Measurement of Interfacial Porosity at the Acrylic Resin/Denture Tooth Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of an acrylic resin combined with an antimicrobial polymer on biofilm formation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of Candida albicans adhesion and biofilm formation on a denture base acrylic resin containing silver nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The occurrence of porosity in reline acrylic resins. Effect of microwave disinfection

Microwave energy has proved to be an effective method for disinfecting acrylic dentures. However, the effect of microwave heating on the porosity of autopolymerising denture reline resins has not been investigated.The purpose of the study was to determine the effect of microwave disinfection on the porosity of autopolymerised denture reline materials (Kooliner-K, New Truliner-NT, Tokuso Rebase Fast-TR and Ufi Gel Hard-UGH) and a conventional heat-polymerised denture base resin (Lucitone 550-L).Specimens (10 mm x 20 mm x 1 mm) were obtained from the impression surface of the palatal mucosa in a single person and divided into four groups (n = 5). The porosity was evaluated after polymerisation (C1), after two cycles of microwave disinfection (MW2), after seven cycles of microwave disinfection (MW7) and after 7 days storage in water at 37 degrees C (C2). Specimens from group MW7 were exposed to microwave disinfection daily being stored in water at 37 degrees C between exposures. All the replicas were sputter coated with gold and micrographs/digital images were taken of each replica using scanning electron microscopy at magnification x 100. The SEM micrographs were then examined using an image analyser to determine the number of pores. Comparison between materials and groups were made using Kruskal-Wallis tests.MW7 resulted in a significant increase in the number from the pores of material K, but decreased in number in reline material TR and UGH reline resin. The number of pores in materials NT and L remained unaffected following microwave disinfection.Differences in the porosity amongst the materials and for different experimental conditions were observed following microwave disinfection.

Effect of reline material and denture base surface treatment on the impact strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of incorporation of 2-tert-butylaminoethyl methacrylate on flexural strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Clinical evaluation of low-level laser therapy and fluoride varnish for treating cervical dentinal hypersensitivity

The aim of this study was to evaluate in vivo the use of low-level galium-aluminium-arsenide (GaAlAs) (BDP 600) laser and sodium fluoride varnish (Duraphat((R))) in the treatment of cervical dentine hypersensitivity. Twelve patients, with at least two sensitive teeth were selected. A total of 60 teeth were included in the trial. Prior to desensitizing treatment, dentine hypersensitivity was assessed by a thermal stimulus and patients' response to the examination was considered to be a control. The GaAlAs laser (15 mW, 4 J/cm(2)) was irradiated on contact mode and fluoride varnish was applied at cervical region. The efficiency of the treatments was assessed at three examination periods: immediately after first application, 15 and 30 days after the first application. The degree of sensitivity was determined following predefined criteria. Data were submitted to analysis and no statistically significant difference was observed between fluoride varnish and laser. Considering the treatments separately, there was no significant difference for the fluoride varnish at the three examination periods, and for laser therapy, significant difference (P < 0.05) was found solely between the values obtained before the treatment and 30 days after the first application. It may be concluded that both treatments may be effective in decreasing cervical dentinal hypersensitivity. Moreover, the low-level GaAlAs laser showed improved results for treating teeth with higher degree of sensitivity.

The Interaction Between N-Isopropylacrylamide-Acrylic Acid-Ethyl Methacrylate Thermosensitive Polymers and Cationic Surfactants

The interaction between cationic surfactants and isopropylacrylamide-acrylic acid-ethyl methacrylate (IPA:AA:EMA) terpolymers has been investigated using steady-state fluorescence and spectrophotometric measurements to assess the effect of the polymer composition on the aggregation process and terpolymers' thermosensitivities. Micropolarity studies using pyrene show that the interaction of cationic surfactants with IPA:AA:EMA terpolymers occurs at surfactant concentrations much smaller than that observed for the pure surfactant in aqueous solution. The critical aggregation concentration (CAC) values decrease with both the hydrocarbon length of the surfactant and the content of ethyl methacrylate. These results were interpreted as a manifestation of the increasing contribution of attractive hydrophobic and electrostatic forces between negatively charged polymer chains and positively charged surfactant molecules. The increase of ethyl methacrylate in the copolymers lowers the CAC due to the larger hydrophobic character of the polymer backbone. The cloud point determination reveals that the lower critical solution temperatures (LCST) depend strongly on the copolymer composition and surfactant nature. The binding of surfactants molecules to the polymer chain screens the electrostatic repulsion between the carboxylic groups inducing a conformational transition and the dehydration of the polymer chain.

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resin

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resinObjectives: The purpose of this study was to evaluate the flexural strength and Vickers hardness of a microwave energy heat-cured acrylic resin by adding different concentrations of silane surface-treated nanoparticle silica.Methods: Acrylic resin specimens with dimensions of 65 x 10 x 2.5 mm were formed and divided into five experimental groups (n = 10) according to the silica concentration added to the acrylic resin mass (weight %) prior to polymerisation : G1, without silica; G2, 0.1% silica; G3, 0.5% silica; G4, 1.0% silica; and G5, 5.0% silica. The specimens were submitted to a three-point flexural strength test and to the Vickers hardness test (HVN). The data obtained were statistically analysed by ANOVA and the Tukey test (alpha = 0.05).Results: Regarding flexural strength, G5 differed from the other experimental groups (G1, G2, G3 and G4) presenting the lowest mean, while G4 presented a significantly higher mean, with the exception of group G3. Regarding Vickers hardness, a decrease in values was observed, in which G1 presented the highest hardness compared with the other experimental groups.Conclusion: Incorporating surface-treated silica resulted in direct benefits in the flexural strength of the acrylic resin activated by microwave energy; however, similar results were not achieved for hardness.

A Strain Gauge Analysis of Microstrain Induced by Various Splinting Methods and Acrylic Resin Types for Implant Impressions

Purpose: The aim of this study was to investigate the level of microstrain that is exerted during polymerization of acrylic resins used for splinting during implant impressions. Material and Methods: Two acrylic resins (GC Pattern Resin, Duralay II) and square transfer coping splinting methods were evaluated by means of strain gauge analysis. Two implants were embedded in a polyurethane block, and the abutments were positioned. Sixty specimens were prepared using two square transfer Copings that were rigidly connected to each other using the acrylic resins. The specimens were randomly divided into three groups of 20 each for the splinting methods: Method 1 was a one-piece method; in method 2, the splint was separated and reconnected after 17 minutes; and in method 3, the splint was separated and reconnected after 24 hours. In each group, half the specimens were splinted with GC Pattern Resin and the other half were splinted with Duralay II. Three microstrain measurements were performed by four strain gauges placed on the upper surface of the polyurethane blocks at 5 hours after resin polymerization for all groups. The data were analyzed statistically. Results: Both resin type and splinting method significantly affected microstrain. interaction terms were also significant. Method 1 in combination with Duralay II produced significantly higher microstrain (1,962.1 mu epsilon) than the other methods with this material (method 2: 241.1 mu epsilon; method 3: 181.5 mu epsilon). No significant difference was found between splinting methods in combination with GC Pattern Resin (method 1: 173.8 mu epsilon; method 2: 112.6 mu epsilon; method 3: 105.4 mu epsilon). Conclusions: Because of the high microstrain generated, Duralay II should not be used for one-piece acrylic resin splinting, and separation and reconnection are suggested. For GC Pattern Resin, variations in splinting methods did not significantly affect the microstrain created. Int J Oral Maxillofac Implants 2012;27:341-345

Application of Nonisothermal Cure Kinetics to the Interaction of Poly(ethylene terephthalate) with Alkyd Resin Varnish

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Non-isothermal decomposition kinetics of the interaction of poly(ethylene terephthalate) with alkyd varnish

The recycling of soft drink bottles poly(ethylene terephthalate) (PET) has been used as an additive in varnish containing alkyd resin. The PET, called to recycled PET (PET-R), was added to the varnish in increasing amounts. Samples of varnish containing PET-R (VPET-R) were used as a film onto slides and its thermal properties were evaluated using thermogravimetry (TG). Throughout the visual analysis and thermal behavior of VPET-R it is possible to identify that the maximum amount of PET-R added to the varnish without changing in the film properties was 2%.The kinetic parameters, such as activation energy (E) and the pre-exponential factor (A) were calculated by the isoconversional Flynn-Wall-Ozawa method for the samples containing 0.5 to 2.0% PET-R. A decrease in the values of E was verified for lower amounts of PET-R for the thermal decomposition reaction. A kinetic compensation effect (KCE) represented by the lnA=-13.42+0.23E equation was observed for all samples. The most suitable kinetic model to describe this decomposition process is the autocatalytic Sestak-Berggren, being the model applied to heterogeneous systems.

Effect of an experimental 4% titanium tetrafluoride varnish on dental erosion by a soft drink

Objectives: This in vitro study assessed the effect of an experimental 4%TiF4 varnish on enamel erosion.Methods: Sixty bovine enamel blocks were randomly allocated to each type of varnish:Duraphat((R)) -D (NaF, 2.26%F), Duofluorid((R))-F(NaF, 2.71% F), TiF4-T(2.45%F) and no-fluoride-P. After application of the varnishes, the blocks were subjected to six sequential pH cycles (cola drink for 10 min and artificial saliva for 50 min, each) per day, during 4 days. After the pH cycles, the blocks were maintained in artificial saliva for 18 h. Enamel alterations were determined in the 2nd and 4th days, using profilometry (wear) and microhardness (%SMHC) tests. Data were tested using ANOVA and Tukey's tests (p < 0.05).Results: the mean %SMHC (+/- S.D.) at the 2nd and 4th day was, respectively, D (-77.26 +/- 5.04(a) and -88.59 +/- 5.11(A)), F (-76.79 +/- 7.82(a) and -88.78 +/- 6.10(A)), T(-88.28 +/- 3.19(b) and -92.04 +/- 2.54(A,B)) and P (-87.96 +/- 2.23(b) and -94.15 +/- 1.14(B)). The mean wear (mu m +/- S.D.) at the 2nd and 4th day was, respectively, D (3.16 +/- 0.32(a) and 7.56 +/- 0.90(A)), F(3.35 +/- 0.78(a,b) and 7.92 +/- 0.98(A)), T (3.81 +/- 0.43(b) and 7.69 +/- 0.76(A)) and P (3.43 +/- 1.13(a,b) and 7.31 +/- 0.53(A)).Conclusions: the NaF varnishes reduced the softening, but had no effect on the reduction of the wear. The TiF4 varnish was not able to reduce the softening and wear. (C) 2007 Elsevier Ltd. All rights reserved.