Assessment of the flexural strength of two heat-curing acrylic resins for artificial eyes

Prosthetic eyes are artificial substitutes for the eyeball, made of heat-curing acrylic resin, serving to improve the esthetic appearance of the mutilated patient and his/her inclusion in society. The aim of this study was to assess the flexural strength of two heat-curing acrylic resins used for manufacturing prosthetic eyes. Thirty-six specimens measuring 64 x 10 x 3.3 mm were obtained and divided into four groups: acrylic resin for artificial sclera N1 (Artigos Odontológicos Clássico, São Paulo, SP, Brazil), heat-cure water technique (GI) and microwave-cured (GII); colorless acrylic resin for prosthetic eyes (Artigos Odontológicos Clássico, São Paulo, SP, Brazil), heat-cure water technique (GIII) and microwave-cured (GIV). Mechanical tests using three point loads were performed in a test machine (EMIC, São José dos Pinhais, PR, Brazil). The analysis of variance and the Tukey test were used to identify significant differences (p < 0.01). Groups GII and GIV presented, respectively, the highest (98.70 ± 11.90 MPa) and lowest means (71.07 ± 8.93 MPa), with a statistically significant difference. The cure method used for the prosthetic eye resins did not interfere in their flexural strength. It was concluded that all the resins assessed presented sufficient flexural strength values to be recommended for the manufacture of prosthetic eyes.

Impact strength of denture base and reline acrylic resins subjected to long-term water immersion

Water may influence the mechanical properties of the acrylic resins. Thus, the effect of water storage on the impact strength (IS) of one denture base (Lucitone 550 - L) and four reline resins (Tokuyama Rebase II - T; UfiGel Hard - U; Kooliner - K; New Truliner - NT) was evaluated. Bars of L were made (60 x 6 x 2 mm) and relined (2 mm) with T, U, K, NT and L. Intact specimens of each material (60 x 6 x 4 mm) were also fabricated for comparative purposes. Specimens were submitted to Charpy impact tests without water storage (control) and after immersion in water for 7, 90 and 180 days. Data (kJ/m 2) analyzed by two-way ANOVA and Tukey's test (p=0.05) revealed that after 90 days, U exhibited an increase in the IS (0.93) compared to 7 days (0.58). K (1.48) and L/K (7.21) exhibited a decrease at the 7-day period (1.01 and 3.23, respectively). NT (0.60) showed an increase in the IS after 180 days (1.52), whereas L/ NT (7.70) showed a decrease (3.17). Water immersion improved the IS of U and NT, and decreased the IS of K, L/K, and L/NT. Water may affect differently the IS of acrylic resins and, consequently, the resistance to fracture of relined denture bases.

Impact strength of denture base and reline acrylic resins: An in vitro study

This study evaluated the impact strength of a denture base resin (Lucitone 550-L) and four reline resins (Tokuyama Rebase II-T; Ufi Gel Hard-U; New Truliner-NT, and Kooliner-K), both intact and in a reline combination (L/L, L/T, L/U, L/NT, and L/K). For each group (n = 20), half of the specimens were thermocycled before testing. Charpy tests were performed, and the impact strengths were calculated. Data were analyzed by two-way analyses of variance and Tukey's test (p = 0.05). For the intact groups, mean impact strength values for L (1.65 and 1.50) were significantly higher than those of the reline resins (0.38-1.17). For the relined groups, the highest mean impact strength values were produced by L/T (5.76 and 5.12), L/NT (6.20 and 6.03), and L/K (5.60 and 5.31) and the lowest by L/U (0.76 and 0.78). There were no significant differences between L and L/L. Thermocycling reduced the impact strength of T (from 0.73 to 0.38) and L/L (from 1.82 to 1.56). © The Author(s) 2012.

Effect of different disinfectants on the microhardness and roughness of acrylic resins for ocular prosthesis

Background: Ocular prosthesis materials should have specific properties for their indication and durability; therefore, it is important to investigate their physical behaviour when affected by several disinfectants. Objectives: This study evaluated the influence of different disinfecting solutions on the microhardness and surface roughness of acrylic resins for ocular prosthesis. Materials and Methods: Fifty samples simulating ocular prostheses were fabricated with N1 resin and colourless resin and divided (n = 10) according to the disinfectant used: neutral soap, Opti-free, Efferdent, 1% hypochlorite (HYC) and 4% chlorhexidine (CHX). Samples were stored in saline solution at 37°C and disinfected during 120 days. Both microhardness and roughness were investigated before, after 60 days and 120 days of disinfection and storage. Microhardness was measured using a microhardner and the roughness with a roughness device. Results: N1 resin showed lower microhardness when compared with colourless resin (p < 0.05). HYC and CHX groups exhibited the highest change of microhardness and roughness values (p < 0.05). An increase in roughness and reduction in microhardness of ocular acrylic resins were observed after both periods of disinfection and storage (p < 0.05). Conclusion: Both disinfection/storage periods affected the microhardness and roughness values of the samples. © 2012 The Gerodontology Society and John Wiley & Sons A/S.

Influence of plaster drying on the amount of residual monomer in heat-cured acrylic resins

Aim: To evaluate the influence of plaster condition, dry or not, on the amount of residual monomer in heat-cured acrylic resin. Methods: Thirty acrylic resin specimens (65×10×3 mm) were fabricated and randomly assigned to 5 groups (n=6). The evaluated resins were heat-cured acrylic resins by conventional or microwave polymerization techniques and the plaster was previously dried in microwave oven in two groups. Each specimen was individually immersed in a test tube containing methanol (7 days) for surface analysis. In the groups for which internal monomer was evaluated, the specimens were fragmented and the small fragments were weighed prior to immersion in methanol. The analysis was made by high performance liquid chromatography (HPLC). Data were analyzed by ANOVA and Tukey test (p<5%) Results: showed statistical differences among the groups. Conclusions: The previous plaster drying influenced the residual monomer amount showing a decrease of these levels.

Effect of intrinsic nanoparticle pigmentation on the color stability of denture base acrylic resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of nanoparticles on color stability, microhardness, and flexural strength of acrylic resins specific for ocular prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Metabolism of L929 cells after contact with acrylic resins. Part 1: Acrylic denture base resins

The purpose of this study was to evaluate the effectiveness of complementary heat treatment and water storage in reducing cytotoxicity of acrylic resins denture bases used in Brazil by the MTT assay. Material and Methods: First, nine specimens were fabricated from metal matrix in the form of discs with 14 mm in diameter and 1.2 mm of thick. Immediately after making, 24 or 48 hours after storage in distilled water, the samples of heat-polymerized resins were divided into 3 groups (n = 3) according to the type of thermal treatment: Group 1: samples were individually exposed to microwave energy (500 W for 3 minutes); Group 2: samples were immersed in water at 550 C for 60 minutes; Group 3: samples did not receive heat treatment. To prepare the extracts, 3 samples of each group were placed into vials containing 3 mL of culture medium and stored at 37°C for 24 hours. L929 cells were used and the MTT assay was performed to analyze the cellular metabolism. Two-factor analysis of variance was used to detect significant among groups at 5% significance. Results: After statistical analysis, the materials were classified according to the cytotoxic effect: non-cytotoxic, slightly cytotoxic; moderately cytotoxic; and strongly cytotoxic. The results showed that the resins ranged from moderately cytotoxic to non-cytotoxic, but no statistically significant difference among experimental groups. Furthermore, the water storage and thermal treatments reduced the cytotoxicity of the resins. Conclusions: It was concluded that the resins studied are potentially toxic and that treatments can decrease their cytotoxicity.

Chromatic stability of acrylic resins of artificial eyes submitted to the accelerated aging and polishing

Esthetics and durability of materials used to fabricate artificial eyes has been an important issue since artificial eyes are essential to restore esthetics and function, protect the remaining tissues and help with patients' psychological therapy. However, these materials are submitted to degrading effects of environmental agents on the physical properties of the acrylic resin. OBJECTIVE: This study assessed the color stability of acrylic resins used to fabricate sclera in three basic shades (N1, N2 and N3) when subjected to accelerated aging, mechanical and chemical polishing. MATERIAL AND METHODS: Specimens of each resin were fabricated and submitted to mechanical and chemical polishing. Chromatic analysis was performed before and after accelerated aging through ultraviolet reflection spectrophotometry. RESULTS: All specimens revealed color alteration following polishing and accelerated aging. The resins presented statistically significant chromatic alteration (p<0.01) between the periods of 252 and 1008 h. CONCLUSIONS: Both polishing methods presented no significant difference between the values of color derivatives of resins.

Evaluation of the Bond Strength of Denture Base Resins to Acrylic Resin Teeth: Effect of Thermocycling

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Unrestricted linear dimensional changes of two hard chairside reline resins and one heat-curing acrylic resin

The selection and use of hard chairside reline resins must be made with regard to dimensional stability, which will influence the accuracy of fit of the denture base. This study compared the dimensional change of two hard chairside reline resins (Duraliner II and Kooliner) and one heat-curing denture base resin (Lucitone 550). A stainless steel mold with reference dimensions (AB, CD) was used to obtain the samples. The materials were processed according to the manufacturer's recommendations. Measurements of the dimensions were made after processing and after the samples had been stored in distilled water at 37° C for eight different periods of time. The data were recorded and then analyzed with analysis of variance. All materials showed shrinkage immediately after processing (p < 0.05). The only resin that exhibited shrinkage after 60 days of storage in water was Duraliner II; these changes could be clinically significant in regard of tissue fit.

Effect of a post-polymerization treatments on the flexural strength and vickers hardness of reline and acrylic denture base resins

This study evaluated the effect of water-bath and microwave post-polymerization treatments on the flexural strength and Vickers hardness of four autopolymerizing reline resins (Duraliner II-D, Kooliner-K, Tokuso Rebase Fast-TR and Ufi Gel Hard C-UGH) and one heat-polymerized acrylic resin (Lucitone 550-L), processed using two polymerization cycles (short cycle - 90 minutes at 73°C and 100°C for 30 minutes; and long cycle - 9 hours at 71°C). For each material, thirty specimens (64 x 10 x 3.3 mm) were made and divided into 3 groups (n=10). Specimens were tested after: processing (control group); water-bath at 55°C for 10 minutes (reline materials) or 60 minutes (L); and microwave irradiation. Flexural strength tests were performed at a crosshead speed of 5 mm/min using a three-point bending device with a span of 50 mm. The flexural strengths values were calculated in MPa. One fragment of each specimen was submitted to Vickers hardness test. Data were analyzed by 2-way ANOVA followed by Tukey's HSD test (α=0.05). L microwaved specimens (short cycle) exhibited significantly higher flexural strength means than its respective control group (p<0.05). Water-bath promoted a significant increase (p<0.05) in flexural strength of K and L (long cycle). The hardness of the tested materials was not influenced by the post-polymerization treatments. Post-polymerization treatments could be used to improve the flexural strength of some materials tested.

Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins

This study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (mTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artifcial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm 2 were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4°C and 60°C). mTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (a=0.05). There was no statisti-caly signifcant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean mTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The mTBS of Biotone artifcial teeth to the denture base acrylic resins was not infuenced by the polymer type, surface treatment or thermocycling.

Bond strength between acrylic resin and maxillofacial silicone

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond strength of denture teeth to acrylic resin: effect of thermocycling and polymerisation methods

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)