Effect of moisture on dental enamel in the interaction of two orthodontic bonding systems

OBJECTIVE: The purpose of this study was to assess by means of scanning electron microscopy (SEM) the remaining adhesive interface after debonding orthodontic attachments bonded to bovine teeth with the use of hydrophilic and hydrophobic primers under different dental substrate moisture conditions. MATERIAL AND METHODS: Twenty mandibular incisors were divided into four groups (n=5). In Group I, bracket bonding was performed with Transbond MIP hydrophilic primer and Transbond XT adhesive paste applied to moist substrate, and in Group II a bonding system comprising Transbond XT hydrophobic primer and adhesive paste was applied to moist substrate. Brackets were bonded to the specimens in Groups III and IV using the same adhesive systems, but on dry dental enamel. The images were qualitatively assessed by SEM. RESULTS: The absence of moisture in etched enamel enabled better interaction between bonding materials and the adamantine structure. The hydrophobic primer achieved the worst micromechanical interlocking results when applied to a moist dental structure, whereas the hydrophilic system proved versatile, yielding acceptable results in moist conditions and excellent interaction in the absence of contamination. CONCLUSION: The authors assert that the best condition for the application of primers to dental enamel occurs in the absence of moisture.

Probabilidade de falha de coroas com infraestrutura em zircônia com diferentes geometrias

Pós-graduação em Odontologia Restauradora - ICT

Heat treatment of pre-hydrolyzed silane increases adhesion of phosphate monomer-based resin cement to glass ceramic

This study evaluated the influence of different forms of heat treatment on a pre-hydrolyzed silane to improve the adhesion of phosphate monomer-based (MDP) resin cement to glass ceramic. Resin and feldspathic ceramic blocks (n=48, n=6 for bond test, n=2 for microscopy) were randomly divided into 6 groups and subject to surface treatments: G1: Hydrofluoric acid (HF) 9.6% for 20 s + Silane + MDP resin cement (Panavia F); G2: HF 9.6% for 20 s + Silane + Heat Treatment (oven) + Panavia F; G3: Silane + Heat Treatment (oven) + Panavia F; G4: HF 9.6% for 20 s + Silane + Heat Treatment (hot air) + Panavia F; G5: Silane + Heat Treatment (hot air) + Panavia F; G6: Silane + Panavia F. Microtensile bond strength (MTBS) test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using stereomicroscope and scanning electron microscope (SEM) to categorize the failure types. Data were analyzed statistically using two-way test ANOVA and Tukey's test (=0.05). Heat treatment of the silane containing MDP, with prior etching with HF (G2: 13.15 ± 0.89a; G4: 12.58 ± 1.03a) presented significantly higher bond strength values than the control group (G1: 9.16 ± 0.64b). The groups without prior etching (G3: 10.47 ± 0.70b; G5: 9.47 ± 0.32b) showed statistically similar bond strength values between them and the control group (G1). The silane application without prior etching and heat treatment resulted in the lowest mean bond strength (G6: 8.05 ± 0.37c). SEM analysis showed predominantly adhesive failures and EDS analysis showed common elements of spectra (Si, Na, Al, K, O, C) characterizing the microstructure of the glass-ceramic studied. Heat treatment of the pre-hydrolyzed silane containing MDP in an oven at 100 °C for 2 min or with hot air application at 50 ± 5 ºC for 1 min, was effective in increasing the bond strength values between the ceramic and resin cement containing MDP.

Avaliação dos preparos da superfície cerâmica para a colagem de acessórios ortodônticos

The purpose of this study was to evaluate the effects of two conditioning methods used to enhance the shear strength of orthodontic brackets bonded to porcelain surfaces. A total of 18 feldspathic specimens were used. The specimens were divided randomly into two groups (n = 9): group free silane, the porcelain specimens were etched with hidrofuoric acid 10% (Acid Gel-Maquira) for 4 minutes followed by adhesive-primer (Transbond XT) and the metallic brackets (Morelli Roth Light .022" x .030") were bonded with a light-cured microfilled resin (Transbond XT Light Cure Orthodontic Adhesive); group silane, the porcelain specimens were etched with hidrofuoric acid 10% (Acid Gel-Maquira) for 4 minutes followed by silane (Silano Ângelus) for 1 minute, adhesive-primer (Transbond XT) and the metallic brackets (Morelli Roth Light .022" x .030") were bonded with a light-cured microfilled resin (Transbond XT Light Cure Orthodontic Adhesive). All specimens were stored in solution of artificial saliva at ambient temperature for 24 hours. The debonding was done with shear strength through a universal testing machine (DL 500-Emic) calibrated with a fixed speed of 1mm/minute. Statical analysis was performed using the Student t test. The results indicated that in the free silane group the mean bond strength was 9,97 MPA, significantly lower than the silane group, that was 12,38 MPa (p < 0,05). The both groups were effective for bonding, although the silane group had the highest bond strength values.

Restaurações cerâmicas minimamente invasivas executadas por cirurgiões dentistas com diferentes níveis de experiência profissional: estudo clínico cego, longitudinal e prospectivo

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)