Effects of light-curing time on the cytotoxicity of a restorative resin composite applied to an immortalized odontoblast-cell line

This in vitro study evaluated the cytotoxic effects of a restorative resin composite applied to an immortalized odontoblast-cell line (MDPC-23). Seventy-two round resin discs (2-mm thick and 4 mm in diameter) were light-cured for 20 or 40 seconds and rinsed, or not, with PBS and culture medium. The resin discs were divided into four experimental groups: Group 1: Z-100/20 seconds; Group 2: Z-100/20 seconds/rinsed; Group 3: Z100/40 seconds; Group 4: Z-100/40 seconds/rinsed. Circular filter paper was used as a control material (Group 5). The round resin discs and filter papers were placed in the bottom of wells of four 24-well dishes (18 wells for each experimental and control group). MDPC-23 cells (30,000 cells/cm(2)) were plated in the wells and allowed to incubate for 72 hours. The zone of inhibition around the resin discs was measured under inverted light microscopy; the MTT assay was carried out for mitochondrial respiration and cell morphology was measured under SEM. The scores obtained from inhibition zone and MTT assay were analyzed with the Kruskal-Wallis followed by Dunnett tests. In Groups 1, 2, 3 and 4, the thickness of the inhibition zone was 1,593 +/- 12.82 mum, 403 +/- 15.49 mum, 1,516 +/- 9.81 mum and 313 +/- 13.56 mum, respectively. There was statistically significant difference among the experimental and control groups at the 0.05 level of significance. The MTT assay demonstrated that the resin discs of the experimental groups 1, 2, 3 and 4 reduced the cell metabolism by 83%, 40.1%, 75.5% and 24.5%. Only between the Groups 2 and 4 was there no statistically significant difference for mitochondrial respiration. Close to the resin discs, the MDPC-23 cells exhibited rounded shapes, with only a few cellular processes keeping the cells attached to the substrate or, even disruption of plasma membrane. Adjacent to the inhibition zone, the cultured cells exhibited multiple fine cellular processes on the cytoplasmic membrane organized in epithelioid nodules, similar to the morphology observed to the control group. Based on the results, the authors may conclude that the Z-100 resin composite light cured for 20 seconds was more cytopathic to MDPC-23 cells than Z-100 light cured for 40 seconds. The cytotoxic effects of the resin discs decreased after rinsing them with PBS and culture medium. This was confirmed by MTT assay and upon evaluation of the inhibition zone, which was narrower following rinsing of the resin discs.

The influence of fermentation time and the presence of salts in the rheology of the fermentation broth of a polysaccharide-producing bacteria free of soil

Rheological studies were carried out in the fermentation broth of a polysaccharide-producing microorganism free of soil. This microorganism was designated 4B. The bacteria 4B was inoculated in the fermentation broth, which consisted of a carbon source and mineral salts, and it was incubated in a rotating agitator at 30 degreesC for 72 h at 210 rpm. A rheometer of concentric cylinders equipped with a thermostatic bath was used and the readings were taken at 25 degreesC. A study was made of the influence of the fermentation time and the readings were made after 24, 48 and 72 h of incubation, using, separately, sucrose and glucose as carbon sources. The influence of the salt concentrations was determined in each carbon source; the salts used were NaCl, KCl and CaCl2 in the concentrations of 0.4%, 1.0%, 2.0% and 3.0%. It was observed that the fermentation broth behaves as a non-Newtonian fluid and it presents pseudoplastic behaviour. Calculations were made of the flow behaviour index (n) and the consistency index (k) of the samples after 24, 48 and 72 h of fermentation, and it was observed that the 72 h sample presented higher k and consequently higher apparent viscosity. of the carbon sources used, the sucrose presented higher viscous broths after 24 and 48 h, and the glucose after 72 h of fermentation. With relation to the effect of the addition of salts, the CaCl2 presented a higher influence on the viscosity of the fermentation broths. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Unrestricted linear dimensional changes of two hard chairside reline resins and one heat-curing acrylic resin

The selection and use of hard chairside reline resins must be made with regard to dimensional stability, which will influence the accuracy of fit of the denture base. This study compared the dimensional change of two hard chairside reline resins (Duraliner II and Kooliner) and one heat-curing denture base resin (Lucitone 550). A stainless steel mold with reference dimensions (AB, CD) was used to obtain the samples. The materials were processed according to the manufacturer's recommendations. Measurements of the dimensions were made after processing and after the samples had been stored in distilled water at 37° C for eight different periods of time. The data were recorded and then analyzed with analysis of variance. All materials showed shrinkage immediately after processing (p < 0.05). The only resin that exhibited shrinkage after 60 days of storage in water was Duraliner II; these changes could be clinically significant in regard of tissue fit.

Calcium salts deposition in rat connective tissue after the implantation of calcium hydroxide-containing sealers

This study was conducted to observe the rat subcutaneous connective tissue reaction to implanted dentin tubes that were filled with mineral trioxide aggregate, Sealapex, Calciobiotic Root Canal Sealer (CRCS), Sealer 26, and the experimental material, Sealer Plus. The animals were sacrificed after 7 and 30 days, and the specimens were prepared for histological analysis after serial sections with a hard-tissue microtome. The undecalcified sections were examined with polarized light after staining according to the Von Kossa technique for calcium. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was irregular tissue, like a bridge, that was Von Kossa-positive. The dentin walls of the tubes exhibited a structure highly birefringent to polarized light, usually like a layer, in the tubules. These results were observed with all the studied materials, except the CRCS, which didn't exhibit any kind of mineralized structure. The results suggest that among the materials studied, the CRCS could have the least possibility of encouraging hard tissue deposition.

The influence of chemical activation on hardness of dual-curing resin cements.

During the cementation of metallic restorations, the polymerization of dual-curing resin cements depends exclusively on chemical activation. This study evaluated the influence of chemical activation compared with dual-curing (chemical and light activation), on the hardness of four dual-curing resin cements. In a darkened environment, equal weight proportions of base and catalyst pastes of the cements Scotchbond Resin Cement, Variolink II, Enforce and Panavia F were mixed and inserted into moulds with cavities of 4 mm in diameter and 2 mm in height. Subsequently, the cements were: 1) not exposed to light (chemical activation = self-cured groups) or 2) photoactivated (dual-curing = dual-cured groups). The Vickers hardness number was measured at 1 hour, 24 hours and 7 days after the start time of cements' spatulation. For all the cements, the hardness values of self-cured groups were lower than those of the respective dual-cured groups at 1 hour and 24 hours. At 7 days, this behavior continued for Variolink II and Panavia F, whilst for Scotchbond Resin Cement and Enforce there was no statistical difference between the two activation modes. All cements showed a significant increase in their hardness values from 1 hour to 7 days for both activation modes. Of the self-cured groups, Scotchbond Resin Cement and Variolink II presented the highest and the lowest hardness values, respectively, for all three times tested. Within the limitations of this study, up to the time of 24 h, chemical activation alone was unable to promote similar hardness as to that obtained with dual-curing.

Influence of activation modes on diametral tensile strength of dual-curing resin cements.

In metallic restorations, the polymerization of dual-curing resin cements depends exclusively on chemical activation. The effect of the lack of photoactivation on the strength of these cements has been rarely studied. This study evaluated the influence of activation modes on the diametral tensile strength (DTS) of dual-curing resin cements. Base and catalyst pastes of Panavia F, Variolink II, Scotchbond Resin Cement, Rely X and Enforce were mixed and inserted into cylindrical metal moulds (4 x 2 mm). Cements were either: 1) not exposed to light (chemical activation = self-cured groups) or 2) photoactivated through mylar strips (chemical and photo-activation = dual-cured groups) (n = 10). After a 24 h storage in 37 masculineC distilled water, specimens were subjected to compressive load in a testing machine. A self-curing resin cement (Cement-It) and a zinc phosphate cement served as controls. Comparative analyses were performed: 1) between the activation modes for each dual-curing resin cement, using Students t test; 2) among the self-cured groups of the dual-curing resin cements and the control groups, using one-way ANOVA and Tukeys test (alpha = 0.05). The dual-cured groups of Scotchbond Resin Cement (53.3 MPa), Variolink II (48.4 MPa) and Rely X (51.6 MPa) showed higher DTS than that of self-cured groups (44.6, 40.4 and 44.5 MPa respectively) (p < 0.05). For Enforce (48.5 and 47.8 MPa) and Panavia F (44.0 and 43.3 MPa), no significant difference was found between the activation modes (p > 0.05). The self-cured groups of all the dual-curing resin cements presented statistically the same DTS as that of Cement-It (44.1 MPa) (p > 0.05), and higher DTS than that of zinc phosphate (4.2 MPa). Scotchbond Resin Cement, Variolink II and Rely X depended on photoactivation to achieve maximum DTS. In the absence of light, all the dual-curing resin cements presented higher DTS than that of zinc phosphate and statistically the same as that of Cement-It (p > 0.05).

Influence of light curing source on microhardness of composite resins of different shades

Introduction: The evolution of light curing units can be noticed by the different systems recently introduced. The technology of LED units promises longer lifetime, without heating and with production of specific light for activation of camphorquinone. However, further studies are still required to check the real curing effectiveness of these units. Purpose: This study evaluated the microhardness of 4 shades (B-0.5, B-1, B-2 and B-3) of composite resin Filtek Z-250 (3M ESPE) after light curing with 4 light sources, being one halogen (Ultralux - Dabi Atlante) and three LED (Ultraled - Dabi Atlante, Ultrablue - DMC and Elipar Freelight - 3M ESPE). Methods: 192 specimens were distributed into 16 groups, and materials were inserted in a single increment in cylindrical templates measuring 4mm x 4mm and light cured as recommended by the manufacturer. Then, they were submitted to microhardness test on the top and bottom aspects of the cylinders. Results: The hardness values achieved were submitted to analysis of variance and to Tukey test at 5% confidence level. It was observed that microhardness of specimens varied according to the shade of the material and light sources employed. The LED appliance emitting greater light intensity provided the highest hardness values with shade B-0.5, allowing the best curing. On the other hand, appliances with low light intensity were the least effective. It was also observed that the bottom of specimens was more sensitive to changes in shade. Conclusion: Light intensity of LED light curing units is fundamental for their good functioning, especially when applied in resins with darker shades.

Relationships between the curing conditions and some mechanical properties of hybrid thermosetting materials

The relationship between the heat of polymerization (ΔH) and activation energy (Ea) parameters, obtained by differential scanning calorimetry (DSC) and the ratio of epoxy resin to hardener of the thermosetting materials based on an organic-inorganic hybrid epoxy resin (OG) was investigated. Activation energy (Ea) and heat of polymerization (ΔH) increased with an increasing OG content, up to 70 wt%. Further increase in OG content to 80wt% reduced Ea and ΔH. Dynamic mechanical analysis indicates that the maximum cross-link density is obtained at 83 wt% OG, whereas fracture toughness and tensile modulus mechanical properties are maximized at 70 wt% OG. ©2006 Sociedade Brasileira de Química.

Influence of cavity preparation and curing method on the marginal seal of resin composite restorations: an in vitro evaluation.

OBJECTIVE: To evaluate the influence of cavity design and photocuring method on the marginal seal of resin composite restorations. METHOD AND MATERIALS: Seventy-two bovine teeth were divided into 2 groups: group 1 received box-type cavity preparations, and group 2 received plate-type preparations. Each group was divided into 3 subgroups. After etching and bonding, Z250 resin composite (3M Espe) was applied in 2 equal increments and cured with 1 of 3 techniques: (1) conventional curing for 30 seconds at 650 mW/cm2; (2) 2-step photocuring, in which the first step was performed 14 mm from the restoration for 10 seconds at 180 mW/cm2 and the second step was performed in direct contact for 20 seconds at 650 mW/cm2; or (3) progressive curing using Jetlite 4000 (J. Morita) for 8 seconds at 125 mW/cm2 and then 22 seconds at 125 mW/cm2 up to 500 mW/cm2. The specimens were thermocycled for 500 cycles and then submitted to dye penetration with a 50% silver nitrate solution. Microleakage was assessed using a stereomicroscope. Data were analyzed using analysis of variance and Tukey test (5% level of significance). RESULTS: A statistically significant difference was found between groups when a double interaction between photocuring and cavity preparation was considered (P = .029). CONCLUSIONS: No one type of cavity preparation or photocuring method prevented micro-leakage. The plate-type preparation showed the worst dye penetration when conventional and progressive photocuring methods were used. The best results were found using the 2-step photocuring with the plate-type preparation.

Diametral tensile strength of dual-curing resin cements submitted exclusively to autopolymerization.

OBJECTIVES: To evaluate, at different times, the diametral tensile strength (DTS) of dual-curing resin cements that were not photopolymerized. METHOD AND MATERIALS: Equal amounts of base and catalyst pastes of Panavia F (Kuraray), Variolink II (Vivadent), Rely X (3M ESPE), and Enforce (Dentsply) were mixed and inserted into cylindrical molds (4 x 2 mm) (n = 10). Cements were not photopolymerized. DTS test was performed in a testing machine at 30 minutes, 1 hour, 24 hours, and 7 days. The specimens were stored in light-proof containers with distilled water at 37 degrees C until the time of assay. An autopolymerizing resin cement (Cement-It, Jeneric Pentron) and a zinc phosphate cement served as controls. One-way analysis of variance (ANOVA) and Tukey test were performed separately for each cement and for each time (P <.05). RESULTS: All cements showed an increase in DTS when tested at 1 and 24 hours. Tests at 24 hours and 7 days revealed no statistically significant differences. In all groups, the zinc phosphate cement had the lowest DTS mean values (2.1 MPa, 3.6 MPa, 6.5 MPa, and 6.9 MPa), while Cement-It (35.1 MPa, 33.6 MPa, 46.9 MPa, and 46.3 MPa) and Enforce (31.9 MPa, 31.7 MPa, 43.4 MPa, and 47.6 MPa) presented the highest DTS mean values. CONCLUSION: All cements presented maximal strength at 24 hours. The dual-curing resin cements, even when nonphotopolymerized, demonstrated higher DTS than the zinc phosphate cement and similar or lower values than the autopolymerizing resin cement.

The effect of different light-curing units on tensile strength and microhardness of a composite resin

The aim of this study was to evaluate the influence of different light-curing units on the tensile bond strength and microhardness of a composite resin (Filtek Z250 - 3M/ESPE). Conventional halogen (Curing Light 2500 - 3M/ESPE; CL) and two blue light emitting diode curing units (Ultraled - Dabi/Atlante; UL; Ultrablue IS - DMC; UB3 and UB6) were selected for this study. Different light intensities (670, 130, 300, and 600 mW/cm2, respectively) and different curing times (20s, 40s and 60s) were evaluated. Knoop microhardness test was performed in the area corresponding to the fractured region of the specimen. A total of 12 groups (n=10) were established and the specimens were prepared using a stainless steel mold composed by two similar parts that contained a cone-shaped hole with two diameters (8.0 mm and 5.0 mm) and thickness of 1.0 mm. Next, the specimens were loaded in tensile strength until fracture in a universal testing machine at a crosshead speed of 0.5 mm/min and a 50 kg load cell. For the microhardness test, the same matrix was used to fabricate the specimens (12 groups; n=5). Microhardness was determined on the surfaces that were not exposed to the light source, using a Shimadzu HMV-2 Microhardness Tester at a static load of 50 g for 30 seconds. Data were analyzed statistically by two-way ANOVA and Tukey's test (p<0.05). Regarding the individual performance of the light-curing units, there was similarity in tensile strength with 20-s and 40-s exposure times and higher tensile strength when a 60-s light-activation time was used. Regarding microhardness, the halogen lamp had higher results when compared to the LED units. For all light-curing units, the variation of light-exposure time did not affect composite microhardness. However, lower irradiances needed longer light-activation times to produce similar effect as that obtained with high-irradiance light-curing sources.

Influence of pre-heat treatment and different light-curing units on Vickers hardness of a microhybrid composite resin

The aim of this study was to evaluate the hardness of a dental composite resin submitted to temperature changes before photo-activation with two light-curing unite (LCUs). Five samples (4 mm in diameter and 2 mm in thickness) for each group were made with pre-cure temperatures of 37, 54, and 60°C. The samples were photo-activated with a conventional quartz-tungsten-halogen (QTH) and blue LED LCUs during 40 s. The hardness Vickers test (VHN) was performed on the top and bottom surfaces of the samples. According to the interaction between light-curing unit and different pre-heating temperatures of composite resin, only the light-curing unit provided influences on the mean values of initial Vickers hardness. The light-curing unit based on blue LED showed hardness mean values more homogeneous between the top and bottom surfaces. The hardness mean values were not statistically significant difference for the pre-cure temperature used. According to these results, the pre-heating of the composite resin provide no influence on Vickers hardness mean values, however the blue LED showed a cure more homogeneous than QTH LCU. © 2009 Pleiades Publishing, Ltd.

Effect of light-curing units on push-out fiber post bond strength in root canal dentin

The purpose of this study was to evaluate the effectiveness of different light-curing units on the bond strength (push-out) of glass fiber posts in the different thirds of the root (cervical, middle and apical) with different adhesive luting resin systems (dual-cure total-etch; dual-cured and self-etch bonding system; and dual-cure self-adhesive cements), Disks of the samples (n = 144) were used, with approximately 1 mm of thickness of 48 bovine roots restored with glass fiber posts, that were luted with resin cements photo-activated by halogen LCU (QTH, Optilux 501) and blue LED (Ultraled), with power densities of 600 and 550 mW/cm 2, respectively. A universal testing machine (MTS 810 Material Test System) was used with a 1 mm diameter steel rod at cross-head speed of 0.5 mm/min until post extrusion, with load cell of 50 kg, for evaluation of the push-out strength in the different thirds of each sample. The push-out strength values in kgf were converted to MPa and analyzed through Analysis of Variance and Tukey's test, at significance level of 5%. The results showed that there were no statistical differences between the QTH and LED LCUs. The self-adhesive resin cement had lower values of retention. The total-etch and self-adhesive system resin cements seem to be a possible alternative for glass fiber posts cementation into the radicular canal and the LED LCU can be applied as an alternative to halogen light on photo-activation of dual-cured resin cements. © 2009 Pleiades Publishing, Ltd.

Effect of light-curing method and indirect veneering materials on the Knoop hardness of a resin cement

This study evaluated the Knoop hardness of a dual-cured resin cement (Rely-X ARC) activated solely by chemical reaction (control group) or by chemical / physical mode, light-cured through a 1.5 mm thick ceramic (HeraCeram) or composite (Artglass) disc. Light curing was carried out using conventional halogen light (XL2500) for 40 s (QTH); light emitting diodes (Ultrablue Is) for 40 s (LED); and Xenon plasma arc (Apollo 95E) for 3 s (PAC). Bovine incisors had their buccal face flattened and hybridized. On this surface a rubber mold (5 mm in diameter and 1 mm in height) was bulk filled with the resin cement. A polyester strip was seated for direct light curing or through the discs of veneering materials. After dry storage in the dark (24 h 37°C), the samples (n = 5) were sectioned for hardness (KHN) measurements, taken in a microhardness tester (50 gF load 15 s). The data were statistically analyzed by ANOVA and Tukey's test (α = 0.05). The cement presented higher Knoop hardness values with Artglass for QTH and LED, compared to HeraCeram. The control group and the PAC/Artglass group showed lower hardness values compared to the groups light-cured with QTH and LED. PAC/HeraCeram resulted in the worst combination for cement hardness values. © 2009 Sociedade Brasileira de Pesquisa Odontológica.