300 resultados para Class V restorations
Resumo:
Purpose: To evaluate the effects of removing dentin collagen exposed by acid etching on the microleakage of bonded restorations with and without flowable composite application and submitted to thermocycling and long-term water storage. Materials and Methods: Standardized Class V cavities were prepared in 180 bovine incisors. They were randomly assigned to three groups according to the adhesive technique used. Conventional group (C): Single Bond was applied according to the manufacturer's instructions and Z250 composite was placed. Hypochlorite group (H): After acid etching a 10% NaOCl aqueous solution was applied for 1 min, then Single Bond and Z250 were applied. Hypochlorite and Flowable group (HF): Similar to group H, but following adhesive application, a thin layer of Natural Flow flowable composite was applied before the Z250. Each group was divided into three subgroups (0, 6, 12), which remained immersed in distilled water for 24 h or 6 or 12 months and underwent 500, 1500 or 2500 thermal cycles, respectively. At the end of each storage time, the specimes were stained with silver nitrate, decalcified, immersed in methyl salicylate for clearing and observed under a stereomicroscope to determine microleakage (scores 0 to 4). The data were analyzed using the Kruskal-Wallis and the Multiple Comparison Tests (α = 0.05). Results: After 12 months, every group showed significant increases in microleakage. There was no significant difference between Groups H and HF for the three different periods of time, but they showed statistically less microleakage than Group C. Conclusion: The removal of dentinal collagen reduced the marginal microleakage when compared to the conventional technique. The use of the flowable composite did not produce significant effects. No technique was completely effective in preventing microleakage.
Resumo:
Purpose: This study tested the null hypothesis that different treatments of saliva-contaminated substrate would not affect microgap formation at the dentin walls of bonded restorations. Materials and Methods: Forty freshly extracted human molars received standardized Class V preparations on buccal and lingual surfaces. The specimens were assigned to four experimental groups (n = 20): [G1] no contamination (control group), [G2] saliva contamination (10 s) after etching followed by 5 s air stream; [G3] saliva contamination after etching and rinsed for 10 s; and [G4] re-etching for 10 s after saliva contamination. All specimens were restored with a one-bottle adhesive (Single Bond, 3M ESPE) and microhybrid composite resin (Filtek Z250, 3M ESPE) according to the manufacturer's instructions. The specimens were thermocycled, sectioned through the center of the restoration, and then processed for SEM. Microgaps were measured at the axial wall at 1500X magnification. The data were submitted to Kruskal-Wallis nonparametric statistical analysis at p < 0.05. Results: The data revealed that different groups resulted in a statistically significant difference (p < 0.01) in gap formation. Air drying [G2] and rinsing [G3] the saliva-contaminated dentin resulted in similar microgap values (p > 0.05). However, re-etching the dentin after saliva contamination [G4] increased microgap formation (p < 0.05) when compared with the groups G1 and G2. Although air drying and rinsing produced results comparable to noncontaminated dentin, the presence of microgaps was not completely eliminated. Conclusion: Contaminated saliva did not prevent hybrid layer formation; however, it did reduce the adaptation of the restorative material to bonded surfaces.
Resumo:
Purpose: The aim of this study was to evaluate the interfacial microgap with different materials used for pulp protection. The null hypothesis tested was that the combination of calcium hydroxide, resin-modified glass ionomer, and dentin adhesive used as pulp protection in composite restorations would not result in a greater axial gap than that obtained with hybridization only. Materials and Methods: Standardized Class V preparations were performed in buccal and lingual surfaces of 60 caries-free, extracted human third molars. The prepared teeth were randomly assessed in six groups: (1) Single Bond (SB) (3M ESPE, St. Paul, MN, USA); (2) Life (LF) (Kerr Co., Romulus, MI, USA) + SB; (3) LF + Vitrebond (VT) (3M ESPE) + SB; (4) VT + SB; (5) SB + VT; (6) SB + VT + SB. They were restored with microhybrid composite resin Filtek Z250 (3M ESPE), according to the manufacturer's instructions. However, to groups 5 and 6, the dentin bonding adhesive was applied prior to the resin-modified glass ionomer. The specimens were then thermocycled, cross-sectioned through the center of the restoration, fixed, and processed for scanning electron microscopy. The specimens were mounted on stubs and sputter coated. The internal adaptation of the materials to the axial wall was analyzed under SEM with × 1,000 magnification. Results: The data obtained were analyzed with nonparametric tests (Kruskal-Wallis, p ≤ .05). The null hypothesis was rejected. Calcium hydroxide and resin-modified glass ionomer applied alone or in conjunction with each other (p < .001) resulted in statistically wider microgaps than occurred when the dentin was only hybridized prior to the restoration. ©2005 BC Decker Inc.
Resumo:
Purpose: The purpose of this study was to verify the influence of surface sealants and dentin adhesive systems on the microleakage of composite restorations. Methods: Class V cavities were made on the buccal faces of 100 permanent third molars and restored with Z250. After 24 hours, they were submitted to polishing and finishing processes. The teeth were divided into groups according to the sealant agent: group 1 - Single Bond; group 2 - Opti Bond Solo Plus; group 3 - Fortify; group 4 - Fortify Plus; and group 5 - control without sealant. The analysis of immediate microleakage was performed in 10 restorations from each group, soon after the sealing. The other 10 specimens from each group were submitted to tooth-brushing and thermal cycles. The teeth were isolated and immersed in 2% methylene blue solution, washed in tap water, and sectioned in the buccolingual direction. The percentage of marginal leakage was calculated using an image analysis program, and results were submitted to analysis of variance and Tukey's test. Results: All the sealed groups demonstrated lower microleakage values compared to the control group. Group 3, sealed with Fortify, presented the lowest mean microleakage values. Conclusion: The application of surface sealants effectively decreased the microleakage in composite resin restorations.
Resumo:
Pós-graduação em Ciências Odontológicas - FOAR
Resumo:
Pós-graduação em Odontologia Restauradora - ICT
Resumo:
The aim of this study was to compare the efficacy of a direct clinical evaluation method with an indirect digital photographic method in assessing the quality of dental restorations. Seven parameters (color, occlusal marginal adaptation, anatomy form, roughness, occlusal marginal stain, luster, and secondary caries) were assessed in 89 Class I and Class II restorations from 36 adults using the modified US Public Health Service/Ryge criteria. Standardized photographs of the same restorations were digitally processed by Adobe Photoshop software, separated into the following four groups and assessed by two calibrated examiners: Group A: The original photograph displayed at 100%, without modifications (IMG100); Group B: Formed by images enlarged at 150% (IMG150); Group C: Formed by digital photographs displayed at 100% (mIMG100), with digital modifications (levels adjustment, shadow and highlight correction, color balance, unsharp Mask); and Group D: Formed by enlarged photographs displayed at 150% with modifications (mIMG150), with the same adjustments made to Group C. Photographs were assessed on a calibrated screen (Macbook) by two calibrated clinicians, and the results were statistically analyzed using Wilcoxon tests (SSPS 11.5) at 95% CI. Results: The photographic method produced higher reliability levels than the direct clinical method in all parameters. The evaluation of digital images is more consistent with clinical assessment when restorations present some moderate defect (Bravo) and less consistent when restorations are clinically classified as either satisfactory (Alpha) or in cases of severe defects (Charlie). Conclusion: The digital photographic method is a useful tool for assessing the quality of dental restorations, providing information that goes unnoticed with the visual-tactile clinical examination method. Additionally, when analyzing restorations using the Ryge modified criteria, the digital photographic method reveals a significant increase of defects compared to those clinically observed with the naked eye. Photography by itself, without the need for enlargement or correction, provides more information than clinical examination and can lead to unnecessary overtreatment.
Resumo:
Background: the purpose of this study was to histomorphometrically evaluate the response of periodontal tissues covering Class V resin restorations in dogs.Methods: After raising a mucoperiosteal flap, bony defects measuring 5 x 5 mm were created on the buccal aspect of the canines of five dogs followed by cavity preparations on the root surface measuring 3 x 3 x 1 mm. Before repositioning the flap to cover the bone defect, the cavities were restored with composite resin (CR) or resin-modified glass ionomer cement (RMGIC) or were left unrestored as control (C). The dogs were euthanized 90 days after surgery. Specimens comprising the tooth and periodontal tissues were removed, processed routinely, cut into longitudinal serial sections in the bucco-lingual direction, and stained with hematoxylin and eosin (H&E) or Masson's trichrome. The most central sections were selected for histomorphometric analysis.Results: Histomorphometric analysis revealed apical migration of epithelial tissue onto the restorative materials (RMGIC and CR). The C group presented significantly longer connective tissue attachment (P < 0.05) than the RMGIC and CR groups and significantly higher bone regeneration (P < 0.05) compared to the RMGIC group. Histologically, the cervical third (CT) of all groups had the most marked chronic inflammatory infiltrate.Conclusions: Within the limits of this study, it can be concluded that the restorative materials used exhibit biocompatibility; however, both materials interfered with the development of new bone and the connective tissue attachment process.
Resumo:
The purpose of this in vitro study was to investigate the cervical marginal leakage in class II restorations with chemically cured resin (P10) and light-cured resin (P30) in two types of cavities: conventional and adhesive. The effect of acid-etching in this area was also observed. Dentine adhesive Scotchbond was used in all experimental groups. Leakage was evidenced by Rodamina B dye penetration after thermocycling procedure between 10 degrees C and 50 degrees C temperature and analysed by using Zeiss Stereoscopic Magnifying Glass (10 X). According to the results obtained marginal leakage occurred in all experimental groups, with lower percentage for adhesives cavities when enamel acid-etching and light-cured resin P30 was used.
Resumo:
The purpose of this in vivo study was to evaluate the clinical performance of a posterior composite resin TRH (Caulk Dentisply) in class I restorations in primary molars. A total of 30 children aged 5 to 8 years old with 49 class I dental lesions in primary molars participated in the study. The cavity preparations involved removal of carious lesion only and the enamel margins were beveled. The results showed after 30 months that, 82% (32/39) of Alfa ratings and 18% (7/39) of Bravo ratings. We concluded that the composite resin TP-H could be used in conservative restorations in primary molars, particularly in the late mixed dentition.
Resumo:
This study assessed cavity preparations produced with different air abrasion tip parameters. Twelve test groups of extracted teeth were prepared to evaluate the parameters of 80 degrees or 45 degrees nozzle angles and 0.38 or 0.48 mm inner tip diameters. All other factors were held constant. A device was made to hold the specimen and air abrasion handpiece that standardized the distance and position relative to the tooth and time of application. The cavities were evaluated by assessing the rounding of the cavosurface margins and cavity floor. Measurements of cavosurface angles and the angle of concavity were made at the deepest portion of the abraded surface using scanning electron micrographs. The cavosurface angles were compared using paired t-test, and the effects of the tip design parameters were analyzed by ANOVA and Duncan's Multiple Range test. From the cavity patterns found in this study, the authors suggest that 80 degrees angle tips are more appropriate than 45 degrees angle tips for making narrow, deep cuts for preventive resin restorations. Conversely, when shallow preparations are needed, as in the case of Class V cavity preparations, cutting patterns of 45 degrees angle tips are more suitable.
Resumo:
Objective: To measure 2-week postoperative sensitivity in Class II composite restorations placed with a self-etching adhesive (Clearfil SE Bond) or a total-etch adhesive (Prime&Bond NT) with or without a flowable composite as cervical increment. Method and materials: Upon approval by the University of Guarulhos Committee on Human Subjects, 100 restorations were inserted in 46 patients who required Class II restorations in their molars and premolars. Enamel and dentin walls were conditioned with a self-etching primer (for Clearfil SE Bond) or etched with 34% phosphoric acid (for Prime&Bond NT). A 1- to 2-mm-thick increment of a flowable composite (Filtek Flow) was used in the proximal box in 50% of the restorations of each adhesive. Preparations were restored with a packable composite (Surefil). The restorations were evaluated preoperatively and 2 weeks postoperatively for sensitivity to cold, air, and masticatory forces using a visual analog scale. Marginal integrity of the accessible margins was also evaluated. Statistical analysis used a mixed linear model with subject as a random effect. Results: Ninety-eight teeth from 44 subjects were observed at 2 weeks. The type of adhesive and use of flowable composite had no significant effects or interaction for any of the four outcomes of interest, ie, change from baseline to 2 weeks in sensitivity and response time for the cold or air stimulus. For the air stimulus, the overall average change from baseline was not significant for either sensitivity or response time. For the cold stimulus, the overall average change from baseline was significant for both sensitivity and response time. No case of sensitivity to masticatory forces was observed. Conclusion: No differences in postoperative sensitivity were observed between a self-etch adhesive and a total-etch adhesive at 2 weeks. The use of flowable composite did not decrease postoperative sensitivity.
Resumo:
Host-derived proteases have been reported to degrade the collagen matrix of incompletely-resin-infiltrated dentin. This study tested the hypothesis that interfacial degradation of resin-dentin bonds may be prevented or delayed by the application of chlorhexidine (CHX), a matrix metalloproteinase inhibitor, to dentin after phosphoric acid-etching. Contralateral pairs of resin-bonded Class I restorations in non-carious third molars were kept under intra-oral function for 14 months. Preservation of resin-dentin bonds was assessed by microtensile bond strength tests and TEM examination. In vivo bond strength remained stable in the CHX-treated specimens, while bond strength decreased significantly in control teeth. Resin-infiltrated dentin in CHX-treated specimens exhibited normal structural integrity of the collagen network. Conversely, progressive disintegration of the fibrillar network was identified in control specimens. Auto-degradation of collagen matrices can occur in resin-infiltrated dentin, but may be prevented by the application of a synthetic protease inhibitor, such as chlorhexidine.
Resumo:
The objective of this in vitro study was to evaluate demineralization around restorations. Class V preparations were made on the buccal and lingual surfaces of each tooth. TPH (Group 1), Fuji II LC (Group 2), Tetric (Group 3), Dyract (Group 4), GS 80 (Group 5) and Chelon Fil (Group 6) were randomly placed in equal numbers of teeth. The teeth were submitted to a pH-cycling model associated with a thermocycling model. Sections were made and the specimens were examined for the presence of demineralization under polarized light microscopy. Demineralization was significantly reduced with Chelon Fil (Group 6). Furthermore, a similar inhibitory effect on the development of demineralization was observed in Groups 2, 4 and 5.