Characterization of BaTi1-xZrxO3 thin films obtained by a soft chemical spin-coating technique

Single-phase perovskite structure BaZrxTi1-xO3 (BZT) (0.05less than or equal toxless than or equal to0.25) thin films were deposited on Pt-Ti-SiO2-Si substrates by the spin-coating technique. The structural modifications in the thin films were studied using x-ray diffraction and micro-Raman scattering techniques. Lattice parameters calculated from x-ray data indicate an increase in lattice (a axis) with the increasing content of zirconium in these films. Such Zr substitution also result in variations of the phonon mode wave numbers, especially those of lower wave numbers, for BaZrxTi1-xO3 thin films, corroborate to the structural change caused by the zirconium doping. on the other hand, Raman modes persist above structural phase transition, although all optical modes should be Raman inactive in the cubic phase. The origin of these modes must be interpreted as a function of a local breakdown of the cubic symmetry, which could be a result of some kind of disorder. The BZT thin films exhibited a satisfactory dielectric constant close to 181-138, and low dielectric loss tan delta<0.03 at the frequency of 1 kHz. The leakage current density of the BZT thin films was studied at elevated temperatures and the data obey the Schottky emission model. Through this analysis the Schottky barrier height values 0.68, 1.39, and 1.24 eV were estimated to the BZT5, BZT15, and BZT25 thin films, respectively. (C) 2004 American Institute of Physics.

Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy

The tendency of the aircraft industry is to enhance customer value by improving performance and reducing environmental impact. In view of availability, aluminum alloys have a historically tendency to faster insertion due to their lower manufacturing and operated production infrastructure. In landing gear components, wear and corrosion control of many components is accomplished by surface treatments of chrome electroplating on steel or anodizing of aluminum. One of the most interesting environmentally safer and cleaner alternatives for the replacement of hard chrome plating or anodizing is tungsten carbide thermal spray coating, applied by the high velocity oxy fuel (HVOF) process. However, it was observed that residual stresses originating from these coatings reduce the fatigue strength of a component.An effective process as shot peening treatment, considered to improve the fatigue strength, pushes the crack sources beneath the surface in most of medium and high cycle cases, due to the compressive residual stress field induced. The objective of this research is to evaluate a tungsten carbide cobalt (WC-Co) coating applied by the high velocity oxy fuel (HVOF) process, used to replace anodizing. Anodic films were grown on 7050-T7451 aluminum alloy by sulfuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on axial fatigue strength of anodic films grown on the aluminum alloy surface is to degrade the stress-life performance of the base material. Three groups of specimens were prepared and tested in axial fatigue to obtain S-N curves: base material, base material coated by HVOF and base material shot peened and coated.Experimental results revealed increase in the fatigue strength of Al 7050-T7451 alloy associated with the WC 17% Co coating. on the other hand, a reduction in fatigue life occurred in the shot peened and coated condition. Scanning electron microscopy technique and optical microscopy were used to observe crack origin sites, thickness and coating/substrate adhesion. (c) 2007 Elsevier B.V. All rights reserved.

SrBi2Nb2O9 thin films deposited by dip coating using aqueous solution

A new approach for SrBi2Nb2O9 (SBN) thin films synthesis using aqueous solution was successfully experienced. The deposition solution was prepared from Sr-Bi-Nb mixed-citrate solution, requiring no special atmosphere and using common reagents. Films were deposited by dip coating onto Pt/Ti/SiO2/Si(100) substrates and hear treated at temperatures ranging from 300 to 700 degrees C. The process of formation and crystallization of SrBi2Nb2O9 thin films, prepared by the aqueous solution method have been studied with particular emphasis on the microstructure of crystallized films. Crystalline phases formation were followed by grazing incident X-ray diffraction (GIXRD), microstructure characterization was evaluated by scanning electron microscopy (SEM) and surface roughness were observed using atomic for ce microscopy (AFM). To reach the desired thickness, substrates were dipped in the deposition solution twice, forming double-layered films. The thickness of each layer ranged from 80 to 100 nm. (C) 1999 Elsevier B.V. Limited. All rights reserved.

Synthesis and photoluminescence study of La1.8Eu0.2O3 coating on nanometric alpha-Al2O3

In this work the La1.8Eu0.2O3 coating on nanometric alpha-alumina, alpha-Al2O3@La1.8Eu0.2O3, was prepared for the first time by a soft chemical method. The powder was heat-treated at 100, 400, 800 and 1200 degrees C for 2 h. X-ray powder diffraction patterns (XRD), transmission electronic microscopy (TEM), emission and excitation spectra, as well as Eu3+, lifetime were used to characterize the material and to follow the changes in structure as the heating temperature increases. The Eu3+ luminescence data revealed the characteristic transitions D-5(0) --> F-7(J) (J = 0, 1 and 3) of Eu3+ at around 580, 591 and 613 nm, respectively, when the powders were excited by 393 nm. The red color of the samples changed to yellow when the powder was annealed at 1200 degrees C. The decrease in the (D-5(0) --> F-7(2))/(D-5(0) --> F-7(1)) ratio from around 5.0 for samples heated at lower temperatures to 3.1 for samples annealed at 1200 degrees C is consistent with a higher symmetry of the Eu3+ at higher temperature. The excitation spectra of the samples also confirms this change by the presence of a more intense and broad band at around 317 nm, instead of the presence of the characteristic peak at 393 mn, which corresponds to the F-7(0) --> L-5(6) transition of the Eu3+. The lifetimes of the D-5(0) --> F-7(2) transition of Eu3+ for the samples heat-treated at 100, 400, 800 and 1200 degrees C was evaluated as 0.57, 0.72, 0.43 and 0.31 ms, respectively. (C) 2006 Elsevier Ltd. All fights reserved.

Microstructure and corrosion resistance of inorganic-organic (ZrO2-PMMA) hybrid coating on stainless steel

Zirconia-polymethylmetacrylate hybrids prepared by a sol-gel method were deposited by dip-coating on stainless steel to improve the resistance against wet corrosion. The effect of the concentration of polymethylmetacrylate and the number of coating applications on the microstructure and corrosion performance of coated samples was investigated. The microstructural properties of samples was analyzed by scanning electron and atomic force microscopy, adhesion tests and profilemeter measurements. The electrochemical corrosion was evaluated through potentiodynamic polarization curves at room temperature. Results show that the sample prepared with 17 vol.% of polymethylmethacrylate has a maximum corrosion resistance, smaller roughness, are hermetic and adherent to the substrate. This film increases the life time of the stainless steel by a factor 30. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Poole-Frenkel effect in Er doped SnO2 thin films deposited by sol-gel-dip-coating

Electrical properties of Er-doped SnO2 thin films obtained by sol-gel-dip-coating technique were measured. When compared to undoped tin dioxide, rare-earth doped films present much higher resistivity, indicating that Er3+ presents an acceptor-like character into the matrix, which leads to a high degree of electric charge compensation. Current-voltage characteristics, measured above room temperature for Er-doped films, lead to non-linear behavior and two conduction regimes. In the lower electric field range the conduction is dominated by Schottky emission over the grain boundary potential barrier, which presents an average value of 0.85 eV. Increasing the applied bias, a second regime of conduction is observed, since the Poole-Frenkel coulombic barrier lowering becomes a significant effect. The obtained activation energy for ionization is 0.67 eV. (C) 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Structure of SnO2 alcosols and films prepared by sol-gel dip coating

To obtain SnO2 films to be used for surface protection of fluoride glasses, a non-aqueous sol-gel route for the preparation was developed. An ethanolic SnO2 colloidal suspension was prepared by thermohydrolysis of SnCl4 solution at 70 degreesC. By using this procedure, redispersable powders with nanometer sized particles were obtained. Films were obtained by dip coating on glass and mica substrates. The structures of the ethanolic precursor suspension and films were compared to those of similar samples prepared by the classical aqueous sol-gel route. Comparative analyses performed by photon correlation spectroscopy demonstrated that the powders obtained by freeze-drying are fully redispersable either in aqueous or in alcoholic solutions at pH greater than or equal to 8. As prepared sols and redispersed colloidal suspensions have hydrodynamic radius distribution (2-14 nm) with an average size close to 7 nm. The variations in film structures with firing temperature were investigated by small-angle X-ray scattering and X-ray reflectometry. The experimental results show that the films have a two level porous structure composed of agglomerates of primary colloidal particles. The sintering of the primary particles leads to the densification of agglomerates and to the formation of inter-agglomerate spatially correlated pores. The volume fraction of intra-agglomerate pores is reduced from approximate to 50% to approximate to 30% by the precipitation of precursor salts partially hydrolyzed in ethanolic solution. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Influence of heat treatment on the optical properties of SnO2 : Sb thin films deposited by dip coating using aqueous solution

Antimony doped tin oxide thin films were deposited on glass by a chemical route derived from Pechini method. Particular emphasis was given to the microstructure of crystallized films. Crystalline phase formation was studied by grazing incident X-ray diffraction and by thermal analyses. Scanning electron microscopy was carried out for microstructure characterization, surface roughness was observed using scanning tunneling microscope and the optical transmittance measurements were performed in the wavelength range of 200-800 nm. (C) 2002 Kluwer Academic Publishers.

Transparent and conductive ZnO : Al thin films prepared by sol-gel dip-coating

Aluminum doped zinc oxide polycrystalline thin films (AZO) were prepared by sol-gel dip-coating process. The sol was prepared from an ethanolic solution of zinc acetate using lithium hydroxide or succinic acid as hydrolytic catalyst. The quantity of aluminum in the sol was varied from 1 to 10 mol%. The structural characteristics studied by X-ray diffractometry were complemented by resistivity measurements and UV-Vis-NIR spectroscopy. The films are transparent from the near ultraviolet to the near infrared, presenting an absorption cut-off at almost 290 nm, irrespective of the nature of the catalyst and doping level. The best conductors were obtained for the AZO films containing 3 mol% of aluminum, prepared under acidic and basic catalysis and sintered at 450 degreesC. Their optical band-gap of 4.4 eV calculated from the absorption cut-off is larger than the values for band-gap widening predicted by the standard model for polar semiconductors. These polycrystalline films are textured with preferential orientation of grains along the wurtzite c-axis or the (100) direction. (C) 2003 Elsevier Ltd. All rights reserved.

Deposition of controlled thickness ultrathin SnO2 : Sb films by spin-coating

The technological interest in transparent conductive oxide films (TCOs) has motivated several works in processing techniques, in order to obtain adequate routes to application. In this way, this work describes a new route to obtain antimony-doped tin oxide (ATO) films, based in colloidal dispersions of oxide nanocrystals. The nanoparticles were obtained by a hydrolisis method, using SnCl2 and SbCl3 in ethanolic solutions. The residual halides were removed by dyalisis, obtaining a limpid and transparent colloidal suspension. By this, the method offers the advantage of producing ultrathin films without organic contaminants. This route was employed to produce films with 5, 10, 14, and 18 mol% Sb doping, with thickness ranging from 40 to 70 nm. The physical characterization of the samples showed a uniform layer deposition, resulting in good packing density and high transmittance. A preliminar electrical study confirmed the low electrical resistivity even in the ultrathin films, in such level similar of reported data. The method described is similar in some aspects to layer-by-layer (LbL) techniques, allowing fine control of thickness and interesting properties for ultrathin films, however, with low cost when compared to similar routes.

Preparation of 9/65/35 PLZT thin films deposited by a dip-coating process

Crack-free polycrystalline PLZT (Pb,a)(Zr,Ti)O-3 thin films with the perovskite structure were prepared by dir-coating using the Pechinis process. Lead acetate, hydrated lanthanum carbonate, zirconium n-propoxide and titanium isopropoxide were used as raw materials. The viscosity of the solution was adjusted in the range of 20 to 56 cP and the films were deposited by a dip-coating process on silicon (100) as substrate. Solutions with ionic concentration of 0.1 and 0.2 M were used. Thin film deposition was accomplished by dipping the substrates in the solution with control of withdrawal speed from 5 to 20 mm/min. The thin films were thermally treated in two steps: at 300 degreesC amid 650 degreesC. The influence of withdrawal speed. viscosity, heating rate and ionic concentration on the morphology of PLZT thin film was discussed. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Hydrogenated amorphous carbon as protective coating for a forming tool

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Lubricating coating prepared by PIIID on a forming tool

In this work, the performance of a-C: H films produced by the hybrid Plasma Immersion Ion Implantation and Deposition technique as lubricating layers for a steel forming tool has been investigated. Hardened steel (AISI M2, 64 HRC) plates coated with a commercial TiN layer were used as substrates and the films were deposited in a vacuum chamber fitted with two parallel-plate electrodes. The discharges were generated in atmospheres composed of 91% C2H2 and 9% Ar by the application of radiofrequency power (13.56 MHz, 100 W) to the upper electrode while the lower one, also used as the sample holder, was biased with high voltage negative pulses (3.6 kV, 30 mu s, 300 Hz). A deposition time of 840 s was used. The effects of the gas pressure, p, on thickness, molecular structure, wettability, surface morphology and topography, hardness and friction coefficient of the films lwere investigated. Film thickness increased from 0.3 to 0.5 mu m when p was increased from 2.7 to 16.5 Pa. Generally, the films were slightly hydrophilic, with contact angles of around 84 degrees, and the deposition decreased the roughness of the steel. A polymer-like structure was detected in high pressure depositions and an amorphous carbon structure derived from the low pressure procedures. Hardness decreased from 8.2 to 7.0 GPa with increasing p. Improvement in tribological performance was indicated by the fall in the friction coefficient from 0.5 to 0.2 as the deposition pressure was reduced. Operating at the latter value (of mu) would lead to a significant reduction in wear and hence to significant economy in diverse industrial applications.

Bioactive coating on titanium implants modified by Nd:YVO4 laser

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)