition sequence as in pure alumina shifted towards higher temperatures. Orthorhombic mullite formation was detected at 1300°C. © 1998 Elsevier Science B.V. All rights reserved.

Effect of 0.4% stannous fluoride gel on Streptococci mutans in relation to elastomeric rings and steel ligatures in orthodontic patients

Background: Patients with fixed orthodontic appliances often experience an absolute increase in the number of Streptococci mutans colony-forming units (cfu). The aim of this investigation was to study the development of biofilm and S. mutans cfu in connection with stainless steel ligatures and elastomeric rings in orthodontic patients treated with and without 0.4% stannous fluoride gel (SFG). Material: Forty-seven patients were divided into 2 groups: those treated with 0.4% SFG for 4 minutes (experimental) and those without 0.4% SFG (control). In each patient, elastomeric rings were used for ligation on 1 side of the dental arch midline, and stainless steel ligatures were used on the opposite side. Saliva samples were collected before and after appliance placement. At 15 and 30 days after appliance placement, biofilm samples from the stainless steel ligatures and the elastomeric rings were collected and subjected to microbiologic procedures and scanning electron microscopy (SEM) analysis. Results: The numbers of S. mutans cfu in the saliva and biofilm were not statistically different between the teeth fitted with elastomeric rings and stainless steel ligatures, or between the experimental and control groups. SEM analysis showed biofilm formation on both ligature ties. Conclusions: Topical application of 0.4% SFG in orthodontic patients with elastomeric rings or stainless steel ligatures does not cause a significant decrease in S. mutans cfu in the saliva and biofilm. Copyright © 2005 by the American Association of Orthodontists.

Temporal evolution of sulfated zirconia sol-gel during dip coating: Analysis of mass drainage with time-varying refractive index

The formation of sulfated zirconia films from a sol-gel derived aqueous suspension is subjected to double-optical monitoring during batch dip coating. Interpretation of interferometric patterns, previously obscured by a variable refractive index, is now made possible by addition of its direct measurement by a polarimetric technique in real time. Significant sensitivity of the resulting physical thickness and refractive index curves (uncertainties of ±7 nm and ±0.005, respectively) to temporal film evolution is shown under different withdrawal speeds. As a first contribution to quantitative understanding of temporal film formation with varying nanostructure during dip coating, detailed analysis is directed to the stage of the process dominated by mass drainage, whose simple modeling with temporal t-1/2 dependence is verified experimentally. © 2006 Elsevier B.V. All rights reserved.